Abstract
Relatively pure, polycrystalline samples of Golden, New Mexico and Transvaal, South Africa chalcopyrite were ground and polished to fit into a density-compatible titanium alloy sandwich assembly and shock loaded (the Golden at 1.2 GPa, the Transvaal at 18 GPa peak pressure). The recovered samples were examined in the transmission electron microscope and observed to contain roughly 103 and 104 times more dislocations respectively than the natural, unshocked materials which contained roughly 107 cm−2. These materials were ground to three size fractions and leached in an acid-dichromate lixiviant at 50 and 70 °C (323 and 343 K). Corresponding size fractions were prepared from the unshocked material and leached for comparison; and these experiments were extended to a range of temperatures up to 90 °C (363 K) using a Bingham Canyon, Utah chalcopyrite. An unambiguous effect of dislocations was observed at the largest size fraction leached at 50 °C (323 K): the reaction rate constant increased from 1.44 × 10−3 to 1.62 × 10−3 to 2.73 × 10−3 min−1 for dislocation densities increasing from roughly 103 cm−2 to 1011 cm−2. A linear relationship in the leaching rate was observed between 25 and 60 °C (298 and 333 K) and the activation energy was calculated to be approximately 12 kcal/mol (50 kJ/mol). Above 60 °C (333 K) a conspicuous rate decrease was observed. This was related to a densification of the sulfur product layer, which at 50 °C (323 K) was a loose, porous precipitate while at 90 °C (363 K) it was a continuous, tenacious, glassy coating on the chalcopyrite particles. In addition, and more importantly, the high-temperature decline in leaching rate was inferred to be associated with adsorption of Cr(VI) ion which decreases with increasing temperature. The anomalous and unpredictable behavior of chalcopyrite leached in acid-dichromate lixiviant was therefore observed to be related to variations in a surface chemisorption mechanism as well as variations in the nature of the sulfur reaction product layer. These effects also mask the influence of crystal defects and other surface-related crystallographic effects in leaching.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Reference
T. Rosenqvist:Principles of Extractive Metallurgy, p. 200, McGraw-Hill Book Co., New York, 1974.
J. Gross and S. R. Zimmerly:Trans. AIME, 1930, vol. 87, pp. 35–40.
J. K. Gerlach, E. D. Gock, and S. K. Ghosh: “Activation and Leaching of Chalcopyrite Concentrates with Dilute Sulfuric Acid”,AIME Internat. Symp. on Hydromet., D. J. I. Evans and R. S. Shoemaker, eds., pp. 403–10, AIME, New York, 1972.
L. W. Beckstead, P. B. Munoz, J. L. Sepulveda, J. A. Herbst, J. D. Miller, F. A. Olsen and M. E. Wadsworth: “Acid Ferric Sulfate Leaching of Attritor-Ground Chalcopyrite Concentrates”,Extractive Metallurgy of Copper: Hydrometallurgy and Electrowinning, vol. II, J. C. Yannopoulus and J. C. Agarwal, eds., chapt. 31, pp. 611–32, AIME, New York, 1976.
L. E. Murr and S. L. Lerner:J. Mater. Sci., 1977, vol. 12, pp. 1349–54.
L. E. Murr and F. I. Grace:Exptl. Mechs., 1979, Vol. 5, pp. 145–156.
W. F. Müller and U. Hornemann:Earth Planet. Sci. Letters, 1969, vol. 7, pp. 251–64.
D. Stöffler:I. Fortshr. Mineral. 1972, vol. 49, pp. 50–113.
R. W. Rohde, B. M. Butcher, J. R. Holland, and C. H. Karnes 9eds.:Metallurgical Effects at High Strain Rates, Plenum Press, New York, 1973.
L. E. Murr and K. P. Staudhammer:Mater. Sci. Engr., 1975, vol. 20, pp. 35–53.
U.C. Frantz and S. S. Hecker: High-rate Mechanical Testing with the LASL Two-Inch Gun, LASL Report LA-6528, Nov., 1976.
R. Kinslow, ed.:High Velocity Impact Phenomena, Academic Press, New York, 1970.
L. E. Murrand S. L. Lerner:J. Mater. Sci., 1978, vol. 13, pp. 2268–72.
L. E. Murr:Electron Optical Applications in Materials Science, McGraw-Hill Book Co., New York, 1970.
R. Shantz: Ph.D. thesis, University of Arizona, Tucson, Ariz., 1974.
R. Shantz and T. M. Morris:Engr. Mining J., 1974, vol. 175, no. 5, pp. 71–72.
G. W. Warren: Ph.D. Dissertation, Dept. of Metallurgical and Fuels Engineering, University of Utah, Salt Lake City, Utah, 1978.
J. D. Miller and H. Q. Portillo: “Silver Catalysis in Ferric Sulfate Leaching of Chalcopyrite”, XIII International Mineral Processing Congress, Warsaw, Poland, 1979.
J. E. Dutrizac:CIM Bulletin, vol. 72, No. 810, 1979, pp. 109–18.
P. B. Munoz, J. D. Miller, and M. E. Wadsworth:Met. Trans. B, 1979, vol. 10B, pp. 149–58.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Murr, L.E., Hiskey, J.B. Kinetic effects of particle-size and crystal dislocation density on the dichromate leaching of chalcopyrite. Metall Trans B 12, 255–267 (1981). https://doi.org/10.1007/BF02654458
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02654458