Abstract
A simple and sensitive electrochemical sensor based on graphene quantum dot-modified pencil graphite electrode (GQD/PGE) was fabricated and used for highly selective and sensitive determination of copper (II) ions in nanomolar concentration by square wave adsorptive stripping voltammetric method. The sensing mechanism could be attributed to the formation of a complex between Cu2+ ions and oxygen-containing groups in GQDs which result in an increased SWV signal in comparison with the bare electrode. Optimization of various experimental parameters such as pre-concentration time, pre-concentration potential, pH, and buffer type which influence the performance of the sensor, was investigated. Under optimized condition, GQD-modified electrode has been used for the analysis of Cu2+ in the concentration range from 50 pM to 4 nM and a lower detection limit of 12 pM with good stability, repeatability, and selectivity. Finally, the practical applicability of GQD-PGE was confirmed via measuring trace amount of Cu (II) in water samples. The GQD/PGE surface could be regenerated by exerting more positive potentials than the stripping potential of the Cu (II) ion and then used for another deposition.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
Copper is essential to all living organisms as a trace nutritional mineral because it involves the synthesis of hemoglobin, a variety of enzymes, and metabolism of the body [1,2,3]. However, copper deficiency or elevated levels of copper can bring about opposite health effects. For instance, copper deficiency can produce anemia-like symptoms or can affect the activity of enzymes and cell metabolism, while elevated levels of Cu2+ in the human body are a health risk of the kidneys, the liver, the central nervous system, and it can increase the blood pressure and the rate of respiration [4, 5]. The imbalance amount of copper ions can cause two classes of genetic diseases, namely Menkes and Wilson [6,7,8]. Due to physiological importance of copper and wide usage of it in industrial and agricultural sectors, determination of copper in various matrices is very important and numerous analytical techniques have been used for the accurate and sensitive determination of trace quantities of copper including atomic absorption spectroscopy (AAS), inductively coupled plasma-atomic emission spectroscopy (ICPAES), inductively coupled plasma-mass spectrometry (ICPMS), UV spectrophotometry, fluorescence, and electrochemical methods [9,10,11,12,13,14,15,16,17,18,19,20,21,22,23,24,25,26,27,28,29,30]. Among these, electrochemical techniques have attracted extra attention because of many advantages such as simplicity, cost-effectiveness, and small instrumentation. Compared to other electrochemical procedures, stripping analysis method has high sensitivity and allows determination of trace amount of substances because of pre-concentrating of analytes at the surface of the working electrode.
Graphene quantum dots (GQDs), a new kind of carbon nanomaterials with features derived from both graphene and QDs, have attracted extensive consideration from researchers due to optical stability, good surface grafting, biocompatibility, low toxicity, and high electrical and thermal conductivity. GQDs with a great surface area and quick electron transferability are one of the best electrode modifiers which can increase the rate of electrochemical reactions and attracted more attention as electrode modifier [31,32,33,34,35]. Recently, Wang et al. developed graphene quantum dots as a fluorescent sensing platform for highly efficient detection of copper (II) ions [36]. Furthermore, novel conjugates of GQDs and gold nanoparticles (AuNPs) are synthesized and used for sensitive electrochemical detection of heavy metal ions [37]. In this work, we used GQD-modified pencil graphite electrode for electrochemical quantification of Cu2+ ions by applying anodic stripping analysis. As shown in Scheme 1, the pencil graphite electrode (PGE) modified by GQD formed a platform for the adsorption of Cu2+ which may be related to the oxygen-containing groups on the GQDs surface. This is the first usage of untreated graphene-type nanoparticles, GQD, for the simple, cheap, sensitive, and selective determination of copper ions with an excellent performance and low detection limit.
Experimental
Instrumentation and reagents
Electrochemical experiments were performed using AUTOLAB PGSTAT 30 electrochemical analysis system and GPES 4.9 software package (Eco Chemie., the Netherlands). The utilized three-electrode system was composed of a modified pencil graphite electrode as the working electrode, a saturated calomel electrode (SCE) as the reference electrode, and a platinum wire as the auxiliary electrode. A digital pH/mV meter (Metrohm, pH Lab 827) was used for pH measurements, and an ultrasonic bath (KODO model JAC1002) was used for cleaning the electrode surface.
All solutions were prepared with deionized water. All chemicals were of analytical grade, purchased from Merck (Darmstadt, Germany), and used without further purification. The pencil graphite was obtained as pencil lead from Rotring Co. Ltd, Germany (R 505210 N), of type H. Dilute solutions of Cu2+ were prepared immediately before the use by diluting the stock solution with proper buffer. Metal ion solutions were prepared by dissolving appropriate amounts of their nitrate salts (Merck, Germany) in deionized water. GQDs were synthesized by pyrolyzing citric acid and dispersing the carbonized products into alkaline solutions [38]. The morphology of GQD was studied by TEM and AFM method.
Fabrication of the working electrode
The body of pencil lead was tightly coated with Teflon band. Electrical contact with the lead was achieved by connecting a copper wire to the metallic holder of the working electrode. The surface was polished on a weighing paper to a smooth finish and then sonicated in doubly distilled water. The GQD-modified electrode was fabricated by referring previous work of our research team [34]. Ten microliters of GQDs with the concentration 3 mg/mL was dropped on the surface of PGE and dried for 4 h at room temperature in a dark place. Then, the modified electrodes were rinsed with doubly distilled water.
Voltammetric measurements
Before determination, the modified electrode was immersed into the Cu2+ solution for adsorption with stirring under optimum potential and time, washed with doubly distilled water, placed in an electrochemical cell containing supporting electrolyte. Square wave stripping voltammetry was used to determine copper(II) from − 0.3 to 0.3 V at a frequency of 15 Hz, an amplitude of 25 mV, a standing time of 40 s, and a step length of 4 mV. Prior to each measurement, the electrode was cleaned at 600 mV for 120 s to remove any deposit from the previous measurement.
Results and discussion
Characterization of GQDs
Figure 1a shows TEM images of GQDs. As can be seen, the synthesized GQDs are uniformly arranged. The morphology of the PGE and GQD/PGE was studied using SEM (Fig. 1b, c), and results represent the presence of numerous round-shaped prepared GQD on the electrode surface. The morphology of GQD was also studied by AFM method. As shown in Fig. 1S, the corresponding AFM image shows a single GQD monolayer thin film.
Electrochemical behavior of bare and GQD-modified electrode
Electrochemical behavior of bare and modified electrodes was studied by cyclic voltammetry with 10 mmol L−1 K3[Fe(CN)6] and 1 M KNO3 as probe solution. Figure 2a shows cyclic voltammograms of the probe solution at bare and GQD-modified PGE. As shown in Fig. 2a, a pair of well-defined redox peaks was found at bare (curve a) and modified PGE (curve b). On GQDs/PGE, the peak potential separation (ΔEP) decreased and the peak current increased obviously. Peak-to-peak separation decrease proves the fact that GQDs have higher electron transfer rate and electrical conductivity compared to bare PGE. The enhanced current response of GQDs/PGE attributed to the increase in the effective surface area of PGE upon the modification which is favorable for the design of a highly sensitive electrochemical platform.
In order to confirm the electrocatalytic activity of the bare and modified electrodes for the determination of Cu2+, the electrochemical experiments were carried out in the absence and presence of Cu2+ (Fig. 2b). Results showed that these electrodes do not show any voltammetric feature (curves a and b) in the absence of Cu2+ ion. Upon dipping the electrodes into the 2 µM Cu2+ solution for 5 min, one pair redox peaks were observed at two electrodes due to the adsorption of Cu2+ on the electrodes, but GQD-modified electrode shows larger and better signal than unmodified electrode (curves c and d).
As shown in Scheme 1, these results might be related to that the oxygen-containing groups on the GQD surface can interact with Cu2+ ions and increase copper deposition on the electrode surface and also related to the high specific surface area, more active sites along the surfaces of GQD, and an increased electron transfer ability of GQD. Because of the above favorable characteristics, the parameters of voltammetric analysis, which affect the stripping signal of target metal ion, were studied and optimized in the following research.
Optimization of the conditions and analytical application
In order to get the maximum sensitivity for trace Cu(II) detection, the effect of following parameters was optimized: (c) deposition potential; (d) deposition time; (e) buffer type and buffer pH value.
Effect of deposition potential and deposition time
One of the very important parameters for stripping analysis is deposition potential. Figure 3a depicts the deposition potential effect on the stripping peak signal of 2.0 nM Cu2+. Based on the achieved results, applying a negative potential favors the deposition of Cu on the electrode and maximum stripping peak current was observed for immobilization potential of − 0.30 V. Therefore, a potential of − 0.30 V was selected for subsequent works.
In stripping techniques involving an accumulation stage, the sensitivity usually depends on the deposition time, because of the increased amount of metal deposited on the electrode surface by increasing the accumulation time. For this reason, the modified electrodes were immersed in a 2 nM Cu2+ stirred solution for a different period of time (Fig. 3b). As it can be seen, the peak current was increased as a function of pre-concentration time up to 180 s and remained constant between 180 and 600 s. No significant signals for analyte were observed without the deposition period. So, a 180-s accumulation time was used in the further experiments.
Effect of pH and electrolyte type
To reach high sensitivity and selectivity, the effect of pH value on the peak current was investigated and the best pH conditions for pre-concentration and determination steps were achieved around pH 6.0 and 5, respectively (Fig. 4a). The obtained results indicate that for pH values lower and higher than 6.0 in the pre-concentration step, the accumulated Cu decreases and may be due to the protonation of oxygen-containing groups on the GQDs surface or competition of OH− with oxygen-containing groups on the GQDs for Cu2+ ions in solution, respectively (Fig. 4a, curve a). In the stripping step, the largest peak current can be obtained at pH 5 (Fig. 4a, curve b). Therefore, pH 6 and pH 5 were used as optimum pH values in pre-concentration and determination steps, respectively.
To investigate the influence of the solution matrix on the extraction and determination steps of Cu2+ ions, the PBS, AcBS, and KNO3 electrolytes were investigated. Results showed that determination buffer has no effect on the obtained signal, and because of the optimum pH of 5 for this step, we used acetate buffer solution in the determination step. For pre-concentration step, results (Fig. 4b) showed that maximum response was observed when 0.1 M PBS used as the buffer in this step. Therefore, 0.1 M PBS and 0.1 M AcBS were used as electrolytes in pre-concentration and determination steps, respectively.
Effect of scan rate
In order to study the nature of the electrode process occurring at the electrode surface, a series of voltammograms of 0.1 μM Cu (II) at various scan rates were also recorded. As shown in Fig. 5, both cathodic peak current and anodic peak current increase linearly with the increase in scan rate. This result confirms that the electron transfer reaction is surface-controlled redox system and Cu (II) adsorbed on the electrode surface.
Calibration plots and detection limit
Figure 6 shows the SWV response of GQD/PGE after interaction with various concentrations of Cu2+. Under the optimum analytical conditions, the sensor showed a linear range from 0.05 to 4 nM (inset of Fig. 6) with the linear correlation coefficient of 0.997. The sensitivity of the developed GQD/PGE was calculated as 997 AM−1, and the detection limit was 0.012 nM based on a signal-to-noise ratio (S/N = 3). The comparison of the proposed electrode with other modified electrodes for Cu (II) detection is shown in Table 1. It can be seen that this method has the comparable detection limit for the Cu (II) detection with the simple electrode preparation procedure.
Interference study
The influence of various metal ions as potential interferents on the determination of copper (II) ions has been investigated by gradual addition of their standard solution to the electrochemical cell until a tolerated concentration causing a maximum relative error of ± 5% in the voltammetric signal of Cu2+ is realized. In order to investigate the interference of some species including Pb(II), Zn (II), Cd (II), Bi(III), Ni (II), Co (II), and Mn(II) and Hg(II) on the determination of Cu2+ using the accumulation potential of − 0.3 V at the concentration level of 2 nM, an extensive measurement was taken. It is found that the presence of (Pb2+, Zn2+, Co2+, Ni2+, Cd2+), (Bi3+ and Mn2+), and Hg2+ in the assay solution is tolerated with a concentration up to 50, 15, and 5 times of Cu2+ concentration, respectively, and determination error of Cu2+ in these conditions was lower than 5%.
Regeneration and repeatability of electrodes
One of the favorable characteristics of our electrode is its easiness in regeneration. Electrodes are easily regenerated by applying the positive potential of 0.6 V for 120 s to remove copper ions from the electrode surface. Based on the obtained results for studying the stability of modified electrode during repetitive stripping voltammetric experiments at the same modified electrode, each prepared electrode could be used for 23 determination experiment without apparent change in obtained results.
The reproducibility of the sensor was evaluated by the analysis of the same concentration of Cu2+ (2 nM) using five prepared GQD/PGE under the same conditions. All sensors exhibited close SWV signal, and a relative standard deviation (RSD) of 1.3% was achieved, which indicated that the reproducibility of the proposed sensor is acceptable. We checked long-term stability of the modified electrode by measuring the response of the Cu2+ from day to day. Results showed that there was no apparent decrease in the current response after 10-day storage, which indicates that the electrode has suitable storage stability.
Analysis of water
To evaluate the analytical reliability and application potential of the proposed sensor to real sample analysis, the GQD/PGE was used for the analysis of copper (II) under the optimized condition in tap water (has been taken from Urmia University) and synthetic water by direct analysis of the water with the modified electrode and the results are shown in Table 2. The attained results for measurement at three different concentrations (Table 2) indicate that the concentration of Cu2+ was accurately determined with the prepared electrode.
Conclusions
We developed an electrochemical sensor based on GQD-modified pencil graphite electrode for the determination of the low concentration of Cu2+ ion by applying anodic stripping analysis. This is for the first time that untreated graphene-type nanoparticles, GQD, are used for the Cu2+ detection. The sensing mechanism could be attributed to the formation of complex between Cu2+ ions and oxygen-containing groups in GQDs which result in an increased SWV signal in comparison with the bare electrode. The results indicate that the prepared sensor has good reproducibility and stability, could meet the selective requirements for environmental application, and be sensitive enough to detect Cu2+ ions in environmental water samples.
References
X. Xiong, L. Yanxia, L. Wei, L. Chunye, H. Wei, Y. Ming, Resour. Conserv. Recycl. 54, 985 (2010)
F. Behlau, J. Belasque, J.H. Graham, R.P. Leite, Crop Prot. 29, 300 (2010)
D. Tanyolac, Y. Ekmekc, S. Ünalan, Chemosphere 67, 89 (2007)
L. Mei, Y. Xiang, N. Li, A. Tong, Talanta 72, 1717 (2007)
Y.H. Chan, J. Chen, Q. Liu, S.E. Wark, D.H. Son, J.D. Batteas, Anal. Chem. 82, 3671 (2010)
G. Crisponi, V.M. Nurchi, D. Fanni, C. Gerosa, S. Nemolato, G. Faa, Coord. Chem. Rev. 254, 876 (2010)
H. Zhao, C. Xue, T. Nan, G. Tan, Z. Li, Q.X. Li, Q. Zhang, B. Wang, Anal. Chim. Acta 676, 81 (2010)
A. Samuele, A. Mangiagalli, M.T. Armentero, R. Fancellu, E. Bazzini, M. Vairetti, A. Ferrigno, P. Richelmi, G. Nappi, F. Blandini, Biochem. Biophys. Acta. 1741, 325 (2005)
M.S. Chan, S.D. Huang, Talanta 51, 373 (2000)
S.L.C. Ferreira, V.A. Lemos, B.C. Moreira, A.C.S. Costa, R.E. Santelli, Anal. Chim. Acta 403, 259 (2000)
Y.P.D. Pena, W. López, J.L. Burguera, M. Burguera, M. Gallignani, R. Brunetto, P. Carrero, C. Rondon, F. Imbert, Anal. Chim. Acta 403, 249 (2000)
G. Khayatian, M. Jodan, S. Hassanpoor, S. Mohebbi, J. Iran. Chem. Soc. 13, 831 (2016)
S. Bahar, F. Karami, J. Iran. Chem. Soc. 12, 2213 (2015)
M. Faraji, Y. Yamini, S. Shariati, J. Hazard Mater. 166, 1383 (2009)
Y. Zhu, K. Inagaki, K. Chiba, J. Anal. At. Spectrom. 24, 1179 (2009)
J.J. Pinto, C. Moreno, M. García-Vargas, Anal. Bioanal. Chem. 373, 844 (2002)
S.E. Ghazy, R.M. El-Shazly, M.S. El-Shahawi, G.A.A. Al-Hazmi, A.A. El-Asmy, J. Iran. Chem. Soc. 3, 140 (2006)
A. Salinas-Castillo, M. Ariza-Avidad, C. Pritz, M. Camprubi-Robles, B. Fernandez, M.J. Ruedas-Rama et al., Chem Comm 49, 1103 (2013)
H.-Y. Xie, J.G. Liang, Z.L. Zhang, Y. Liu, Z.K. He, D.W. Pang, Spectrochim. Acta Mol. Biomol. Spectrosc. 60, 2527 (2004)
J. Jakmunee, J. Junsomboon, Talanta 77, 172 (2008)
T. Poursaberi, L. Hajiagha-Babaei, M. Yousefi, S. Rouhani, M. Shamsipur, M. Kargar-Razi, Electroanalysis 13, 1513 (2001)
A. Afkhami, H. Khoshsafar, T. Madrakian, A. Shirzadmehr, J. Iran. Chem. Soc. 11, 1373 (2014)
M. Mazloum-Ardakani, M.K. Amini, M. Dehghan, E. Kordi, M.A. Sheikh-Mohseni, J. Iran. Chem. Soc. 11, 257 (2014)
L. Cui, J. Wu, J. Li, Y. Ge, H. Ju, Biosens. Bioelectron. 55, 272 (2014)
V.K. Gupta, M. Lütfi Yola, N. Atar, Z. Ustundag, A.O. Solak, Electrochim. Acta 112, 541 (2013)
Y. Si, J. Liu, A. Wang, S. Niu, J. Wan, Instrum. Sci. Technol. 43, 357 (2015)
L. Ding, Y. Gao, J. Di, Biosens. Bioelectron. 83, 9 (2016)
M.B. Gholivand, A. Sohrabi, S. Abbasi, Electroanalysis 19, 1609 (2007)
L. Cui, J. Wu, J. Li, Y. Ge, H. Ju, Biosens. Bioelectron. 55, 272 (2014)
M. Majidian, J.B. Raoof, S.-R. Hosseini, R. Ojani, J. Iran. Chem. Soc. 14, 1263 (2017)
J. Zhao, G.F. Chen, L. Zhu, G.X. Li, Electrochem. Commun. 13, 31 (2011)
M. Roushani, Z. Abdi, Sens. Actuators B 201, 503 (2014)
F. Tan, L. Cong, X. Li, Q. Zhao, H. Zhao, X. Quan, J. Chen, Sens. Actuators B 233, 599 (2016)
M. Hasanzadeh, N. Hashemzadeh, N. Shadjou, J. Eivazi-Ziaei, M. Khoubnasabjafari, A. Jouyban, J. Mol. Liq. 221, 354 (2016)
M. Hasanzadeh, A. Mokhtarzadeh, A. Karimzadeh, N. Shadjou, S. Sadeghi, A. Jouyban, J. Mater. Sci.: Mater. Electron. 27, 6488 (2016)
F. Wang, Z. Gu, W. Lei, W. Wang, X. Xia, Q. Hao, Sens. Actuators B 190, 516 (2014)
S.L. Ting, S. Jing Ee, A. Ananthanarayanan, K.C. Leong, P. Chen, Electrochim. Acta 172, 7 (2015)
M. Amjadi, J.L. Manzoori, T. Hallaj, J. Lumin. 153, 73 (2014)
S. Huang, L. Zhang, S. Lu, Q. Xiao, C. Huang, J. Sheng, W. Su, Microchim. Acta 182, 2529 (2015)
J.F. Wang, C. Bian, Simultaneous detection of copper. Electroanalysis 24, 1783 (2012)
X.X. Xu, G.T. Duan, Y. Li, G.Q. Liu, J.J. Wang, H.W. Zhang, Z.F. Dai, W.P. Cai, ACS Appl. Mater. Interfaces. 6, 65 (2014)
A. Bobrowski, M. Putek, J. Zarebski, Electroanalysis 24, 1071 (2012)
D.L. Zhao, X.F. Guo, T.T. Wang, N. Alverez, V.N. Shanov, W.R. Heineman, Electroanalysis 26, 488 (2014)
C. Prado, S.J. Wilkins, F. Marken, R.G. Compton, Electroanalysis 14, 262 (2002)
A. Mylonakis, A. Economou, P.R. Fielden, N.J. Goddard, A. Voulgaropoulos, Electroanalysis 16, 524 (2004)
K. De Wael, P. Westbroek, J. De Strycker, E. Gasana, E. Temmerman, Microchem. J. 77, 85 (2004)
H.L. Liu, S.W. Li, D.M. Sun, Y. Chen, Y.M. Zhou, T.H. Lu, J Mater Chem B 2, 2212 (2014)
M. Bagherzadeh, M. Pirmoradian, F. Riahi, Electrochim. Acta 115, 573 (2014)
R. Shabani, S.A. Mozaffari, S.W. Hosain, M. SaberTehrani, Iran. J. Sci. Technol. A 33, 336 (2009)
Acknowledgements
We gratefully acknowledge the partial financial support by the Nanotechnology Research Center and Faculty of Chemistry, Urmia University.
Author information
Authors and Affiliations
Corresponding author
Electronic supplementary material
Below is the link to the electronic supplementary material.
Rights and permissions
About this article
Cite this article
Ahour, F., Taheri, M. Anodic stripping voltammetric determination of copper (II) ions at a graphene quantum dot-modified pencil graphite electrode. J IRAN CHEM SOC 15, 343–350 (2018). https://doi.org/10.1007/s13738-017-1235-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13738-017-1235-5