Abstract
We report on the temperature-dependent contact resistivity and high-temperature stability of the annealed Ni/Au ohmic contacts to p-type GaN in air. As the measure temperature increases from 25°C to 390°C, both the specific contact resistivity (ρ c) and sheet resistance (R sh) decrease by factors ∼10, contributing to the 10-fold increase in current at 390°C compared with that at 25°C. It was also observed that the ρ c was further reduced by 36%, i.e., from 2.2 × 10−3 Ω cm2 to 1.4 × 10−3 Ω cm2, during the 48-h high-temperature stability test at 450°C in air, showing excellent stability of the contacts. An increase in ρ c was observed after the contacts were subjected to 500°C in air. Higher temperature stress led to a significant increase in ρ c. The contacts show rectifying I–V characteristics after being subjected to 700°C for 1 h. The degradation mechanics were analyzed with the assistance of transmission electron microscopy and energy dispersive x-ray spectroscopy.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
P.G. Neudeck, R.S. Okojie, and L.-Y. Chen, Proc. IEEE 90, 1065 (2002).
H.A. Mantooth, M.M. Mojarradi, and R.W. Johnson, IEEE Power Electron. Soc. Newslett. 18, 9 (2006).
R.W. Johnson, J.L. Evans, P. Jacobsen, J.R. Thompson, and M. Christopher, IEEE Trans. Electron. Packag. Manuf. 27, 164 (2004).
W.J. Pulliam, P.M. Russler, and R.S. Fielder, Proc. SPIE 4578, 229 (2002).
T. George, K.-A. Son, R.A. Powers, L.Y. Del Castillo, and R. Okojie, 2005 IEEE Sensors (2005).
A. Luque and A. MartíSol. Energy Mater. Sol. Cells 58, 147 (1999).
Y. Yang, W. Yang, W. Tang, and C. Sun, Appl. Phys. Lett. 103, 083902 (2013).
M. Hou and D.G. Senesky, Appl. Phys. Lett. 105, 081905 (2014).
F. Lin, B. Shen, S. Huang, F.J. Xu, L. Lu, J. Song, F.H. Mei, N. Ma, Z.X. Qin, and G.Y. Zhang, J. Appl. Phys. 105, 093702 (2009).
F. Iucolano, F. Roccaforte, A. Alberti, C. Bongiorno, S.D. Franco, and V. Raineri, J. Appl. Phys. 100, 123706 (2006).
J.K. Sheu, Y.K. Su, G.C. Chi, P.L. Koh, M.J. Jou, C.M. Chang, C.C. Liu, and W.C. Hung, Appl. Phys. Lett. 74, 2340 (1999).
J.-K. Ho, C.-S. Jong, C.C. Chiu, C.-N. Huang, C.-Y. Chen, and K.-K. Shih, Appl. Phys. Lett. 74, 1275 (1999).
J.-K. Ho, C.-S. Jong, C.C. Chiu, C.-N. Huang, K.-K. Shih, L.-C. Chen, F.-R. Chen, and J.-J. Kai, J. Appl. Phys. 86, 4491 (1999).
L.-C. Chen, J.-K. Ho, C.-S. Jong, C.C. Chiu, K.-K. Shih, F.-R. Chen, J.-J. Kai, and L. Chang, Appl. Phys. Lett. 76, 3703 (2000).
S. Zhao, Y. Shi, H. Li, and Q. He, Nucl. Instrum. Methods Phys. Res. Sect. B 268, 1435 (2010).
H. Omiya, F.A. Ponce, H. Marui, S. Tanaka, and T. Mukai, Appl. Phys. Lett. 85, 6143 (2004).
G.K. Reeves and H.B. Harrison, IEEE Electron Device Lett. 3, 111 (1982).
D. Steigerwald, S. Rudaz, H. Liu, R.S. Kern, W. Götz, and R. Fletcher, JOM 49, 18 (1997).
D. Sawdai, D. Pavlidis, and D. Cui, IEEE Trans. Electron Devices 46, 1302 (1999).
I. Daumiller, C. Kirchner, M. Kamp, K.J. Ebeling, and E. Kohn, IEEE Electron Device Lett. 20, 448 (1999).
Acknowledgements
The work presented herein was funded in part by the Advanced Research Projects Agency-Energy (ARPA-E), U.S. Department of Energy, under award number DE-AR0000470.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Zhao, S., McFavilen, H., Wang, S. et al. Temperature Dependence and High-Temperature Stability of the Annealed Ni/Au Ohmic Contact to p-Type GaN in Air. J. Electron. Mater. 45, 2087–2091 (2016). https://doi.org/10.1007/s11664-015-4278-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-015-4278-3