Abstract
A hybrid nanomaterial was synthesized that consists of poly(5-indolylboronic acid) acting as a molecular imprint (MIP), and of fluorescent carbon dots (CDs). The combination of CDs and MIP endowed the hybrid with stable fluorescence and template selectivity. The addition of glucose causes aggregation and quenching of fluorescence. Aggregation is due to the formation of covalent bonds between the cis-diols of glucose molecules and boronic acid side groups. The fluorometric signal, obtained at excitation/emission wavelengths of 350/450 nm, varies in the 5 to 750 μM glucose concentration range, with a 0.5 μM detection limit. The assay is not interfered by various biomolecules including fructose and was successful applied to the determination of glucose in (spiked) serum. In our perception, the results make this glucose assay an attractive new tool for clinical applications.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
Glucose is one of the most immediate energy sources and metabolic intermediates of cells and plays an essential role in cellular metabolism [1]. It has been shown that abnormal glucose transport in the human body may lead to diabetes or some cancers [2]. Regular glucose detection is generally based on electrochemistry [3], colorimetry [4] and spectrophotometry [5, 6]. The electrochemistry approach often suffers from instability, contamination of the electrode, and high cost [7, 8]. Colorimetry- and spectrophotometry- based methods face challenges in continuous monitoring because of interferences from blood colour and slow detection time lags [9, 10]. To solve these issues, it is important to find high-performance glucose detection materials that are simple and low-cost.
Carbon dots (CDs), because of their unique optical properties, have become a rising star in the carbon family and have attracted considerable interest [11, 12]. In addition, most of the CDs reported possess many specialties similar to those of carbon materials and have demonstrated superiority in photoluminescence (PL) performances, such as tunable PL, excellent thermal stability, and high photostability and electrical conductivity, Hence, CDs appear to be promising in the fields of photochemical catalysis, drug and gene delivery, biological detection, and biomedicine [13, 14].
Due to its high stability and selectivity, low cost and ease of preparation, molecular imprinting polymer (MIP) is a promising strategy for biological molecule recognition [15, 16]. It is generally accepted as an effective tool for clinical analysis, environmental monitoring, and diagnostics [17, 18]. Currently, conductive polymers, including polypyrrole, polyindole and polyaniline, have aroused enormous interest for researchers because of their unique electronic, thermal, and optical performances [19, 20]. Moreover, it is generally known that boronic acid groups are the most widely employed for glucose determination because they undergo cis-diol complexation with glucose. For fluorescent composites, they can serve as either fluorophores or quenchers. The tight but reversible recognition of diol-containing species gives rapid and sensitive response to glucose. [16, 21].
While boronic acid based optical materials have demonstrated high sensitivity for glucose detection, they are probably not suitable for practical glucose detection because they interact not only with glucose but with other saccharides as well [21, 22]. To enhance the selectivity of boronic acid based optical materials, MIPs are introduced as detection materials due to their selective response to the target molecule. However, there is a critical issue when using MIP in biological samples, the selective extraction and rebinding performance of MIP are sharply reduced when the materials fabricated in non-polar organic media are used in aqueous biological solvents. This is because the cavity induced by the template exfoliation probably generates deformation when MIP synthesized with non-polar solvents is applied in aqueous solutions. The superior selectivity and rebinding property of MIP can be retained when the samples are dissolved in the media used in the MIP preparation [18]. Herein, a boronic acid group-functionalized molecularly imprinted CDs hybrid was prepared as a novel PL probe for label free glucose detection (Scheme 1). The designed glucose-imprinted hybrid combines several key advantages into a single material, including simple preparation, tunable and stable fluorescent performance, outstanding structural stability and chemical inertness, and highly selective, sensitive, and reversible binding with glucose. Importantly, glucose can be well distinguished from both its analogues and the various potential interfering substances in a biological sample, which is beneficial for application as a practical platform for glucose monitoring.
Results and discussion
Choice of materials
Boronic acid groups are an ideal recognition element for the determination of saccharides, which have been studied widely [22]. Polyindole is an organic conductive polymer, which combines the optical and electronic performances of metals and semiconductors, showing many attractive properties such as corrosion inhibition property, thermal stability, and low toxicity. The polymer chains of polyindole, in combination with a boronic acid, lead to a novel polymer that is useful for the special recognition of glucose and other polyols by a change in its optical properties [20, 23]. Carbon dots have excellent PL properties with oxygen-containing functional groups, which serve the purpose of immobilizing the carbon dots around PInA.
Synthesis, composition, and morphology of CDs and the glucose-imprinted CDs hybrid
Our strategy for preparing the glucose-imprinted CDs hybrid involves the synthesis of the water-dispersible CDs bearing surface hydroxyl/carboxyl groups, followed by one-step fabrication of molecularly imprinted hybrid in the presence of boronic acid groups (Scheme 1). The optical performances of CDs and the glucose-imprinted CDs hybrid were assessed by UV-visible absorption spectra and fluorescence spectra. From Fig. 1a, an absorption peak of free CDs is observed at 353 nm, which may be ascribed to n-π* transitions of the C = O bond and trapping of excited-stage energy by the surface states [24]. For the glucose-imprinted CD hybrid, there is a slight red shift for the absorption peak at 362 nm (Fig. 1b). This is because of the interaction between the aromatic rings of CDs and the poly(5-indolylboronic acid) (PInA) functional groups [25]. In contrast, pristine PInA has almost no absorption above 260 nm (Fig. 1b). In addition, the fluorescence spectra of both CDs (Fig. 1a) and the glucose-imprinted CDs hybrid (Fig. 1b) display a symmetric emission peak under the irradiation of exciting light. Moreover, a water-dispersed glucose-imprinted CDs hybrid solution displays an intense blue fluorescence color under UV light at 365 nm, showing a faint yellow color in sunlight (Insets in Fig. 1b). This fact suggests the free zig-zag effect with a carbine-like triplet ground state of σ1π1 and that the blue emission is originated from the intrinsic states in the highly crystalline structure [11].
The morphology of the prepared materials was characterized by TEM, and representative results are shown in Fig. 2. It is found that the CDs display a monodisperse nanoparticles structure distributed in the range of 3.5 to 9.3 nm with an average value of 7.1 nm (Fig. S1A). More details of individual CDs are presented in the HRTEM image (inset of Fig. 2a); the lattice fringe of 0.23 nm is in good agreement with that reported for 100 spaces of carbon [11]. The above results suggest that the CDs typically consist of dots based on carbon particles, which are arranged without apparent aggregation. Furthermore, the TEM image of the glucose-imprinted CDs hybrid (Fig. 2b) shows a typical microsphere structure with a part of the CDs at the periphery of PInA, which is probably due to the π–π interaction between the sp2 π clouds of CDs and PInA [19]. Moreover, their size distribution ranges from 200 to 370 nm with an average diameter of 284 nm (Fig. S1B).
The surface and chemical composition were investigated using FT-IR spectrum and XPS. Figure 3a shows the FT-IR spectra of PInA, CDs and the glucose-imprinted CDs hybrid. An obvious broad absorption peak at 3410 cm−1 suggests the presence of the stretching vibration bands of O − H. The vibrational absorption band of C − O and C = O conjugated with condensed aromatic carbons are observed at 1248 and 1719 cm−1, respectively. These oxygen-containing functional groups not only help the CDs to be dispersed well in water but also form hydrogen bonds with PInA, thus immobilizing the CDs stably around the PInA. For the glucose-imprinted CDs hybrid, a new absorption peak of O − H groups at 3376 cm−1 appears due to the strong hydrogen bond between the surface carboxylic acid and hydroxyl groups of CDs and PInA. The C − N bonding vibration appears at 1389 cm−1 and is different from that of PInA at 1400 cm−1, because of the protonation from the carboxylic acid groups of CDs [17, 26]. Additionally, the vibration absorption band at 1090 cm−1 that can be ascribed to B − O − H emerged in both PInA and the glucose-imprinted CDs hybrid, indicating the successful introduction of boronic acid groups [11]. For more insight, XPS measurements were performed. Figure 3b shows that the prepared glucose-imprinted CDs hybrid has four XPS peaks of C 1 s (284 eV), O 1 s (528 eV), N 1 s (400 eV), and B 1 s (190 eV) (Fig. S2), compared with those of CDs involving C 1 s (284 eV) and O 1 s (531 eV), and PInA involving C 1 s (284 eV), B 1 s (189 eV), N 1 s (400 eV), and O 1 s (529 eV) [21, 26]. This further confirms the existence of boronic acid groups.
Detection properties of the glucose-imprinted CDs hybrid
The resultant CDs and glucose-imprinted CDs hybrid demonstrates obvious responses at different pH values (Fig. S3). The fluorescence emission intensity of CDs is apparently pH-dependent, in which the fluorescence intensity reaches the maximum value in a neutral environment and is reduced in strong acidic and alkali solutions. This is attributed to the hydrogen bonds between the surface oxygen-containing groups of CDs in the acid condition, leading to aggregation and fluorescence weakening of CDs [21, 26]. On the other hand, the reducing fluorescence intensity in alkali solution is induced by the deprotonation of carboxyl groups in CDs, enhancing the electrostatic repulsions between them and overcoming the tendency of aggregation by layer-layer stacking. It is also observed that the fluorescence response of the glucose-imprinted CDs hybrid at different pH values shows a similar tendency to that of CDs. These results confirm the fact that the photoluminescence of CDs is derived in part from small sp2 clusters incorporating with surface oxygen-containing groups including carboxylic groups, in which the chemical structure depends on the pH of the solution [27].
The fluorescence responses of the glucose-imprinted CDs hybrid and the non-imprinted CDs hybrid in the presence and absence of glucose were studied at different pH values. The fluorescence quenching efficiency (F 0 /F, F 0 and F are the fluorescence intensities in the absence and presence of glucose, respectively) of the glucose-imprinted CDs hybrid at different pH values is superior to that of the non-imprinted CDs hybrid. Figure 4 demonstrates no obvious change in the fluorescence intensity. These phenomena confirm the specific affinity of the molecularly imprinted CDs hybrid towards glucose. This is because of not only the binding sites but also the well-built imprinting cavities for glucose. Furthermore, we propose that the specific PL quenching of this glucose-imprinted CDs hybrid can be attributed to the formation of boronate complexes between glucose and the glucose-imprinted CDs hybrid. The boronic acid groups on the surface of the glucose-imprinted CDs hybrid allow covalent bridging of the two pairs of cis-diols of the glucose molecule, forming a large aggregation. With the formation of CDs assembly, the PL intensity becomes well-quenched [11]. A similar mechanism was reported in boronic acid functionalized inorganic quantum dots as the signal readout [28, 29].
Further research on the fluorescence quenching effect of glucose towards glucose-imprinted CDs hybrid solution at pH 7.0 is demonstrated in Fig. 5. It can be observed that the relationship between the fluorescence quenching efficiency and the concentrations of glucose can be satisfactorily fitted according to the Stern − Volmer equation:
where F 0 and F are the fluorescence intensities in the absence and presence of glucose, respectively. K sv is the quenching constant of glucose, and C glu is the concentration of glucose [19, 30,31,32,33,34,35].
When glucose is added into the system, it shows a good linear correlation between the concentration of glucose and F 0 /F in the range of 5–750 μM with a correlation coefficient of R 2 = 0.9913. A limit of detection (LOD) of 0.5 μM is achieved for glucose determination based on the signal-to-noise ratio of 3. When a concentration of glucose higher than 5 μM is added into the system, due to the accessibility of the cis-diol units of glucose by the boronic acid group of the glucose-imprinted CDs hybrid, a large assembly containing CDs may form. With the formation of CDs aggregate, the fluorescence of CDs becomes well-quenched. The possibility of aggregate formation increases with increasing glucose concentration, with the PL intensity reducing linearly until the concentration of glucose is 750 μM. At a concentration of glucose more than 750 μM, the quenching tendency of the fluorescence of CDs slows down, because the excessive glucose cannot fully interact with the glucose-imprinted CDs hybrid. To our knowledge, the above results with a wider linear range and lower LOD are comparable to or better than those of previous quantum dots-based fluorescent detection systems (Table S1). To investigate the stability of the glucose-imprinted CDs hybrid, the fluorescent spectra were examined after the hybrid was stored for 10, 20, 30, and 45 days (Fig. S4). An apparent quenching is not discovered after 10 days. 95.4% of the fluorescent intensity is retained after 20 days, and 92.7% is retained after a month. After 45 days, 90.2% of the fluorescent intensity is still retained. The above results show that the prepared hybrid possesses excellent stability.
Effect of other biomolecules
To apply this analytical method to actual practice, a selectivity study was performed in the presence of possible coexisting interfering substances, including AA, DA, GSH, UA, NE, 5-HIAA and DOPAC. An obvious selective quenching effect by glucose is shown in Fig. 6a over other interferents in this assay. This result further confirms the outstanding specificity of the glucose-imprinted CDs hybrid towards glucose, which is mainly due to the specific binding between them as well as the tailor made imprinted cavities for glucose. Moreover, we also investigated the fluorescence behaviours of the prepared materials in the presence of the glucose analogues (maltose, lactose, fructose and sucrose). Figure 6b shows that the above four analogues have little effects (enhancement or quenching). Such high specific recognition is due to the stereostructure properties of glucose and the recognition mechanism of the present strategy. The boronic acid groups of the glucose-imprinted CDs hybrid are fastened by a pair of cis-diols in glucose forming large assemblies [16]. Unlike glucose, fructose has no additional cis conformational diol, which cannot cross-link the glucose-imprinted CDs hybrid and leads to the corresponding fluorescent quenching [21]. This is why no obvious change in PL is observed in the presence of fructose. Similar to the case for lactose, sucrose and maltose have no additional cis-diol units to change the PL of the glucose-imprinted CDs hybrid by cross-linking aggregation [25].
Detection of glucose in real samples
To demonstrate the potential applicability of the approach for glucose analysis, the detection of glucose in real samples was carried out. As shown in Table 1, the concentrations of glucose in human serum samples are in good agreement with the results measured by a commercial blood glucose monitor. Furthermore, standard addition experiments were also carried out. The recoveries of different known amounts of added glucose are obtained from 92.7 to 107.5%, and the relative standard deviation (RSD) is less than 5.54%. The outstanding recovery confirms excellent accuracy for glucose determination in biological samples, suggesting the practicability of the detection system.
Conclusion
In summary, we reported a boronic acid group functionalized molecularly imprinted CDs hybrid using glucose and indolylboronic acid. By taking advantages of CDs, molecular imprinting technique, and fluorescence spectroscopy methodology, the prepared glucose-imprinted CDs hybrid proved to be simple in design and economical in operation for glucose determination with high sensitivity and selectivity. More importantly, glucose detection in real human samples was achieved with satisfactory results, which may provide a new strategy for simple, low-cost and sensitive determination of glucose. However, because of the irreversibility of fluorescence response, this glucose-imprinted CDs hybrid is probably suitable for single-shot assays rather than online monitoring, which might be a challenge for fluorescence detection.
References
Zhang ZY, Chen ZP, Cheng FB, Zhang YW, Chen LX (2017) Highly sensitive on-site detection of glucose in human urine with naked eye based on enzymatic-like reaction mediated etching of gold nanorods. Biosens Bioelectron 89:932–936
Steiner MS, Duerkop A, Wolfbeis OS (2011) Optical methods for sensing glucose. Chem Soc Rev 40:4805–4839
Arakawa T, Kuroki Y, Nitta H, Chouhan P, Toma K, Sawada S, Takeuchi S, Sekita T, Akiyoshi K, Minakuchi S, Mitsubayashi K (2015) Mouthguard biosensor with telemetry system for monitoring of saliva glucose: a novel cavitas sensor. Biosens Bioelectron 84:106–111
Hoa LT, Chung JS, Hur SH (2016) A highly sensitive enzyme-free glucose sensor based on Co3O4 nanoflowers and 3D graphene oxide hydrogel fabricated via hydrothermal synthesis. Sens Actuators B Chem 223:76–82
Lin LP, Song XH, Chen YY, Rong MC, Zhao TT, Wang YR, Jiang YQ, Chen X (2015) Intrinsic peroxidase-like catalytic activity of nitrogen-doped graphene quantum dots and their application in the colorimetric detection of H2O2 and glucose. Anal Chim Acta 869:89–95
Chen S, Hai X, Chen XW, Wang JH (2014) In situ growth of silver nanoparticles on graphene quantum dots for ultrasensitive colorimetric detection of H2O2 and glucose. Anal Chem 86:6689–6694
Hao TF, Wei X, Nie YJ, Xu YQ, Lu K, Yan YS, Zhou ZP (2016) Surface modification and ratiometric fluorescence dual function enhancement for visual and fluorescent detection of glucose based on dual-emission quantum dots hybrid. Sens Actuators B Chem 230:70–76
Liu XJ, Yang WX, Chen LL, Jia JB (2016) Synthesis of copper nanorods for non-enzymatic amperometric sensing of glucose. Microchim Acta 183:2369–2375
Yuan J, Cen Y, Kong XJ, Wu S, Liu CLW, Yu RQ, Chu X (2015) MnO2-nanosheet-modified upconversion nanosystem for sensitive turn-on fluorescence detection of H2O2 and glucose in blood. ACS Appl Mater Interfaces 7:10548–10555
Wang H, Yi JH, Velado D, Yu YY, Zhou SQ (2015) Immobilization of carbon dots in molecularly imprinted microgels for optical sensing of glucose at physiological pH. ACS Appl Mater Interfaces 7:15735–15745
Bradley SJ, Kroon K, Laufersky G, Röding M, Goreham RV, Gschneidtner T, Schroeder K, Moth-Poulsen K, Andersson M, Nann T (2017) Heterogeneity in the fluorescence of graphene and graphene oxide quantum dots. Microchim Acta 184:871–878
Zhang FW, Wen QJ, Hong MZ, Zhuang ZY, Yu Y (2017) Efficient and sustainable metal-free GR/C3N4/CDots ternary heterostructrues for versatile visible-light-driven photoredox applications: towards synergistic interaction of carbon materials. Chem Eng J 307:593–603
Arcudi F, Dordevic L, Prato M (2016) Synthesis, separation, and characterization of small and highly fluorescent nitrogen-doped carbon nanodots. Angew Chem Int Ed 55:2107–2112
Li Y, Zhao Y, Cheng HH, Hu Y, Shi GQ, Dai LM, Qu LT (2011) Nitrogen-doped graphene quantum dots with oxygen-rich functional groups. J Am Chem Soc 134:15–18
Niu MC, Pham-Huy C, He H (2016) Core-shell nanoparticles coated with molecularly imprinted polymers: a review. Microchim Acta 183:2677–2695
Dai H, Xiao DL, He H, Li H, Yuan DH, Zhang C (2015) Synthesis and analytical applications of molecularly imprinted polymers on the surface of carbon nanotubes: a review. Microchim Acta 182:893–908
Zhou X, Wang AQ, Yu CF, Wu SS, Shen J (2015) Facile synthesis of molecularly imprinted graphene quantum dots for the determination of dopamine with affinity-adjustable. ACS Appl Mater Interfaces 7:11741–11747
Wu WT, Shen J, Li YX, Zhu HB, Banerjee P, Zhou SQ (2012) Specific glucose-to-SPR signal transduction at physiological pH by molecularly imprinted responsive hybrid microgels. Biomaterials 33:7115–7125
Zhou X, Ma PP, Wang AQ, Yu CF, Qian T, Wu SS, Shen J (2015) Dopamine fluorescent sensors based on polypyrrole/graphene quantum dots core/shell hybrids. Biosens Bioelectron 64:404–410
Pringsheim BE, Terpetschnig E, Piletsky SA, Wolfbeis OS (1999) A polyaniline with near-infrared optical response to saccharides. Adv Mater 10:865–868
Shen PF, Xia YS (2014) Synthesis-modification integration: one-step fabrication of boronic acid functionalized carbon dots for fluorescent blood sugar sensing. Anal Chem 86:5323–5329
Na WD, Liu H, Wang MY, Su XG (2017) A boronic acid based glucose assay based on the suppression of the inner filter effect of gold nanoparticles on the orange fluorescence of graphene oxide quantum dots. Microchim Acta 184:1463–1470
Mader HS, Wolfbeis OS (2008) Boronic acid based probes for microdetermination of saccharides and glycosylated biomolecules. Microchim Acta 162:1–34
Pan D, Zhang J, Li Z, Wu M (2010) Hydrothermal route for cutting graphene sheets into blue-luminescent graphene quantum dots. Adv Mater 22:734–738
Qu ZB, Zhou XG, Gu L, Lan RM, Sun DD, Yu DJ, Shi GY (2013) Boronic acid functionalized graphene quantum dots as a fluorescent probe for selective and sensitive glucose determination in microdialysate. Chem Commun 49:9830–9832
Zhang L, Zhang ZY, Liang RP, Li YH, Qiu JD (2014) Boron-doped graphene quantum dots for selective glucose sensing based on the “abnormal” aggregation-induced photoluminescence enhancement. Anal Chem 86:4423–4430
Fuyuno N, Kozawa D, Miyauchi Y, Mouri S, Kitaura R, Shinohara H, Yasuda T, Komatsu N, Matsuda K (2014) Drastic change in photoluminescence properties of graphene quantum dots by chromatographic separation. Adv Opt Mater 2:983–989
Wu WT, Zhou T, Berliner A, Banerjee P, Zhou SQ (2010) Glucose-mediated assembly of phenylboronic acid modified CdTe/ZnTe/ZnS quantum dots for intracellular glucose probing. Angew Chem Int Ed 49:6554–6558
Freeman R, Bahshi L, Finder T, Gill R, Willner I (2009) Competitive analysis of saccharides or dopamine by boronic acid-functionalized CdSe–ZnS quantum dots. Chem Commun 7:764–766
Valipour M, Banihabib ME, Behbahani SMR (2013) Comparison of the ARMA, ARIMA, and the autoregressive artificial neural network models in forecasting the monthly inflow of Dez dam reservoir. J Hydrol 476:433–441
Viero DP, Valipour M (2017) Modeling anisotropy in free-surface overland and shallow inundation flows. Adv Water Resour 104:1–14
Valipour M (2017) Global experience on irrigation management under different scenarios. J Water Land Dev 32:95–102
Valipour M (2016) Variations of land use and irrigation for next decades under different scenarios. Braz J Irrig Drain 88:262–288
Valipour M (2016) How much meteorological information is necessary to achieve reliable accuracy for rainfall estimations? Agriculture 6:53
Valipour M, Peng D, Sefidkouhi MAG, Raeini−Sarjaz M (2017) Selecting the best model to estimate potential evapotranspiration with respect to climate change and magnitudes of extreme events. Agric Water Manag 180:50–60
Acknowledgments
This work was supported by the Fundamental Research Funds for the Central Non-profit Research Institution of CAF (CAFYBB2017ZX003), the Fundamental Research Funds of Research Institute of Forest New Technology (CAFYBB2017SY033).
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
The author(s) declare that they have no competing interests.
Electronic supplementary material
ESM 1
(DOC 971 kb)
Rights and permissions
About this article
Cite this article
Zhou, X., Gao, X., Liu, M. et al. A poly(5-indolylboronic acid) based molecular imprint doped with carbon dots for fluorometric determination of glucose. Microchim Acta 184, 4175–4181 (2017). https://doi.org/10.1007/s00604-017-2448-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00604-017-2448-0