Abstract
Water pollution threatens environment and human health. Common polymer-based sorbents are used to trap pollutants by these sorbents are difficult to separate from treated water and, in turn, their application is limited. Alternatively, nanomaterials with magnetic features offer the advantage of fast and easy magnetically-assisted separation. Moreover, the surface modification of magnetic nanoparticles with biopolymers enhances their adsorptive capabilities. We review recent developments on magnetic biosorbents for water treatment. We present chemical strategies for the surface modification of magnetic nanoparticles with biopolymers to obtain highly effective, robust and reusable biosorbents. This can be done by two strategies: in situ functionalization and post-synthesis functionalization. Post-synthesis functionalization is done in two distinct stages, the synthesis of the magnetic nanoparticles and the surface functionalization, thus allowing better control of each stage individually. Surface functionalization involves either simple coating or the covalent attachment of the biopolymer chains to the surface. Overall, covalent immobilization of the biopolymer onto the particle’s surface is recommended to ensure successful recycling and reuse of the biosorbents without significant loss of adsorption capacity. Finally, we discuss the performance of several magnetic biosorbents in the uptake of heavy metal species and organic pollutants from water.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
Magnetic nanomaterials have attracted increased attention in the last decade for application as biosorbents in water remediation processes (Sousa et al. 2015; Mehta et al. 2015; Simeonidis et al. 2016; Adeleye et al. 2016; Reddy and Yun 2016). Owing to reduced size, nanomaterials possess large surface area-to-volume ratio available, which is a desirable feature for adsorptive applications (Madhura et al. 2019). Nanomaterials possessing magnetic features are easily and quickly separated from treated water in the presence of an external magnetic field, which clearly represents an advantage in relation to non-magnetic biosorbents. Iron oxides nanoparticles are the most widely used in research for treatment of polluted water owing to low cost and moderate environmental impact (Tang and Lo 2013; Su 2017). Enhancement of adsorptive capacity of magnetic nanoparticles and selectivity toward target pollutants can be achieved via the chemical functionalization of the particles surfaces.
The search for eco-friendly and low-cost biosorbents has prompted the interest for new biopolymer-based nanomaterials and their use in water decontamination (Crini 2005; Daniel-da-Silva et al. 2013; Dehabadi and Wilson 2014; Carpenter et al. 2015). Surface modification with biopolymers, i.e., polymers occurring in nature, provides to the particles surfaces novel functional groups that may confer affinity toward a wide diversity of pollutants (Xu et al. 2012; Boamah et al. 2015; Vandenbossche et al. 2015). Besides being available on a sustainable basis, biopolymers present the advantages of low cost, biodegradability and reduced toxicity (Nair et al. 2017; Rebelo et al. 2017; Resch-Fauster et al. 2017; Divya and Jisha 2017) (Fig. 1).
Ideally, a biosorbent for water remediation should fulfill the following requirements: specificity to target pollutants, high adsorptive performance, rapid adsorption, cost-effective, environmentally non-toxic, reusability and ease of separation from treated water. Low toxicity and easy magnetic separation can be in principle met by the simple combination of biopolymers with magnetic iron oxides. However, a rational design of the surface of the magnetic nanoparticles is needed to attain specificity, high adsorption capacity and reusability. Advances in nanotechnology and in the field of colloidal science have extended the ability to tailor the surface of magnetic nanoparticles and to tune their physical–chemical properties to suit specific applications (Wu et al. 2015; Bohara et al. 2016).
This review aims to provide a critical overview of the most recent developments in the field of magnetic biosorbents for application in water treatment. Primary attention is given to the chemical strategies used for the surface modification of magnetic nanoparticles with biopolymers aiming to obtain highly effective and robust biosorbents with magnetic properties. The performance of the magnetic biosorbents in the uptake of heavy metal species and organic pollutants from water is discussed.
This article is an abridged version of the chapter published by Soares et al. (2018) in the series Environmental Chemistry for a Sustainable World (https://www.springer.com/series/11480).
Magnetically assisted water treatment
Magnetic nanoparticles for water treatment
Magnetic separation relies on the fact that magnetic nanoparticles can be manipulated by an external magnetic field gradient. For the effective magnetic separation of micrometric or nanosized materials from a viscous flow, the magnetic force produced by the external magnetic field must overcome the drag force associated with the carrier fluid. Larger magnetic nanoparticles present higher magnetic susceptibilities that originate higher particle velocities. In other words, larger particles are more efficient for magnetic separation. On the other hand, for adsorptive applications, smaller magnetic particles are desirable, owing to high surface area-to-volume ratio.
Iron oxide nanoparticles, more specifically magnetite (Fe3O4) and maghemite (γ-Fe2O3), are by far the most extensively investigated magnetic nanoparticles for water treatment due to their adequate magnetic properties, low cost, chemical inertness and low toxicity (Xu et al. 2012; Kaur et al. 2014; Mehta et al. 2015; Su 2017). The easy synthesis, coating or surface functionalization, and the facility of tuning the size and particle shape provide huge versatility to these materials. Magnetite nanoparticles exhibit unique size-dependent magnetic properties. Bulk magnetite is a ferrimagnetic material composed of multiple magnetic domains. Due to such magnetic domains, bulk magnetite exhibits a hysteresis curve when magnetization is plotted versus magnetic field and a permanent magnetization in the absence of a magnetic field is observed. The decrease in the particle size to the nanoscale brings consequences in terms of magnetic properties. Below a critical particle size (~ 25 nm for Fe3O4), it is energetically more favorable for particles to be composed by single magnetic domains and therefore exhibit superparamagnetic behavior. The magnetization curve of superparamagnetic nanoparticles does not exhibit hysteresis which means that in the absence of an external magnetic field these particles have zero magnetization, no coercivity and less tendency to agglomerate, an important feature for adsorptive applications. However, for applications in magnetic separation ferromagnetic particles are usually preferable over superparamagnetic nanoparticles because they show higher magnetophoretic response, thus leading to faster separations.
Preparative methods of magnetic iron oxides
As described in the previous section, the properties of magnetic nanoparticles are strongly dependent on the particle size and shape. Thus, a number of synthetic strategies have been developed for the synthesis of magnetic nanoparticles with uniform morphology, narrow size distribution and tailored properties, as extensively reviewed elsewhere (Laurent et al. 2008; Wu et al. 2015; Ling et al. 2015). Examples of methods for the synthesis of colloidal magnetite nanoparticles include the co-precipitation method (Roth et al. 2015; Pušnik et al. 2016; Lin et al. 2017), the oxidative hydrolysis (Girginova et al. 2010; Reguyal et al. 2017), the hydrothermal treatment (Cheng et al. 2016; Gyergyek et al. 2017; Bhavani et al. 2017) and the thermal decomposition of iron-containing molecular precursors (Jiang et al. 2014a; Glasgow et al. 2016; Bartůněk et al. 2016).
Surface modification of magnetic nanoparticles with biopolymers
Herein we will draw our attention on the synthetic procedures for the production of magnetic biosorbents, via the surface modification of magnetic nanoparticles with biopolymers. Preparative methods to obtain magnetic biosorbents in the particulate form, including composite nanoparticles, microparticles and hydrogel beads, will be addressed.
Biopolymers extracted from natural sources present the advantages of biodegradability, reduced toxicity and low cost. Coating magnetic nanoparticles with biopolymers improves their stability against oxidation and provides functional groups to capture target pollutants from water (Avérous and Pollet 2012; Wu et al. 2015; Bohara et al. 2016). In addition, biopolymers improve the colloidal stability of the magnetic nanoparticles in aqueous media and prevent the formation of magnetic aggregates, which otherwise could contribute to diminish the available surface area and sorption capacity (Wu et al. 2008; Mehta et al. 2015). Colloidal stability is improved either due to steric shielding caused by biopolymer chains or due to electrostatic repulsions between charged moieties present in the biopolymer.
Polysaccharides are among the most commonly used biopolymers for preparing magnetic biosorbents. Examples of polysaccharides are listed in Table 1. They can provide distinct ionic character such as neutral, anionic or cationic, variable chemical functionalities and physical properties to the magnetic biosorbents. Surface modification with polysaccharides allows to enhance and to tune the chemical affinity toward specific target pollutants.
Strategies for surface functionalization
The surface of magnetic nanoparticles, typically magnetic iron oxide nanocrystals containing surface hydroxyl groups, can react with different functional groups. Owing to this broad reactivity, there is a range of strategies for the surface modification of magnetic nanoparticles with biopolymers, which can be carried out either in situ during nanoparticle synthesis, or using post-synthesis routes, i.e., ex situ (Bohara et al. 2016; Su 2017). The main interactions that can be present in the adsorption mechanism of biopolymers onto magnetic nanoparticles are electrostatic interactions, hydrophobic interactions and hydrogen bonding (Avérous and Pollet 2012; Bohara et al. 2016). As a result of the many strategies available for surface modification, several distinct structures of magnetic bionanocomposites can be obtained, including core–shell structure, multicores or matrix-dispersed structure, shell–core–shell and Janus-type hetero-structures (Wu et al. 2015; Bohara et al. 2016) (Fig. 2).
In situ surface functionalization
This is a one-pot synthesis strategy where both the synthesis of magnetic nanoparticles and their surface functionalization are carried out. The biopolymer and the precursor of magnetic nanoparticles are added simultaneously and the coating process starts as soon as nucleation occurs, preventing further growth of the particles (Bohara et al. 2016). This method benefits from the ability of the biopolymer to interact with metal ions from the precursors of magnetic nanoparticles and from the nanoparticles’ surface. The metal ion–biopolymer interaction may occur through different modes including complexation and hydrogen bonding (Boury and Plumejeau 2015). Hence, owing to these interactions the biopolymer can play a key role in either the nucleation or particle growth steps. For example, starch was employed to effectively control and tune the size of Fe3O4 nanoparticles prepared by oxidation–precipitation of ferrous hydroxide (Tancredi et al. 2015). The size of the nanoparticles was tuned from 15 to 100 nm by changing the time of starch addition to the reaction mixture. Starch acted as a kinetically control agent that affected the size, size distribution and aggregation state of the magnetic nanoparticles. Starch-coated Fe3O4 nanoparticles were water dispersible, presenting good colloidal stability. In our group, it has been observed that the particle size and the stability toward oxidation of Fe3O4 nanoparticles generated by co-precipitation in the presence of carrageenan, strongly depended on the type and concentration of carrageenan used (Daniel-da-Silva et al. 2007).
The in situ synthesis of magnetic nanoparticles is typically performed using wet chemical routes that require aqueous environment and mild conditions of temperature, compatible with the presence of the biopolymer. Among in situ strategies, the co-precipitation of ferric and ferrous ions under alkaline conditions is the most commonly used route to prepare biopolymer-coated magnetite (Fe3O4) nanoparticles (Lee et al. 1996; Kim et al. 2014). Generally, nanocomposite structures obtained are core–shell structures or mosaic (matrix-dispersed) structures (Wu et al. 2015; Bagheri and Julkapli 2016). Nevertheless, the morphology and the thickness of the polymer shell are difficult to control using this methodology. Owing to these limitations and even though the one-step synthesis is less time-consuming, magnetic biosorbents prepared by in situ procedures have been less reported. Some representative examples are described below that illustrate the usefulness of in situ strategy for the functionalization of magnetic nanoparticles aiming applications in the removal of pollutants from water.
Magnetic iron oxide nanoparticles were prepared by co-precipitation in the presence of chitosan, followed by the addition of the cross-linker glutaraldehyde (Yang et al. 2016a; Azari et al. 2017) to impart mechanical robustness to the biosorbent. Small nanoparticles, with an average size of 5 nm (Yang et al. 2016a) and 50 nm (Azari et al. 2017), and narrow particle size distribution were obtained. The nanoparticles were homogeneously dispersed and embedded in the biopolymer matrix. These biosorbents showed good adsorption of mercury species (Azari et al. 2017) even in the presence of competitive cations. In alternative to glutaraldehyde addition, more environmental friendly cross-linking strategies are being explored. For example, κ-carrageenan-coated magnetite nanoparticles of 4 nm size were prepared by co-precipitation and then cross-linked with chitosan (Mahdavinia and Mosallanezhad 2016). The electrostatic interactions between positively charged amino groups of chitosan and negatively charged sulfate groups of κ-carrageenan could produce stable complexes, with affinity for cationic dyes.
Several examples could be found concerning biopolymer-coated magnetic nanophases obtained by in situ co-precipitation that were subsequently modified in post-synthetic steps. In those systems, the biopolymer serves as a springboard for the addition of reactive groups aiming to improve the adsorption capacity. For instance, amino acids and diethylenetriamine were grafted at the surface of chitosan-coated magnetite nanoparticles (size 10–50 nm) prepared via co-precipitation, using epichlorohydrin as cross-linker (Galhoum et al. 2015a, 2017). The materials showed binding affinity for uranyl and Dy(III) ions.
Ex situ surface functionalization
This procedure is divided into two distinct stages, synthesis and surface modification, which allows better control of each stage individually. It can involve the simple coating of magnetic nanoparticles with biopolymers, physically or chemically cross-linked or the covalent attachment of the biopolymer chains to the surface of the nanoparticles. The latter usually requires the use of a linker such as functional alkoxysilanes (Laurent et al. 2008; Sun et al. 2008; Begin-Colin and Felder-Flesch 2012).
Ionic cross-linking of biopolymer coating
Several natural polyelectrolytes have the ability to undergo ionotropic gelation, i.e., to cross-link in the presence of counter ions to form hydrogels (Jiang et al. 2014b; Nie et al. 2016; Valle et al. 2017). This ability combined with extrusion or emulsification techniques has been widely explored for the encapsulation of magnetic nanoparticles, to form magnetic composites particles with different sizes and shapes. For example, magnetic alginate core–shell type particles were fabricated using a method of electro-coextrusion and employed as a biosorbent for separation of fluoride from aqueous solution (Zhang et al. 2016). In this method, the solutions of alginate and Fe3O4 nanoparticles were injected simultaneously through a concentric nozzle using an electrostatic spinning machine and dropped into a solution of CaCl2 for alginate cross-linking. The resulting particles comprised a core of aggregated Fe3O4 nanoparticles coated by a shell of alginate. Because lanthanum (Lewis hard acid) shows high chemical affinity to fluoride anions (Lewis hard base), the Ca2+ ions of the alginate were then replaced by La3+ ions, through cation exchange. The resulting particles were able to uptake F− ions from solution owing to Lewis acid-based interactions.
Magnetite nanoparticles were coated with κ-carrageenan and used to remove methylene blue from aqueous solutions (Salgueiro et al. 2013). The coating was performed by simple dispersion of the Fe3O4 nanoparticles in κ-carrageenan solution followed by the addition of K+ ions to promote sol–gel transition by physical cross-linking. These biosorbents show high methylene blue adsorption capacity due to electrostatic interactions between the cationic dye and the ester sulfate moieties of carrageenan. Nevertheless, marked loss of adsorption capacity after regeneration and reuse was observed. This loss was ascribed to possible leaching of κ-carrageenan that was physically adsorbed at the surface of nanoparticles.
Covalent cross-linking of biopolymer coating
The mechanical and chemical stability of the biosorbent is an important aspect to consider, namely to ensure successful recycling and reuse of the biosorbents without loss of adsorption capacity. Covalent cross-linking is a versatile method to improve the robustness of the biosorbents. It results in the enhancement of the mechanical properties and insolubility of the biopolymer coating, as the chains are tied together by strong covalent linkages (Maitra and Shukla 2014). Some recent examples of covalently cross-linked magnetic biosorbents include cross-linked chitosan and quaternary chitosan particles prepared using a reverse-phase suspension cross-linking technique (Li et al. 2016a; Song et al. 2017; Funes et al. 2017). It is worth noting that glutaraldehyde is still one of the most frequently used cross-linkers, in spite of its known ecotoxicity (Leung 2001; Hu et al. 2017; Christen et al. 2017). Alternative and much less toxic cross-linkers such as genipin (Muzzarelli 2009; Pujana et al. 2014) have been barely investigated for applications in water remediation (Laus and de Fávere 2011; Mondal et al. 2015).
Coating by complexation of polyelectrolytes
Coating of magnetic nanoparticles can be also performed by the complexation of polyelectrolytes oppositely charged. Most of biopolymers are polyelectrolytes, i.e., macromolecules that are either charged or, under suitable conditions, can become charged. Hence, biopolymers can undergo complexation in the presence of other oppositely charged biopolymers (Luo and Wang 2014) or synthetic polyelectrolytes (Gentile et al. 2015). The assembly of oppositely charged polyelectrolytes and magnetic nanoparticles is mainly governed by strong but reversible electrostatic interactions, as well as hydrogen bonds. The layer-by-layer assembly technique is a simple and versatile method for the fabrication of polymer-based coatings and has been widely used to modify spherical and planar inorganic substrates (Srivastava and Kotov 2008). This method involves the sequential adsorption of oppositely charged biopolymers onto the surface of the nanoparticles. The thickness of the polymer coating can be tuned by varying the number of layers deposited and the properties of the polymer solutions. Using a distinct approach, magnetic chitosan/carrageenan microspheres with high efficient adsorption capacity toward both cationic and anionic dyes and heavy metal ions in wastewater were prepared (Liang et al. 2017). The microspheres were fabricated via emulsification procedure from the homogeneous chitosan/carrageenan solution.
Grafting of biopolymers onto magnetic particles surface
Another strategy explored for the preparation of magnetic biosorbents is the grafting of the biopolymer onto the surface of magnetic nanoparticles. The biopolymer can be directly grafted onto the surface of the particle (Badruddoza et al. 2011; Lu et al. 2016) or after surface functionalization with ligands that will subsequently link to the biopolymer (Bini et al. 2012; Rodriguez et al. 2017). This strategy might also involve the coating with a thin layer of amorphous silica (SiO2). The SiO2 shells protect magnetic iron oxides from oxidation and ion leaching and provide a suitable surface for further chemical modification aiming the grafting of the biopolymers onto its surface. For example, carboxymethylated carrageenans were grafted onto the surface of amino-functionalized silica-coated magnetite nanoparticles, via carbodiimide chemistry (Daniel-da-Silva et al. 2015). The biosorbents showed good methylene blue adsorption due to electrostatic interactions between the carrageenan and the dye. Owing to the covalent immobilization of the carrageenan, the particles were reusable without significant loss of the adsorption capacity.
Bio-hybrid coatings
In alternative to the grafting of biopolymers at the surfaces of silica-coated nanoparticles, the biopolymer can be introduced in the silica network, yielding an organic–inorganic hybrid material enriched in biopolymer, herein designated by bio-hybrid material. Our group has developed a method for the encapsulation of Fe3O4 nanoparticles with bio-hybrid siliceous shells comprising a polysaccharide covalently grafted to the siliceous network (Soares et al. 2016, 2017a; Fernandes et al. 2017). The encapsulation was performed through a one-step procedure, involving the hydrolysis and condensation of a mixture of tetraethyl orthosilicate and an alkoxysilane covalently bound to the biopolymer, in the presence of the magnetic particles. This method was successfully used with polysaccharides having distinct chemical nature and ionic character, namely κ-carrageenan (Soares et al. 2016, 2017b; Fernandes et al. 2017), chitosan (Soares et al. 2017a) and starch (Fernandes et al. 2017). In comparison with the post-encapsulation grafting, this method allowed to obtain surfaces highly enriched with biopolymer functional groups. The resulting magnetic biosorbents were highly effective in the removal of the organic pollutants paraquat, methylene blue and metoprolol from aqueous solutions (Soares et al. 2016, 2017b; Fernandes et al. 2017). Magnetic hybrids prepared from chitosan were tested for the uptake of nonpolar organic solvents from water (Soares et al. 2017a).
Adsorptive applications of magnetic bionanocomposites in water treatment
In this section, the most recent magnetic bionanocomposites for the cleanup of emerging pollutants from water is reviewed taking into consideration adsorptive technologies. Table 2 provides an overview of several materials that have been successfully used for the removal of inorganic and organic pollutants.
Removal of heavy metal species
Due to their well-known toxicity, heavy metals such as lead, cadmium, arsenic, mercury and chromium have been considered priority pollutants since they pose the greatest concern regarding human exposure (Bashir et al. 2019; Malik et al. 2019).
A wide variety of magnetic bionanocomposites have been proposed for the effective removal of Pb(II) from water under several operating conditions (Charpentier et al. 2016; Luo et al. 2016; Wang et al. 2016; Li et al. 2017; Sahraei et al. 2017; Sengupta et al. 2017; Chen et al. 2017b). Pb(II) can have a serious impact on human health mainly due to increased oxidative stress, with a highly detrimental effect on the hematopoietic, renal, reproductive and central nervous system (Flora et al. 2012). Recently, a chitosan/polyethylenimine-grafted magnetic composite has been reported with an impressive maximum adsorption capacity 341 mg g−1 of Pb(II) and 321 mg g−1 of Cd(II) (Li et al. 2017). With an optimum performance in pH range 6–7, the isotherm studies indicated a good agreement with the Langmuir isotherm for both metals. The adsorption process was thermodynamically favorable and endothermic in nature. The good removal efficiency could be attributed to the biopolymer at the surface of the particles, which resulted in a higher number of amino groups with superior uptake efficiency. Furthermore, the chitosan/polyethylenimine-grafted magnetic composite could be effectively regenerated for five cycles while keeping good performance and stability. Magnetic hydrogel beads containing gum tragacanth in its composition have also been reported for the effective cleanup of Pb(II) and Cu(II) from water (Sahraei et al. 2017), with a maximum adsorption capacity of 81 and 69 mg g−1, respectively, at pH 6. The good removal capacity was ascribed to the presence of several chelating sulfonic acid, carboxylic acid and hydroxyl and amino groups.
Magnetic carboxymethyl chitosan nanoparticles have also been proposed for the cleanup of Pb(II), Cu(II) and Zn(II). By preparing the materials through a simple one-step chemical precipitation method, their adsorption efficiency was determined with values of 243, 232 and 131 mg g−1 at pH 5.2 (Charpentier et al. 2016). The good sorption capacity was attributed to the availability of a large number of carboxyl groups which are able to coordinate to metal ions.
Cadmium is a highly toxic heavy metal, and its exposure even at very low concentrations has been linked to several diseases in humans (Satarug et al. 2009). Recently, a composite of carbon disulfide-modified magnetic ion-imprinted chitosan–Fe(III) has been reported for the simultaneous cleanup of Cd(II) and tetracycline from water (Chen et al. 2017a). The presence of pores in the composite along with the functional groups of the biopolymer resulted in good uptake efficiency (194 and 516 mg g−1 for Cd(II) and tetracycline, respectively).
Arsenic, which is a metalloid that can induce toxic effects even at low concentrations (Tchounwou et al. 2012; Chen et al. 2015; Bibi et al. 2017), has a wide distribution in nature. Several forms of arsenic exist with distinct oxidation states; however, the forms with As(III) (arsenite) and As(V) (arsenate) are the ones that raise the greatest concern. These forms are toxic for aquatic systems (Kumari et al. 2017) and are related to several diseases in humans and with carcinogenic effects. An As(III)-imprinted magnetic Fe3O4–N-(2-hydroxy) propyl-3-trimethyl ammonium chitosan composite has been presented for the removal of As(III) from water (Song et al. 2017). The use of this quaternary chitosan resulted in improved dispersion of the composite in water and delivered a high number of cationic biding sites that promoted the removal of As(III) species under optimal pH conditions (pH 6). Magnetic chitosan beads have also been proposed for the removal of As(V) from water (Martínez-Cabanas et al. 2016).
Mercury is a heavy metal with well-known toxicity. It is a natural element with a wide distribution in nature; however, a great portion of mercury bioaccumulation is originated from anthropogenic activity. Mercury and its several forms have been identified as priority hazardous substance by the European Union (directive 2008/105/EC) and the United States Environmental Protection Agency. An itaconic acid-grafted magnetite nanocellulose composite has been purposed for the removal of mercury from water (Anirudhan and Shainy 2015). The maximum adsorption capacity obtained was 240 mg g−1 and the material exhibited a good reuse capacity, being recycled for six cycles. Recently, magnetic chitosan modified with glutaraldehyde was also purposed for the Hg(II) water remediation (Azari et al. 2017). In this case, glutaraldehyde was important to promote the fixation of chitosan, resulting in superior stability and, consequently, in a large number of strong chelating sites.
Chromium is another natural occurring heavy metal, being Cr(III) the most stable form and widely distributed in nature. Even though Cr(III) has an important biological role, it is now accepted that the exposure to high levels has been linked to adverse health effects. The presence of Cr(VI) in drinking water is of serious concern since it can easily enter the cells when compared with Cr(III) (Barceloux and Barceloux 1999; Wilbur et al. 2012; Ni et al. 2014). A pyridinium–diethylenetriamine magnetic chitosan was proposed for the efficient removal of Cr(VI) from water (Sakti et al. 2015). The use of pyridinium units along with chitosan delivered several functional groups (amines and quaternary amines) that promoted the electrostatic interaction with the metal.
Removal of organic compounds
Every day, different classes of organic pollutants are discharged with the potential to contaminate drinking water sources. Some examples include dyes, pharmaceuticals, pesticides, solvents or many other organic by-products originated from industrial manufacturing (Dsikowitzky and Schwarzbauer 2014; Cizmas et al. 2015; Crini et al. 2019). There is now great evidence that a large diversity of hazardous organic pollutants is present in drinking water sources, with an alarming negative impact on human health or aquatic ecosystem. To address this problem, different types of bionanocomposites have been purposed for the adsorption of organic pollutants. Furthermore, many bionanocomposites have been explored for the uptake of several common less toxic dyes, given their prevalent use as molecular models for preliminary assessment of material performance. A well-known example of such case is methylene blue. Recently, our group explored the ability of hybrid magnetic biosorbents containing a siliceous shell with covalently linked κ-carrageenan for the uptake of methylene blue from water (Soares et al. 2017b). The experimental results indicated a Z-type isotherm, with a maximum adsorption capacity of 530 mg g−1. In addition, the material could be recycled for six cycles without loss in performance or stability. The biopolymer had an important role by providing anionic ester sulfate groups that could establish electrostatic interactions with the cationic dye under optimal pH conditions. A gelatin-based magnetic nanocomposite comprising carboxylic acid-functionalized carbon nanotube has also been reported for the uptake of methylene blue and direct red 80 (Saber-Samandari et al. 2017). The authors proposed that the gelatin delivered cationic functional groups that can remove the organic pollutants from water through electrostatic interactions. Alginate beads containing dispersed polydopamine CoFe2O4 particles were reported for the uptake methylene blue, crystal violet and malachite green (Li et al. 2016b). It was shown that the presence of carboxylate, catechol and amino groups provided important binding sites for the removal of the organic dyes through electrostatic interactions.
In addition to dyes, other organic pollutants have also been investigated for water remediation, given the rising concerns regarding their impact on human health and the ecosystems. For example, our group explored the ability of hybrid magnetic nanoparticles containing κ-carrageenan for the uptake of metoprolol (beta blocker) (Soares et al. 2016) and paraquat (herbicide) (Fernandes et al. 2017). The good performance of the material, 447 and 257 mg g−1 for metoprolol and paraquat, respectively, and recycling capacity make it as a good candidate for the water remediation of these pollutants. Magnetic cellulose ionomer/layered double hydroxide has been successfully used for the removal of diclofenac from water (Hossein et al. 2016). The pyridinium rings of cellulose ionomer provided several binding sites for the removal of diclofenac. A composite material based on chitosan and magnetic carbon nanotubes has been employed for the removal of tetracycline (Ma et al. 2015). The adsorption profile fitted well with the Freundlich isotherm model with a maximum performance of 104 mg g−1. In addition, the biosorbent could be recycled for ten cycles while keeping good performance.
Conclusion
The application of magnetic bionanocomposite particles for the uptake of pollutants in water treatment has emerged as an interesting alternative to conventional sorbents. These biosorbents offer clear advantages of magnetic separation and tuned affinity for a variety of pollutants. The rational design of the surface of these materials is essential, in order to attain robust and reusable biosorbents with high adsorption capacities. Thus, this article dedicated a specific section to the most relevant chemical strategies for the surface modification of magnetic nanoparticles with biopolymers, aiming the production of magnetic biosorbents optimized and specialized in the targeted pollutants. A direct outcome of the use of optimized biosorbent particles is the reduction in quantities of solids needed in the water treatment, which, apart from bringing down the costs of water remediation, also reduces the potential environmental effects of the exhausted sorbents disposed. The use of nature occurring biopolymers anticipates potential bio- and eco-compatibility of the magnetic biosorbents.
References
Adeleye AS, Conway JR, Garner K et al (2016) Engineered nanomaterials for water treatment and remediation: costs, benefits, and applicability. Chem Eng J 286:640–662. https://doi.org/10.1016/j.cej.2015.10.105
Anirudhan TS, Shainy F (2015) Effective removal of mercury(II) ions from chlor-alkali industrial wastewater using 2-mercaptobenzamide modified itaconic acid-grafted-magnetite nanocellulose composite. J Colloid Interface Sci 456:22–31. https://doi.org/10.1016/j.jcis.2015.05.052
Arya V, Philip L (2016) Adsorption of pharmaceuticals in water using Fe3O4 coated polymer clay composite. Microporous Mesoporous Mater 232:273–280. https://doi.org/10.1016/j.micromeso.2016.06.033
Avérous L, Pollet E (2012) Environmental silicate nano-biocomposites, 1st edn. Springer, London
Azari A, Gharibi H, Kakavandi B et al (2017) Magnetic adsorption separation process: an alternative method of mercury extracting from aqueous solution using modified chitosan coated Fe3O4 nanocomposites. J Chem Technol Biotechnol 92:188–200. https://doi.org/10.1002/jctb.4990
Badruddoza AZM, Tay ASH, Tan PY et al (2011) Carboxymethyl-β-cyclodextrin conjugated magnetic nanoparticles as nano-adsorbents for removal of copper ions: synthesis and adsorption studies. J Hazard Mater 185:1177–1186. https://doi.org/10.1016/j.jhazmat.2010.10.029
Bagheri S, Julkapli NM (2016) Modified iron oxide nanomaterials: functionalization and application. J Magn Magn Mater 416:117–133. https://doi.org/10.1016/j.jmmm.2016.05.042
Barceloux DG, Barceloux D (1999) Chromium. J Toxicol Clin Toxicol 37:173–194. https://doi.org/10.1081/CLT-100102418
Bartůněk V, Průcha D, Švecová M et al (2016) Ultrafine ferromagnetic iron oxide nanoparticles: facile synthesis by low temperature decomposition of iron glycerolate. Mater Chem Phys 180:272–278. https://doi.org/10.1016/j.matchemphys.2016.06.007
Bashir A, Malik LA, Ahad S et al (2019) Removal of heavy metal ions from aqueous system by ion-exchange and biosorption methods. Environ Chem Lett 17:729–754. https://doi.org/10.1007/s10311-018-00828-y
Bée A, Obeid L, Mbolantenaina R et al (2017) Magnetic chitosan/clay beads: a magsorbent for the removal of cationic dye from water. J Magn Magn Mater 421:59–64. https://doi.org/10.1016/j.jmmm.2016.07.022
Begin-Colin S, Felder-Flesch D (2012) Functionalisation of magnetic iron oxide nanoparticles. In: Thanh NTK (ed) Magnetic nanoparticles: from fabrication to clinical applications. CRC Press, Boca Raton, pp 151–192
Bhavani P, Rajababu CH, Arif MD et al (2017) Synthesis of high saturation magnetic iron oxide nanomaterials via low temperature hydrothermal method. J Magn Magn Mater 426:459–466. https://doi.org/10.1016/j.jmmm.2016.09.049
Bibi S, Kamran MA, Sultana J, Farooqi A (2017) Occurrence and methods to remove arsenic and fluoride contamination in water. Environ Chem Lett 15:125–149. https://doi.org/10.1007/s10311-016-0590-2
Bini RA, Marques RFC, Santos FJ et al (2012) Synthesis and functionalization of magnetite nanoparticles with different amino-functional alkoxysilanes. J Magn Magn Mater 324:534–539. https://doi.org/10.1016/j.jmmm.2011.08.035
Boamah PO, Huang Y, Hua M et al (2015) Sorption of heavy metal ions onto carboxylate chitosan derivatives—a mini-review. Ecotoxicol Environ Saf 116:113–120. https://doi.org/10.1016/j.ecoenv.2015.01.012
Bohara RA, Thorat ND, Pawar SH (2016) Role of functionalization: strategies to explore potential nano-bio applications of magnetic nanoparticles. RSC Adv 6:43989–44012. https://doi.org/10.1039/C6RA02129H
Boury B, Plumejeau S (2015) Metal oxides and polysaccharides: an efficient hybrid association for materials chemistry. Green Chem 17:72–88. https://doi.org/10.1039/C4GC00957F
Carpenter AW, de Lannoy C-F, Wiesner MR (2015) Cellulose nanomaterials in water treatment technologies. Environ Sci Technol 49:5277–5287. https://doi.org/10.1021/es506351r
Charpentier TVJ, Neville A, Lanigan JL et al (2016) Preparation of magnetic carboxymethylchitosan nanoparticles for adsorption of heavy metal ions. ACS Omega 1:77–83. https://doi.org/10.1021/acsomega.6b00035
Chen G, Shi H, Tao J et al (2015) Industrial arsenic contamination causes catastrophic changes in freshwater ecosystems. Sci Rep 5:17419. https://doi.org/10.1038/srep17419
Chen A, Shang C, Shao J et al (2017a) Carbon disulfide-modified magnetic ion-imprinted chitosan-Fe(III): a novel adsorbent for simultaneous removal of tetracycline and cadmium. Carbohydr Polym 155:19–27. https://doi.org/10.1016/j.carbpol.2016.08.038
Chen K, He J, Li Y et al (2017b) Removal of cadmium and lead ions from water by sulfonated magnetic nanoparticle adsorbents. J Colloid Interface Sci 494:307–316. https://doi.org/10.1016/j.jcis.2017.01.082
Cheng W, Xu X, Wu F, Li J (2016) Synthesis of cavity-containing iron oxide nanoparticles by hydrothermal treatment of colloidal dispersion. Mater Lett 164:210–212. https://doi.org/10.1016/j.matlet.2015.10.170
Cho E, Tahir MN, Choi JM et al (2015) Novel magnetic nanoparticles coated by benzene- and beta-cyclodextrin-bearing dextran, and the sorption of polycyclic aromatic hydrocarbon. Carbohydr Polym 133:221–228. https://doi.org/10.1016/j.carbpol.2015.06.089
Christen V, Faltermann S, Brun NR et al (2017) Cytotoxicity and molecular effects of biocidal disinfectants (quaternary ammonia, glutaraldehyde, poly(hexamethylene biguanide) hydrochloride PHMB) and their mixtures in vitro and in zebrafish eleuthero-embryos. Sci Total Environ 586:1204–1218. https://doi.org/10.1016/j.scitotenv.2017.02.114
Cizmas L, Sharma VK, Gray CM, McDonald TJ (2015) Pharmaceuticals and personal care products in waters: occurrence, toxicity, and risk. Environ Chem Lett 13:381–394. https://doi.org/10.1007/s10311-015-0524-4
Crini G (2005) Recent developments in polysaccharide-based materials used as adsorbents in wastewater treatment. Prog Polym Sci 30:38–70. https://doi.org/10.1016/j.progpolymsci.2004.11.002
Crini G, Torri G, Lichtfouse E et al (2019) Dye removal by biosorption using cross-linked chitosan-based hydrogels. Environ Chem Lett. https://doi.org/10.1007/s10311-019-00903-y
Daniel-da-Silva AL, Trindade T, Goodfellow BJ et al (2007) In situ synthesis of magnetite nanoparticles in carrageenan gels. Biomacromol 8:2350–2357. https://doi.org/10.1021/bm070096q
Daniel-da-Silva A, Carvalho R, Trindade T (2013) Magnetic hydrogel nanocomposites and composite nanoparticles—a review of recent patented works. Recent Pat Nanotechnol 7:153–166. https://doi.org/10.2174/18722105113079990008
Daniel-da-Silva AL, Salgueiro AM, Creaney B et al (2015) Carrageenan-grafted magnetite nanoparticles as recyclable sorbents for dye removal. J Nanoparticle Res 17:302. https://doi.org/10.1007/s11051-015-3108-0
Dehabadi L, Wilson LD (2014) Polysaccharide-based materials and their adsorption properties in aqueous solution. Carbohydr Polym 113:471–479. https://doi.org/10.1016/j.carbpol.2014.06.083
Ding C, Sun Y, Wang Y et al (2017) Adsorbent for resorcinol removal based on cellulose functionalized with magnetic poly(dopamine). Int J Biol Macromol 99:578–585. https://doi.org/10.1016/j.ijbiomac.2017.03.018
Divya K, Jisha MS (2017) Chitosan nanoparticles preparation and applications. Environ Chem Lett 16:1–12. https://doi.org/10.1007/s10311-017-0670-y
Dsikowitzky L, Schwarzbauer J (2014) Industrial organic contaminants: identification, toxicity and fate in the environment. Environ Chem Lett 12:371–386. https://doi.org/10.1007/s10311-014-0467-1
Duman O, Tunç S, Polat TG, Bozoğlan BK (2016) Synthesis of magnetic oxidized multiwalled carbon nanotube-κ-carrageenan-Fe3O4 nanocomposite adsorbent and its application in cationic methylene blue dye adsorption. Carbohydr Polym 147:79–88. https://doi.org/10.1016/j.carbpol.2016.03.099
Fan C, Li K, Li J et al (2017) Comparative and competitive adsorption of Pb(II) and Cu(II) using tetraethylenepentamine modified chitosan/CoFe2O4 particles. J Hazard Mater 326:211–220. https://doi.org/10.1016/j.jhazmat.2016.12.036
Fernandes T, Soares S, Trindade T, Daniel-da-Silva A (2017) Magnetic hybrid nanosorbents for the uptake of paraquat from water. Nanomaterials 7:68. https://doi.org/10.3390/nano7030068
Flora G, Gupta D, Tiwari A (2012) Toxicity of lead: a review with recent updates. Interdiscip Toxicol 5:47–58. https://doi.org/10.2478/v10102-012-0009-2
Funes A, de Vicente J, de Vicente I (2017) Synthesis and characterization of magnetic chitosan microspheres as low-density and low-biotoxicity adsorbents for lake restoration. Chemosphere 171:571–579. https://doi.org/10.1016/j.chemosphere.2016.12.101
Galhoum AA, Atia AA, Mahfouz MG et al (2015a) Dy(III) recovery from dilute solutions using magnetic-chitosan nano-based particles grafted with amino acids. J Mater Sci 50:2832–2848. https://doi.org/10.1007/s10853-015-8845-z
Galhoum AA, Mafhouz MG, Abdel-Rehem ST et al (2015b) Cysteine-functionalized chitosan magnetic nano-based particles for the recovery of light and heavy rare earth metals: uptake kinetics and sorption isotherms. Nanomaterials 5:154–179. https://doi.org/10.3390/nano5010154
Galhoum AA, Mahfouz MG, Atia AA et al (2015c) Amino acid functionalized chitosan magnetic nanobased particles for uranyl sorption. Ind Eng Chem Res 54:12374–12385. https://doi.org/10.1021/acs.iecr.5b03331
Galhoum AA, Mahfouz MG, Gomaa NM et al (2017) Chemical modifications of chitosan nano-based magnetic particles for enhanced uranyl sorption. Hydrometallurgy 168:127–134. https://doi.org/10.1016/j.hydromet.2016.08.011
Gentile P, Carmagnola I, Nardo T, Chiono V (2015) Layer-by-layer assembly for biomedical applications in the last decade. Nanotechnology 26:422001. https://doi.org/10.1088/0957-4484/26/42/422001
Gholami M, Vardini MT, Mahdavinia GR (2016) Investigation of the effect of magnetic particles on the crystal violet adsorption onto a novel nanocomposite based on κ-carrageenan-g-poly(methacrylic acid). Carbohydr Polym 136:772–781. https://doi.org/10.1016/j.carbpol.2015.09.044
Girginova PI, Daniel-da-Silva AL, Lopes CB et al (2010) Silica coated magnetite particles for magnetic removal of Hg2+ from water. J Colloid Interface Sci 345:234–240. https://doi.org/10.1016/j.jcis.2010.01.087
Glasgow W, Fellows B, Qi B et al (2016) Continuous synthesis of iron oxide (Fe3O4) nanoparticles via thermal decomposition. Particuology 26:47–53. https://doi.org/10.1016/j.partic.2015.09.011
Gyergyek S, Makovec D, Jagodič M et al (2017) Hydrothermal growth of iron oxide NPs with a uniform size distribution for magnetically induced hyperthermia: structural, colloidal and magnetic properties. J Alloys Compd 694:261–271. https://doi.org/10.1016/j.jallcom.2016.09.238
Hong H-J, Jeong HS, Kim B-G et al (2016) Highly stable and magnetically separable alginate/Fe3O4 composite for the removal of strontium (Sr) from seawater. Chemosphere 165:231–238. https://doi.org/10.1016/j.chemosphere.2016.09.034
Hossein BM, Shemirani F, Shirkhodaie M (2016) Aqueous Co(II) adsorption using 8-hydroxyquinoline anchored γ-Fe2O3@chitosan with Co(II) as imprinted ions. Int J Biol Macromol 87:375–384. https://doi.org/10.1016/j.ijbiomac.2016.02.077
Hu W, Murata K, Zhang D (2017) Applicability of LIVE/DEAD BacLight stain with glutaraldehyde fixation for the measurement of bacterial abundance and viability in rainwater. J Environ Sci 51:202–213. https://doi.org/10.1016/j.jes.2016.05.030
Jiang F, Li X, Zhu Y, Tang Z (2014) Synthesis and magnetic characterizations of uniform iron oxide nanoparticles. Phys B Condens Matter 443:1–5. https://doi.org/10.1016/j.physb.2014.03.009
Jiang et al (2014) Jiang X-S, Mathew MP, Du J (2014b) Polyelectrolyte hydrogels: thermodynamics. In: Visakh PM, Bayraktar O, Picó GA (eds) Polyelectrolytes: thermodynamics and rheology. Springer, Switzerland, pp 183–214
Kaur R, Hasan A, Iqbal N et al (2014) Synthesis and surface engineering of magnetic nanoparticles for environmental cleanup and pesticide residue analysis: a review. J Sep Sci 37:1805–1825. https://doi.org/10.1002/jssc.201400256
Kim J-H, Kim S-M, Kim Y-I (2014) Properties of magnetic nanoparticles prepared by co-precipitation. J Nanosci Nanotechnol 14:8739–8744. https://doi.org/10.1166/jnn.2014.9993
Kim H-R, Jang J-W, Park J-W (2016) Carboxymethyl chitosan-modified magnetic-cored dendrimer as an amphoteric adsorbent. J Hazard Mater 317:608–616. https://doi.org/10.1016/j.jhazmat.2016.06.025
Kumar ASK, Jiang S-J (2017) Synthesis of magnetically separable and recyclable magnetic nanoparticles decorated with β-cyclodextrin functionalized graphene oxide an excellent adsorption of As(V)/(III). J Mol Liq 237:387–401. https://doi.org/10.1016/j.molliq.2017.04.093
Kumari B, Kumar V, Sinha AK, Ahsan J, Ghosh AK, Wang H, DeBoeck G (2017) Toxicology of arsenic in fish and aquatic systems. Environ Chem Lett 15:43–64. https://doi.org/10.1007/s10311-016-0588-9
Laurent S, Forge D, Port M et al (2008) Magnetic iron oxide nanoparticles: synthesis, stabilization, vectorization, physicochemical characterizations, and biological applications. Chem Rev 108:2064–2110. https://doi.org/10.1021/cr068445e
Laus R, de Fávere VT (2011) Competitive adsorption of Cu(II) and Cd(II) ions by chitosan crosslinked with epichlorohydrin–triphosphate. Bioresour Technol 102:8769–8776. https://doi.org/10.1016/j.biortech.2011.07.057
Lee J, Isobe T, Senna M (1996) Magnetic properties of ultrafine magnetite particles and their slurries prepared via in-situ precipitation. Colloids Surf A Physicochem Eng Asp 109:121–127. https://doi.org/10.1016/0927-7757(95)03479-X
Leung H-W (2001) Ecotoxicology of glutaraldehyde: review of environmental fate and effects studies. Ecotoxicol Environ Saf 49:26–39. https://doi.org/10.1006/eesa.2000.2031
Li K, Li P, Cai J et al (2016a) Efficient adsorption of both methyl orange and chromium from their aqueous mixtures using a quaternary ammonium salt modified chitosan magnetic composite adsorbent. Chemosphere 154:310–318. https://doi.org/10.1016/j.chemosphere.2016.03.100
Li X, Lu H, Zhang Y et al (2016b) Fabrication of magnetic alginate beads with uniform dispersion of CoFe2O4 by the polydopamine surface functionalization for organic pollutants removal. Appl Surf Sci 389:567–577. https://doi.org/10.1016/j.apsusc.2016.07.162
Li B, Zhou F, Huang K et al (2017) Environmentally friendly chitosan/PEI-grafted magnetic gelatin for the highly effective removal of heavy metals from drinking water. Sci Rep 7:43082. https://doi.org/10.1038/srep43082
Liang X, Duan J, Xu Q et al (2017) Ampholytic microspheres constructed from chitosan and carrageenan in alkali/urea aqueous solution for purification of various wastewater. Chem Eng J 317:766–776. https://doi.org/10.1016/j.cej.2017.02.089
Lin S, Lin K, Lu D, Liu Z (2017) Preparation of uniform magnetic iron oxide nanoparticles by co-precipitation in a helical module microchannel reactor. J Environ Chem Eng 5:303–309. https://doi.org/10.1016/j.jece.2016.12.011
Ling D, Lee N, Hyeon T (2015) Chemical synthesis and assembly of uniformly sized iron oxide nanoparticles for medical applications. Acc Chem Res 48:1276–1285. https://doi.org/10.1021/acs.accounts.5b00038
Lu S, Li H, Zhang F et al (2016) Sorption of Pb(II) on carboxymethyl chitosan-conjugated magnetite nanoparticles: application of sorbent dosage-dependent isotherms. Colloid Polym Sci 294:1369–1379. https://doi.org/10.1007/s00396-016-3893-8
Lü T, Chen Y, Qi D et al (2017) Treatment of emulsified oil wastewaters by using chitosan grafted magnetic nanoparticles. J Alloys Compd 696:1205–1212. https://doi.org/10.1016/j.jallcom.2016.12.118
Luo Y, Wang Q (2014) Recent development of chitosan-based polyelectrolyte complexes with natural polysaccharides for drug delivery. Int J Biol Macromol 64:353–367. https://doi.org/10.1016/j.ijbiomac.2013.12.017
Luo X, Lei X, Xie X et al (2016) Adsorptive removal of lead from water by the effective and reusable magnetic cellulose nanocomposite beads entrapping activated bentonite. Carbohydr Polym 151:640–648. https://doi.org/10.1016/j.carbpol.2016.06.003
Ma J, Zhuang Y, Yu F (2015) Facile method for the synthesis of a magnetic CNTs-C@Fe-chitosan composite and its application in tetracycline removal from aqueous solutions. Phys Chem Chem Phys 17:15936–15944. https://doi.org/10.1039/C5CP02542G
Madhura L, Singh S, Kanchi S et al (2019) Nanotechnology-based water quality management for wastewater treatment. Environ Chem Lett 17:65–121. https://doi.org/10.1007/s10311-018-0778-8
Mahdavinia GR, Mosallanezhad A (2016) Facile and green rout to prepare magnetic and chitosan-crosslinked κ-carrageenan bionanocomposites for removal of methylene blue. J Water Process Eng 10:143–155. https://doi.org/10.1016/j.jwpe.2016.02.010
Mahdavinia GR, Hasanpour S, Behrouzi L, Sheykhloie H (2016) Study on adsorption of Cu(II) on magnetic starch-g-polyamidoxime/montmorillonite/Fe3O4 nanocomposites as novel chelating ligands. Starch Stärke 68:188–199. https://doi.org/10.1002/star.201400255
Maitra J, Shukla VK (2014) Cross-linking in hydrogels—a review. Am J Polym Sci 4:25–31. https://doi.org/10.5923/j.ajps.20140402.01
Malik LA, Bashir A, Qureashi A, Pandith AH (2019) Detection and removal of heavy metal ions: a review. Environ Chem Lett. https://doi.org/10.1007/s10311-019-00891-z
Martínez-Cabanas M, López-García M, Barriada JL et al (2016) Green synthesis of iron oxide nanoparticles. Development of magnetic hybrid materials for efficient As(V) removal. Chem Eng J 301:83–91. https://doi.org/10.1016/j.cej.2016.04.149
Mehta D, Mazumdar S, Singh SK (2015) Magnetic adsorbents for the treatment of water/wastewater—a review. J Water Process Eng 7:244–265. https://doi.org/10.1016/j.jwpe.2015.07.001
Mondal S, Li C, Wang K (2015) Bovine serum albumin adsorption on glutaraldehyde cross-linked chitosan hydrogels. J Chem Eng Data 60:2356–2362. https://doi.org/10.1021/acs.jced.5b00264
Muzzarelli RAA (2009) Genipin-crosslinked chitosan hydrogels as biomedical and pharmaceutical aids. Carbohydr Polym 77:1–9. https://doi.org/10.1016/j.carbpol.2009.01.016
Nair NR, Sekhar VC, Nampoothiri KM, Pandey A (2017) Biodegradation of biopolymers. In: Pandey A, Negi S, Soccol CR (eds) Current developments in biotechnology and bioengineering. Elsevier, Amsterdam, pp 739–755
Neeraj G, Krishnan S, Kumar PS et al (2016) Performance study on sequestration of copper ions from contaminated water using newly synthesized high effective chitosan coated magnetic nanoparticles. J Mol Liq 214:335–346. https://doi.org/10.1016/j.molliq.2015.11.051
Ni W, Huang Y, Wang X et al (2014) Associations of neonatal lead, cadmium, chromium and nickel co-exposure with DNA oxidative damage in an electronic waste recycling town. Sci Total Environ 472:354–362. https://doi.org/10.1016/j.scitotenv.2013.11.032
Nie J, Wang Z, Hu Q (2016) Chitosan hydrogel structure modulated by metal ions. Sci Rep 6:36005. https://doi.org/10.1038/srep36005
Pujana MA, Pérez-Álvarez L, Iturbe LCC, Katime I (2014) Water soluble folate-chitosan nanogels crosslinked by genipin. Carbohydr Polym 101:113–120. https://doi.org/10.1016/j.carbpol.2013.09.014
Pušnik K, Goršak T, Drofenik M, Makovec D (2016) Synthesis of aqueous suspensions of magnetic nanoparticles with the co-precipitation of iron ions in the presence of aspartic acid. J Magn Magn Mater 413:65–75. https://doi.org/10.1016/j.jmmm.2016.04.032
Rebelo R, Fernandes M, Fangueiro R (2017) Biopolymers in medical implants: a brief review. Proc Eng 200:236–243. https://doi.org/10.1016/j.proeng.2017.07.034
Reddy DHK, Yun Y-S (2016) Spinel ferrite magnetic adsorbents: alternative future materials for water purification? Coord Chem Rev 315:90–111. https://doi.org/10.1016/j.ccr.2016.01.012
Reguyal F, Sarmah AK, Gao W (2017) Synthesis of magnetic biochar from pine sawdust via oxidative hydrolysis of FeCl2 for the removal sulfamethoxazole from aqueous solution. J Hazard Mater 321:868–878. https://doi.org/10.1016/j.jhazmat.2016.10.006
Resch-Fauster K, Klein A, Blees E, Feuchter M (2017) Mechanical recyclability of technical biopolymers: potential and limits. Polym Test 64:287–295. https://doi.org/10.1016/j.polymertesting.2017.10.017
Rodriguez AFR, Costa TP, Bini RA et al (2017) Surface functionalization of magnetite nanoparticle: a new approach using condensation of alkoxysilanes. Phys B Condens Matter 521:141–147. https://doi.org/10.1016/j.physb.2017.06.043
Roth H-C, Schwaminger SP, Schindler M et al (2015) Influencing factors in the CO-precipitation process of superparamagnetic iron oxide nano particles: a model based study. J Magn Magn Mater 377:81–89. https://doi.org/10.1016/j.jmmm.2014.10.074
Saber-Samandari S, Saber-Samandari S, Joneidi-Yekta H, Mohseni M (2017) Adsorption of anionic and cationic dyes from aqueous solution using gelatin-based magnetic nanocomposite beads comprising carboxylic acid functionalized carbon nanotube. Chem Eng J 308:1133–1144. https://doi.org/10.1016/j.cej.2016.10.017
Sahraei et al (2017) Sahraei R, Sekhavat Pour Z, Ghaemy M (2017) Novel magnetic bio-sorbent hydrogel beads based on modified gum tragacanth/graphene oxide: removal of heavy metals and dyes from water. J Clean Prod 142:2973–2984. https://doi.org/10.1016/j.jclepro.2016.10.170
Sakti SCW, Narita Y, Sasaki T et al (2015) A novel pyridinium functionalized magnetic chitosan with pH-independent and rapid adsorption kinetics for magnetic separation of Cr(VI). J Environ Chem Eng 3:1953–1961. https://doi.org/10.1016/j.jece.2015.05.004
Salgueiro AM, Daniel-da-Silva AL, Girão AV et al (2013) Unusual dye adsorption behavior of κ-carrageenan coated superparamagnetic nanoparticles. Chem Eng J 229:276–284. https://doi.org/10.1016/j.cej.2013.06.015
Satarug S, Garrett SH, Sens MA, Sens DA (2009) Cadmium, environmental exposure, and health outcomes. Environ Health Perspect 118:182–190. https://doi.org/10.1289/ehp.0901234
Sengupta A, Rao R, Bahadur D (2017) Zn2+—silica modified cobalt ferrite magnetic nanostructured composite for efficient adsorption of cationic pollutants from water. ACS Sustain Chem Eng 5:1280–1286. https://doi.org/10.1021/acssuschemeng.6b01186
Simeonidis K, Mourdikoudis S, Kaprara E et al (2016) Inorganic engineered nanoparticles in drinking water treatment: a critical review. Environ Sci Water Res Technol 2:43–70. https://doi.org/10.1039/C5EW00152H
Soares SF, Simões TR, António M et al (2016) Hybrid nanoadsorbents for the magnetically assisted removal of metoprolol from water. Chem Eng J 302:560–569. https://doi.org/10.1016/j.cej.2016.05.079
Soares SF, Rodrigues MI, Trindade T, Daniel-da-Silva AL (2017a) Chitosan-silica hybrid nanosorbents for oil removal from water. Colloids Surf A Physicochem Eng Asp 532:305–313. https://doi.org/10.1016/j.colsurfa.2017.04.076
Soares SF, Simões TR, Trindade T, Daniel-da-Silva AL (2017b) Highly efficient removal of dye from water using magnetic carrageenan/silica hybrid nano-adsorbents. Water Air Soil Pollut 228:87. https://doi.org/10.1007/s11270-017-3281-0
Soares SF, Fernandes T, Trindade T, Daniel-da-Silva AL (2018) Surface engineered magnetic biosorbents for water treatment. In: Crini G, Lichtfouse E (eds) Green adsorbents for pollutant removal. Environmental chemistry for a sustainable world. Springer, Cham, pp 301–342. https://doi.org/10.1007/978-3-319-92111-2_9
Sohni S, Gul K, Ahmad F et al (2017) Highly efficient removal of acid red-17 and bromophenol blue dyes from industrial wastewater using graphene oxide functionalized magnetic chitosan composite. Polym Compos. https://doi.org/10.1002/pc.24349
Song W, Gao B, Xu X et al (2016a) Adsorption of nitrate from aqueous solution by magnetic amine-crosslinked biopolymer based corn stalk and its chemical regeneration property. J Hazard Mater 304:280–290. https://doi.org/10.1016/j.jhazmat.2015.10.073
Song W, Gao B, Xu X et al (2016b) Adsorption–desorption behavior of magnetic amine/Fe3O4 functionalized biopolymer resin towards anionic dyes from wastewater. Bioresour Technol 210:123–130. https://doi.org/10.1016/j.biortech.2016.01.078
Song X, Li L, Geng Z et al (2017) Effective and selective adsorption of As(III) via imprinted magnetic Fe3O4/HTCC composite nanoparticles. J Environ Chem Eng 5:16–25. https://doi.org/10.1016/j.jece.2016.11.016
Sousa FL, Daniel-da-Silva AL, Silva NJO, Trindade T (2015) Bionanocomposites for magnetic removal of water pollutants. In: Thakur VK (ed) Eco-friendly polymer nanocomposites: chemistry and applications. Springer, Berlin, pp 279–310
Srivastava S, Kotov NA (2008) Composite layer-by-layer (LBL) assembly with inorganic nanoparticles and nanowires. Acc Chem Res 41:1831–1841. https://doi.org/10.1021/ar8001377
Su C (2017) Environmental implications and applications of engineered nanoscale magnetite and its hybrid nanocomposites: a review of recent literature. J Hazard Mater 322:48–84. https://doi.org/10.1016/j.jhazmat.2016.06.060
Sun C, Lee J, Zhang M (2008) Magnetic nanoparticles in MR imaging and drug delivery. Adv Drug Deliv Rev 60:1252–1265. https://doi.org/10.1016/j.addr.2008.03.018
Tancredi P, Botasini S, Moscoso-Londoño O et al (2015) Polymer-assisted size control of water-dispersible iron oxide nanoparticles in range between 15 and 100nm. Colloids Surf A Physicochem Eng Asp 464:46–51. https://doi.org/10.1016/j.colsurfa.2014.10.001
Tang SCN, Lo IMC (2013) Magnetic nanoparticles: essential factors for sustainable environmental applications. Water Res 47:2613–2632. https://doi.org/10.1016/j.watres.2013.02.039
Tanhaei B, Ayati A, Lahtinen M et al (2016) A magnetic mesoporous chitosan based core-shells biopolymer for anionic dye adsorption: kinetic and isothermal study and application of ANN. J Appl Polym Sci 133:43466. https://doi.org/10.1002/app.43466
Tchounwou PB, Yedjou CG, Patlolla AK, Sutton DJ (2012) Heavy metal toxicity and the environment. EXS 101:133–164. https://doi.org/10.1007/978-3-7643-8340-4_6
Valle LJ, Díaz A, Puiggalí J (2017) Hydrogels for biomedical applications: cellulose, chitosan, and protein/peptide derivatives. Gels 3:27. https://doi.org/10.3390/gels3030027
Vandenbossche M, Jimenez M, Casetta M, Traisnel M (2015) Remediation of heavy metals by biomolecules: a review. Crit Rev Environ Sci Technol 45:1644–1704. https://doi.org/10.1080/10643389.2014.966425
Wang Y, Li L, Luo C et al (2016) Removal of Pb2+ from water environment using a novel magnetic chitosan/graphene oxide imprinted Pb2+. Int J Biol Macromol 86:505–511. https://doi.org/10.1016/j.ijbiomac.2016.01.035
Wilbur S, Abadin H, Fay M, Yu D, Tencza B, Ingerman L, Klotzbach J, James S (2012) Toxicological profile for chromium. U.S. Department of Health and Human Services, Washington (DC)
Wu W, He Q, Jiang C (2008) Magnetic iron oxide nanoparticles: synthesis and surface functionalization strategies. Nanoscale Res Lett 3:397–415. https://doi.org/10.1007/s11671-008-9174-9
Wu W, Wu Z, Yu T et al (2015) Recent progress on magnetic iron oxide nanoparticles: synthesis, surface functional strategies and biomedical applications. Sci Technol Adv Mater 16:023501. https://doi.org/10.1088/1468-6996/16/2/023501
Xiao C, Liu X, Mao S et al (2017) Sub-micron-sized polyethylenimine-modified polystyrene/Fe3O4/chitosan magnetic composites for the efficient and recyclable adsorption of Cu(II) ions. Appl Surf Sci 394:378–385. https://doi.org/10.1016/j.apsusc.2016.10.116
Xu P, Zeng GM, Huang DL et al (2012) Use of iron oxide nanomaterials in wastewater treatment: a review. Sci Total Environ 424:1–10. https://doi.org/10.1016/j.scitotenv.2012.02.023
Yang D, Qiu L, Yang Y (2016a) Efficient adsorption of methyl orange using a modified chitosan magnetic composite adsorbent. J Chem Eng Data 61:3933–3940. https://doi.org/10.1021/acs.jced.6b00706
Yang X, Jin D, Zhang M et al (2016b) Fabrication and application of magnetic starch-based activated hierarchical porous carbon spheres for the efficient removal of dyes from water. Mater Chem Phys 174:179–186. https://doi.org/10.1016/j.matchemphys.2016.02.073
Zhang L, Zhong L, Yang S et al (2015) Adsorption of Ni(II) ion on Ni(II) ion-imprinted magnetic chitosan/poly(vinyl alcohol) composite. Colloid Polym Sci 293:2497–2506. https://doi.org/10.1007/s00396-015-3626-4
Zhang Y, Lin X, Zhou Q, Luo X (2016) Fluoride adsorption from aqueous solution by magnetic core-shell Fe3O4@alginate-La particles fabricated via electro-coextrusion. Appl Surf Sci 389:34–45. https://doi.org/10.1016/j.apsusc.2016.07.087
Acknowledgements
This work was developed in the scope of the Project CICECO-Aveiro Institute of Materials, POCI-01-0145-FEDER-007679 (FCT Ref. UID/CTM/50011/2013) and UID/CTM/50011/2019, financed by national funds through the FCT/MEC, and when appropriate cofinanced by the European Regional Development Fund (FEDER) under the PT2020 Partnership Agreement. S. F. Soares thanks the Fundação para a Ciência e Tecnologia (FCT) for the PhD Grant SFRH/BD/121366/2016. T. Fernandes thanks FCT for the PhD Grant SFRH/BD/130934/2017. A. L. D.-d.-S. acknowledges FCT for the research contract under the Program ‘Investigador FCT’ 2014.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Soares, S.F., Fernandes, T., Trindade, T. et al. Recent advances on magnetic biosorbents and their applications for water treatment. Environ Chem Lett 18, 151–164 (2020). https://doi.org/10.1007/s10311-019-00931-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10311-019-00931-8