Abstract
This paper was focused on significantly increasing the ductility and strength of as-cast CNTs/AZ91D nanocomposites by solid solution (T4) and aging treatment (T6). The CNTs/AZ91D nanocomposite fabricated by permanent gravity casting assisted with ultrasonic processing was subject to as-cast, T4 and T6 treatment and the mechanical properties were tested. The results showed that the ductility and the tensile strength of the nanocomposites after T4 treatment were increased by 23.8 percent and 82.8 percent compared with the as-cast properties. After T6 treatment, the tensile strength and especially the yield strength of the nanocomposites was increased by 26.2 and 17.6 percent, while its ductility was still increased by 20.7 percent. The strengthening and toughing mechanisms of the nanocomposites were discussed based on the microstructure characterization results.
Access provided by Autonomous University of Puebla. Download to read the full chapter text
Chapter PDF
Similar content being viewed by others
Keywords
References
X. J. Wang et al., “Influences of Extrusion Parameters on Microstructure and Mechanical Properties of Particulate Reinforced Magnesium Matrix Composites,” Materials Science and Engineering A, 528 (2011), 6387–6392.
Shiying Liu et al., “Fabrication of Carbon Nanotubes Reinforced AZ91D Composites by Ultrasonic Processing,” Transactions of Nonferrous Metals Society of China, 20 (2010), 1222–1227
Congyang Zhang, Rongyu Feng, Wenzhen Li, “Effect of Heat Treatment on Microstructure and Mechanical Properties of Squeeze Cast n-SiCp/AZ91D Magnesium Matrix Composites,” Rare Metal Mateirals and Engineering, 44 (2) (2015), 463–468.
E. T. Thostenson, Z. F. Ren and T. W. Chou, “Advances in the science and technology of carbon nanotubes and their composites: a review,” Composites Science and Technology, 61 (13) (2001), 1899–1912.
B. L. Mordike, “Magnesium and Magnesium Alloys,” Journal of Japanese Institute of Light Metal, 51 (1) (2001), 2–13.
Y. Zojima, “Platform Science and Technology for Advanced Magnesium Alloys,” Materials Science Forum, 350–351 (2000), 3–18.
Author information
Authors and Affiliations
Editor information
Rights and permissions
Copyright information
© 2016 TMS (The Minerals, Metals & Materials Society)
About this paper
Cite this paper
Feng, R., Zhu, L., Li, W. (2016). Enhanced Ductility with Significant Increase in Strength of As-Cast CNTs/AZ91D Nanocomposites. In: TMS 2016 145th Annual Meeting & Exhibition. Springer, Cham. https://doi.org/10.1007/978-3-319-48254-5_11
Download citation
DOI: https://doi.org/10.1007/978-3-319-48254-5_11
Publisher Name: Springer, Cham
Print ISBN: 978-3-319-48624-6
Online ISBN: 978-3-319-48254-5
eBook Packages: Chemistry and Materials ScienceChemistry and Material Science (R0)