Abstract
A novel flame retardant, zinc hydroxystannate-decorated graphene oxide (ZHS/GO) nanohybrid, was successfully prepared and well characterized. Herein, the ZHS nanoparticles could not only enhance the flame retardancy of GO with the synergistic flame-retardant effect of ZHS but also prevent the restack of GO to improve the mechanical properties of poly (vinyl chloride) (PVC) matrix. The structure characterization showed ZHS nanoparticles were bonded onto the surface of GO nanosheets and the ZHS nanoparticles were well distributed on the surface of GO. Subsequently, resulting ZHS/GO was introduced into flexible PVC and fire hazards and mechanical properties of PVC nanocomposites were investigated. Compared to neat PVC, thermogravimetric analysis exhibited that the addition of ZHS/GO into PVC matrix led to an improvement of the charring amount and thermal stability of char residue. Moreover, the incorporation of 5 wt.% ZHS/GO imparted excellent flame retardancy to flexible PVC, as shown by increased limiting oxygen index, reduced peak heat release rate, and total heat release tested by an oxygen index meter and a cone calorimeter, respectively. In addition, the addition of ZHS/GO nanohybrids decreased the smoke products and increased the tensile strength of PVC. Above-excellent flame-retardant properties are generally attributed to the synergistic effect of GO and ZHS, containing good dispersion of ZHS/GO in PVC matrix, the physical barrier of GO, and the catalytic char function of ZHS.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Background
Recently, graphene (GR) and graphene oxide (GO) are widely used in fabricating advanced composites to provide elevated mechanical performance, excellent electrical properties, etc, due to their outstanding physiochemical properties [1–6]. Among them, many studies also demonstrate that GR and GO are promising flame retardants, which can act as barriers reducing the heat released, insulating against the transfer of combustion gases, and increasing residual char [7–9]. However, for GR and GO, achieving an excellent flame retardancy usually needs a little high loading [10]. Moreover, bare GR and GO possess a propensity to aggregate because of strong van der Waals attractions and π-π attraction between the nanosheets, resulting in decreasing their flame retardancy and deteriorating mechanical properties of polymer matrix. Therefore, the use of GR or GO alone as the flame retardant still remains a challenge.
As is well known, a combination of two or more components can sometimes present a synergistic effect and may impart an excellent flame retardancy to polymers [11]. Particularly, synergistic effects have been extensively found in the family of graphene-based composites in recent years. For instance, the addition of Ce-MnO2-GR hybrid sheets can impart excellent flame-retardant properties to an epoxy matrix duo to the synergistic effect [10]. A synergistic effect has also been observed between ZnS and GR in epoxy resin [12]. In addition, the synergistic effects of Ni-Fe-layered double hydroxide/GR hybrids appear in epoxy resin [13]. Surface modification of GR with layered molybdenum disulfide depicts a synergistic reinforcement on reducing fire hazards of epoxy resins [14]. More importantly, the abovementioned modifiers, Ce-MnO2, ZnS, Ni-Fe-layered double hydroxide, and MoS2, could also inhibit the aggregation of GR and improve the dispersion of GR in polymer matrix, resulting in improved mechanical properties of polymer matrix.
In recent years, zinc hydroxystannate (ZHS) has attracted growing attention owing to significantly improving flame retardancy of poly (vinyl chloride) (PVC). Compared with other inorganic flame retardants, ZHS have outstanding properties, such as low addition, low toxicity, and high efficiency, and will become a useful replacement of the conventional inorganic fillers [15–17]. Unfortunately, ZHS as flame retardant is less competitive in terms of cost and has a poor compatibility like other inorganic fillers in PVC bringing about the deterioration of mechanical properties, which is undesirable for the fabrication of high-performance materials. To overcome this drawback, our previous studies have made efforts to synthesize a composite flame retardant with core-shell structure: nano-ZHS coated by a macromolecule flame retardant, and the nanocomposite flame retardant not only significantly improves flame-retardant and smoke suppression properties of PVC but also does no damage to mechanical properties of PVC [18]. However, this coating technique is relatively complicated. Therefore, a succinct and effective method should be found to improve flame retardancy of ZHS to reduce the usage of ZHS.
Bearing those perspectives in mind, we use ZHS nanoparticles to modify the GO nanosheets to form ZHS/GO nanohybrids utilizing an electrostatic interaction. Herein, ZHS is expected to prevent the aggregation of GO, and GO could also prohibit the aggregation of ZHS, resulting in improving the compatibility between ZHS/GO and PVC matrix. Furthermore, the novel flame retardant, ZHS/GO, was achieved with excellent flame retardancy, using the synergistic effect between ZHS and GO.
Methods
Preparation of GO nanosheets
GO nanosheets were prepared from purified natural graphite through the method reported by Hummers and Offeman [19].
Preparation of ZHS/GO nanohybrids
In a typical procedure, 0.27 g of zinc sulfate heptahydrate and 10.29 mg of as-prepared GO were added to 100 ml of distilled water, followed by sonication for half an hour. Subsequently, 0.28 g of sodium stannate tetrahydrate was dissolved in 20 ml distilled water and added into the above solution, and then the reaction system was maintained at 5 °C for 5 h. Thereafter, 0.27 g of zinc sulfate heptahydrate was added into the above reactant and kept stirring for another 1 h. The final precipitate was collected by filtration and washed several times with distilled water to remove the remaining impurities. In the next step, as-prepared products were dried in an air atmosphere at 80 °C for 12 h. For comparison, bare ZHS nanoparticles were also prepared using the same route without the addition of GO.
Preparation of ZHS/GO/PVC composite
Preparation of PVC nanocomposite containing 5 wt.% ZHS/GO has similar processing condition with the procedure of DOPO-VTS-ZHS/PVC reported in our literature [20], while DOPO-VTS-ZHS was instead by ZHS/GO in this study. Meantime, for comparison, pristine PVC and PVC nanocomposites with 5 wt.% contents ZHS or GO were also prepared under the same processing conditions.
Apparatus and experimental method
The morphology and microstructure of as-prepared samples were documented by an X’ Pert Pro MPD X-ray powder diffractometer (XRD), a JEM-2010 transmission electron microscopy (TEM), and an AVATAR360 Fourier transform infrared (FTIR) spectrometer, respectively. Dispersion state of additives in PVC matrix was observed on a scanning electron microscope (SEM) (Nova Nano SEM 450 instrument with an acceleration voltage of 5 kV). Thermogravity analysis (TGA) were conducted on a DSC6200 thermal analyzer at the scanning rate of 10 °C/min. Flame retardancy were carried out by a JF-3 oxygen index meter and a FTT Cone calorimeter, respectively. The tensile strength of the nanocomposites was measured according to the Chinese standard method (GB T1040-92) with a WDW-10D electronic universal testing instrument at the cross head speed of 20 mm/min at 23 °C. Dynamic mechanical analysis (DMA) was performed using a DMA 861e instrument (Metter Toledo Instruments Inc., Swiss Confederation) at a fixed frequency of 10 Hz and a temperature range from 30 to 150 °C at a linear heating rate of 5 °C/min.
Results and discussion
Structure characterization of ZHS/GO
In Fig. 1, the XRD patterns of ZHS/GO exhibit prominent peaks, which can be indexed as the hexagonal structure phase of ZHS. However, no signal for any other phases of GO could be detected in the ZHS/GO nanohybrids. It may be because the regular layer stacking of GO is destroyed due to the crystal growth of ZHS between the interlayers of GO, leading to the disappearance of the diffraction peaks for GO. Therefore, XRD results suggest that the ZHS nanoparticles might have become attached to these GO nanosheets.
Because the regular layer stacking of GO is destroyed, there is no any XRD signal of GO in resultant ZHS/GO. Therefore, Raman scattering was used to document the existence of GO. Figure 2 shows Raman spectra of ZHS nanoparticles and ZHS/GO nanocomposites. As shown in Fig. 2, the Raman spectra of both GO and ZHS/GO exhibit two typical peaks of GO at about 1593 cm−1 (G band) and 1357 cm−1 (D band), which indicates the existence of GO in the ZHS/GO nanocomposites. Combined with the XRD results of ZHS/GO nanocomposites, this further proves that ZHS nanoparticles may be bonded onto the surface of GO.
The morphology and microstructure of ZHS/GO nanohybirds are shown in Fig. 3. As can be observed from Fig. 3a, GO nanosheets are highly transparent with folding at the edges, suggesting a very small thickness. Because of their high specific area, GO nanosheets aggregated and formed a stacked graphitic structure when their dispersion solvent was completely evaporated. It is clearly shown in Fig. 3b that the diameter of pristine ZHS nanoparticles is in the range of 40–50 nm. The TEM image of ZHS/GO nanocomposites (Fig. 3c) clearly illustrates that ZHS nanoparticles are distributed on the surface of GO nanosheets. The distribution of ZHS nanoparticles on GO nanosheets is uniform and has no obvious aggregation or free nanoparticles are detected. Furthermore, the TEM picture shows that the diameter of the ZHS nanoparticles is in the range of 50–60 nm, this may be because GO nanosheets facilitate the nucleation of ZHS to lead to a bigger diameter.
Figure 4 shows FTIR spectra of GO nanosheets and ZHS/GO nanohybrids. As to GO nanosheets, a strong and broad absorption at 3400 cm−1 is attributed to O–H stretching vibration. The absorption peak of GO nanosheets at 1620 cm−1 due to the C=C stretching vibration, the one at 1410 cm−1, is attributed to the tertiary C-OH group, and those at 1261 and 1067 cm−1 are assigned to the C–O stretching vibration of –COOH and C–OH groups situated at edges of GO nanosheets [21]. Similarly, after the electrostatic assembly of GO and ZHS, the above stretching of groups situated at GO sheets also appears in ZHS/GO FTIR spectra. However, all the absorption peaks of oxygen-containing functional groups are weaker than those in GO nanosheets. Besides, ZHS/GO shows two peaks at about 780 and 546 cm−1, which are assigned to the characteristic stretching vibration of SnO and ZnO stretching, respectively [22]. Moreover, the characteristic peak of C–OH group at 1067 cm−1 in ZHS/GO nanohybrids disappears; it is because that the strong absorption intensities of (Sn)O–H at 1177 cm−1 covers the C–OH stretching vibration. In conclusion, the weaker peaks of oxygen-containing functional groups, the new peaks of SnO and ZnO stretching, and the disappeared characteristic peak indicate that ZHS nanoparticles are successfully loaded on the large surface of GO during the electrostatic assembly process thereby affording ZHS/GO nanohybrids.
TGA curves of GO nanosheets, ZHS nanoparticles, and ZHS/GO nanohybrids are shown in Fig. 5. For ZHS, the mass loss is the lowest, 21 %, which is mainly due to the dehydroxylation of ZnSn(OH)6 generating ZnSnO3. For GO, in agreement with previous reports in the literature, the main mass loss (32 %) takes place around the 100–300 °C range, corresponding to the decomposition of labile oxygen functional groups present in the material [23]. There is also a mass loss (6 %) below 100 °C, which can be attributed to the removal of adsorbed water and a slower, steady mass loss (56 %) over the whole temperature range between 400 and 600 °C, which can be assigned to the removal of more stable oxygen functionalities. As for ZHS/GO nanohybrids, after ZHS nanoparticles are bonded onto GO, the total weight loss is 22 %, between ZHS and GO, which should be closely related to the dehydroxylation of ZHS and oxidation of GO. It may be the tin compounds can react with the GO in higher temperature making the GO to become stable. All indicated that ZHS nanoparticles are bonded onto the surface of GO.
The possible formation mechanism of ZHS/GO is proposed according to the above TEM, XRD, FTIR, and TGA analyses. Figure 6 schematically illustrates the formation mode of ZHS/GO nanohybrids. It is well known that there are considerable oxygen-containing functional groups on the surface of GO nanosheets. At the same time, the GO nanosheets in the pH range of 4 to 11.5 can lead to deprotonation of the oxygen-containing acidic groups, which establishes a negative surface charge density [24]. The large number of the negative charge which contains carboxylate (COO−) anion and phenolate anion (–C–O–) [25] etc. on the surface of GO nanosheets could capture and bond with Zn2+ in zinc sulfate solution through electrostatic attraction. Subsequently, the sodium stannate solution was added, the growth of zinc hydroxystannate by way of chemical reaction between Zn2+ cation and SnO3 2− anion. Finally, ZHS nanocrystals further assembled and became ZHS/GO nanostructures driven by the minimization of surface energy.
Morphology of PVC and its nanocomposites
SEM is a widely used technique to evaluate the dispersion level of fillers in a polymeric matrix. Figure 7 shows the images of the fractured surfaces for pure PVC and its nanocomposites. The fracture roughness of the polymer materials may demonstrate the dispersion state and interfacial interaction to some degree [26]. For pure PVC, it presents a uniform surface morphology revealing a rather smooth surface (Fig. 7a). Meanwhile, the GO nanosheets agglomerated obviously in the PVC matrix because of the re-stack of them (Fig. 7c). When ZHS nanoparticles are incorporated into PVC, the dispersion of ZHS seems to be uniform; however, some aggregates are still observed (Fig. 7b). Compared to pristine ZHS particles, the dispersion of ZHS/GO nanohybrids were improved (Fig. 7d). Herein, the fracture surfaces of ZHS/GO/PVC are much rougher than those of ZHS/PVC and GO/PVC, indicating the better dispersion and stronger interfacial interaction of ZHS/GO/PVC. The well-dispersed nanoparticles are generally due to the oxygen-containing groups acting as anchoring sites for ZHS on the surface of GO. The results demonstrate better dispersion of ZHS/GO in the PVC matrix than ZHS or GO alone in the PVC matrix, and the dispersion of the nanofillers is crucial for the performance of the nanocomposites.
Thermal degradation of PVC and its nanocomposites
Figure 8 shows the TGA curves of PVC and corresponding nanocomposites containing 5 wt.% each flame retardant. And some important data are summarized in Table 1. As shown in Fig. 8a, the thermal decomposition of flexible PVC composites is simply divided into two stages. The first stage in the temperature range of 150–380 °C is attributed to the dehydrochlorination of the polymer chain and plasticizer degradation. And the second stage beyond 430 °C mainly contains cyclization of conjugated polyene sequences to form aromatic compounds and oxidation of the unstable char. However, compared with neat PVC, the temperature at the maximum rate of weight loss at the first stage of decomposition (Td,max1) of ZHS/PVC nanocomposite was obviously lower than that of PVC, while on the contrary, the Td,max1 of GO/PVC was slightly higher than that of PVC. That is because ZHS can catalyze HCl released from PVC and promote the early crosslinking to the PVC compound, while the GO has not the catalytic action. However, for GO/PVC, the physical barrier effect of GO can inhibit the mass and heat loss of polymer; therefore, the Td,max1 of GO/PVC was slightly increased. For the ZHS/GO/PVC nanocomposite, it presents a little degradation behavior compared to the neat PVC. These results attributed to the combination of the cross-linking effect of ZHS nanoparticles and good mass barrier effects of GO. The temperature at the maximum rate of weight loss at the second stage of decomposition (Td,max2) of ZHS/PVC, GO/PVC, and ZHS/GO/PVC was obviously higher than that of PVC. These results revealed that the stability of the residue was enhanced. To the aspect of the formation of the char, the residues at 650 °C of ZHS/GO/PVC is significantly increased, owning to a catalyze carbonization effect of ZHS and the physical barrier function of GO. Furthermore, from DTG profiles (Fig. 8b), the maximum mass loss rate of ZHS/GO/PVC decreases significantly, suggesting that ZHS/GO nanocomposites function as a barrier to inhibit the mass loss during the thermal degradation process.
Fire hazard evaluated by LOI and cone calorimetry
The LOI values of all nanocomposites are presented in Table 1. The LOI value increases drastically from 24.5 to 27.2 % when the ZHS was added into PVC composites. The LOI value of GO/PVC nanocomposite exhibits an insignificant increase. However, this value is still higher than the neat PVC system, which increased 24.5 to 25.9 %. In contrast, the LOI value of ZHS/GO/PVC nanocomposites improves significantly, namely, from 24.5 to 28.5 % when ZHS/GO was added. The results indicate that ZHS/GO imparts a good flame retardancy on PVC at low filler loadings which are probably due to the shielding effect of GO and the catalyzing charring effect of ZHS (Fig. 9 and Table 2).
The flammability of polymer materials is commonly characterized by cone calorimeter, which is very effective to evaluate their flame-retardant properties under real-world fire conditions. Heat release rate (pHRR), total heat release (THR), smoke production rate (SPR), and total smoke release (TSR) curves for PVC and its composites are shown in Fig. 9, and some important parameters are listed in Table 2. As shown in Fig. 9a, incorporating 5 wt.% ZHS or GO into PVC generates pHRR decrease to 242.5 and 327.1 kW/m2, corresponding to a 35.7 and 13.2 % reduction compared to pure PVC, respectively. The pHRR and THR for ZHS/GO/PVC show a further decrease compared to the GO/PVC or ZHS/PVC, which are just 185.5 and 33.45 kW/m2 corresponding to a 50 and 59.7 % reduction to pure PVC, respectively. In addition, the samples having ZHS/GO nanohybrids show the lowest SPR, TSR, and AMLR compared to other nanocomposites, which conforms well to the TGA, pHRR, and THR results. The superior flame retardancy of ZHS/GO/PVC mainly includes three reasons: the barrier effect of GO, which retards the permeation of heat and the escape of volatile degradation products; the catalytic carbonization effect of ZHS to form more and better chars, which decrease the flammability of PVC; and the ZHS-contained Zn element should play an important role to eliminate volatile organic compounds and toxic gases during combustion reactions [27]. The proposed mechanism for the improved fire-resistant properties of the ZHS/GO/PVC nanocomposite is illustrated in Fig. 10. During the combustion process, the ZHS nanoparticles loaded on GO prevent the GO from re-stacking and result in the good dispersion. Meanwhile, GO can function as a physical barrier to absorb degradation products and extend contact time with ZHS catalyst. Degradation products continually collect on the GO, which serves as a template for the formation of char. Furthermore, the degradation products are catalytically converted into char by the combination of the physical barrier effect of GO and the catalytic effect of ZHS.
The mechanical properties of PVC and its nanocomposites
The values of tensile strength of PVC and its nanocomposites with different additives are presented in Table 1. Pure PVC shows a high tensile strength of 12.9 MPa. When ZHS and GO are added, the tensile strength at break of composite is increased to 13.4 and 13.2 MPa, respectively. In addition, the tensile strength at break of ZHS/GO/PVC nanocomposite increases from 12.9 to 14.3 MPa. The increase of the tensile strength could be interpreted on the basis of following factors: the strong interfacial adhesion and good dispersion of ZHS/GO in the PVC, resulting in effective load transfer from the polymer to GO [28]; the enhancement of crosslink density is due to the hydroxyl on the surface of nanoparticles [29]; and the viscous energy absorption and crack deflection [30]. Especially, ZHS nanoparticles could prevent the restack of GO and GO could also ensure ZHS nanoparticles remain well dispersed in PVC, thereby enhancing the tensile strength. In addition, the ternary structure could absorb much more energy than the binary nanocomposites [31, 32], namely, the effective synergistic strengthening in ZHS/GO/PVC achieves the high mechanical properties, superior to ZHS/PVC and GO/PVC nanocomposites (Fig. 11).
Dynamic mechanical analysis (DMA) test was performed to determine the reinforcement of ZHS/GO on the dynamic mechanical properties of the PVC nanocomposites. Figure 11 shows the storage modulus of neat PVC and its nanocomposites. It can be seen that the storage modulus of either ZHS/PVC or GO/PVC is increased compared to that of neat PVC within the entire temperature range, which is attributed to the reinforcement effect of additives. Similar with the tensile strength, the storage modulus of ZHS/GO/PVC nanocomposite further increased compared to ZHS/PVC and GO/PVC, which is also attributed to the synergistic reinforcement effect of ZHS/GO nanohybrids in polymer matrix.
Conclusions
ZHS/GO nanocomposites were successfully synthesized. The morphological characterization showed that the synthetic ZHS/GO nanocomposites exhibited some independent and separate ZHS nanoparticles are well distributed on the surface of GO. TGA revealed that the ZHS/GO nanocomposites could enhance the residue yield compared with pure GO. The incorporation of 5 wt.% ZHS/GO nanocomposites into PVC led to the improvement of Td,max2, char residue, DTG peak value, LOI, and mechanical properties compared to those of pure PVC. Furthermore, the pHRR and THR values for ZHS/GO/PVC were significantly reduced by 50 and 59.7 %, respectively, compared to those of pure PVC. Moreover, the amount of organic volatiles released during the combustion of PVC was significantly reduced after incorporating ZHS/GO. The improved flame retardancy was obtained through the synergistic effect between ZHS nanoparticles and GO nanosheets, resulting from the physical barrier effect acted by GO in combination with the effect of ZHS.
References
Eda G, Fanchini G, Chhowalla M (2008) Large-area ultrathin films of reduced graphene oxide as a transparent and flexible electronic material. Nat Nanotechnol 3:270
Liu CG, Yu ZN, Neff D, Zhamu A, Jang BZ (2010) Graphene-based supercapacitor with an ultrahigh energy density. Nano Lett 10:4863
Gong SS, Cui W, Zhang Q, Cao AY, Jiang L, Cheng QF (2015) Integrated ternary bioinspired nanocomposites via synergistic toughening of reduced graphene oxide and double-walled carbon nanotubes. ACS Nano 9:11568
Cheng QF, Duan JL, Zhang Q, Jiang L (2015) Learning from nature: constructing integrated graphene-based artificial nacre. ACS Nano 9:2231
Cheng QF, Jiang L, Tang ZY (2014) Bioinspired layered materials with superior mechanical performance. Acc Chem Res 47:1256
Wang JF, Cheng QF, Tang ZY (2012) Layered nanocomposites inspired by the structure and mechanical properties of nacre. Chem Soc Rev 41:1111
Huang GB, Gao JR, Wang X, Liang HD, Ge CH (2012) How can graphene reduce the flammability of polymer nanocomposites. Mater Lett 66:187
Han YQ, Wu Y, Shen MX, Huang XL, Zhu JJ, Zhang XG (2013) Preparation and properties of polystyrene nanocomposites with graphite oxide and graphene as flame retardants. J Mater Sci 48:4214
Ming P, Song ZF, Gong SS, Zhang YY, Duan JL, Zhang Q, Jiang L, Cheng QF (2015) Nacre-inspired integrated nanocomposites with fire retardant properties by graphene oxide and montmorillonite. J Mater Chem A 3:21194
Jiang SD, Bai ZM, Tang G, Song L, Stec AA, Hull TR, Zhan J, Hu Y (2014) Fabrication of Ce-doped MnO2 decorated graphene sheets for fire safety applications of epoxy composites: flame retardancy, smoke suppression and mechanism. J Mater Chem A 2:17341
Mochane MJ, Luyt AS (2015) Synergistic effect of expanded graphite, diammonium phosphate and Cloisite 15A on flame retardant properties of EVA and EVA/was phase-change blends. J Mater Sci 50:3485
Jiang SD, Bai ZM, Tang G, Hu Y, Song L (2014) Synthesis of ZnS decorated graphene sheets for reducing fire hazards of epoxy composites. Ind Eng Chem Res 53:6708
Wang X, Zhou S, Xing WH, Yu B, Feng XM, Song L, Hu Y (2013) Self-assembly of Ni-Fe layered double hydroxide/graphene hybrids for reducing fire hazard in epoxy composites. J Mater Chem A 1:4383
Wang D, Zhou KQ, Yang W, Xing WY, Hu Y, Gong XL (2013) Surface modification of graphene with layered molybdenum disulfide and their synergistic reinforcement on reducing fire hazards of epoxy resins. Ind Eng Chem Res 52:17882
Jiao YH, Wang X, Peng F, Xu JZ, Gao JG, Meng HJ (2014) Increased flame retardant, somoke suppressant and mechanical properties of semi-rigid polyvinyl chloride (PVC) treated with zinc hydroxystannate coated dendritic fibrillar calcium carbonate. J Macromol Sci B 53:541
Qu HQ, Wu WH, Zheng YJ, Xie JX, Xu JZ (2011) Synergistic effects of inorganic tin compounds and Sb2O3 on thermal properties and flame retardancy of flexible poly(vinyl chloride). Fire Saf J 46:462
Cusack PA, Hornsby PR (1999) Zinc stannate-coated fillers: novel flame retardants and smoke suppressants for polymeric materials. J Vinyl Addit Technol 5:21
Li ZW, Shao B, Huang YS, Li XH, Zhang ZJ (2014) Effect of core-shell zinc hydroxystannate nanoparticle-organic macromolecule composite flame retardant prepared by masterbatch method on flame-retardnat behavior and mechanical properties of flexible poly(vinyl chloride). Polym Eng Sci 10:1983
Hummers WS, Offeman RE (1958) Preparation of graphitic oxide. J Am Chem Soc 80:1339
Gao TT, Li ZW, Yu LG, Zhang ZJ (2015) Preparation of zince hydroxystannate nanocomposites coated by organnophosphorus and investigation of their effect on mechanical properties and flame retardancy of poly (vinyl chloride). RSC Adv 5:99291
Jeong HK, Lee YP, Lahaye RJWE, Park MH, An KH, Kim IJ, Yang CW, Park CY, Ruoffand RS, Lee YH (2008) Evidence of graphitic AB stacking order of graphite oxides. J Am Chem Soc 130:1362
Hornsby PR, Cusack PA, Cross M, To′th A, Zelei B, Marosi G (2003) Zinc hydroxystannate-coated metal hydroxide fire retardants: fire performance and substrate-coating interactions. J Mater Sci 38:2893
Zhao YC, Song XY, Song QS, Yin Z (2012) A facile route to the synthesis copper oxide/reduced graphene oxide nanocomposites and electrochemical detection of catechol organic pollutant. Cryst Eng Comm 14:6710
Whitby RLD (2014) Chemical control of graphene architecture: tailoring shape and properties. ACS Nano 8:9733
Konkena B, Vasudevan S (2012) Understanding aqueous dispersibility of grapheme of graphene oxide and reduced grapheme oxide through pKa measurements. J Phys Chem Lett 3:867
Alamri H, Low IM (2012) Effect of water absorption on the mechanical properties of nano-filler reinforced epoxy nanocomposites. Mater Des 42:214
Sanz O, Delgado JJ, Navarro P, Arzamendi G, Gandia LM, Montes M (2011) VOCs combustion catalyzed by platinum supported on manganese octahedral molecular sieves. Appl Catal B-Environ 110:231
Qian XD, Yu B, Bao CL, Song L, Wang BB, Xing WY, Hu Y, Yuen RKK (2013) Silicon nanoparticles decorated graphene composites: preparation and reinforcement on the fire safety and mechanical propertied of polyurea. J Mater Chem A 1:9827
Amigues P, Teichner SJ (1966) Mechanism of the catalytic oxidation of carbon monoxide on zinc oxide. Discuss Faraday Soc 41:362
Min KS, Lee B, Shi HK, Lee JA, Spinks GM, Gambhir S, Wallace GG, Kozlov ME, Baughman RH, Seon JK (2012) Synergistic toughening of composite fibres by self-alignment of reduced graphene oxide and carbon nanotubes. Nat Commun 3:650
Wang JF, Cheng QF, Lin L, Jiang L (2014) Synergistic toughening of bioinspired poly(vinyl alcohol)-clay-nanofibrillar cellulose artificial nacre. ACS Nano 8:2739
Wan SJ, Li YC, Peng JS, Hu H, Cheng QF, Jiang L (2015) Synergistic toughening of graphene oxide-molybdenum disulfide-thermoplastic polyurethane ternary artificial nacre. ACS Nano 9:708
Acknowledgments
This work is supported by National Basic Research Program of China, Grant No. 2015CB674703, Science and Technology Research Program of Henan Educational Committee, Grant No. 16A430001 and National Natural Science Foundation of China, Grant No. 21371050.
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors’ contributions
TG did the experiment, data collection, and draft writing; LC and ZW gave their contributions on the experimental design and guidance; LY gave his contributions on the paper modification; ZL and ZZ took part in the contributions on the research design, data analysis, and discussion, as well as the main paper organization. All authors read andapproved the final manuscript.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Gao, T., Chen, L., Li, Z. et al. Preparation of zinc hydroxystannate-decorated graphene oxide nanohybrids and their synergistic reinforcement on reducing fire hazards of flexible poly (vinyl chloride). Nanoscale Res Lett 11, 192 (2016). https://doi.org/10.1186/s11671-016-1403-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-016-1403-z