Abstract
Macroscopic sliding between two solids is triggered by the propagation of a micro-slip front along the frictional interface. In certain conditions, sliding is preceded by the propagation of aborted fronts, spanning only part of the contact interface. The selection of the characteristic size spanned by those so-called precursors remains poorly understood. Here, we introduce a 1D toy model of precursors between a slider and a track in which the fronts are quasi-static self-healing slip pulses. When the slider’s thickness is large compared to the elastic correlation length and when the interfacial stiffness is small compared with the bulk stiffness, we provide an analytical solution for the length of the first precursor, \(\varLambda\), and the shear stress field associated with it. These quantities are given as a function of the bulk material parameters, the frictional properties of the interface and the macroscopic loading conditions. Analytical results are in quantitative agreement with the numerical solution of the model. In contrast with previous models, our model predicts that \(\varLambda\) does not depend on the frictional breaking threshold of the interface. Our results should be relevant to the various systems in which self-healing slip pulses have been observed.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
Despite the importance of friction [1, 2], several fundamental aspects of the problem, such as a detailed description of the beginning of sliding motion, are still not fully understood. Recent experiments allowed visualization of the onset of sliding in a variety of experimental situations for sphere-on-plane [3, 4] or plane-on-plane [5–8] contacts, for randomly rough [3–7] or micro-structured [8] surfaces, for side-driven [5–7] or top-driven [3, 4, 8] loading. These experiments have revealed that sliding initiation is always mediated by the propagation of micro-slip (rupture) fronts, separating a stuck region and a slipping region, along the contact interface. Propagation was found either quasi-static (controlled by the external loading) [3, 4, 8] or dynamic [5–7] with a variety of speeds from supersonic to anomalously slow [5, 9]. Fronts spanning the whole contact precipitate macroscopic relative motion (sliding) of the bodies in contact. Before that, a series of aborted fronts spanning a portion of the contact only may be observed [6, 7]. Such fronts are called precursors and will be the object of the present work.
In side-driven plane-on-plane contacts [6, 7], all precursors were observed to nucleate near the trailing edge of the contact, where the loading is applied. The first precursor propagates through the shear and normal stress fields produced by the initial loading of the system. After the precursor has stopped, the mechanical state of the interface is modified all along the ruptured path, so that the next fronts will propagate through the stress field prepared by the previous ones [6]. In this context, successive precursors were observed to propagate longer and longer distances [6, 7]. Here, we will address the problem of the selection of the characteristic length of the first precursor.
Several models have previously been used to investigate the series of precursors to sliding. Braun et al. [10] used a dynamic simulation in which the slider was modeled as a chain of blocks coupled by springs, while the interface was treated as a set of “frictional” springs with random breaking thresholds. They reproduced both a series of precursors of increasing length and a modification of the stress field by the precursors. These results stimulated the study of simplified models that would still reproduce series of precursors. In Refs. [7, 11–13], the interface was described by the phenomenological Amontons–Coulomb law of friction: the interface is pinned until the local ratio of shear to normal stress reaches the static friction coefficient \(\mu _{\rm s}\); the interface is then locally slipping and characterized by a kinetic friction coefficient \(\mu _{\rm k} < \mu _{\rm s}\). All these models produce series of growing precursors nucleated at the trailing edge. Maegawa et al. [7] further showed that an asymmetric normal loading influences the precursor length. Scheibert and Dysthe [11] showed that a similar effect is obtained for a symmetric normal loading, as soon as the friction force is not applied exactly in the plane of the contact interface. Amundsen et al. [12] showed that, to be realistic, 1D models should involve an intrinsic length scale for the interfacial stress variations, for instance through the introduction of the shear stiffness of the interface. Trømborg et al. [13] showed that in 2D models, such a length scale naturally arises when introducing the system’s boundary conditions and bulk elasticity.
In all the above simplified models [7, 11–13], each broken contact point repins when its slipping velocity goes back to zero. As a consequence, the observed rupture mode is crack-like, i.e., the precursor front separates a stick region from a region slipping almost everywhere behind it. Recently, however, Braun and coworkers have used a different friction law [14, 15]: the friction between two solids results from multiple individual micro-junctions which break under stress and immediately form again elsewhere. As a consequence, the rupture mode of the interface is of the self-healing slip pulse type, i.e., the slipping part of the interface is confined between the rupture front and a repinning front.
The scope of this work is to propose a toy model, which incorporates this alternative friction law within a 1D elastic model of a solid slider, and use it to investigate the kinematics of the onset of sliding. We will show that, assuming quasi-static propagation, this toy model enables analytic predictions for the length of the first self-healing precursor and the shear stress field associated with it. We emphasize that the self-healing mode is not just a theoretical concept: It was observed in various experiments using widely different materials and loading conditions (see e.g., [8, 16, 17]). Comparatively, as far as the onset of sliding is concerned, it has received much less interest than the crack-like mode. This is why we believe that the present toy model is a valuable first step toward a better understanding of the full dynamics of self-healing slip pulses.
2 Toy Model
We consider that macroscopic contacts are made of a large number of micro-junctions in parallel, with an average distance \(a_{\rm c}\). Let an individual junction (micro-contact, bridge, solid island, etc.) have an average radius \(r_{\rm c}\) and height \(h_{\rm c}\). Considering it as a cylindrical flexible “rod”, we may estimate its elastic constant as \(k_{\rm c} = 3 \pi E r_{\rm c}^4 / 4 h_{\rm c}^3\), where \(E\) is the Young modulus of the material [14]. Elastic theory introduces a characteristic size \(\lambda _{\rm c}\) (known as elastic correlation length) below which the frictional interface behaves rigidly [14, 18]. Typical values of the correlation length lie in the \(\mu\)m scale. The set of \(N_{\rm c} = \lambda _{\rm c}^2 /a_{\rm c}^2\) contacts within the area \(\lambda _{\rm c}^2\) is considered as an effective contact (the \(\lambda\)-contact introduced in [14, 15]) with elastic constant \(k = N_{\rm c} k_{\rm c}\).
At length scales larger than \(\lambda _{\rm c}\), the slider’s bulk is deformable and two distinct points along the interface can move by different amounts. To account for this elasticity, imagine that the slider is discretized into cubic blocks of size \(\lambda _{\rm c}^3\). The elastic coupling between adjacent blocks is modeled by springs connecting only the nearest neighbors, the stiffness of which can be worked out (see below) as functions of only two elastic parameters, Young’s modulus \(E\) and Poisson’s ratio \(\nu\). Because we aim at providing analytical solutions, we progressively reduce the dimensionality of the slider from 3D to 1D. A sketch of the final 1D model is shown in Fig. 1 (right). First the model is reduced to 2D (Fig. 1 left) by reducing the thickness of the slider to only one block’s size, \(\lambda _{\rm c}\). Then, the height of the slider is modeled as a bilayer of blocks: The bottom-most layer (interfacial layer IL) is left as in the 2D model. Each block of the IL having a size \(\lambda _{\rm c}\), it is connected to the track through a single \(\lambda\)-contact. In the upper part of the slider (US), each vertical slice is assumed to behave rigidly, with neighboring slices being connected by internal springs. Note that a similar, though different, model was previously introduced in [19].
Let us consider a slider of length \(L\), height \(H\) and thickness \(W=\lambda _{\rm c}\) (by assumption). We assume that both \(L\) and \(H\) are much larger than \(\lambda _{\rm c}\). Note that in this 1D model, \(H\) should be interpreted as some effective height where the driving force is applied. The horizontal stiffnesses \(K\) and \(K_{\rm L}\) in the IL and US, respectively, can be derived to be:
and
The total transverse stiffness of the slider is \(ELW/2H(1+\nu)\). We assume that we can ascribe the totality of this stiffness to the \(L/\lambda _{\rm c}\) transverse springs \(K_{\rm T}\) connecting the IL to the US. \(K_{\rm T}\) thus reads:
Note that \({K_{\rm T}}/{K_{\rm L}} \sim \left( {\lambda _{\rm c}}/{H}\right) ^2 <<1\). This is a consequence of the rigid connection of the blocks constituting the US (from left to right in Fig. 1). We chose as an assumption to ascribe the totality of the transverse rigidity of the slider to only one plane between the IL and the US. Let us emphasize that, as a matter of fact, there is no exact way to capture 3D elasticity within a 1D model, even qualitatively. In particular, the stress profile in response to a side loading decays as a power law in 3D, whereas it decays exponentially in 1D. The scope of our toy model is thus merely to help us investigate analytically the consequences of the self-healing nature of the rupture on the propagation length. We will see that an important parameter of the toy model is the ratio of interfacial to bulk stiffness \(k/K\). The interface is denoted as stiff if \(k/K \sim 1\) and soft when \(k/K \ll 1\); we concentrate on the latter case, which corresponds to most experimental situations.
The system can be described by three variables: \(u_{\rm t}(x)\) describes the displacement field of the US, \(u(x)\) is the displacement field of the blocks in the IL, and \(u_{\rm b}(x)\) is the displacement of attachment points of the IL to the track.
The stress in the IL is then given by
while the stress which is driving the IL is equal to
The whole system is driven by imposing the displacement of the leftmost block of the US as \(u_{\rm t} (0,t)=v_{\rm d} t\), with \(v_{\rm d}\) an arbitrarily small velocity.
3 Self-healing Slip Pulse-Like Rupture
The frictional behavior of each junction connecting the IL to the track is the following. It acts as a spring of elastic constant \(k\) as long as its stretching remains below a critical value \(u_{\rm s} = f_{\rm s} /k\) but breaks and immediately repins with zero stretching when the local shear stress reaches \(\sigma _{\rm s} = f_{\rm s} /\lambda _{\rm c}^2\).
When a loading is applied to the slider, it is transmitted differently to each \(\lambda\)-contact due to elasticity of the slider. The leftmost \(\lambda\)-contact is the first to reach its breaking threshold, slide and locally relax the interface. This causes an extra stress on the neighboring contacts, which tend to slide too, so that sliding events propagate as a kink, extending the initial relaxed domain. Such a scenario may be described as a solitary wave [14, 15]. The rupture mode is of the self-healing slip pulse type, with a pulse width equal to the lateral size of one contact, \(\lambda _{\rm c}\), because a broken contact repins immediately, before the breaking of its neighbor. Note that, in the absence of the US, and for a displacement controlled loading of the left edge of the slider, no propagation would occur: the first block would not move after breaking of its \(\lambda\)-contact, and thus its right-neighbor would not be further loaded to its breaking threshold.
In order to simplify the analysis, we suppose the existence of a hierarchy of times. Namely, we assume that the pushing rate is adiabatically slow, \(v_{\rm d} \rightarrow 0\), while the sound speed (which determines the rate of propagation of the elastic stress) is very large, \(v_{\rm R} \rightarrow \infty\). Therefore, when a front propagates, it is accompanied by a quasi-static stress field defined by mechanical equilibrium of the forces acting on the interface layer (inertia effects are ignored). In the following, we show that there exists a typical length scale \(\it \Lambda\) , which characterizes the stress accumulation and thus the precursor length.
4 Equations to be Solved
In the discrete model, we have \(x=i \lambda _{\rm c}\), \(u_{\rm t}(x) \rightarrow u_{\rm t,i}\), \(u(x) \rightarrow u_{\rm i}\) and \(u_{\rm b}(x) \rightarrow u_{bi}\). In equilibrium, the displacements should satisfy
In the continuum approximation, these equations reduce to the set of equations:
where \(\kappa _{\rm T} = (K_{\rm T} /K_{\rm L})^{1/2} /\lambda _{\rm c}\), \(\kappa = [(k + K_{\rm T})/K]^{1/2} /\lambda _{\rm c}\) and \(\beta = K_{\rm T} / (K_{\rm T} + k )\).
A key trick of our analytical approach is that the general solution of the equation \(u'' (x) = \kappa ^2 \, [ u(x) - w(x) ]\) is \(u(x) = D \, e^{\pm \kappa x} - \kappa \int_0 ^{x} {\rm d}\xi \, w (\xi ) \sinh [ \kappa (x - \xi ) ] \,\).
As we impose the position of the left-hand side (trailing edge) of the US, we have
while the left-hand side of the IL is free so that
To simplify considerations, we ignore the right-hand-side boundary conditions assuming that the chain is infinite, \(L \rightarrow \infty\), so that \(u_{\rm t} (\infty ) = u(\infty ) = u_{\rm b} (\infty ) =0\).
Let initially, at \(t=0\), the system be completely relaxed: \(u_{\rm t} (x) = u(x) = 0\) and \(u_{\rm b} (x) = u_{\rm b}^{(0)} (x) = 0\). We then start to push slowly the trailing edge of the US, so that \(U_{\rm t}=v_d t\) with \(v_d \rightarrow 0\). The solution of Eqs. (6)–(10) is:
where \(\kappa _{^{1}_{2}}^2 = \frac{1}{2} (\kappa ^2 + \kappa _{\rm T}^2 \pm \sqrt{\mathcal {D}} )\), \(\alpha _{^{1}_{2}} = \frac{1}{2} [ 1 - ( \kappa ^2 \pm \sqrt{\mathcal {D}} / \kappa _{\rm T}^2 )]\), \({\mathcal {D}} = ( \kappa ^2 - \kappa _{\rm T}^2 )^2 + 4 \beta \kappa ^2 \kappa _{\rm T}^2\), \(D_{10} = (\alpha _2 U_{\rm t} - u_{\rm c})/(\alpha _2 - \alpha _1)\), \(D_{20} = (u_{\rm c} - \alpha _1 U_{\rm t})/(\alpha _2 - \alpha _1)\) and \(u_{\rm c} \equiv u(0) = U_{\rm t} \, [\lambda _{\rm c} \beta \kappa ^2 (\kappa _1 - \kappa _2) + (K_{\rm T} /K) \sqrt{\mathcal {D}}]/ [\lambda _{\rm c} \kappa _{\rm T}^2 (\alpha _2 \kappa _2 - \alpha _1 \kappa _1) + \lambda _{\rm c}^2 \kappa ^2 \sqrt{\mathcal {D}}]\).
The positions \(U_{\rm t}\) and \(u_{\rm c}\) grow together until the trailing edge of the US reaches a position \(U_{t0}\) where the left end of the IL achieves the threshold value \(u_{\rm s}\) at some time \(t_1 = U_{t0} /v_d\). At \(t=t_1\) the leftmost \(\lambda\)-contact breaks and attaches again with zero stretching, \(u_{\rm b} (0) = u_{\rm b}^{(1)} (0) = u_{\rm s}\), and the whole system relaxes, adjusting itself to a new configuration with \(u_{\rm t} (0) = U_{t0}\), \(u_{\rm b} (0) = u_{\rm s}\) and \(u_{\rm b} (x \ge \lambda _{\rm c}) =0\). After relaxation, all contacts have shifted to the right, so that the IL stress \(\sigma _{\rm c} (x)\) for \(x \ge \lambda _{\rm c}\) increases. As a consequence, the stress on the second contact has grown above the threshold \(\sigma _{\rm s}\) so that it must break too. This domino-like process will continue until the stress at some (\(s_0\)-th) contact will remain below the threshold. This first passage distance defines a characteristic length \(\varLambda = s_0 \lambda _{\rm c}\) which controls the kinematics of the onset of sliding.
We emphasize that the driving stress \(\sigma _d (x)\), Eq. (5), changes self-consistently during front propagation, as \(u(x)\) changes. The moving self-healing crack leaves behind itself relaxed contacts. When the front reaches a position \(s\), the current shapes of the displacement fields \(\widetilde{u}_{\rm t} (x;s)\) and \(\widetilde{u}(x;s)\) are given by solution of Eqs. (6)–(8). The current displacement of the bottom surface of the IL, \(\widetilde{u}_{\rm b} (x; s)\), is determined by the current propagation length of the front:
while ahead the moving front the contacts are still loaded,
With these conditions, the functions \(\widetilde{u}_{\rm t} (x;s)\) and \(\widetilde{u}(x;s)\) take the following form. For the front tail (\(x < s\)):
where
with \(b_1 = (1-\beta ) \kappa ^2 / (\kappa _1 (\alpha _2 - \alpha _1))\) and \(b_2 = - b_1 \kappa _1 /\kappa _2\).
Ahead of the front (\(x > s\)):
The coefficients \(D_{1} (s)\), \(D_{2} (s)\), \(D_{11} (s)\), \(D_{12} (s)\), \(D_{21} (s)\) and \(D_{22} (s)\) in Eqs. (15)–(20) are functionals of the function \(u_{\rm b}^{(0)} (x)\) and should be determined by the two left-hand-side boundary conditions (9) and (10) and the following four continuity conditions at \(x=s \pm 0\):
which finally lead to a set of integral equations that has to be solved self-consistently.
5 Numerical Solution
A typical solution of the equations for the first front passage, for a completely relaxed IL initially (\(u_{\rm b}^{(0)} (x) =0\)), is shown in Fig. 2. We have assumed that front propagation is fast compared with the slow pushing, so that the leftmost block of the US has no opportunity to move before the precursor arrests.
In these conditions, and when the slider’s height is much larger than \(\lambda _{\rm c}\), the displacement field in the US is approximately unchanged upon propagation of the precursor, even if the displacement in the IL almost double upon front propagation (Fig. 2a). Because the \(\lambda\)-contacts repin immediately after breaking, they also immediately start to load again as the next \(\lambda\)-contacts relax and the precursor propagates. As a consequence, the stress behind the front is increasing with the distance to the front (Fig. 2b). Ahead of the front, the relaxed \(\lambda\)-contacts induce an extra loading of the unbroken contacts ahead of the front, characterized by a stress peak at the front location (Fig. 2b). This extra stress \(\varDelta \sigma _{\rm c}\) is enough to bring initially less stressed contacts up to their threshold. However, because the initial stress is a decaying function of \(x\), the extra stress is sufficient to bring the contacts above their threshold only over a finite length \(\varLambda\) (Fig. 2c).
6 Analytical Solution
For the first precursor arising from a completely relaxed IL (\(u_{\rm b}^{(0)} (x) =0\)), we found some analytical results. The full proof is available in “Appendix”. Here, we will only provide the main results and the assumptions made to get them.
We assume that the elastic correlation length is much smaller than the slider’s thickness (\(\lambda _{\rm c} \ll H\)). Since \(\lambda _{\rm c}\) is typically in the micrometer range, this assumption is valid for a large range of macroscopic systems. We also assume that the interfacial stiffness is much smaller than the internal stiffness of the slider (\(k \ll K\)). For rough interfaces, this assumption is also generally true [4]. Based on the results of Fig. 2a, we assume that the displacement field in the US is given by \(u_{\rm t} (x) \approx U_{t0} e^{-\kappa _2 x}\) and does not change during front propagation. Under these assumptions, we find an analytical expression for the length \(\varLambda\) of the first precursor (Eq. (66) in the “Appendix”). This expression approximates, for \(\varLambda \gg \kappa ^{-1}\) (i.e., large \(H/ \lambda _{\rm c}\) and/or \(k/K\)), to
where \(\varPsi _1 = 1+\lambda _{\rm c} \kappa _2 /(1+ \lambda _{\rm c} \kappa )\).
The analytical results are shown in Fig. 3. \(\varLambda\) is found to increase quasi-linearly with the height of the slider (Fig. 3a) and to increase quasi-logarithmically with the stiffness of the interface (Fig. 3b). Comparison with the numerical results shows a quantitative agreement. We also checked that molecular dynamics simulations of the model agree with the analytical results (not shown).
7 Discussion
As for any toy model, we cannot expect our model to reproduce quantitatively experimental results. In this discussion, we will thus mainly list the consequences of the various simplifying assumptions that we made in order to allow for an analytical solution.
We have shown that in our model, the onset of sliding is characterized by precursory self-healing slip pulses. The characteristic length \(\varLambda\) of the first precursor is controlled by two parameters, \(H/\lambda _{\rm c}\) and \(k/K\), determined by the slider and interface properties. Importantly, \(\varLambda\) does not depend on the threshold value \(\sigma _{\rm s}\). This result is due to the fact that we use linear elasticity and immediate repinning of \(\lambda\)-contacts in a completely relaxed state. As a consequence, all curves in Fig. 2c are unmodified if \(\sigma _{\rm s}\) is changed, and thus the length \(\varLambda\) is also unchanged.
This threshold independence of \(\varLambda\) would mean that, if the interface would obey Amontons’ law of friction (\(\sigma _{\rm s} = \mu _{\rm s} \sigma _n\), with \(\mu _{\rm s}\) the static friction coefficient and \(\sigma _n\) the normal stress) locally (at the \(\lambda\)-contacts scale), \(\varLambda\) would not depend on \(\mu _{\rm s}\). This is a major difference with previous precursor models [11–13], in which the length of the first (crack-like) precursor depends explicitly on \(\mu _{\rm s}\). The independence of \(\varLambda\) with \(\mu _{\rm s}\) implies an independence with the normal load on the system, as long as the type of loading (pure side loading) is unchanged.
If an additional uniform shear stress \(\sigma _0\) is applied to the top surface of the slider, then the threshold will decrease, \(\sigma _{\rm s} \rightarrow \sigma _{\rm s} - \sigma _0\). In such conditions, the crack will nucleate at a lower macroscopic force and will propagate over a longer distance. Moreover, if \(\sigma _0 > \sigma _f\), where \(\sigma _f\) is the Griffith threshold (see e.g., Eq. (35) in Ref. [14] obtained for a simpler 1D model), then the crack will never stop, so that \(\varLambda \rightarrow \infty\).
We have considered a constant value of \(\sigma _{\rm s}\) along the interface. Let us consider a non-uniform normal load of the form \(\sigma _n (x) = \sigma _{n0} + \epsilon x\), as in top-driven systems with friction-induced torque [11]. The thresholds thus also depend on \(x\), \(\sigma _{\rm s} (x) = \sigma _{s0}+ \mu _{\rm s} \epsilon x\). \(\varLambda\) will depend on the asymmetry parameter \(\epsilon\) roughly as \(\varLambda (\epsilon ) \approx \varLambda (0) (1-\epsilon )\).
We have assumed that broken contacts are immediately restored with zero stretching. Instead, one may assume that the contacts repin after some delay time \(\tau _d\) [9, 10, 20]. Assuming a constant \(\tau _d\), the width of the self-healing crack will increase from \(\lambda _{\rm c}\) to \(v \tau _d\), with \(v\) the (minimal) propagation velocity of the front (see Refs. [14, 15]), and the length \(\varLambda\) will increase to \(\varLambda + v \tau _d\). Note that experimentally, the repinning conditions is generally unraveled. In gels, however, the interface was reported to re-stick when the slip velocity behind the rupture tip decreases back to a critical velocity depending of the gel composition [17, 21].
In the presence of inertia, which has been neglected in the present quasi-static model, the IL blocks will be able to continue increasing the load on their right-hand neighbors even after repinning of their individual \(\lambda\)-contacts. This extra loading is expected to help breaking further contacts and thus increase the precursor length. In contrast, the front nucleation process will be unaffected because it originates from a static state of the system.
We have assumed that all \(\lambda\)-contacts behave as classical springs with a sawtooth-shape dependence \(u(\sigma _{\rm c}\)). In real systems, they are composed of \(N_{\rm c}\) micro-junctions with a distribution of thresholds \(P_{\rm c} (f_{\rm s})\). If \(P_{\rm c} (f_{\rm s})\) is wide enough, the elastic instability will disappear, and the \(\lambda\)-contacts will smoothly slide with the pushing velocity \(v_d\) after reaching the stretching \(u_{\rm s}\) [22, 23]. No discrete precursor will thus be observed, as a quasi-static front will continuously run through the interface.
Here, we have considered the first precursor only. After its propagation, the system is left in the stress state shown in solid line in Fig. 2b. If the system is further loaded, the leftmost \(\lambda\)-contact will again be the first to reach its breaking threshold, and a second precursor will nucleate. It will propagate through the stress field left by the previous event, itself modified by the additional loading and this scenario will repeat itself. We have run numerical simulations for the series of precursors and found that all precursors propagate roughly over the same length \(\varLambda\) (between precursors, the stress peak left at the precursor extremity does propagate further quasi-statically due to the increased external loading). This is not in agreement with experimental data [6, 7] and previous precursor models producing crack-like (rather than self-healing-like) rupture [7, 11–13], in which successive precursors propagate over increasing lengths.
This discrepancy disappears if aging of the \(\lambda\)-contacts — a newborn contact has a smaller size and thus a lower breaking threshold force \(f_{\rm s}\) — is taken into account [23, 24]. We checked this numerically by considering a time-increasing \(f_{\rm s}\). The previously broken region of the interface is characterized by “younger” contacts and therefore by smaller thresholds than the “old” unbroken part of the system. Hence, the next front will pass this region more easily and propagate deeper into the system. This process repeats itself until a precursor would span the whole interface and trigger macroscopic sliding of the interface. Note that in these numerical results, there is a competition between the aging and loading time scales, while the front propagation time scale is kept much smaller than the loading time scale.
The proposed toy model is important for all systems in which friction instabilities are central, from tribology to geophysics. It helps clarifying the problem of the selection of the size of the slipping part of the interface as a function of the bulk material properties, interfacial parameters and loading conditions. It will be particularly relevant to systems in which self-healing slip pulses have been observed (e.g., [8, 16, 17, 21]). Our results emphasize the fact that the behavior of precursors is intimately related to the repinning rule of the interface (at vanishing velocity for crack-like rupture; immediately in the present model). We thus advocate for an increased experimental effort to better constrain these repinning rules, which will be very useful to propose improved models for the onset of frictional sliding.
References
Persson, B.N.J.: Sliding Friction: Physical Principles and Applications. Springer, Berlin (1998)
Braun, O.M., Naumovets, A.G.: Nanotribology: Microscopic mechanisms of friction. Surf. Sci. Rep. 60, 79 (2006)
Chateauminois, A., Fretigny, C., Olanier, L.: Friction and shear fracture of an adhesive contact under torsion. Phys. Rev. E 81, 026106 (2010)
Prevost, A., Scheibert, J., Debrégeas, G.: Probing the micromechanics of a multi-contact interface at the onset of frictional sliding. Eur. Phys. J. E 36, 17 (2013)
Rubinstein, S.M., Cohen, G., Fineberg, J.: Detachment fronts and the onset of dynamic friction. Nature 430, 1005 (2004)
Rubinstein, S.M., Cohen, G., Fineberg, J.: Dynamics of precursors to frictional sliding. Phys. Rev. Lett. 98, 226103 (2007)
Maegawa, S., Suzuki, A., Nakano, K.: Precursors of global slip in a longitudinal line contact under non-uniform normal loading. Tribol. Lett. 38, 313 (2010)
Romero, V., Wandersman, E., Debrégeas, G., Prevost, A.: Probing locally the onset of slippage at a model multicontact interface. Phys. Rev. Lett. 112, 094301 (2014)
Trømborg, J.K., Sveinsson, H.A., Scheibert, J., Thøgersen, K., Amundsen, D.S., Malthe-Sørenssen, A.: Slow slip and the transition from fast to slow fronts in the rupture of frictional interfaces. Proc. Natl. Acad. Sci. USA 111, 8764–8769 (2014)
Braun, O.M., Barel, I., Urbakh, M.: Dynamics of transition from static to kinetic friction. Phys. Rev. Lett. 103, 194301 (2009)
Scheibert, J., Dysthe, D.K.: Role of friction-induced torque in stick-slip motion. EPL 92, 54001 (2010)
Amundsen, D.S., Scheibert, J., Thøgersen K., Trømborg J., Malthe-Sørenssen A.: 1D Model of precursors to frictional stick-slip motion allowing for robust comparison with experiments. Tribol. Lett. 45, 357 (2012)
Trømborg, J., Scheibert, J., Amundsen, D.S., Thøgersen, K., Malthe-Sørenssen, A.: Transition from static to kinetic friction: Insights from a 2D model. Phys. Rev. Lett. 107, 074301 (2011)
Braun, O.M., Peyrard, M., Stryzheus, D.V., Tosatti, E.: Collective effects at frictional interfaces. Tribol. Lett. 48, 11 (2012)
Braun, O.M., Peyrard, M.: Crack in the frictional interface as a solitary wave. Phys. Rev. E 85, 026111 (2012)
Lykotrafitis, G., Rosakis, A.J., Ravichandran, G.: Self-healing pulse-like shear ruptures in the laboratory. Science 313, 1765 (2006)
Ronsin, O., Baumberger, T., Hui, C.Y.: Nucleation and propagation of quasi-static interfacial slip pulses. J. Adhes 87, 504 (2011)
Caroli, C., Nozieres, P.: Hysteresis and elastic interactions of microasperities in dry friction. Eur. Phys. J. B 4, 233 (1998)
Brörmann, K., Barel, I., Urbakh, M., Bennewitz, R.: Friction on a microstructured elastomer surface. Tribol. Lett. 50, 3 (2013)
Thøgersen, K., Trømborg, J.K., Sveinsson, H.A., Malthe-Sørenssen, A., Scheibert, J.: History-dependent friction and slow slip from time-dependent microscopic junction laws studied in a statistical framework. Phys. Rev. E 89, 052401 (2014)
Baumberger, T., Caroli, C., Ronsin, O.: Self-healing slip pulses and the friction of gelatin gels. Eur. Phys. J. E 11, 85 (2003)
Braun, O.M., Peyrard, M.: Modeling friction on a mesoscale: Master equation for the earthquakelike model. Phys. Rev. Lett. 100, 125501 (2008)
Braun, O.M., Peyrard, M.: Master equation approach to friction at the mesoscale. Phys. Rev. E 82, 036117 (2010)
Braun, O.M., Peyrard, M.: Role of aging in a minimal model of earthquakes. Phys. Rev. E 87, 032808 (2013)
Acknowledgments
We wish to express our gratitude to M. Peyrard for numerous useful discussions. We thank J. K. Trømborg for a careful reading of the manuscript. This work was supported by a Dnipro Hubert Curien Partnership (Grant No. 28225UH) and by the People Programme (Marie Curie Actions) of the European Union’s 7th Framework Programme (FP7/2007–2013) under Research Executive Agency Grant Agreement 303871. O.B. acknowledges a partial support from the NASU “RESURS” program.
Author information
Authors and Affiliations
Corresponding author
Appendix: Analytical derivation of Eq. (25)
Appendix: Analytical derivation of Eq. (25)
Let us introduce two dimensionless parameters
so that \(K_{\rm L} = K/h\), \(K_{\rm T} = Kh/2(1+\sigma )\), \(\beta = 1/(1+b)\), \(1-\beta = b/(1+b)\), \((\lambda _{\rm c} \kappa _{\rm T})^2 = hq/b\), \((\lambda _{\rm c} \kappa )^2 = q \, (1+b)/b\),
where \(b = 2(1+\sigma )q/h\), and consider the typical system with \(h, q \ll 1\). In this case \(\varepsilon \ll 1\), so that \(\kappa _1^2 \approx \kappa ^2 (1+\beta \varepsilon )\) and \(\kappa _2^2 \approx \kappa ^2 \varepsilon \, (1-\beta ) = q \varepsilon /\lambda _{\rm c}^2\), or
In accordance with the numerics (see Fig. 2a), let us assume that in the case of \(h, q \ll 1\) the displacement field in the US is given by
and does not change during front propagation. Before nucleation of the first precursor, the solution of Eq. (7) is
The right-hand-side boundary condition, \(u(x) \rightarrow 0\) at \(x \rightarrow \infty\), gives us
while the left-hand-side boundary condition (Eq. (10)) leads to the equation
Thus, before nucleation of the first precursor, the IL displacement field is
Equation (33) allows us to couple the parameters \(U \equiv u_{\rm t} (0)\) and \(u_{\rm c} \equiv u(0)\):
where
When the displacement of the IL trailing edge reaches the threshold value \(u_{\rm s}\) at some \(U=U_0 = u_{\rm s} ( 1+ \kappa _2 /\kappa ) / (\beta \varPsi _1)\), the front starts to propagate. In this case the solution of Eq. (7), ahead of the propagating front, \(x>s\), where \(u_{\rm b} (x) =0\) so that \(w(x) = \beta u_{\rm t} (x) = \beta U_0 e^{-\kappa _2 x}\), is given by
The right-hand-side boundary condition gives us the coefficient \(A_4 (s)\),
so that Eq. (36) takes the form
Behind the propagating front, \(x<s\), where \(w(x) = \beta \, u_{\rm t} (x) + (1-\beta ) \, u_{\rm b} (x)\) and \(u_{\rm b} (x) = \widetilde{u}(x+0;x) = A_3 (x) + A_4 (x)\), the solution of Eq. (7) is given by
where
so that \({\mathcal {F}} (0) =0\) and \({\mathcal {F}}' (0) =0\).
The coefficients \(A_{\dots } (s)\) in these equations are determined by the boundary and continuity conditions. The left-hand-side boundary condition (Eq. (10)) couples the coefficients \(A_1 (s)\) and \(A_2 (s)\). Using \(u_{\rm b} (0)=u_{\rm s}\), \(\widetilde{u}(0;s) = A_2 (s)\) and \(\widetilde{u}'(0;s) = \kappa A_1 (s)\), we obtain
The continuity conditions (Eqs. (23) and (24)) lead to two equations
and
where
Taking the difference and sum of Eqs. (44) and (45), we obtain two new equations:
Using Eq. (43), Eqs. (46) and (47) may be rewritten as
Combining these equations, we finally come to the integral equation for the coefficient \(A_3 (s)\):
where
so that
From Eq. (52) we find that
Differentiating Eq. (52), we obtain a differential equation for \(A_3 (s)\):
From Eq. (56) we obtain that at short distances, \(s \ll \kappa ^{-1}\), \(A_3 (s) \approx A_3 (0) (1+ \gamma _3 s)\), where
From Eqs. (37) and (56) it follows that \(\widetilde{u} (s+0;s) = A_3 (s) + A_4 (s) \approx A_0 \, (1+\gamma s)\) at short distances, \(s \ll \kappa ^{-1}\), where
and
while for long distances, \(s \gg \kappa ^{-1}\), \(\widetilde{u} (s+0;s)\) decays exponentially,
The function \(\widetilde{u} (s+0;s)\) may be approximated as
where
and comparing Eqs. (59) and (61), we obtain a nonlinear equation, which defines the value \(\kappa _3\):
Then, the IL stress ahead of the front is \(\sigma _{\rm c} (s) = k \, \widetilde{u} (s+0;s) /\lambda _{\rm c}^2\), and the equation \(\sigma _{\rm c} (\varLambda ) = \sigma _{\rm s}\) defines the characteristic length \(\varLambda\):
where \(y\) is determined by the solution of the equation \({\mathcal {B}} y = (y+C)^{\alpha }\) with \({\mathcal {B}} = (1+C)^{\alpha } k A_0 /(\sigma _{\rm s} \lambda _{\rm c}^2)\).
Using Eq. (60), \(\varLambda\) may approximately be presented as
Equation (65) corresponds to the analytical solution for \(\varLambda\), whereas Eq. (66) corresponds to the approximated analytical solution provided as Eq. (25) in the main text.
Rights and permissions
About this article
Cite this article
Braun, O.M., Scheibert, J. Propagation Length of Self-healing Slip Pulses at the Onset of Sliding: A Toy Model. Tribol Lett 56, 553–562 (2014). https://doi.org/10.1007/s11249-014-0432-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11249-014-0432-y