Abstract
The interface zone between cortical bone and threaded non-alloyed titanium implants inserted in the rabbit tibia for 12 months was examined by light and electron microscopy. The implants were removeden bloc with the perfusion-fixed surrounding bone and the undecalcified specimens were, after osmification, dehydrated and embedded in plastic resin (LR White). In ground sections (about 10 µm thick) cortical bone appeared to be in direct contact with the implant surface and the implants were thus “osseointegrated”. Sections for light microscopy (1 µm thick) and electron microscopy (40 nm to 0.5 µm) were prepared by using an electropolishing technique by which the bulk part of the metal was electrochemically removed and a fracture technique by which the implant was separated from the embedded tissue before sectioning. In the electropolished specimens an unmineralized zone, 2–10 µm wide, was observed at the interface. The interface zone contained osteoid-like tissue (densely packed collagen fibrils, osteocyte canaliculi) but in general no deposits of calcium mineral. This feature of the interface could not be observed in specimens prepared by the fracture technique, indicating that the electropolishing technique had induced serious artefacts, including decalcification of the interface bone. In sections prepared by the fracture technique, mineralized bone was present very close to the implant surface. No gradient of mineral was observed. A thin layer of amorphous material (100–200 nm wide) was present peripheral to the mineralized bone. An electron dense line about 100 nm wide was formed at the border between the mineralized bone and the amorphous layer. The dense layer had the same characteristics as the lamina limitans observed around osteocyte lacunae and canaliculi or the zone between areas of bone with different degree of mineralization.
Our observations suggest that mineralized bone reached close to the surface of titanium implants inserted in the rabbit tibia for 12 months but that a direct contact is not established.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
P. I. BRÅNEMARK, G. A. ZARB and T. ALBREKTSSON (eds), “Tissue-integrated prostheses: osseointegration in clinical dentistry” (Quintessence, Chicago, 1985).
T. ALBREKTSSON, P. -I. BRÅNEMARK, H.-A. HANSSON and J. LINDSTRÖM,Acta. Orthop. Scand. 52 (1981) 155.
L. LINDER, K. OBRANT and G. BOIVIN, ibid.2 (1989) 135.
T. ALBREKTSSON, P. I. BRÅNEMARK, H. A. HANSSON, B. IVARSSON and U. JONSSON, in “Clinical applications of biomaterials”, edited by T. Albrektsson and P. I. Brånemark (John Wiley & Sons Ltd, 1982).
T. ALBREKTSSON, H. A. HANSSON and B. IVARSSON,Biomaterials 6 (1985) 97.
T. ALBREKTSSON and H. A. HANSSON, ibid.7 (1986) 201.
L. M. BJURSTEN, L. EMANUELSSON, L. E. ERICSON, P. THOMSEN, J. LAUSMANN, L. MATTSON, U. ROLANDER and B. KASEMO, ibid.11 (1990) 596.
L.-E. ERICSON, L. SENNERBY, G. BOKHEDE, L. EMANUELSSON and P. THOMSEN,Adv. Biomater. 9 (1990) 333.
L.-E. ERICSON, B. R. JOHANSSON, A. ROSENGREN, L. SENNERBY and P. THOMSEN, in “The bone-biomaterial interface”, edited by J. Davis (Toronto University Press), in press.
K. DONATH and G. A. BREUNER,J. Oral Pathol. 11 (1982) 318.
J. LAUSMAA and L. LINDER,Biomaterials 9 (1988) 277.
P. THOMSEN and L. E. ERICSON, ibid.6 (1985) 421.
A. TJELLSTRÖM, M. JACOBSSON and T. ALBREKTSSON,Int. J. Oral Maxillofac. Implants 3 (1988) 287.
C. JOHANSSON and T. ALBREKTSSON, ibid.2 (1987) 69.
P. CHRISTEL, A. MEUNIER and M. THERIN,J. Appl. Biomater. 1 (1990) 205.
A. ROSENGREN, B. JOHANSSON and L.-E. ERICSON, in Transactions 16th Annual Meeting of the Society for Biomaterials (1990) p. 222.
J. SCHERFT,J. Ultrastruct. Res. 64 (1978) 173.
C. A. VAN BLITTERSWIJK, J. J. GROTE, W. KUYPERS, C. J. G. BLOEK-VAN HOEK and W. T. H. DAEMS,Biomaterials 6 (1985) 243.
A. E. CLARK, L. L. HENCH and H. A. PASCHALL,J. Biomed. Mater. Res. 10 (1976) 161.
C. A. VAN BLITTERSWIJK, S. C. HESSELING, J. VAN DER BRINK, H. LEENDERS and D. BAKKER, in “The bone-biomaterial interface”, edited by J. Davis (Toronto University Press), in press.
J. JOHANSSON, J. LAUSMAA, M. ASK, H.-A. HANSSON and T. ALBREKTSSON,J. Biomed. Engng 11 (1989) 3.
L. SENNERBY, L. E. ERICSON, P. THOMSEN, V. TEKHOLM and P. ASTRANC,Clin. Oral Iumpl Res. 2 (1991) 103
L. SENNERBY, P. THOMSEN and L. E. ERICSON,Int. J. Oral. Maxillofac Implants 7 (1992) 62.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Sennerby, L., Thomsen, P. & Ericson, L.E. Ultrastructure of the bone-titanium interface in rabbits. J Mater Sci: Mater Med 3, 262–271 (1992). https://doi.org/10.1007/BF00705291
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00705291