A simple four-node isoparametric finite element with five degrees of freedom, based on Reddy’s third-order shear deformation theory, is elaborated and used in a model for analizing the bending of laminated plates. The results obtained are compared with solutions given by the three-dimensional elasticity and other theories.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1. Introduction
The use of composites materials is growing progressively compared with traditional materials, basically in the fields of application where powerful and lightweight structures are needed [1]. Laminated composite materials are extensively used in many fields, for example, in marine, civil, and mechanical engineering, and are characterized by a light weight, high strength, and high corrosion resistance. A review of recent applications and the development of composite structures for future naval ships and submarines is given in [2].
In the last decades, the finite-element method has become established as a powerful calculation tool and the most widely used method to analyze the complex behavior of composite structures [3].Review [4] reflects the recent development of the method for investigation of laminated composite plates.
Modeling of the stresses and strains of laminated composite plates is still considered as important subject of research, although many theories, such as, e.g., the classical laminated plate theory (CLPT) have been proposed for this purpose. In the early days, the CLPT was used for modeling thin laminated plates, but it neglects the transverse effect of shear deformation [5, 6]. This effect is taken into account in the first-order shear deformation theory (FSDT) [7–11], but it is considered constant across the thickness of the plates. Higher-order theories can describe the nonlinear shear deformations in the thickness direction without any correction factor [12–15]. Reddy proposed a third-order shear deformation theory (TSDT) [16, 17] based on a single-layer approach. It considers a parabolic variation of the transverse shear stresses across the plate thickness and satisfies zero shear stress boundary conditions on the top and bottom of the plate, but requires the C1 continuity of the second-order derivative of transverse displacements. This theory encounters problems when the finite-element method is used, namely the requirement of C1 continuity of displacements for common edges between two elements [18] can be satisfied only in the case of thin plate elements [19].
Many authors encountered this problem and mentioned that C1-continuous elements are computionally inefficient and the accuracy of solution is questionable [20–24].
The objective of this paper is to employ Reddy’ third-order shear deformation theory to analyze the bending of a laminated plate by using a simple isoparametric four-node finite element with five degrees of freedom at each node.
2. Kinematics
According to Reddy’s third-order shear deformation theory (TSDT) [17], the displacement field can be expressed as
where u,v,w,ψ x , and ψ y are five unknown midplane displacement functions of the plate, and h is its thickness (see Fig. 1).
The linear strains associated with the displacement field are
where
3. Constitutive Equations
The constitutive equations for a single layer [11] can be written as
where Q ij are material constants in the material axes of the layer:
The stress–strain relations in the laminate coordinates x, y, and z of a kth layer [11] are given by the relations
where the constants \( {\overline{Q}}_{ij} \) are expresses as
Here, c = cos θ,and s = sin θ, and θ is the angle between the global and local axes of each layer.
4. Equilibrium Equation
The static equations of the theory can be derived using the principle of virtual work, and the variation of strain energy is calculated from the equation [17]
In terms of stresses, strains, and external forces, this equatin can be expressed as
where
Inserting Eqs. (1) into stress–strain relations (2), we have
After integrating these stresses across the thickness of each layer and summation, the generalized force–strain relations are obtained in the form [17]
where
Inserting Eqs.(4) into Eq. (3) gives
with
the strain matrixes can be written as follows:
where c 1 = − 4/3h 2 and c 2 = − 4/h 2.
5. Finite-Element Formulation
For the present study, a four-node quadrilateral C0-continuous isoparametric finite element [25] with five degrees of freedom u,v,w,ψ x , and ψ y at each node is employed:
The real element is determined from the reference space (ξη) by a geometric transformation based on the positions of nodes in the real space (x, y).Our formulation requires the first- and second-order derivatives, therefore, the following processing operations (see Appendix) [26, 27] are used:
Inserting strain matrix (14) into Eq (5), the elementary stiffness matrix is written as follows:
The integrals in Eq. (7) are computed numerically. The stiffness integral is obtained by considering a simple four-node finite element, 2×2 Gauss points for the bending contribution, and a 1×1 point for the shear contribution [25].
This formulation gave good results for the transverse shear stresses, but not for the normal stress and the deflection displacement w, for which an optimization procedure using a function f of the ratio a/h was performed.
Optimization of the normal stress and deflection displacement at different thicknesses required specific values of the function f (a/h).These values were plotted and interpolated to obtain a proper function f (a/h) (Fig. 2). The strain matrices [B 2 κ ] and [B s κ ] were multiplied by this function to improve results.
6. Numerical Examples
The material constants used in examples were as follows: E 1/E 2 = 25, G 12 = G 13 = 0.5E 2, G 23 = 0.2E 2, and v = 0.25.
6.1. Example 1
Deflections of a three layer (0/90/0) square laminate simply supported at all edges and subjected to a uniformly distributed load were analyzed at different mesh divisions and thickness ratios a/h. The nondimensional deflections \( \overline{w} \) calculated at the centre of the plate were compared with those found in [17] and [22]. They are given in Table. 1. Calculation results converged and the error decreased with increasing number of elements with different thickness ratios a/h. The deflection \( \overline{w} \) was calculated by the formula
6.2. Example 2
A three-layer (0/90/0) square laminate simply supported at all edges and subjected to a sinusoidally distributed load was considered at different thickness ratio a/h, and its nondimensional deflection \( \overline{w} \) and stresses \( {\overline{\sigma}}_{xx},{\overline{\sigma}}_{yy},{\overline{\sigma}}_{xy},{\overline{\sigma}}_{xz}, \) and \( {\overline{\sigma}}_{yz} \) were calculated (Table 2). It is seen that the results for the deflection and stresses are closer to those given by the exact 3D elasticity solution [28] than predictions of the HSDT and FSDT [22]. However, in the cases of a/h= 4 and 10, the normal stress \( {\overline{\sigma}}_{xx} \) is comparable to that calculated by the FSDT. The normalized deflection and stresses were calculated by the formulas
6.3. Example 3
A four-layer (0/90/90/0) square laminate simply supported at all edges and subjected to a sinusoidally distributed load was considered at different thickness ratios a/h. Table 3 shows that the calculated nondimensional transverse displacement \( \overline{w} \) and stresses \( {\overline{\sigma}}_{xx},{\overline{\sigma}}_{yy},{\overline{\sigma}}_{xy},{\overline{\sigma}}_{xz}, \) and \( {\overline{\sigma}}_{yz} \) are much closer to those given by the 3D elasticity solution [30] than predictions of the HSDT and FSDT [17]. It is also seen that the normal stress \( {\overline{\sigma}}_{xx} \) at a/h= 4 and 10 is comparable to that given by the FSDT. The normalized deflection and stresses were calculated by the formulas
In Fig. 3, the nondimensional transverse shear stresses \( {\overline{\sigma}}_{xz} \) and \( {\overline{\sigma}}_{yz} \) at their maximum points are indicated. It is seen that the stresses are discontinuous, vary parabolically across the plate thickness, and satisfy zero boundary conditions on the top and bottom surfaces of the plate. In the midplane z/h = 0 at a/h= 10, the present formulation gives value of the transverse shear stress \( {\overline{\sigma}}_{xz} \) very close to that predicted by the 3D elasticity solution. Also, it gives a good result for the transverse shear stress \( {\overline{\sigma}}_{yz} \) at a/h= 10. The transverse shear stress \( {\overline{\sigma}}_{xz} \) in the present formulation at a/h = 4 in the midplane z/h = 0 is the closest to the value of 0.219 given by the 3D elasticity theory. The same is true for the transverse shear stress \( {\overline{\sigma}}_{yz} \) at a/h = 4 in the midplane z/h = 0.
7. Conclusion
A simple finite element with four nodes and five degrees of freedom u, v, w,ψ x , and ψ y at each node, based on the theory of third-order shear deformation theory which requires the second-order derivative of C1-continuous transverse displacements, was used in a model to analyze the bending of laminated plates. The results obtained for the transverse shear stresses are compared with the 3D elasticity solution, where they have a parabolic distribution across the thickness of the plates and satisfy zero boundary conditions on their top and bottom surfaces. This approach gave good results for the transverse shear stresses, but was not efficient for the normal stress and the transverse displacement, therefore, an optimization procedure for them was performed, which led to results close to the 3D elasticity solution.
References
S. K. Gill, M. Gupta, and P. Satsangi, “Prediction of cutting forces in machining of unidirectional glass-fiber-reinforced plastic composites,” Frontiers of Mechanical Engineering, 8, No. 2. 187-200 (2013).
A. Mouritz et al., “Review of advanced composite structures for naval ships and submarines,” Compos. Struct., 53, No. 1, 21-42 (2001).
A. Tati and A. Abibsi, “Un element fini pour la flexion et le flambage des plaques minces stratifiees en materiaux composites,” Revue Des Composites Et Des Materiaux Avances, 17, No. 3, 279–296 (2007).
Y. Zhang and C. Yang, “Recent developments in finite element analysis for laminated composite plates,” Compos. Struct., 88, No. 1, 147-157 (2009).
R. Mindlin, “Influence of rotary inertia and shear in flexural motions of isotropic elastic plates,” J. Appl. Mech., 18, 31-38 (1951).
J. M. Whitney and A. W. Leissa, “Analysis of heterogeneous anisotropic plates,” J. Appl. Mech., 36, No. 2, 261-266 (1969).
J. N. Reddy, Energy and Variational Methods in Applied Mechanics, N. Y., John Wiley, 1984.
E. Reissner, “The effect of transverse shear deformations on the bending of elastic plates,” J. Appl. Mech., 12, A69-A77 (1945).
E. Reissner, “A consistent treatment of transverse shear deformations in laminated anisotropic plates,” AIAA J., 10, No. 5, 716-718 (1972).
J. M. Whitney, “The effect of transverse shear deformation on the bending of laminated plates,” J. Compos. Mater., 3, No. 3, 534-547 (1969).
J. N. Reddy, Mechanics of Laminated Composite Plates and Shells: Theory and Analysis, CRC Press, Boca Raton, FL, Second Edition, 2004.
R. Christensen K. Lo, and E. Wu, “A high-order theory of plate deformation part 1: homogeneous plates,” J. Appl. Mech., 44, No. 7, 663-668 (1977).
S. Mau, “A refined laminated plate theory,” J. Appl. Mech., 40, No. 2, 606-607 (1973).
C.-T. Sun, “Theory of laminated plates,” J. Appl. Mech., 38, No. 1, 231-238 (1971).
J. Whitney and C. Sun, “A higher order theory for extensional motion of laminated composites,” J. of Sound and Vibration, 30, No. 1, 85-97 (1973).
J. N. Reddy, “A refined nonlinear theory of plates with transverse shear deformation,” Int. J. of Solids and Structures, 20, No. 9, 881-896 (1984).
J. N. Reddy, “A simple higher-order theory for laminated composite plates,” J. Appl. Mech., 51, No. 4, 745-752 (1984).
N. N. Khoa and T. I. Thinh, “Finite element analysis of laminated composite plates using high order shear deformation theory,” Vietnam J. of Mechanics, 29, No. 1, 47-57 (2008).
J. L. Batoz and M. B. Tahar, “Evaluation of a new quadrilateral thin plate bending element,” Int. J. for Numerical Methods in Engineering, 18, No. 11, 1655-1677 (1982).
C. H. Thai et al., “Analysis of laminated composite plates using higher-order shear deformation plate theory and nodebased smoothed discrete shear gap method,” Appl. Mathematical Modelling, 36, No. 11, 5657-5677 (2012).
H. Fukunaga, N. Hu, and G. Ren, “FEM modeling of adaptive composite structures using a reduced higher-order plate theory via penalty functions,” Int. J. of Solids and Structures, 38, No. 48,. 8735-8752 (2001).
A. H. Sheikh and A. Chakrabarti, “A new plate bending element based on higher-order shear deformation theory for the analysis of composite plates,” Finite Elements in Analysis and Design, 39, No. 9, 883-903 (2003).
T. Kant and B. Pandya, “A simple finite element formulation of a higher-order theory for unsymmetrically laminated composite plates,” Compos. Struct., 9, No. 3, 215-246 (1988).
L. V. Tran, C. H. Thai, and H. Nguyen-Xuan, “An isogeometric finite element formulation for thermal buckling analysis of functionally graded plates,” Finite Elements in Analysis and Design, 73, 65-76 (2013).
A. J. Ferreira, MATLAB codes for finite element analysis: solids and structures, 157, Springer, 2008,.
J. V. Kouri, Improved Finite Element Analysis of Thick Laminated Composite Plates by the Predictor Corrector Technique and Approximation of C (1) Continuity with a New Least Squares Element, DTIC Document, 1991.
J. Reddy, E. Barbero, and J. Teply, “A plate bending element based on a generalized laminate plate theory,” Int. J. for Numerical Methods in Engineering, 28, No. 10, 2275-2292 (1989).
N. Pagano, “Exact solutions for rectangular bidirectional composites and sandwich plates,” J. Compos. Mater., 4, No. 1, 20-34 (1970).
Z. Wu, R. Chen, and W. Chen, “Refined laminated composite plate element based on global–local higher-order shear deformation theory,” Compos. Struct., 70, No. 2, 135-152 (2005).
N. Pagano and H. J. Hatfield, “Elastic behavior of multilayered bidirectional composites,” AIAA J., 10, No. 7, 931-933 (1972).
Author information
Authors and Affiliations
Corresponding author
Additional information
Russiam translation published in Mekhanika Kompozitnykh Materialov, Vol. 52, No. 2, pp. 367-384, March-April, 2016.
Appendix
Appendix
The matrix of the first-order derivative can be presented as
To obtain the second-order derivatives, the chain rule is successively applied to these relations, resulting in
Rights and permissions
About this article
Cite this article
Belkaid, K., Tati, A. & Boumaraf, R. A Simple Finite Element with Five Degrees of Freedom Based on Reddy’s Third-Order Shear Deformation Theory. Mech Compos Mater 52, 257–270 (2016). https://doi.org/10.1007/s11029-016-9578-z
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11029-016-9578-z