Distinct morphologies of electromigration-induced voids and failures are shown for Al, Al-2%Cu, and Al-2%Cu-l% Si narrow (1–6 µm) unpassivated thin film conductors. SEM and TEM images typically show large non-fatal voids and narrow slit-like open circuit failures for all film conditions and accelerated test conditions. Evidence for transgran-ular slit failures is shown for 1.33 µm wide conductors. A simple model for void growth is presented which accounts for the void morphologies seen. The observed morphologies and the results of void growth modelling suggest that slit voids nucleate after other voids and rapidly produce failure. These conclusions are discussed in terms of ‘classical’ models for electromigration failure processes and resistance and noise power monitoring techniques.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
I. A. Blech and E. S. Meieran, Appl. Phys. Lett.11, 263 (1967).
R. Rosenberg and L. Berenbaum, Appl. Phys. Lett.12, 201 (1968).
I. A. Blech and E. S. Meieran, J. Appl. Phys.40, 485 (1969).
L. Berenbaum and R. Rosenberg, Thin Solid Films4, 187 (1969).
M. J. Attardo and R. Rosenberg, J. Appl. Phys.41, 2381 (1970).
M. J. Attardo, R. Rutledge and R. C. Jack, J. Appl. Phys.42, 4343 (1971).
L. Berenbaum and B. Patnaik, Appl. Phys. Lett.18, 284 (1971).
R. Rosenberg, J. Vac. Sci. Technol.9, 263 (1971).
S. J. Horowitz and I. A. Blech, Mat. Sci. Eng.10, 169 (1972).
J. E. Sanchez Jr., L. T. McKnelly and J. W. Morris Jr., submitted to Appl. Phys. Lett. (1990).
B. N. Agarwala, G. Digiacoma and R. R. Joseph, This Solid Films34, 165(1976).
J. T. Yue, W. P. Funsten and R. Y. Taylor, Proc. 23rd Int. Reliability Phys. Symp. IEEE Eds., (IEEE, Orlando, FL, 1985), 126–137.
K. Hinode, N. Owada, T. Nishida and K. Mukai, J. Vac. Sci. Technol. B5, 518 (1987).
T. Hosoda, H. Yagi and H. Tsuchikawa, Proc. 27th Int. Reliability Phys. Symp., IEEE Eds., (IEEE, Phoenix, AZ, 1989), 202–206.
J. W. McPherson and C. F. Dunn, J. Vac. Sci. Technol. B5, 1321 (1987).
S. Vaidya, T. T. Sheng and A. K. Sinha, Appl. Phys. Lett.36, 464 (1980).
J. Cho and C. V. Thompson, Appl. Phys. Lett.54, 2577 (1989).
M. Hasunuma, H. Kaneko, A. Sawabe, T. Kawanoue, Y. Kohanawa, S. Komatsu and M. Miyauchi, IEDM Techn. Digest, IEEE Eds., (IEEE, Washington, DC, 1989), 677–680.
S. Vaidya, D. B. Fraser and W. S. Lindenberger, J. Appl. Phys.51, 4475 (1980).
C. V. Thompson and J. Cho, IEEE Electron Device Lett.7, 667 (1986).
P. Chaudhari, J. Vac. Sci. Technol.9, 520 (1972).
B. Bacconier, G. Lormand, M. Papapietro, M. Archard and A.-M. Papon, J. Appl. Phys.64, 6483 (1988).
S. A. Hackney, Scripta Met.22, 1273 (1988).
R. W. Thomas and D. W. Calabrese, Proc. 21st Int. Reliability Phys. Symp. IEEE Eds., (IEEE, 1983), 1–9.
E. Levine and J. Kitcher, Proc. 22nd Int. Reliability Phys. Symp., IEEE Eds., (IEEE, Las Vegas, NV, 1984), 242–249.
H. B. Hungtington and A. R. Grone, J. Phys. Chem. Solids20, 76 (1961).
V. Teal, S. Vaidya and D. B. Fraser, Thin Solid Films136, 21 (1986).
K. P. Rodbell and S. R. Shatynski, IEEE J. Sol. St. CircuitsSC-19, 98 (1984).
R. H. Koch, J. R. Lloyd and J. Cronin, Phys. Rev. Lett.55, 2487 (1985).
J. G. Cottle, and T. M. Chen, J. Electron. Mater.17, 467 (1988).
J. Pelz and J. Clarke, Phys. Rev. B36, 4479 (1987).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Sanchez, J.E., McKnelly, L.T. & Morris, J.W. Morphology of electromigration-induced damage and failure in Al alloy thin film conductors. J. Electron. Mater. 19, 1213–1220 (1990). https://doi.org/10.1007/BF02673335
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF02673335