Abstract
Sn-rich alloys in the Sn-Ag-Cu system are being studied for their potential as Pb-free solders. Thus, the location of the ternary eutectic involving L, (Sn), Ag3Sn and Cu6Sn5 phases is of critical interest. Phase diagram data in the Sn-rich corner of the Sn-Ag-Cu system are measured. The ternary eutectic is confirmed to be at a composition of 3.5 wt.% Ag, 0.9 wt.% Cu at a temperature of 217.2±0.2°C (2σ). A thermodynamic calculation of the Sn-rich part of the diagram from the three constituent binary systems and the available ternary data using the CALPHAD method is conducted. The best fit to the experimental data is 3.66 wt.% Ag and 0.91 wt.% Cu at a temperature of 216.3°C. Using the thermodynamic description to obtain the enthalpy- temperature relation, the DTA signal is simulated and used to explain the difficulty of liquidus measurements in these alloys.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
NCMS Report 0401RE96, Lead-Free Solder Project (Ann Arbor, MI: National Center for Manufacturing Sciences, August 1997).
J. Bath, C.A. Handwerker, and E. Bradley, NEMI Group Recommends “Standardized” Lead-Free Solder Alternative, to be submitted to Circuit Assembly Magazine.
E. Gebhardt and G. Petzow, Z. Metallkde. 50, 597 (1959).
V.N. Fedorov, O.E. Osinchev, and E.T. Yushkina referenced in Phase Diagrams of Metallic Systems, Vol. 26, eds. N.V. Ageev and L.A. Petrova (Moscow, USSR: VINITI, 1982), pp. 149–150.
C.M. Miller, I.E. Anderson, and J.F. Smith, J. Electron. Mater. 23, 595 (1994).
U.S. patent 5,527,628 (1996).
M.E. Loomans and M.E. Fine, Metall. Mater. Trans. A 31A, 1155 (2000).
R.I. Wu and J.H. Perepezko, Metall. Mater. Trans. A 31A, 497 (2000).
Y.-M. Muggianu, M. Gambino, and J.-P. Bros, J. Chim. Phys. 72, 85 (1975).
U.R. Kattner and W.J. Boettinger, J. Electron. Mater. 23, 603 (1994).
W.J. Boettinger, C.A. Handwerker, and U.R. Kattner, The Mechanics of Solder Alloy Wetting and Spreading, ed. F.G. Yost, F.M. Hosking, and D.R. Frear (New York: Van Nostrand Reinhold, 1993), pp. 103–140.
F.H. Hayes, H.L. Lukas, G. Effenberg, and G. Petzow, Z. Metallkde. 77, 749 (1986).
A.T. Dinsdale, CALPHAD 15, 317 (1991).
C.-S. Oh, J.-H. Shim, B.-J. Lee, and D.N. Lee, J. Alloys Compds. 238, 155 (1996).
J.-H. Shim, C.-S. Oh, B.-J. Lee, and D.N. Lee, Z. Metallkde. 87, 205 (1996).
H. Krieg, unpublished research (Stuttgart, Germany: Max-Planck-Institut für Metallforschung, 1982).
S. Chada, W. Laub, R.A. Fournelle, and D. Shangguan, J. Electron. Mater. 28, 1194 (1999).
H.L. Lukas, E.Th. Henig, and B. Zimmermann, CALPHAD 1, 225 (1977).
T.B. Massalski, ed. in chief, Binary Alloy Phase Diagrams, 1st ed. (Materials Park, OH: ASM International, 1986), pp. 964–965: 2nd ed. (Materials Park, OH: 1990), pp. 1481–1483.
W.J. Boettinger, unpublished research (Gaithersburg MD: NIST, 2000).
P.-Y. Chevalier, Thermochim. Acta 136, 45 (1988).
T.L. Ngai and Y.A. Chang, CALPHAD 5, 267 (1981).
I. Ansara, LPTCM-ENSEEG, Grenoble, France, private communication, 1993.
B.-J. Lee, KRISS, Taejon, South Korea, private communication, 1999.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Moon, K.W., Boettinger, W.J., Kattner, U.R. et al. Experimental and thermodynamic assessment of Sn-Ag-Cu solder alloys. J. Electron. Mater. 29, 1122–1136 (2000). https://doi.org/10.1007/s11664-000-0003-x
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s11664-000-0003-x