Abstract
Here, we investigated the magnetic and magnetocaloric (MC) properties of manganites labeled PrCaBaMnO and PrCaBaMnBiO, with compositions Pr0.55Ca0.05Ba0.40Mn1−xBixO3 (x = 0 and 0.02), respectively. The solid-state reaction method was used for sample preparation, and the structural properties were checked using X-ray diffraction (XRD). Temperature dependence of magnetization (M(T)) measurements was carried out in the range of 5–300 K under 100 Oe field to determine the transition temperature of the manganites. Magnetic entropy change (\(-\Delta {S}_{\text{M}}\)) values were computed from field-dependent magnetization (M(H)) measurements. For the 2 T magnetic field values, the \(-\Delta {{S}_{ }}_{\text{M}}^{\text{max}}\) values for the PrCaBaMnO and PrCaBaMnBiO manganites are 3.15 and 2.86 Jkg-1K-1, respectively. Relative Cooling Power (RCP) values were calculated from the temperature dependence of \(-\Delta {S}_{\text{M}}\) (T) curves, resulting in 82.4 and 88.6 Jkg-1 for PrCaBaMnO and PrCaBaMnBiO, respectively. Banerjee’s criterion and Franco’s universal master curve confirmed that the transition type for the studied manganites is second order.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
Refrigeration and air conditioning technologies, commonly referred to as traditional cooling systems, play a vital role in our daily lives, relying on the compression/expansion principle of gases. These systems, which remain at low levels compared to other systems in terms of energy efficiency, have high energy consumption. In these systems, which are known to reach thermodynamically limited values, high-vibration compressors are used that cause high energy consumption and excessive noise. Additionally, gases used in these systems as refrigerants have adverse effects on the environment [1]. Consequently, there is a need for research and regulations to reduce the energy consumption in refrigeration and air conditioning processes and reduce the effects of traditional systems on the environment.
Refrigeration systems based on different thermodynamic effects have been developed to replace these conventional systems [2]. Among these alternatives, magnetic refrigeration (MR) systems are more advantageous in terms of energy consumption and efficiency and are considered the future of the cooling technologies [3]. MR systems operate based on the magnetocaloric effect (MCE) principle, which is one of the reversible thermodynamic effects with potential applications in various technologies [4,5,6]. MCE is the observed change in temperature of the material due to the change in entropy of the magnetic material as a result of exposure to an external magnetic field. This effect involves two fundamental processes: adiabatic temperature change (\(\Delta {T}_{\text{ad}}\)) and magnetic entropy change (\(-\Delta {S}_{\text{M}}\)) [7]. The most essential condition for designing a magnetic cooler is to obtain magnetic material with a high \(-\Delta {S}_{\text{M}}\) and a high \(\Delta {T}_{\text{ad}}\) value within the operating temperature range [8]. MR systems have been developed in which Gd and Gd-based alloys are used as cooling substances [9]. The practical application of these material systems has not been feasible for some critical reasons [5]. Factors affecting their commercial use include high raw material costs, challenging and complex production techniques, high thermal and magnetic hysteresis, etc. [10] Materials that can be used as cooling materials should not have these and similar negative features. Considering these criteria, manganites are among the material groups with high potential to be considered as a suitable cooling element for MR systems. Although the manganites have relatively low \(-\Delta {S}_{\text{M}}\) values compared to other material groups, they have desirable properties such as low raw material cost, simple and inexpensive production techniques, and a second-order phase transition (SOMT). One of the reasons why manganites are in a more advantageous position compared to other material groups is that their magnetic phase transition temperature (TC) can be adjusted with doping [10].
The structural properties of manganites have a great impact on their magnetic and MC properties. Therefore, it is necessary to briefly mention the structural properties of manganites. Manganites are a group of materials represented by the chemical equation with ABO3, crystallizing in the perovskite structure, and containing manganese ions as the B-site element [11]. Numerous investigations have been conducted to examine the magnetic and MC properties of La and Pr-based manganites [11,12,13,14,15]. In many of these studies, it is aimed to investigate the effects of factors such as change in the average ionic radius of the A-site , Mn3+/ Mn4+ ratio, cationic mismatch effect, sintering temperature, and doping of A and B-sites [14, 16,17,18,19,20]. The structural, magnetic, and MC properties of Pr0.55Ca0.05Ba0.40Mn1-xBixO3 (x = 0 and 0.02) manganites, which have not been studied before, are presented in this study. The results of the analysis and measurements performed to examine the structural, magnetic, and MC properties of the samples are given in detail.
2 Experimental procedure
In this study, the solid-state reaction method was chosen due to its simplicity and ease of application for sample preparation. Detailed information about the processes of the method has been provided in our previous work [11, 20]. Sigma Aldrich brand Pr2O3 (99.9%), CaO (99.995%), BaO (99.995%), Bi2O3 (99.99%), and MnO2 (99.99%) chemicals were used in sample production. Stoichiometric amounts of these starting chemicals were ground and mixed in an agate mortar for 6×10 minutes. The powder mixture was calcined in air at 600 °C for 6 hours. After this process, a second grinding process was applied under the same conditions (for 6×10 minutes for a total of 60 minutes). Then, the powder sample was pressed to form tablets. The tablets were subjected to the sintering process at 1200 °C for 24 hours. The synthesized samples Pr0.55Ca0.05Ba0.4Mn1−xBixO3 (x = 0 and 0.02) have been labeled as PrCaBaMnO for x = 0 and PrCaBaMnBiO for x = 0.02, respectively. To determine the crystal symmetry and phase purity of the samples, X-ray diffraction (XRD) measurements were executed at room temperature. The surface morphology of the PrCaBaMnO and PrCaBaMnBiO manganites was analyzed using scanning electron microscopy (SEM). The magnetic measurements were performed by a physical property measurement system (PPMS) equipped with a vibrating sample magnetometer (VSM) module.
3 Results and discussions
The diffraction patterns obtained from XRD analyses of PrCaBaMnO and PrCaBaMnBiO manganites are presented in Fig. 1. In the diffraction patterns of the manganites, the red dots and solid black lines represent observed and calculated data, respectively. The green ticks show Bragg diffraction positions. The difference between the calculated and observed data is illustrated by the blue line. Sharp and narrow-based diffraction peaks interpreted as good and homogeneous crystallization of the samples are seen from the XRD patterns [21]. A very weak diffraction peak consistent with the BaMnO2.98 impurity phase was detected in the diffraction patterns of both samples, showing antiferromagnetic (AFM) properties [22]. The volume fraction of the impurity phase [23] is 3.6 % and 3.5 % for PrCaBaMnO and PrCaBaMnBiO manganites, respectively. The diffraction peaks of the studied manganites overlap with the Pbnm space group belonging to the orthorhombic crystal structure. In Table 1, lattice parameters and unit cell volume (V) acquired from the XRD refinement for PrCaBaMnO and PrCaBaMnBiO manganites using FULLPROF software are provided. Although a change in the lattice parameters was detected with the addition of Bi, no change in the crystal structure was observed. As seen from Table 1, the unit cell volume (V) of the PrCaBaMnBiO manganite is smaller than that of PrCaBaMnO manganite. Although an increase in the V value was thought due to the larger ionic radius of the Bi ion, a decrease in V value was noticed [24]. It is thought that this decrease is a result of the chemical pressure induced in the Mn octahedral as a consequence of the change in lattice parameters [25]. This decrease may also be attributed to the electronic configuration of Bi3+ ions that are identified by their 6s2 electrons which can create local distortion and hybridize with oxygen’s 2p orbitals [16]. The change in lattice parameters and decrease in V value may affect the magnetic and MC properties. The stability of the perovskite structure is controlled by the Goldschmidt tolerance factor (tG) given below [26]:
The terms of \(\langle {r}_{\text{A}}\rangle\) and \(\langle {r}_{\text{B}}\rangle\) given in the equation state the mean ionic radii of A and B-sites, respectively. The term \({r}_{\text{O}}\) is the ionic radius of the oxygen ion. For PrCaBaMnO and PrCaBaMnBiO manganites, the tG values have been calculated based on Shannon’s effective ionic radii list [24]. The tG values of the studied manganites are represented in Table 1. The obtained values confirm that the samples crystallize in the perovskite structure [27, 28]. The tG values calculated for the samples are compatible with the orthorhombic structure. As expected, a decrease in tG has been observed with doping Bi at a concentration of x = 0.02 to the Mn-site since Bi3+ ions have larger ionic radii than Mn3+ ions [24]. The average crystalline size (DXRD) of the PrCaBaMnO and PrCaBaMnBiO manganites was calculated using the Debye Scherrer equation as follows [20].
where λ is the x-ray wavelength (λ=1.54060 Å), κ is the grain shape factor, β denotes the full width at half maximum of the most intense peak, and θ is the Bragg diffraction angle. In Table 1, the calculated β and DXRD values are provided. It is released that the β value decreases with the Bi substitution for Mn, leading to an increase in the DXRD value. The discrepancy in the ionic radii of the Mn3+ and Bi3+ ions may contribute to an enhancement in DXRD values.
To investigate surface morphology and determine the average particle size (D) of the manganites, SEM images at 20 kx magnification were attained (inset of Fig. 2). The SEM images of both samples show particles of different sizes and shapes and intergranular spaces. Grain boundaries are more apparent for PrCaBaMnBiO manganite than that of the other. Therefore, we can say that the sharpness of the grain boundaries increases with the Bi substitution. ImageJ software was used to determine the D of the manganites. The size of 100 randomly selected particles was measured with this program and their histograms were obtained (See Fig. 2). The histograms reveal granular structures of different sizes in both samples. The average particle size (DSEM) was approximately determined by Gaussian fit. DSEM for the PrCaBaMnO and PrCaBaMnBiO manganites was determined as 0.79 and 0.83 μm, respectively. Although the particle size and the clarity of the grain boundaries are positively influenced by the Bi substitution, an increase in the volume of the intergranular spaces is also observed. The magnetic and MC properties of the studied manganites may decrease due to the deterioration of intergranular conduction with the increased volume of intergranular spaces. When compared to the D calculated from SEM and XRD, it is observed that the DSEM is higher than that of DXRD. It implies that the grains are formed by several crystallites due to internal stresses or defects in the structure. The agglomeration degree, indicating the average number of crystallites forming a single grain, is determined by the DSEM /DXRD ratio [29].
To determine the TC values of PrCaBaMnO and PrCaBaMnBiO manganites, low field M(T) measurements were made in both the ZFC and FC processes under a magnetic field of 100 Oe and in the temperature range of 5–300 K. The M(T) curves of PrCaBaMnO and PrCaBaMnBiO manganites are given in Fig. 3. When the M(T) curves were examined, it is observed that the samples exhibit a particular magnetization value at low-temperature values, and the magnetization value decreases with increasing temperature and rapidly drops to zero. The temperature at which the magnetization value decreases to zero occurs represents the magnetic phase transition temperature, TC. This change observed in the M(T) curves is a transition specific to FM materials, and the material showed a transition to paramagnetic (PM) phase in TC. The decrease in the magnetization value of the samples as the temperature increases is due to the increasing thermal interaction energy disrupting magnetic couplings in the structure [30]. Although the temperature-dependent variations of the curves obtained in the ZFC and FC processes behave similarly at temperatures above TC, these curves in the low-temperature region exhibit different behaviors. The ZFC curves for both samples enhance with increasing temperature. This behavior may be due to the coexistence of AFM and FM clusters [31]. For both samples, a separation is observed in the low-temperature region due to the different temperature dependence of the ZFC and FC curves. The separation observed at low temperatures indicates that the samples exhibit a spin-glass-like behavior [32,33,34]. This separation allows us to have an idea about the long-range or short-range magnetic interaction in the material and the magnitude of the magnetic anisotropy of the structure [34, 35]. Materials with high magnetic anisotropy exhibit spins ordered in a preferential orientation, and in the ZFC process, their spins remain locked in random orientations. If a magnetic field is applied to the material after the cooling process, the measured magnetization value changes depending on the anisotropy of the material. Systems with high magnetic anisotropy may exhibit a low magnetization value in the ZFC curve at low temperatures, as the applied field strength may not be sufficient to direct the spins, resulting in differences between the magnetization curves measured during cooling in the FC process. When the magnetization value increases, the lower the magnetization value of the ZFC curve at low temperatures, the higher the anisotropy of the structure [36]. Considering the explanations given above, it can be said that the magnetic interaction is short-range [37]. The TC values were determined by obtaining the dM/dT-T curve from the M(T) data obtained in the ZFC process. This is one of the most widely used methods to determine the TC value. In this method, the temperature value corresponding to the minimum point of the dM/dT-T curve gives the TC value. The TC values of PrCaBaMnO and PrCaBaMnBiO manganites were determined as 164 and 154 K, respectively. The observed decrease in the TC value with Bi substitution to the Mn-site may be due to the weakening of double exchange (DE) interactions [38, 39]. In addition, it is seen that the magnetic phase transition of the Bi-doped sample occurs in a wider temperature range than that of undoped manganite. A large value of \(-\Delta {S}_{\text{M}}\) is generally observed when the magnetic phase transition occurs sharply [40] and the expansion in the magnetic phase transition temperature range with Bi-element substitution into the Mn-site can cause a decrease in the \(-\Delta {S}_{\text{M}}\) value.
The M(H) curves of PrCaBaMnO and PrCaBaMnBiO manganites obtained from M(H) measurements performed under 0–5 T field change at 4 K temperature intervals around TC are given in Fig. 4. In the low-temperature region, it is observed that the magnetization values initially increase rapidly with the field and reach saturation above a field value of 0.5 T. No further change in magnetization value is observed with increasing field. This is characteristic of ferromagnetic materials and is the result of the orientation of all magnetic moments in the direction of the field. In the high-temperature region (above TC), the M(H) curves exhibit a linear variation with the applied field, representing paramagnetism. In summary, the transition from the FM state to the PM state observed in the M(T) measurements is also clearly seen in the M(H) curves.
The main components defining the MCE are the \(-\Delta {S}_{\text{M}}\) ve \(\Delta {T}_{\text{ad}}\) values. Indirect measurement methods are commonly used to determine the \(-\Delta {S}_{\text{M}}\) value. Initially, the TC of the samples is identified, and isothermal M(H) measurements are performed around the TC. The numerical value of the \(-\Delta {S}_{\text{M}}\) value can be determined by using the data obtained from these measurements and the following equation.
The terms Mi and Mi+1 given in Eq. (3) are abbreviations that express magnetization values at Ti and Ti+1 temperatures, respectively. The \(-\Delta {S}_{\text{M }}\left(T\right)\) curves obtained for various magnetic field change (\(\Delta H\)) values of PrCaBaMnO and PrCaBaMnBiO manganites are given in Fig. 5. When the curves are examined, it is seen that it gives a maximum peak around TC, which is called the maximum \(-\Delta {S}_{\text{M}}\)(\(-\Delta {{S}_{ }}_{\text{M}}^{\text{max}}\)) value [41]. It is observed that there is an enhancement in \(-\Delta {{S}_{ }}_{\text{M}}^{\text{max}}\) values due to the increase in magnetization of PrCaBaMnO and PrCaBaMnBiO manganites with the increase of the external applied field. In addition, it is observed that the peak position of \(-\Delta {{S}_{ }}_{\text{M}}^{\text{max}}\) for PrCaBaMnO and PrCaBaMnBiO manganites moves to high temperature with increasing magnetic field. This behavior may arise from the magnetic field dependence of the TC [42, 43]. For the PrCaBaMnO manganite, the \(-\Delta {{S}_{ }}_{\text{M}}^{\text{max}}\) value calculated under 2 T magnetic field was calculated as 3.15 Jkg-1K-1. Under the same magnetic field value, this value is 2.86 Jkg-1K-1 for the PrCaBaMnBiO manganite. According to the results obtained, the replacement of the Bi-element with Mn at low rates causes a decrease in the value of \(-\Delta {{S}_{ }}_{\text{M}}^{\text{max}}\). It is considered that this decrease is due to the increase in the volume of intergranular spaces obtained from SEM analyses and the reduction in particle sizes.
For MS systems, the magnetic material must meet particular criteria to be considered a cooling element [44]. Although the material has high \(-\Delta {S}_{\text{M}}\) ve \(\Delta {T}_{\text{ad}}\) values under low field is the primary condition for being considered as a candidate cooler, it is not sufficient to meet this criterion. Apart from these two parameters, the RCP value, which determines the cooling capacity of the MS system to be designed, must be high and the hysteresis (thermal and magnetic) effect affecting the performance of the cooler must be negligible [11]. Thermal hysteresis is associated with the reversibility of the MCE of a magnetic heat sink, while magnetic hysteresis is connected to the operating efficiency of a magnetic heat sink [10]. The RCP value of the materials is calculated by \(\text{RCP}=\left|-\Delta {S}_{\text{M}}^{\text{max}}\right|\times {\updelta T}_{FWHM}\) equation. The \({\updelta T}_{FWHM}\) term is the full width at half the maximum of the \(-\Delta {S}_{\text{M}}\) (T) curve. For PrCaBaMnO and PrCaBaMnBiO manganites, the RCP values were calculated as 82.4 and 88.6 Jkg-1 under 2 T magnetic fields, respectively. Although the \(-\Delta {{S}_{ }}_{\text{M}}^{\text{max}}\) value of PrCaBaMnBiO manganite is lower than PrCaBaMnO, its RCP value is higher. This result may stem from the magnetic phase transition occurring in a broader temperature range of the PrCaBaMnBiO manganite. In order to compare the results obtained with the literature, the \(-\Delta {{S}_{ }}_{\text{M}}^{\text{max}}\) and RCP values of some Pr-based manganites for varied \(\Delta H\) values are given in Table 2.
It is necessary to identify the type of magnetic phase transition of materials that can be used as cooling substances in MS systems. Materials in which the phase transition is attended by a structural transition exhibit First-Order Magnetic Transition (FOMT). The use of materials that exhibit transition of this type in technological applications is not suitable because the performance of the magnetic cooler is adversely affected. Second-order magnetic transition (SOMT) materials have high potential for applications. This transition of magnetic materials exhibiting SOMT usually occurs over a wide temperature range, and as a result, high RCP values may be achieved. There are many methods used to determine the type of magnetic phase transition [45,46,47,48,49]. The widely used method for determining the type of magnetic transition is the Banerjee criterion [45]. In this criterion, H/M–M2 curves (described as Arrott plots) are obtained by using the data obtained from isothermal M(H) measurements. Considering the sign of the slopes of these curves around TC, the type of magnetic transition is decided. The positive slope of the Arrott curves around TC implies that the type of magnetic transition is second order. The negative slope states that the kind of magnetic phase transition is first order. In light of these statements, the Arrott curves were obtained to determine the type of magnetic phase transitions of PrCaBaMnO and PrCaBaMnBiO manganites (Fig. 6). The Arrott curves of the PrCaBaMnO and PrCaBaMnBiO manganites have a positive slope around TC. Consequently, it can be said that the magnetic phase transition of the studied manganites is of the second order. To check whether the methods used in determining the type of magnetic phase transition are compatible with each other, the phenomenological method proposed by Franco et al known as the universal master curve was also used [47, 50]. In this method, the rescaled temperature (θ) dependence of −\(\Delta {S}_{\text{M}}(T)/\) \(-\Delta {S}_{\text{M}}^{\text{max}}\) is obtained. The θ is calculated from the following equations;
where Tr1 and Tr2 are the temperatures above and below TC, respectively. In this approach, if the curves obtained for different \(\Delta H\) values collapse to a single curve, the nature of magnetic phase transition is second order [51]. The −\(\Delta {S}_{\text{M}}(T)/\) \(-\Delta {S}_{\text{M}}^{\text{max}}\)(θ) curves for PrCaBaMnO and PrCaBaMnBiO manganites are given in Fig. 7. It is seen that the curves for both manganites are reduced to a single curve. According to the obtained curves for both manganites, it can be said that the magnetic phase transition type is second order. These methods used to determine the magnetic phase transition are consistent with each other.
4 Conclusions
In the present work, the structural, magnetic, and magnetocaloric properties of Pr0.55Ca0.05Ba0.40Mn1−xBixO3 (x = 0 and 0.02) manganites prepared by the solid-state reaction method were examined. XRD analyses were performed to determine the crystal structure of manganites and to examine the effect of Bi contribution on lattice parameters and unit cell volume. It is understood from the XRD results that both manganites crystallize in the orthorhombic crystal structure. No change in the crystal structure was induced by Bi doping to the manganese region. However, the unit cell volume of the PrCaBaMnO and PrCaBaMnBiO manganites was decreased with the substitution. In light of the information obtained from SEM analysis, it was observed that a small Bi substitution to the Mn-site caused a decrease in the volume of interparticle spaces and the size of the particles. From M(T) measurements, the TC values of PrCaBaMnO and PrCaBaMnBiO manganites were identified as 164 and 154 K, respectively. Compared to undoped PrCaBaMnO manganite, a decrease implying deterioration of DE interactions in the TC value of Bi-doped PrCaBaMnBiO manganite was observed. For the PrCaBaMnO and PrCaBaMnBiO manganites, the \(-\Delta {{S}_{ }}_{\text{M}}^{\text{max}}\) values calculated under 2 T magnetic fields were calculated as 3.15 and 2.86 Jkg-1K-1, respectively. The RCP values are 82.4 and 88.6 Jkg-1 at 2 T magnetic fields. A higher RCP value was calculated for the PrCaBaMnBiO manganite, implying that the magnetic phase transition occurs in a broader temperature range. According to Banerjee’s criterion and Franco’s universal master cure, both manganites show SOMT. The \(-\Delta {{S}_{ }}_{\text{M}}^{\text{max}}\) and RCP values of the studied manganites are within acceptable limits for low-temperature applications especially (100–200 K).
Data availability
All data generated or used during the study are available from the corresponding author by request.
References
D. Swathi, N.K. Yadav, N. Kumar Swamy, N. Pavan Kumar, Magnetocaloric Materials For Green Refrigeration (Elsevier Inc., Amsterdam, 2023)
J. Steven Brown, P.A. Domanski, “Review of alternative cooling technologies. Appl. Therm. Eng. 64, 252–262 (2014)
O. Sari, M. Balli, From conventional to magnetic refrigerator technology. Int. J. Refrig. 37, 8–15 (2014)
A. Kitanovski, Energy applications of magnetocaloric materials. Adv. Energy Mater. 10, 1903741–1903741 (2020)
A. Kitanovski, P.W. Egolf, Innovative ideas for future research on magnetocaloric technologies. Int. J. Refrig. 33, 449–464 (2010). https://doi.org/10.1016/j.ijrefrig.2009.11.005
V.I. Zverev, A.P. Pyatakov, A.A. Shtil, A.M. Tishin, Novel applications of magnetic materials and technologies for medicine. J. Magn. Magn. Mater. 459, 182–186 (2018). https://doi.org/10.1016/j.jmmm.2017.11.032
A.M. Tishin, Y.I. Spichkin, “Magnetocloric Effect and Its Applications (IOP publishing, Bristol, 2003), pp.4–401
B. Monfared, B. Palm, Material requirements for magnetic refrigeration applications. Int. J. Refrig. 96, 25–37 (2018). https://doi.org/10.1016/j.ijrefrig.2018.08.012
V.K. Pecharsky, K.A. Gschneidner, Advanced magnetocaloric materials: what does the future hold? Int. J. Refrig. 29(8), 1239–1249 (2006). https://doi.org/10.1016/j.ijrefrig.2006.03.020
M.-H. Phan, S.-C. Yu, Review of the magnetocaloric effect in manganite materials. J. Magn. Magn. Mater. 308, 325–340 (2007). https://doi.org/10.1016/j.jmmm.2006.07.025
A.O. Ayaş, S.K. Çetin, G. Akça, M. Akyol, A. Ekicibil, Magnetic refrigeration: current progress in magnetocaloric properties of perovskite manganite materials. Mater. Today Commun. 35, 105988 (2023). https://doi.org/10.1016/j.mtcomm.2023.105988
N. Nedelko, S. Lewinska, A. Pashchenko, I. Radelytskyi, R. Diduszko, E. Zubov, W. Lisowski, J.W. Sobczak, K. Dyakonov, A. Ślawska-Waniewska, V. Dyakonov, H. Szymczak, Magnetic properties and magnetocaloric effect in La0.7Sr0.3-xBixMnO3 manganites. J. Alloys and Compd. 640, 433–439 (2015). https://doi.org/10.1016/j.jallcom.2015.03.126
S. Kılıç Çetin, M. Acet, A. Ekicibil, Effect of Pr-substitution on the structural, magnetic and magnetocaloric properties of (La1-xPrx)0.67Pb0.33MnO3 (0.0 ≤ x ≤ 0.3) manganites. J. Alloys Compd. 727, 1253–1262 (2017). https://doi.org/10.1016/j.jallcom.2017.08.199
G. Akça, Enhancement of magnetic entropy change in La0.57Nd0.1Sr0.33-xCaxMnO3 manganites. J. Mater. Sci. Mater. Electron. 33, 26495–26512 (2022). https://doi.org/10.1007/s10854-022-09328-w
V.E. Salazar-Muñoz, A. Lobo Guerrero, S.A. Palomares-Sánchez, Review of magnetocaloric properties in lanthanum manganites. J. Magn. Magn. Mater. (2022). https://doi.org/10.1016/j.jmmm.2022.169787
A. Krichene, P.S. Solanki, S. Rayaprol, V. Ganesan, W. Boujelben, D.G. Kuberkar, B-site bismuth doping effect on structural, magnetic and magnetotransport properties of La0.5Ca0.5Mn1−xBixO3. Ceram. Int. 41, 2637–2647 (2015). https://doi.org/10.1016/j.ceramint.2014.10.163
A. Selmi, R. M’Nassri, W. Cheikhrouhou-Koubaa, N. Chniba Boudjada, A. Cheikhrouhou, Influence of transition metal doping (Fe Co, Ni and Cr) on magnetic and magnetocaloric properties of Pr0.7Ca0.3MnO3 manganites. Ceram. Int. 41, 10177–10184 (2015). https://doi.org/10.1016/j.ceramint.2015.04.123
G. Akça, S.K. Çetin, M. Güneş, A. Ekicibil, Magnetocaloric properties of (La1−xPrx)0.85K0.15MnO3 (x=0.0, 0.1, 0.3 and 0.5) perovskite manganites. Ceram. Int. 42(2016), 19097–19104 (2016). https://doi.org/10.1016/j.ceramint.2016.09.070
S.K. Çetin, M. Acet, M. Güneş, A. Ekicibil, M. Farle, Magnetocaloric effect in (La1−xSmx)0.67Pb0.33MnO3 (0 ≤ x ≤ 0.3) manganites near room temperature. J. Alloys Compd. 650, 285–294 (2015). https://doi.org/10.1016/j.jallcom.2015.07.217
A.O. Ayaş, A. Kandemir, S.K. Çetin, G. Akça, M. Akyol, A. Ekicibil, Investigation of the effect of sintering temperature on structural, magnetic and magnetocaloric properties in PrCaMn2O6 double perovskite manganite system. J. Mater. Sci. Mater. Electron. 33, 7357–7370 (2022). https://doi.org/10.1007/s10854-022-07843-4
J. Fan, L. Pi, L. Zhang, W. Tong, L. Ling, B. Hong, Y. Shi, W. Zhang, D. Lu, Y. Zhang, Magnetic and magnetocaloric properties in second-order phase transition La1−xKxMnO3 and their composites. Phys. B Condens. Matter. 532(2016), 166–171 (2018). https://doi.org/10.1016/j.physb.2017.03.031
Y. Fang, M. Li, F. Chen, Observation of Magnetic phase transition and magnetocaloric effect in Ba1−xSrxMnO3−δ. J. Supercond. Nov. Magn. 31, 3787–3792 (2018). https://doi.org/10.1007/s10948-018-4648-1
A.I. Abou-Aly, R. Awad, S.A. Mahmoud, M.M. Barakat, EPR studies of (Bi, Pb)-2223 phase substituted by ruthenium ions. J. Alloys Compd. 509, 7381–7388 (2011). https://doi.org/10.1016/j.jallcom.2011.03.160
R.D. Shannon, Revised effective ionic radii in halides and chalcogenides. Acta Cryst. A32, 751 (1976)
C.H. Shen, C.C. Chen, R.S. Liu, R. Gundakaram, S.F. Hu, J.M. Chen, Internal chemical pressure effect and magnetic properties of La0.6(Sr0.4-xBax)MnO3. J. Solid State Chem. 156, 117–121 (2001). https://doi.org/10.1006/jssc.2000.8970
A.S. Bhalla, R. Guo, R. Roy, The perovskite structure: a review of its role in ceramic science and technology. Mater. Res. Innov. 4, 3–26 (2000). https://doi.org/10.1007/s100190000062
S. Tarhouni, A. Mleiki, I. Chaaba, H. Ben Khelifa, W. Cheikhrouhou-Koubaa, M. Koubaa, A. Cheikhrouhou, E.K. Hlil, Structural, magnetic and magnetocaloric properties of Ag-doped Pr0.5Sr0.5-xAgxMnO3 manganites (0.0≤x≤0.4). Ceram. Int. 43, 133–143 (2017). https://doi.org/10.1016/j.ceramint.2016.09.122
L.D. Mendonca, A. D’Souza, M.S. Murari, M.D. Daivajna, Magneto transport anomaly of bismuth substituted (La, Na) MnO3. J. Supercond. Nov. Magn. 33, 1809–1819 (2020). https://doi.org/10.1007/s10948-020-05430-4
A. Degreeeysam, A. Moheb, E. Joudaki, High surface area nano-sized La0.6Ca0.4MnO3 perovskite powder prepared by low temperature pyrolysis of a modified citrate gel. Cent. Eur. J. Chem. 7, 809–817 (2009). https://doi.org/10.2478/s11532-009-0083-2
M.D. Daivajna, V.P.S. Neeraj Kumar, B.G. Awana, J. Benedict Christopher, S.O. Manjunath, K.Z. Syu, Y.K. Kuo, A. Rao, Electrical, magnetic and thermal properties of Pr0.6−xBixSr0.4MnO3 manganites. J. Alloys Compd. 588, 406–412 (2014). https://doi.org/10.1016/j.jallcom.2013.11.033
H. Gencer, S. Atalay, H.I. Adiguzel, V.S. Kolat, Magnetocaloric effect in the La0.62Bi0.05Ca0.33MnO3 compound. Phys. B Condens. Matter. 357(2005), 326–333 (2005). https://doi.org/10.1016/j.physb.2004.11.084
N. Chau, D.T. Hanh, N.D. Tho, N.H. Luong, Spin glass-like behavior, giant magnetocaloric and giant magnetoresistance effect in PrPb manganites. J. Magn. Magn. Mater. 303, 335–338 (2006). https://doi.org/10.1016/j.jmmm.2006.01.094
N.H. Luong, D.T. Hanh, N. Chau, N.D. Tho, T.D. Hiep, Properties of perovskites La1−xCdxMnO3. J. Magn. Magn. Mater. 290–291, 690–693 (2005). https://doi.org/10.1016/j.jmmm.2004.11.338
B. Kumar, J.K. Tiwari, H.C. Chauhan, S. Ghosh, Multiple magnetic phase transitions with different universality classes in bilayer La1.4Sr1.6Mn2O7 manganite. Sci. Rep. 11, 1–17 (2021). https://doi.org/10.1038/s41598-021-00544-8
A. Coşkun, E. Taşarkuyu, A.E. Irmak, S. Aktürk, High magnetic entropy change in La0.70Ca0.21Ag0.09MnO3 compound. J. Alloys Compd. 669, 217–223 (2016). https://doi.org/10.1016/j.jallcom.2016.01.230
S. Kılıç Çetin, G. Akça, M.S. Aslan, A. Ekicibil, Role of nickel doping on magnetocaloric properties of La0.7Sr0.3Mn1−xNixO3 manganites. J. Mater. Sci. Mater. Electron. 32, 10458–10472 (2021). https://doi.org/10.1007/s10854-021-05702-2
J. Fan, L. Xu, X. Zhang, Y. Shi, W. Zhang, Y. Zhu, B. Gao, B. Hong, L. Zhang, W. Tong, L. Pi, Y. Zhang, Effect of A-site average radius and cation disorder on magnetism and electronic properties in manganite La0.6A0.1Sr0.3MnO3 (A = Sm, Dy, Er) (A = Sm, Dy, Er). J Mater Sci 50, 2130–2137 (2015)
I. Kammoun, W. Cheikhrouhou-Koubaa, W. Boujelben, A. Cheikhrouhou, Bi doping effects on the physical properties of Pr0.6Sr0.4Mn1-xBixO3 (0 ≤ x ≤ 0.2) manganese oxides. J. Alloys Compd. 452, 195–199 (2008). https://doi.org/10.1016/j.jallcom.2006.11.069
M.R. Laouyenne, M. Baazaoui, S. Mahjoub, W. Cheikhrouhou-Koubaa, M. Oumezzine, Enhanced magnetocaloric effect with the high tunability of bismuth in La0.8Na0.2Mn1−xBixO3 (0 ≤ x ≤ 0.06) perovskite manganites. J. Alloys Compd. 720, 212–220 (2017). https://doi.org/10.1016/j.jallcom.2017.05.269
F. Saadaoui, M.M. Nofal, R. M’Nassri, M. Koubaa, N. Chniba-Boudjada, A. Cheikhrouhou, Magnetic and magnetocaloric properties of La0.55Bi0.05Sr0.4CoO3 and their implementation in critical behaviour study and spontaneous magnetization estimation. RSC Adv. 9, 25064–25074 (2019). https://doi.org/10.1039/C9RA04141A
A. Bhattacharyya, S. Chatterjee, S. Giri, S. Majumdar, Magnetotransport and magnetocaloric effect in Ho2In. Eur. Phys. J. B 70, 347–351 (2009)
L. Zhang, L. Li, R. Li, J. Fan, L. Ling, W. Tong, Z. Qu, S. Tan, Y. Zhang, Spin–lattice coupling studied by magnetic entropy and EPR in the CdCr 2 S 4 system. Solid State Commun. 150, 2109–2113 (2010). https://doi.org/10.1016/j.ssc.2010.09.017
M.S. Anwar, S. Kumar, F. Ahmed, N. Arshi, G.W. Kim, C.G. Lee, B.H. Koo, “Large magnetic entropy change in La0.55Ce0.2Ca0.25MnO3 Perovskite.” J. Magn. 31, 457–460 (2011). https://doi.org/10.4283/jmag.2011.16.4.457
T. Gottschall, K.P. Skokov, M. Fries, A. Taubel, I. Radulov, F. Scheibel, D. Benke, S. Riegg, O. Gutfleisch, Making a cool choice: the materials library of magnetic refrigeration. Adv. Energy Mater. 9, 1901322 (2019). https://doi.org/10.1002/aenm.201901322
B.K. Banerjee, On a generalised approach to first and second order magnetic transitions. Phys. Lett. 12, 16–17 (1964). https://doi.org/10.1016/0031-9163(64)91158-8
V. Franco, J.S. Blázquez, A. Conde, Field dependence of the magnetocaloric effect in materials with a second order phase transition: a master curve for the magnetic entropy change. Appl. Phys. Lett. 89(22), 222512 (2006). https://doi.org/10.1063/1.2399361
C.M. Bonilla, J. Herrero-Albillos, F. Bartolomé, L.M. García, M. Parra-Borderías, V. Franco, Universal behavior for magnetic entropy change in magnetocaloric materials: an analysis on the nature of phase transitions. Phys. Rev. B 81(22), 1–7 (2010)
H. Yamada, K. Fukamichi, T. Goto, Itinerant-electron metamagnetism and strong pressure dependence of the curie temperature. Phys. Rev. B 65, 024413 (2001). https://doi.org/10.1103/PhysRevB.65.024413
G. Akça, S. Kılıç Çetin, A. Ekicibil, Structural, magnetic and magnetocaloric properties of (La1−xSmx)0.85K0.15MnO3 (x = 0.0, 0.1, 0.2 and 0.3) perovskite manganites. Ceram. Int. 43, 15811–15820 (2017). https://doi.org/10.1016/j.ceramint.2017.08.150
V. Franco, A. Conde, J.M. Romero-Enrique, J.S. Blázquez, A universal curve for the magnetocaloric effect: an analysis based on scaling relations. J. Phys. Condens. Matter 20, 285207 (2008). https://doi.org/10.1088/0953-8984/20/28/285207
H. Yang, Q. Wu, N. Yu, Y. Yu, M. Pan, P. Zhang, H. Ge, Study of magnetic and magnetocaloric effect of Pr0.5Sr0.5-xNaxMnO3 manganites. J. Solid State Chem. 282, 121072 (2020)
R. Thaljaoui, W. Boujelben, M. Pękała, K. Pękała, J. Mucha, A. Cheikhrouhou, Structural, magnetic and transport study of monovalent Na-doped manganite Pr0.55Na0.05Sr0.4MnO3. J. Alloys Compd. 558, 236–243 (2013). https://doi.org/10.1016/j.jallcom.2013.01.008
H. Ben Khlifa, R. M’Nassri, W. Cheikhrouhou-Koubaa, E.K. Hlil, A. Cheikhrouhou, Effects of synthesis route on the structural, magnetic and magnetocaloric properties of Pr0.8K0.2MnO3. Ceram. Int. 43, 1853–1861 (2017). https://doi.org/10.1016/j.ceramint.2016.10.144
R. M’Nassri, W. Cheikhrouhou-Koubaa, M. Koubaa, N. Boudjada, A. Cheikhrouhou, Magnetic and magnetocaloric properties of Pr0.6−xEuxSr0.4MnO3 manganese oxides. Solid State Commun. 151, 1579–1582 (2011). https://doi.org/10.1016/j.ssc.2011.07.027
J. Fan, L. Pi, L. Zhang, W. Tong, L. Ling, B. Hong, Y. Shi, W. Zhang, D. Lu, Y. Zhang, Magnetic and magnetocaloric properties of perovskite manganite Pr0.55Sr0.45MnO3. Phys. B 406, 2289–2292 (2011). https://doi.org/10.1016/j.physb.2011.03.056
A. Jerbi, A. Krichene, N. Chniba-Boudjada, W. Boujelben, Magnetic and magnetocaloric study of manganite compounds Pr0.5A0.05Sr0.45MnO3 (A=Na and K) and composite. Phys. B 477, 75–82 (2015). https://doi.org/10.1016/j.physb.2015.08.022
R. M’Nassri, A. Selmi, N.C. Boudjada, a. Cheikhrouhou, Field dependence of magnetocaloric properties of 20% Cr-doped Pr0.7Ca0.3MnO3 perovskite. J. Therm. Anal. Calorim. 129, 53–64 (2017). https://doi.org/10.1007/s10973-017-6110-1
M. Shi, P. Bisht, A. Kumar, R.N. Mahato, Magnetic and magnetocaloric properties of the nanocrystalline Pr0.7Ba0.2Ca0.1MnO3 sample. AIP Adv. 11, 015239 (2021). https://doi.org/10.1063/9.0000088
A. Varvescu, I.G. Deac, Critical magnetic behavior and large magnetocaloric effect in Pr0.67Ba0.33MnO3 perovskite manganite. Phys. B 470–471, 96–101 (2015). https://doi.org/10.1016/j.physb.2015.04.037
R. Jemai, R. M’Nassri, A. Selmi, H. Rahmouni, K. Khirouni, N. ChnibaBoudjada, A. Cheikhrouhou, Composition dependence of physical properties in Pr0.7Ca0.3Mn1−xNixO3. J. Alloys Compd. 693, 631–641 (2017)
Funding
Open access funding provided by the Scientific and Technological Research Council of Türkiye (TÜBİTAK). This work was supported by the Research Fund of Çukurova University, Adana, Turkey, under grant contract no. FBA-2020-13314.
Author information
Authors and Affiliations
Contributions
All authors contributed to conceptualization; SKÇ and GA contributed to experimental design; SKÇ carried out measurements; GA and SKÇ contributed to manuscript composition and material preparation; GA and SKÇ contributed to writing-review and editing; GA, SKÇ, and AE contributed to supervision. All authors have read and agreed to the published version of the manuscript.
Corresponding author
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Ethical approval
Not Applicable.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Akça, G., Kılıç Çetin, S. & Ekicibil, A. Study of magnetocaloric properties of small Bi-doped Pr0.55Ca0.05Ba0.40Mn1−xBixO3 manganites. J Mater Sci: Mater Electron 35, 1442 (2024). https://doi.org/10.1007/s10854-024-13214-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s10854-024-13214-y