Abstract
Low-cycle fatigue behavior of the Sn-Ag-Cu ternary-eutectic alloy was investigated under a fully reversed loading condition. The solder alloy exhibited cyclic softening early in the fatigue life and continued to soften as the number of fatigue cycles increased. Following cyclic loading, numerous microcracks were found in the microstructure. Most of the microcracks were located along the grain boundaries in the areas with finer grains. The areal density of the microcracks increased with both strain amplitude and cycle number. By combining percolation theory with microcracking analysis, the cycle-dependent softening behavior was shown to result from accumulation of microcrack density with fatigue cycles.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
I. Ohnuma, M. Miyashita, K. Anzai, X.J. Liu, H. Ohtani, R. Kainuma, and K. Ishida, J. Electron. Mater. 29, 1137 (2000).
K.W. Moon, W.J. Boettinger, U.R. Kattner, F.S. Biancaniello, and C.A. Handwerker, J. Electron. Mater. 29, 1122 (2000).
I. Shohji, T. Yoshida, T. Takahashi, and S. Hioki, Mater. Trans. 43, 1854 (2002).
W. Ren, Z. Qian, M. Lu, S. Liu, and D. Shangguan, J. Electron. Packaging 121, 271 (1999).
K. Suganuma, Curr. Op. Solid State Mater. Sci. 5, 55 (2001).
J.H. Lau and Y.H. Pao, Solder Joint Reliability of BGA, CSP, Flip Chip, and Fine Pitch SMT Assemblies (New York: McGraw-Hill, 1997).
S. Choi, K.N. Subramanian, J.P. Lucas, and T.R. Bieler, J. Electron. Mater. 29, 1249 (2000).
C. Kanchanomai, Y. Miyashita, and Y. Mutoh, J. Electron. Mater. 31, 456 (2002).
Y. Kariya and M. Otsuka, J. Electron. Mater. 27, 1229 (1998).
R.W. Hertzberg, Deformation and Fracture Mechanics of Engineering Materials (New York: John Wiley & Sons, 1996), pp. 557–566.
W.J. Plumtree, C.R. Gagg, and S. Peters J. Electron. Mater. 30, 1178 (2001).
S. Vaynaman, M.E. Fine, and D.A. Jeannotte, Metall. Trans. A 19, 1051 (1988).
C. Kanchanomai, Y. Miyashita, Y. Mutoh, and S.L. Mannan, Mater. Sci. Eng. A 345, 90 (2003).
C. Kanchanomai, Y. Miyashita, and Y. Mutoh, Int. J. Fatigue 24, 987 (2002).
M.E. Fine, Metall. Trans. A 11A, 365 (1980).
V. Stolkarts, L.M. Keer, and M.E. Fine, J. Mech. Phys. Solids 47, 2451 (1999).
B. Budiansky and R.J. O’Connel, Int. J. Solids Struct. 12, 81 (1976).
L.M. Kachanov, Introduction to Continuum Damage Mechanics (Boston, MA: Kluwers Academic Publishers, 1986).
R. Zallen, The Physics of Amorphous Solids (New York: John Wiley & Sons, 1983).
W. Koster and H. Franz, Metall. Rev. 21, 1 (1961).
J. Zhao, Y. Mutoh, Y. Miyashita, and S.L. Mannan, J. Electron. Mater. 31, 879 (2002).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Zeng, QL., Wang, ZG., Xian, AP. et al. Cyclic softening of the Sn-3.8Ag-0.7Cu lead-free solder alloy with equiaxed grain structure. J. Electron. Mater. 34, 62–67 (2005). https://doi.org/10.1007/s11664-005-0181-7
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s11664-005-0181-7