Abstract
The 1050 aluminum alloy strip was prepared by means of electromagnetic and ultrasonic cast rolling on the modified asymmetric twin roll caster, and then the aluminum substrate for presensitized plate was prepared through cold rolling and annealing. The effects of electromagnetic and ultrasonic cast rolling on microstructure, mechanical properties, surface roughness and electrolytic corrosion properties of 1050 aluminum substrate were studied. The results show that electromagnetic and ultrasonic cast rolling can decrease the average crystallite size of aluminum substrate by 5 μm, increase the crystal boundaries with uniform distribution, and make the second-phase particles with smaller size distributed dispersively in the substrate, meanwhile, it can increase the tensile strength, elongation and micro-hardness by 4.58%, 9.85% and HV 2, respectively, reduce the surface roughness, make the surface appearance more even, electrolytic corrosion polarization curve of aluminum substrate more smooth and the surface corrosion pits with regular shape more dispersive.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
ZHANG Rong-wang. Current market situation and marketing strategy of PS plate substrate in China [J]. China Metal Bulletin, 2010, 15(16): 42–43. (in Chinese)
JOHNSON J, ANDERSSON C, LESTELIUS M, JARNSTROM L, RATTO P, BLOHM E. Some properties of flexographic printing plates and aspects of print quality [J]. Appita Journal, 2009, 62(5): 371–378.
MA Yi-wen, LIU Xin. Analysis and control of influencing factors for electro-grinding quality of PS plate [J]. Aluminium Fabrication, 2012, 25(2): 47–51. (in Chinese)
CHANG Jiang, GONG Xue, SUN Zhi-hui. Study on regeneration pre-sensitized offset plate based on the nondestructive testing method [J]. Advanced Materials Research, 2012, 380: 348–351.
Van ALPHEN L, NAUWEN P, SLAKHORST J. The relation between the composition, the structure parameters and the etch ability of alloyed A1-cathode foils for electrolytic capacitors [J]. Zeitschrift fur Metallkunde, 1979, 70(3): 158–167.
LI Hong-ying, ZENG Zai-de, WANG Chang-jian. Effects of cold deformation on electrolytic corrosion properties of PS plate [J]. Corrosion & Protection, 2007, 28(8):194–197. (in Chinese)
LI Chun-hong, ZENG Su-min, WANG Shui-bing, LI Chun-mei, CHEN Zhi-qian, CHENG Nan-pu. Study on preparation of 1052H19 aluminum substrate PS plate [J]. Journal of Southwest University (Natural Science Edition), 2008, 30(3): 152–157. (in Chinese)
YANG Dong. Study on electromagnetically cast-rolling technology of PS plate substrate and its properties [D]. Changsha: Central South University, 2009: 21–60. (in Chinese)
ZHU Q F, ZHAO Z H, ZUO Y B, WANG X J, CUI J Z. Effect of low frequency electromagnetic field on as casting structure and surface quality of horizontal direct chill casting 7075 alloy [J]. International Journal of Cast Metals Research, 2012, 25(2): 93–99.
LI Jin-tao, XU Guang-ming, CUI Jian-zhong. Effect of magnetostatic field on microstructure of 5005 aluminum alloy sheet by roll-casting [J]. Advanced Materials Research, 2011, 189–193: 4018–4021.
METAN V, EIGENFELD K, RABIGER D, LEONHARDT M, ECKERT S. Grain size control in Al-Si alloys by grain refinement and electromagnetic stirring [J]. Journal of Alloys and Compounds, 2009, 487(1/2): 163–172.
METAN V, EIGENFELD K. Controlling mechanical and physical properties of Al-Si alloys by controlling grain size through grain refinement and electromagnetic stirring [J]. European Physical Journal Special Topics, 2013, 220(1): 139–150.
ZHANG Hai-tao, CUI Jian-zhong. Production of super-high strength aluminum alloy billets by low frequency electromagnetic casting [J]. Transactions of Nonferrous Metals Society of China, 2011, 21(10): 2134–2139.
MAO Da-heng, ZHANG Yun-fang, NIE Zhao-hui, LIU Qiao-hong, ZHONG Jue. Effects of ultrasonic treatment on structure of roll casting aluminum strip [J]. Journal of Central South University of Technology, 2007, 14(3): 363–369.
ZHANG Li-hua, YU Jun, ZHANG Xiao-ming. Effect of ultrasonic power and casting speed on solidification structure of 7050 aluminum alloy ingot in ultrasonic field [J]. Journal of Central South University of Technology, 2010, 17(3): 431–436.
Author information
Authors and Affiliations
Corresponding author
Additional information
Foundation item: Project(2014CB046702) supported by the National Basic Research Program of China; Project supported by the Postdoctoral Science Foundation of Central South University, China
Rights and permissions
About this article
Cite this article
Shi, C., Mao, Dh. & Fu, Zl. Effect of electromagnetic and ultrasonic cast rolling on microstructure and properties of 1050 aluminum substrate for presensitized plate. J. Cent. South Univ. 22, 422–429 (2015). https://doi.org/10.1007/s11771-015-2538-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11771-015-2538-2