Abstract
New enthalpy measurements above 2000 K have resulted in a complete reassessment and revision of the high temperature thermodynamic properties of hafnium. Values have been assessed to 4900 K and include a selected enthalpy of sublimation at 298.15 K of 621 ± 5 kJ/mol and a derived boiling point of 4850 K at one atmosphere pressure. A comparison is given between selected properties of the Group 4 elements to consider periodic trends.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
Previous reviews on hafnium were by Hultgren et al.,[1] Spencer,[2] Gurvich et al.[3] and JANAF[4] whilst Onufriev et al.[5] reviewed values for the alpha phase. A further review is justified by including new drop calorimetry measurements above 2000 K determined by Rösner-Kuhn et al.[6] so that definite values can be calculated for the thermodynamic properties of the beta and liquid phases where previously only estimated values were available. As with zirconium, one of the major problems in carrying out experiments on hafnium is the avoidance of oxidation which could explain the rejection of a marked number of transition and melting points determinations as given in Tables 9 and 11 and the significant departure of specific heat and enthalpy values from selected values as given in Tables 12 and 13. A further complication for hafnium is that nearly all measurements were carried out on samples containing zirconium. Specific heat and enthalpy values were corrected using the Kopp-Neumann Rule as described in “Correction of Specific Heat and Enthalpy Values for Zirconium Content” section but this does introduce an increased uncertainty since this very often required an extrapolation of the zirconium values beyond their limits of phase stability.
From the evaluations in Tables 8 and 10, 2016 ± 20 K is selected for the transformation from the hexagonal close-packed alpha phase to the body-centred cubic beta phase and 2502 ± 20 K for the melting point. Wherever possible values have been corrected to the ITS-90 temperature scale[7,8] and to the currently accepted atomic weight of 178.49 ± 0.02.[9]
Alpha Phase
Roberts[10] selects 0.128 K as the superconducting temperature but there does not appear to be any specific heat measurements in the superconducting region. Therefore only the normal state is considered with the following values obtained for the electronic coefficient (γ) and the limiting Debye temperature (ΘD) as given in Table 1.
The selected values were combined with the specific heat measurements of Westrum[16] (5.8-349 K) to give values covering the range up to 298.15 K as given in Table 17. Additional specific heat determinations in the low temperature region by Cristescu and Simon[17] (13-210 K), Wolcott[11,12] (1.2-20 K) and by Burk et al.[18] (10-200 K) are compared with the selected values in Table 12.
In the high temperature region of the alpha phase, enthalpy measurements of Hawkins et al.[19] (339-1348 K) and Kats et al.[20] (1220-2001 K in the alpha phase) agree closely and also show a natural continuity from the low temperature data. The measurements of Hawkins et al. had already been corrected for zirconium content and were therefore only corrected for temperature scale (from IPTS-48 to ITS-90) but although the measurements of Kats et al. were on samples containing 0.78 wt.% zirconium no corrections were applied because of the very large extrapolation which would have been required for the alpha zirconium values. The combined values were fitted to the following equation with an overall accuracy of ±173 J/mol (1.33%):
The high temperature thermodynamic properties of all of the condensed phases are given in Table 19. The deviations of other specific heat and enthalpy alpha phase measurements from the selected values are given in Tables 12 and 13 respectively except for the specific heat measurements of Rumyantsev et al.[21] (1000-1900 K) which were given only in the form of a small graph.
Beta Phase
New drop calorimetry enthalpy measurements of Rösner-Kuhn et al.[6] (2096-2455 K in the beta phase) were corrected for 3 wt.% zirconium content using the values for beta zirconium selected by Arblaster[22] and fitted to the following equation with an overall accuracy of ±945 J/mol (1.37%):
The derived enthalpy of transition is 5040 ± 960 J/mol which can be compared with original experimental values given in Table 2. The derived specific heat is 37.15 ± 1.45 J/mol K.
The highly discrepant value obtained by Kats et al. is the main reason why their beta phase measurements were not included in the evaluation. The deviations of other specific heat and enthalpy beta phase measurements from the selected values are given in Tables 12 and 13 respectively.
Liquid
New drop calorimetry enthalpy measurements of Rösner-Kuhn et al.[6] (2339-2988 K in the liquid phase) were corrected for 3 wt.% zirconium content using the values for liquid zirconium selected by Arblaster[22] and fitted to the following equation with an overall accuracy of ±1691 J/mol (1.59%):
The derived enthalpy of fusion is 19885 ± 1937 J/mol which can be compared with original experimental values given in Table 3. The derived entropy of fusion is 7.95 ± 0.77 J/mol K and the derived specific heat is 36.26 ± 1.76 J/mol K
In addition, from entropy trends, Chekhovskoi and Kats[30] gives an equation which is equivalent to an entropy of fusion of 10.23 J/mol K for hafnium, equivalent to an enthalpy of fusion of 25,600 J/mol whilst Rösner-Kuhn et al.[31] estimates an entropy of fusion of 8.30 J/mol K equivalent to an enthalpy of fusion of 20,770 J/mol. The deviations of other specific heat and enthalpy liquid phase measurements from the selected values are given in Tables 12 and 13 respectively.
Gas Phase
Enthalpy of Sublimation
For values given in Table 5 in the form of the Clausius-Clapeyron equation a “pseudo” Third Law value was calculated by evaluating the enthalpy of sublimation at the temperature extremes and averaging. The values obtained give a reasonable estimate compared to the values which would have been obtained if all of the data had been available. Because of a lack of detail as to what temperature scales were used in the measurements then no attempt was made to correct the values to ITS-90 from would be contemporary temperature scales.
Because of the close agreement between derived Third Law enthalpies of sublimation the measurements of Kibler et al.[39], Ackermann and Rauh[26] and Koch et al.[42] were accepted and averaged, with the assigned accuracy taking into account differences between ΔH(II) and ΔH(III) values. Because the other measurements showed poor agreement between ΔH(II) and ΔH(III) values they were rejected.
Vapour Pressure
The vapour pressure curve for the alpha phase as given in Table 6 was evaluated from free energy functions for the solid and the gas at 25 K intervals from 1400 to 2000 K and the transition temperature. For the beta phase the vapour pressure curve was evaluated at 25 K intervals from 2025 to 2500 K and the transition temperature and melting point and for the liquid at 50 K intervals from 2550 to 4900 K and the melting point.
Selection of the Transition Temperature and the Melting Point
Transition temperatures and melting points were corrected for atomic percent zirconium content based on the hafnium-zirconium binary system.[43] Separate correction values obtained for the solidus and liquidus equations were averaged as were values obtained for the alpha-beta and beta-alpha transition equations. Because of the provisional nature of the phase diagram, samples with high zirconium contents requiring large temperature corrections were not included in evaluating the selected values. Also because of a general lack of knowledge as to what temperature scales were used then only the selected values were corrected to ITS-90. Transition temperatures included in the evaluation are given in Table 8 and those not included in Table 9. Melting points included in the evaluation are included in Table 10 and those not included in Table 11.
Correction of Specific Heat and Enthalpy Values for Zirconium Content
Values for specific heat are reduced to J/kg K and for enthalpy to J/kg. Using the Kopp-Neumann Rule;
where X is the mass fraction of zirconium and C°p and (H°T−H°298.15) for zirconium are evaluated at the same experimental temperature as that of the alloy
A Comparison Between the Present Evaluation and Previous Reviews
The boiling point calculated from the selected values of Gurvich et al.[3] at 4973 K at one atmosphere pressure is 123 K higher than the presently selected value of 4850 K whilst the boiling point given by JANAF[4] as 4964 K at one bar pressure is 119 K higher than the selected value of 4845 K. Since enthalpies of sublimation and the calculated free energy functions of the gas phase are similar in all three reviews then the differences are due to differences between the estimated values for the condensed phases in the previous reviews compared to the experimental values used in the present review. In the case of Gurvich et al. they estimated an enthalpy of fusion 6 kJ/mol higher than the present value and a specific heat for the liquid 8 J/mol K higher whilst JANAF estimated an enthalpy of fusion 9 kJ/mol higher although the selected specific heat of the liquid is only 1.5 J/mol K higher. However the result is that at 4900 K the free energy function of the liquid phase from the evaluation of Gurvich et al. is 2.55 J/mol K higher than the present value and from the evaluation of JANAF 3.33 J/mol K higher. The effect on the net free energy function is to lower the vapour pressure curve in both cases and lead to higher boiling points. It is therefore suggested that the much lower boiling point obtained in the present review is due to the use of actual experimental values.
A Comparison Between Group 4 Element Properties
The present evaluation for hafnium is combined with reviews on titanium by Desai[89] and on zirconium by Arblaster[22] and are summarised in Table 14. Since the three elements have similar electronic structures with the same sequencing of electrons in the outermost shells: Ti 3 s2 (10) 4 s2 (2); Zr 4 s2 (10) 5 s2 (2); Hf 5 s2 (10) 6 s2 (2) then this would suggest that the properties of hafnium could have been predicted. However this does not appear to be the case. The crystallographic and melting transition properties of titanium and zirconium can generally be considered to be similar but the values for hafnium show distinct differences mainly due to the marked increase in the stability of the hexagonal close-packed alpha phase. However in the case of the coherency of the condensed phases the enthalpy of sublimation and boiling points of zirconium and hafnium are very close whilst the values for titanium are different.
References
R. Hultgren, P.D. Desai, D.T. Hawkins, M. Gleiser, K.K. Kelley, and D.D. Wagman, Selected Values of the Thermodynamic Properties of the Elements, American Society for Metals, Metals Park, OH, 1973
P.J. Spencer, Hafnium: Physico-Chemical Properties of It’s Compounds and Alloys. I. Thermochemical Properties, Atomic Energy Review Special Issue No 8, K.L. Komarek, Ed., International Atomic Energy Agency, Vienna, 1981, p 9-53
L.V. Gurvich, I.V. Veits, V.A. Medvedev, G.A. Bergman, V.S. Yungman, G.A. Khachkuruzov, V.S. Yorish, O.V. Dorofeeva, E.L. Osina, P.I. Tolmach, I.N. Przheval’skii, I. Nazarenko, N.M. Aristova, E.A. Shenyavskaya, L.N. Gorokhov, A.L. Rogatskii, M.E. Emifov, V.Y. Leonidov, Y.G. Khait, A.G. Efimova, S.E. Tomberg, A.V. Gusarov, N.E. Khandamirova, G.N. Yurkov, L.R. Fokin, L.F. Kuratova, and A.D. Gol’dshtein in V.P. Glushko, L.V. Gurvich, G.A. Bergman, I.V. Veits, V.A. Medvedev, G.A. Khachkuruzov, V.S. Yungman (Ed), “Termodinamicheskie Svoistva Individual’nykh Veshchestv (Thermodynamic Properties of Individual Substances)”, Vol. 4, Nauka, Moscow, 1982
M.W. Chase Jr., NIST-JANAF Thermochemical Tables, 4h Edn, J. Phys. Chem. Ref. Data, Monograph No. 9, 1998
S.V. Onufriev, V.A. Petukhov, V.R. Pesochin, and V.D. Tarasov, The Thermophysical Properties of Hafnium in the Temperature Range from 293 to 2000 K, Teplofiz. Vys. Temp., 2008, 46, p 230-238 [High. Temp., 2008, 46, p 203-211]
M. Rösner-Kuhn, K. Drewes, H. Franz, and M.G. Frohberg, Enthalpy Measurements of the Solid High-Temperature β-Phase and the Liquid Phase of Hafnium (3 wt.% Zr) by Levitation Drop Calorimetry, Mater. Sci. Eng., 2001, A308, p 60-64
T.B. Douglas, Conversion of Existing Calorimetrically Determined Thermodynamic Properties to the Basis of the International Temperature Scale of 1968, J. Res. Nat. Bur. Stand., 1969, 73A, p 451-470
R.D. Weir and R.N. Golding, On the Conversion of Thermodynamic Properties to the Basis of the International Temperature Scale of 1990, J. Chem. Thermodyn., 1996, 28, p 261-276
M.E. Wieser, N. Holden, T.B. Coplen, J.K. Böhlke, M. Berglund, W.A. Brand, P. de Bièvre, M. Gröning, R.D. Loss, J. Meija, T. Hirata, T. Prohaska, R. Schoenberg, G. O’Connor, T. Walczyk, S. Yoneda, and X.-K. Zhu, Atomic Weights of the Elements 2011, Pure Appl. Chem., 2013, 85, p 1047-1078
B.W. Roberts, Survey of Superconductive Materials and Critical Evaluation of Selected Properties, J. Phys. Chem. Ref. Data, 1976, 5, p 581-821
N.M. Wolcott, The Atomic Heats of Titanium, Zirconium and Hafnium, Philos. Mag., 1957, 2, p 1246-1254
N.M. Wolcott, “The Specific Heat of Transition Metals”, Conference Physique des Basses Temperature. Paris, Sep 1955, Centre National de la Recherche Scientifique et UNESCO, Paris, 1956, p 286-289
G.D. Kneip, Jr., J.O. Betterton, Jr., and J.O. Scarbrough, Low Temperature Specific Heats of Titanium, Zirconium and Hafnium, Phys. Rev., 1963, 130, p 1687-1692
J.O. Betterton, Jr, and J.O. Scarbrough, Low-Temperature Specific Heats of Zr-Ti, Zr-Hf and Zr-Sc Alloys, Phys. Rev., 1968, 168, p 715-725
E.W. Collings and J.C. Ho, Magnetic-Susceptibility and Low-Temperature Specific-Heat Studies of Ti, Zr and Hf, Phys. Rev. B, 1971, 4, p 349-356
E.F. Westrum Jr., Appendix III : Heat Capacity and Thermodynamic Properties from 5 to 350 K, Thermodynamics and Kinetic Studies for a Refractory Materials Program, Air Force Materials Laboratory, Research and Technology Division, Air Force System Command, Wright-Patterson Air Force Base, OH, L.A. McClaine (Ed.), Rept. ASD-TDR-62-204, Part III, April 1964, p 189-196
S. Cristescu and F. Simon, Die Spezifischen Wärmen von Beryllium, Germanium und Hafnium bei tiefen Temperaturen, Z. Physik. Chem. B, 1934, 25, p 273-282
D.L. Burk, I. Esterman, and S.A. Friedberg, The Low Temperature Specific Heats of Titanium, Zirconium and Hafnium, Z. Physik. Chem., 1958, 16, p 183-193
D.T. Hawkins, M. Onillon, and R.L. Orr, High Temperature Heat Content of Hafnium, J. Chem. Eng. Data, 1963, 8, p 628-629
S.A. Kats, V.Y. Chekhovskoi, and M.D. Kovalenko, Thermophysical Properties of Zirconium and Hafnium at High Temperatures, Teplofiz. Vys. Temp., 1985, 23, p 395-397
A.V. Rumyantsev, I.N. Makarenko, and S.N. Banchila, Thermal, Electrical and Radiative Properties of Titanium, Zirconium and Hafnium in the Temperature Region 1000-2100 K, Inzh. Fiz. Zh. 1979, 36, p 581-587 [J. Eng. Phys. Thermophys, 1979, 36, p 377-381]
J.W. Arblaster, Thermodynamic Properties of Zirconium, Calphad, 2013, 43, p 32-39
M.M. Martynyuk, and V.I. Tsapkov, The Resistivity, Enthalpy and Phase Transitions of Titanium, Zirconium and Hafnium During Pulse Heating, Izv. Akad. Nauk SSSR, Metally, 1974, 2, 181-185 [Russ. Metall. Metally, 1974, 2, p 108-112]
V.E. Peletskii, and V.P. Druzhinin, Experimental Study of Some Physical Properties of Hafnium at High Temperatures, Teplofiz. Vys. Temp., 1971, 9, p 539-545 [High Temp. 1971, 9, p 490-495]
A. Cezairliyan and J.L. McClure, Temperature and Energy of α → β Transformation in Hafnium-3w/0 Zirconium, High Temp. High Press., 1976, 8, p 461-467
R.J. Ackermann and E.G. Rauh, The Thermodynamics and Vaporization of Thorium, Hafnium and Zirconium, J. Chem. Thermodyn., 1972, 4, p 521-532
P.-F. Paradis, T. Ishikawa, and S. Yoda, Non-Contact Measurements of the Thermophysical Properties of Hafnium-3 mass% Zirconium at High Temperatures, Int. J. Thermophys., 2003, 24, p 239-258
V.N. Korobenko, O.A. Polyakova, and A.I. Savvatimskii, Heat Capacity of Liquid Hafnium from the Melting Point to the Boiling Point at Atmospheric Pressure, Teplofiz. Vys. Temp. 2005, 43, 39-44 [High Temp. 2005, 43, p 38-44]
C. Cagran, T. Hüpf, B. Wilthan, and G. Pottlacher, Selected Thermophysical Properties of Hf-3%Zr from 2200 K to 3500 K Obtained by a Fast Pulse-Heating Technique, High Temp. High Press., 2008, 37, p 205-219
V.Ya. Chekhovskoi and S.A. Kats, Investigations of the Thermophysical Properties of Refractory Metals Near the Melting Point, High Temp-High Press., 1981, 13, p 611-616
M. Rösner-Kuhn, K. Drewes, H. Franz, and M.G. Frohberg, Calculation of the Entropy of Fusion for the Group IVb Metals Titanium, Zirconium and Hafnium by the Vacancy Theory, Z. Metallkd., 2000, 91, p 838-841
H.G. Kolsky, R.M. Gilmer, and P.W. Gilles, The Thermodynamic Properties of 54 Elements Considered as Ideal Monatomic Gases. U.S. Atomic Energy Commission Rept. LA 2110, 1957
P.J. Mohr, B.N. Taylor, and D.B. Newell, CODATA Recommendations of the Fundamental Physical Constants: 2010, Rev. Mod. Phys., 2012, 84, p 1527-1605
P.J. Mohr, B.N. Taylor, and D.B. Newell, CODATA Recommendations of the Fundamental Physical Constants: 2010, J. Phys. Chem. Ref. Data, 2012, 41, p 043109-1-043109-84
W.F. Meggers, and C.E. Moore, The First Spectrum of Hafnium (Hf I), Natl. Bur. Stand. Monogr., 1976, 153
J.F. Wyart, A Systematic Study of Even Configurations in the Neutral Atoms of the Platinum Group, Phys. Scripta, 1978, 18, p 87-95
L. Matsuoka and S. Hasegawa, Two-Color Resonance Ionization Spectroscopy of Rydberg States of Hafnium Atoms, Phys. Rev. A, 2006, 74, 062515 (8 pp)
M.B. Panish and L. Reif, Thermodynamics of the Vaporization of Hf and HfO2: Dissociation Energy of HfO, J. Chem. Phys., 1963, 38, p 253-256
G.M. Kibler, T.F. Lyon, M.J. Linevsky, and V.J. De Santis, Carbonization of Plastics and Refractory Materials Research. Vol. II : Refractory Materials, Air Force Materials Laboratory, Research and Technology Division, Air Force Systems Command, Wright-Patterson Air Force Base, OH, Technical Report WADD-TR-60-646, Part II, 1964, p 32-66
P.E. Blackburn, Vapor Pressures over Zirconium Carbide, Zirconium Diboride, Hafnium Carbide and Hafnium Diboride, Thermodynamics and Kinetic Studies for a Refractory Materials Program, Air Force Materials Laboratory, Research and Technology Division, Air Force Systems Command, Wright-Patterson Air Force Base, OH, L.A. McClaine (Ed.), Technical Report. ASD-TR-62-204, Part III, 1964, p 98-120
O.C. Trulson, P.O. Schissel, and H.W. Goldstein, Research on Physical and Chemical Principles Affecting High Temperature Materials for Rocket Nozzles, P.N. Walsh (Ed.), Final Report., Vol. 1, Appendix XII, AEC Accession No. 46956, Report No. NP15514, 1965
R.K. Koch, W.E. Anable, and R.A. Beall, “Vapor Pressures of Liquid Columbium (2740° to 3140°K) and Liquid Hafnium (2500° to 2810°K). U.S. Bur. Mines Rept. Invest. 7125, 1968
J.P. Abriata, J.C. Bolcich, and H.A. Peretti, The Hf-Zr (Hafnium-Zirconium) System, Bull. Alloy Phase Diag., 1982, 3, p 29-34
D.K. Deardorff and H. Kato, The Transformation Temperature of Hafnium, Trans. Met. Soc. AIME, 1959, 215, p 876-877
D.K. Deardorff and H. Kato, Discussion of the Constitution Diagram Tungsten-Hafnium, Trans. Met. Soc. AIME, 1963, 227, p 264-265
N.H. Krikorian and T.C. Wallace, The Effect of Oxygen and Nitrogen on the Hafnium α-β Transition, J. Electrochem. Soc., 1964, 111, p 1431-1433
C. Zwikker, Transitions in Zirconium and Hafnium, Physica, 1926, 6, p 361-365
P.J. Duwez, The Allotropic Transformation of Hafnium, J. Appl. Phys., 1951, 22, p 1174-1175
R.K. McGeary, Progress Report, Westinghouse Electric Corp. Bettis Atomic Power Division, Pittsburgh, Report No. WAPD-RM-92, L.S. Castleman, R.K. McGeary, Z.M. Shapiro, C.R. Simcoe, D.E. Thomas (Ed.), 1951
J.D. Fast, The Allotropic Transformation of Hafnium and a Tentative Equilibrium Diagram of the System Zirconium-Hafnium, J. Appl. Phys., 1952, 23, p 350-351
E.D. Gibson, B.A. Loomis, and O.N. Carlson, Thorium-Zirconium and Thorium-Hafnium Alloy Systems, Trans. ASM, 1958, 50, p 348-369
D.T. Peterson and D.J. Beernsten, The Uranium Hafnium Equilibrium System, Trans. ASM, 1960, 52, p 763-780
A. Taylor, N.J. Doyle, and B.J. Kagle, The Constitution Diagram of the Molybdenum—Hafnium Binary System, J. Less Common Met., 1961, 3, p 265-280
R.G. Ross and W. Hume-Rothery, High Temperature X-Ray Metallography, J. Less Common Met., 1963, 5, p 258-270
B.C. Giessen, I. Rump, and N.J. Grant, The Constitution Diagram Tungsten-Hafnium, Trans. Met. Soc. AIME, 1962, 224, p 60-64
B.C. Giessen, I. Rump, and N.J. Grant, Discussion of the Constitution Diagram Tungsten-Hafnium, Trans. Met. Soc. AIME, 1963, 227, p 264-265
R.E. Siemens, H.R. Babitzke, and H. Kato, Columbium-Hafnium Equilibrium Diagram, U.S. Bur. Mines Rept. Invest. 6492, 1964
R.G. Bedford, High-Temperature Electrical Resistivity and Allotropic Transformation Temperature of Hafnium, J. Appl. Phys., 1965, 36, p 113-117
R.F. Domagala and R. Ruh, The Hafnium-Oxygen System, ASM Trans. Q, 1965, 58, p 164-175
P.A. Romans, O.G. Paasche, and H. Kato, The Transition Temperature of Hafnium, J. Less Common Met., 1965, 8, p 213-215
H.D. Heetderks, G. Rudy, T. Eckert, Ternary Phase Equilibria in Transition Metal-Boron-Carbon-Silicon Systems, Aerojet-General Corps., Air Force Materials Laboratory, Research and Technology Division., Air Force Systems Command, Wright-Patterson Air Force Base, OH, Rept. AFML-TR-65-2, Part III: Special Experimental Techniques, Vol. I: High Temperature Differential Thermal Analysis, 1965
E. Rudy, Ternary Phase Equilibria in Transition Metal-Boron-Carbon-Silicon Systems, Aerojet-General Corps., Air Force Materials Laboratory, Research and Technology Division., Air Force Systems Command, Wright-Patterson Air Force Base, OH, Report AFML-TR-65-2, Part I: Related Binary Systems, Vol. IV: Hf-C System, 1965
G.N. Bates and G. Barnes, The Solid-Phase Transformation in Hafnium, Appl. Phys. Lett., 1967, 11, p 75-77
E. Rudy and St. Windisch, The Phase Diagrams Hafnium-Vanadium and Hafnium-Chromium, J. Less Common Met., 1968, 15, p 13-26
O.N. Carlson, F.A. Schmidt, and J.C. Sever, Electrotransport of Carbon, Nitrogen and Oxygen in Hafnium Metal, Met. Trans., 1973, 4, p 2407-2411
R.B. Russell, On the Zr-Hf System, J. Appl. Phys., 1953, 24, p 232-233
D.K. Deardorff and E.T. Hayes, Melting Point Determination of Hafnium, Zirconium and Titanium, Trans. Met. Soc. AIME, 1956, 206, p 509-511
S.P. Garg and R.J. Ackermann, The High Temperature Phase Diagrams for Zirconium-Molybdenum and Hafnium-Molybdenum, Met. Trans., 1977, 8A, p 239-244
J.P. Hiernaut, F. Sakuma, and C. Ronchi, Determination of the Melting Point and the Emissivity of Refractory Metals with a Six-Wavelength Pyrometer, High Temp. High Press., 1989, 21, p 139-148
J.H. De Boer and J.D. Fast, Über die Darstellung der reinen Metalle der Titangruppe durch thermische Zersetzung ihrer Jodide. III. Hafnium, Z. Anorg. Allgem. Chem., 1930, 187, p 198-208
G.B. Skinner, C.W. Beckett, and H.L. Johnston, Thermal, Structural, Electrical Magnetic and Other Physical Properties of Titanium Zirconium, Hafnium and Thorium and Some of Their Simple Compounds, Ohio State University Technical Report No. 102-AC49/2-100-3, 1950
F.B. Litton, Preparation and Some Properties of Hafnium Metal, J. Electrochem. Soc., 1951, 98, p 488-494
H.K. Adenstadt, Physical, Thermal and Electrical Properties of Hafnium and High Purity Zirconium, Trans. ASM, 1951, 44, p 949-973
F.H. Spedding, Quarterly Summary Research Report in Metallurgy, U.S. Atomic Energy Commission, Iowa State College Report ISC-531, 1955
O.N. Carlson, F.A. Schmidt, and H.A. Wilhelm, Preparation of Zirconium and Hafnium Metals by Bomb Reduction of Their Fluorides, J. Electrochem. Soc., 1957, 104, p 51-56
V.K. Grigorovich, Structure of Liquid Metals in Connection with Their Electron Structure, Izv. Akad. Nauk SSSR Otd. Tekh. Nauk Met. Toplivo, 1960, (6), p 93-109
E. Rudy and P. Stecher, Zum Aufbau des Systems Hafnium-Sauerstoff, J. Less Common Met., 1963, 5, p 78-89
R.V. Sara, The Hafnium Carbon System, Trans. Met. Soc. AIME, 1965, 233, p 1683-1691
D.K. Deardorff, M.I. Copeland, L.L. Odin, and H. Kato, The Hafnium-Vanadium System, U.S. Bur. Mines Rept. Invest. 6594, 1965
R.J. Ackermann and E.G. Rauh, Determination of Liquidus Curves for the Th-W, Th-Ta, Zr-W and Hf-W Systems: The Anomalous Behaviour of Metallic Thorium, High Temp. Sci., 1972, 4, p 272-282
A. Cezairliyan and J.L. McClure, Measurement of Melting Point and Radiance Temperature (at Melting Point and at 653 nm) of Hafnium-3 (wt.%) Zirconium by a Pulse Heating Method, J. Res. Nat. Bur. Stand., 1976, 80A, p 659-662
N.D. Milošević and K.D. Maglić, Thermophysical Properties of Solid Phase Hafnium at High Temperatures, Int. J. Thermophys., 2006, 27, p 530-553
L.P. Filippov, and R.P. Yurchak, High Temperature Investigations of the Thermal Properties of Solids, Inzh. Fiz. Zh., 1971, 21, 561-577 [J. Eng. Thermophys. 1971, 21, p 1209-1220]
L.P. Filippow, Untersuchung der Thermischen Eigenschaften im Stoff an der Moskauer Universität, Int. J. Heat Mass Transfer, 1973, 16, p 865-885
A.V. Arutyunov, S.N. Banchila, and L.P. Filippov, Thermal, Electrical and Emissive Properties of Hafnium in the High-Temperature Region, Teplofiz. Vys. Temp., 1972, 10, p 425-428 [High Temp. 1972, 10, p 375-377]
A. Cezairliyan and J.L. McClure, Simultaneous Measurements of Specific Heat, Electrical Resistivity and Hemispherical Total Emittance by a Pulse Heating Technique: Hafnium-3 (wt.%) Zirconium, 1500 to 2400 K, J. Res. Nat. Bur. Stand., 1975, 79A, p 431-436
I.B. Fieldhouse, and J.I. Lang, Measurement of Thermal Properties, Armour Research Foundation, Wright Air Development Division, Air Research and Development Command, United States Air Force, Wright-Patterson Air Force Base, OH, WADD Technical Report 60-904, 1961
Y.A. Golutvin, and E.G. Maslennikova, The Heat Capacity of Metallic Hafnium, Izv. Akad. Nauk SSSR Metally 1970, 5, 174-183 [Russian Metallurgy Metally, 1970, 5, p 129-135]
P.D. Desai, Thermodynamic Properties of Titanium, Int. J. Thermophys., 1987, 8, p 781-794
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Arblaster, J.W. Thermodynamic Properties of Hafnium. J. Phase Equilib. Diffus. 35, 490–501 (2014). https://doi.org/10.1007/s11669-014-0319-5