Abstract
The study presents the mechanical and durability properties of concrete made up of recycled-waste-polyethylene (PE) and waste-polyethylene-terephthalate (PET)-based aggregate as replacement of natural fine and coarse aggregate, respectively. For this purpose, compressive strength, sorptivity, water permeability, aggressive exposure in acid, base, marine and wastewater, impact resistance, abrasion loss including surface and Cantabro, gas permeability, rapid chloride penetration test (RCPT), elevated temperature and leachability test of microplastic were performed. The experimental works were performed for different volumetric replacement (0–40%) of natural fine and coarse aggregates by PE and PET made aggregate respectively for different curing periods. The experimental results revealed that the sorptivity of PE-based concrete was lowest. Water permeability coefficient signified that with the increase of percentage of PET water permeability increased. In case of aggressive exposure test, the percentage of residual mass and residual strength for all replacement was decreased with the increase in exposure period. Further, impact resistance test result signified that energy absorption increased with the increase of PE and PET percentages. Cantabro and surface abrasion weight loss showed similar trend. Carbonation depth was increased with increasing percentages of PE and PET signified strength decreased with increase of percentages of PE and PET when subjected in CO2. RCPT test results demonstrated that with increase of PE and PET percentages chloride ion penetrability was reducing. It is observed that below 100 °C temperature, compressive strength of all mix proportions was not affected with elevated temperature. Moreover, the PET-based concrete showed no presence of microplastic in case of leachability test.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
The generation of waste plastic has increased day by day worldwide (Gondal et al. 2022; Jadhav et al. 2022). According to UNEP, around 400 million tonnes of waste plastic are produced annually worldwide with a growth of 4.6% per year. As management methods, 9% of all globally generated waste plastic is recycled and 12% is burned (da Luz Garcia et al. 2021). Remaining 79% of waste plastic are either disposed in landfill or in aquatic systems. Indiscriminate disposal and open burning of plastic wastes result in serious environmental problems including emission of toxic and hazardous air pollutants like dioxins, furan and particulate matter, increase in microplastic and heavy metal concentrations in aquatic system through degradation processes and reduction in water permeability and soil fertility of agricultural fields. Voluminous generations of single used plastic have increased significantly worldwide in recent years as the safety equipment to fight against the COVID-19 pandemic. Though Indian Government restricted the use of single use plastic from July 2022 but India alone was reported to generate 5.58 million tons of single use plastic per year. About 20% of the total waste plastic is of polyethylene terephthalate (PET) type, and 29% is made up of items with polyethylene(PE) foundation (Nvironment 2011).
The significant increase in single-use plastic waste (PW) motivates researchers to find effective, safe, low-cost and sustainable methods to manage it in urgent basis (Zhang et al. 2023). The desired characteristics like low water adsorption capacity, corrosion resistance, low electrical and thermal conductivity and high impact resistance capacity of waste plastic suggest the material may be one of the potential eco-friendly and effective alternatives of natural coarse and fine aggregate in cement concrete production and includes PW in circular economy. Life cycle assessment (Zhang et al. 2023) of plastic waste also proves that recycling of PW can improve environment by reducing global warming (Tian et al. 2020) potential and human toxicity. Around 60–80% of concrete is made up of aggregate (Naderi and Kaboudan 2021). To achieve this requirement, aggregate usage worldwide is around 13.12 billion tonnes per year (Islam and Shahjalal 2021).
Extraction of natural aggregates from quarry is a highly environmentally negative activity led to subsequent energy use and related greenhouse gas (GHG) emissions, degradation of landscape and land stability, pollution of water resources, pollution of the atmosphere due to particulate matter, societal impacts due to vandalism, etc.
Recycling of waste plastic as replacement of natural aggregates can be a hopeful approach to reduce the number of environmental hazards, social issues and health risks associated with extraction of natural aggregates (Jain et al. 2022). In past, several research works were conducted on the determination of strength (Sim and Park 2011; Gu and Ozbakkaloglu 2016) of waste plastic aggregate-based concrete. However, very few studies are available on the durability properties (Zega and Di Maio 2011) of waste plastic aggregate-based concrete. Akçaözoğlu et al. (2010) reported that mortar specimens with 100% PET aggregates had more water absorption values than a mortar with PET and sand aggregate. Choi et al. (2009) found sorptivity coefficient of mortars by replacing the 25–75% finer portion of natural aggregates (NA) with lightweight aggregate (LWA), which was made by coating sand with PET at a temperature of 50 °C in an airtight mixer. It was evaluated that by adding 25% of the PET aggregate sorptivity increased up to 52%. Further, Ohemeng and Ekolu (2019) obtained 31% drop of sorptivity coefficient when 75% of natural fine aggregates (FAs) were replaced by low-density polyethylene (LDPE)(Frigione 2010). Majeed et al. (2019) explored that up to 12% CA can be replaced beneficially by high-density polyethylene (HDPE) in terms of water adsorption capacity. He further added that additional 6% of HDPE resulted 75% increase in water adsorption capacity. Silva et al. (2013) demonstrated that the permeability of the flaky particles is greater than that of the PET-pelleted particles in concrete. Saxena et al. (2018) suggested that for concrete containing coarse and fine PET particles, liquid permeability is more due to higher void content. Lee et al. (2019) found out that the water penetration rate decreases due to modification of microstructure pore system and bond qualities of PET. Jain et al. (2020) observed that there is a decrease of water penetration depth of concrete with fine aggregate (FA) partially replaced by LDPE granules made from plastic bag waste.
According to the investigation carried out both by Janfeshan Araghi et al. (2015) and by Nikbin et al. (2016), degradation rate of weight increases and load sustain decreases of concrete specimens with PET immersed for 60 days in 5% sulphuric acid solution. Saxena et al. (2018) and Jain et al. (2020) established that PET-based concrete performs better when it is exposed to low-velocity impact loads as it has enhanced energy absorption capacity. Jain et al. (2020) evaluated that the abrasion resistance in terms of the loss in thickness was decreased by 50% when 20% of FA was replaced using HDPE. Alqahtani et al. (2018) found out a reduction in abrasion values ranging from 29 to 58%, for the replacement levels of CA from 25 to 100% using LDPE by volume. Galvão et al. (2011) examined mass loss for concrete samples containing 0%, 2.5% and 5% PET aggregates under erosion and abrasion and reported that the concrete with 5% PET aggregates had greater resistance to abrasion than the control mix. Furthermore, according to Ferreira et al. (2012), abrasion resistance of concrete increased by using PET as FA and CA in concrete. Saikia and de Brito (2014) also opined that PET aggregates in concrete tend to enhance abrasion resistance, when replacement levels were increased by 10% flaky aggregates.
According to the research conducted by Sim and Park (2011) and Mercante et al. (2018), penetration gases, such as carbon dioxide or other suspended ions, may have an unfavourable impact on the durability of embedded steel reinforcement and composite materials. According to the research outcome of Akçaözoğlu et al. (2010), the mortars having both sand and PET had deeper carbonation levels than mortars carrying only 100% PET. Furthermore, Silva et al. (2013) found that the carbonation depth (Sim and Park 2011) increased in concrete containing 15% PET aggregates than control concrete due to the increase in porosity of the mix. According to the research performed by Gavela et al. (2013), no carbonation was observed in any specimens exposed up to 240 days, which were prepared by adding polypropylene (PP) and HDPE in concrete. Almeshal et al. (2020) reported chloride ion penetration (Sim and Park 2011) increased with increase of plastic waste aggregate in concrete. Further, Silva et al. (2013) determined that chloride penetration coefficient increased up to 57% by substitution of 15% fine aggregate (FA) with flaky PET particles in concrete. Alqahtani et al. (2018) suggested that the chloride permeability in concrete may be significantly reduced by using recycled synthetic aggregates in concrete. Islam et al. (2022) conducted elevated temperature test and found that at high temperatures, compressive strength decreased by 10.8% and 34% at 100 °C and 200 °C respectively. Saxena et al. (2018) reported that residual compressive strength of concrete subjected to temperatures at 300° and 600 °C were reduced when both FA and CA were replaced with 5–20% PET aggregates by volume. In another study, Correia et al. (2014) observed decrease in residual compressive strength when PET flakes and pellets were used in concrete and heated to 600° and 800 °C. Sojobi and Owamah (2014) found that the residual compressive strength of concrete heated to 500 °C was greater when up to 15% of FA (by weight) was replaced by LDPE. LDPE demonstrated greater performance than PET aggregates in concrete for durability study conducted by Galvão et al. (2011).
The different studies in the literature that have explored the use of waste plastic aggregate (WPA) as a replacement of natural fine aggregate (NFA) and natural coarse aggregate (NCA) in cement concrete have largely focused on its impact on mechanical properties. Past literature signifies that limited durability study was conducted for cement concrete by replacing NCA and NFA by WPA made from single use PET and PE respectively. Thus, to fill the gap in the literature related to using waste plastic aggregate as a replacement of NCA and NFA in concrete, this study was conducted to examine the effects of incorporating WPA on the mechanical property (compressive strength) and durability of concrete before recommending WPA as replacement of natural aggregates. The durability tests include sorptivity test, water permeability test, aggressive exposure test of acid, base, marine and municipal waste water, impact resistance test, abrasion loss test including surface and Cantabro, gas permeability test, rapid chloride penetration test (RCPT), elevated temperature test and leachability of microplastic test. To evaluate the microstructural change due to addition of plastic waste-based aggregates, optical microscope tests were also performed for all concrete mixtures at 28 days of curing period. This research will fill an important gap between practice and the literature related to durability of WPA-based concrete.
Materials and methods
Material
In the present study to prepare concrete mix, locally available Portland pozzolanic cement of 43-grade comply to IS-part-I (1489)(Table 1) was used. Clean river sand having dry compacted bulk density of 1600 kg/m3 and fineness modulus of 2.84 with specific gravity 2.66 was employed as fine aggregate (Table 2). As coarse aggregate, naturally obtained crushed stone having specific gravity of 2.76, maximum particle size of 20 mm and dry compacted bulk density of 1650 kg/m3 was used (Table 2). The sieve analysis revealed that the coarse aggregate and the fine aggregate were in grading zone II according to IS 383 (1970) (Fig. 1b). To enhance the workability of concrete while utilizing lower water-cement ratios, a super plasticizer (CONPLAST SP 430 DIS admixture) confirming (ASTM C494-19 2019) was applied. Natural fine aggregate (NFA) and natural coarse aggregate (NCA) were replaced by PE- and PET-made aggregate, respectively. Cutting PET bottles into small bits that can pass through a 20-mm screen and be retained in a 10-mm sieve were allowed for the creation of coarse aggregates. Despite being flaky, they were employed as a partial replacement of natural coarse aggregate because of their hardness. On the other hand, melting PE and cutting it into beads were used to create fine aggregates with a diameter of 1 to 5 mm. Table 3 illustrates the characteristics of PET- and PE-based aggregates used in the present study. Both types of aggregates were gathered from a nearby recycling facility. The flowchart of processing of the PET and PE aggregates utilized in the present research is presented in Fig. 1a. The aggregates were heated with natural sand to improve the binding strength between cementitious matrix and plastic aggregates and decrease the gap at the interfacial transition zone (ITZ). Figure 1b depicts the gradation of plastic aggregates used, which were obtained from sieve analyses.
Experimental methods
Mix design
Mix designs for concrete of the M30 grade were carried out in the current experiment following (IS 10262 (Revised) 2019). For 0% replacement level (Control mix) and constant water–cement (W/C) ratio 0.37, the quantities of water (IS-456:2000) cement, natural fine aggregate (NFA), natural coarse aggregate (NCA) and chemical additive (superplasticizer) for M30 grade concrete were determined as 165 kg, 410 kg, 690 kg, 1170 kg, and 4.08 kg per cubic meter of concrete, respectively. The quantity of chemical additive was determined based on the workability of the fresh concrete mixture from trial–error process to ensure the good quality of the concrete mixture. In this investigation, to evaluate the effects of replacing NFA and NCA by PE- and PET-made aggregates on mechanical and durability properties of concrete, three trials each having four mixtures were prepared keeping W/C ratio constant (0.37) (Table 4). In the first trial, PE-made aggregate was employed to replace NFA at different volumetric replacement percentages, including 10%, 20%, 30%, and 40%, and denoted as PE10, PE20, PE30, and PE40, respectively (Table 4). Only naturally occurring coarse aggregates (NCAs) were swapped out with PET-made aggregates in the second trial and were denoted as PET10, PET20, PET30, and PET40, respectively (Table 4). In the third trial, both PET- and PE-made aggregates were used in place of the coarse and fine aggregates, respectively, that were naturally obtained and were denoted as WPA10, WPA20, WPA30, and WPA40, respectively (Table 4). All the mixtures were made triplicate, and average of the test results was reported. Table 4 contains the mix proportions for 4 replacement levels for all trials keeping W/C ratio same and same chemical admixture.
Casting and curing of sample specimen
All the constituents of concrete were measured with 0.005 g accuracy. At first, all the constituents of concrete were mixed thoroughly to achieve homogeneous mixture by hand on a waterproof frame. The mixture was then carefully added with tap water (IS-456:2000) and chemical additives to ensure that no water was wasted during mixing. The compaction of the sample was improved using a vibrating instrument. 100 mm × 100 mm × 100 mm cubes and cylinders with a diameter of 100 mm and heights of 200 mm, respectively, were cast to examine subsequent mechanical and durability qualities. After casting, the samples were initially cured under ambient conditions at 27 °C and 90% relative humidity for the first 24 h, after which they were demoulded and immersed in normal water in the curing tank until testing. Sample preparation and curing of test specimens are depicted in Fig. 2.
Testing procedures
As mechanical property of concrete, the compressive strength test was performed according to IS:516-1959 (1959) using compression testing machine. The cross-sectional views of concrete mix samples are presented in Fig. 2a, b. The durability properties of concrete were investigated using the sorptivity test, the water permeability test, exposure test in different adverse medium like acid, alkaline, marine and municipal wastewater, resistance to impact loads, resistance to abrasion, gas penetration test, chloride ion penetration test and elevated temperature effect test. Different information related to the size of the testing sample and details of curing periods are presented in Table 5 regarding the mechanical and durability study. The sorptivity test was carried out according to ASTM C1585 (2013) by measuring the Ca(OH)2 solution absorption rate due to capillary action with respect to the cross-sectional area of concrete specimen cured at various times exposed to the Ca(OH)2 solution up to 2 mm height from the base at various time as 3, 6, 9, 12, 15, 20, 30, 45, 60, 75, and 120 min (Fig. 3a–c). To maintain the lime solution depth 2 mm from the base of concrete during the test, the solution was continuously poured into the tray. In this experiment, the sorptivity coefficient (S) is calculated using Eq. (1).
where S (g/mm2/min1/2) is the sorptivity coefficient, t is the time in minutes, and I (g/mm2) is the total amount of Ca(OH)2 solution absorbed per unit cross-sectional area of the concrete specimen, which is known as capillary suction rate. The permeability of concrete specimens (100 mm × 100 mm × 100 mm) was determined after 28 days curing adopting the forced technique using 0.3 MPa (3 bar) of hydrostatic pressure for 72 h in a permeability apparatus according to the standard procedure (DIN 1048-5:1991-06 2015) as presented in Fig. 4a–f. After testing, the depth of penetration of water through the specimens was measured after dividing it in half using a compression device and the depth of penetrations are shown in Table 6. Using observed water depth and a modified version of Darcy's law, the coefficient of water permeability (kw) is calculated using Eq. (2) as follows:
where kw is the permeability coefficient (m/s), x is the penetration depth (m), t is the experiment period (s), and h is the water head (m). By integrating Eq. (2), one can easily deduce the permeability coefficient using Eq. (3).
Here xt represents the penetration depth at time t. Since the water flow is irregular and related to sorptivity, it makes more sense to use the average depth of water penetration when calculating kw rather than the maximum depth.
To study the effects of adverse environmental exposure test on concrete, three randomly selected concrete cubes were exposed to acid (5% H2SO4 (Fig. 5a–c) and 5% HNO3 (Fig. 6a–c) solution to maintain pH 0.3–0.5), alkaline water (5%NaOH solution) (Fig. 7a, b), marine water (Fig. 8a, b) and municipal wastewater (Fig. 9a, b) collected from sewer line for different curing periods as mentioned in Table 5. The acid resistance test was done as per ASTM C1898 (2020). The adverse effects of exposure by different solutions on concrete for different curing periods were expressed in terms of percentages of residual mass (RM) (Eq. 4) and residual strength (RS) (Eq. 5).
where B is the average mass of the three samples after a specific amount of time spent in an exposure solution, and A is the average mass of three samples before immersion in the exposure solution.
where C and D represent, respectively, the average compressive strength values of three samples before and after being stored in an exposure solution.
As a quasi-brittle substance, concrete has a very low tensile strength, a little amount of ductility, and a weak resistance to cracking when utilized as plain concrete. These characteristics severely restrict its use to high strain-rate loadings such as collisions, explosions and earthquakes. In the past, there has been a great deal of research on using polymers in the form of fibres to get around these restrictions (Islam and Shahjalal 2021). The impact resistance of plastic waste concrete was tested using drop weight test equipment, as shown in Fig. 10a–c, which consists of a typical manually operated at 3.5-kg compaction hammer allowed to drop from 0.73 m following the work mentioned in Thiyagarajan (2014). The specimen was positioned within the impact testing apparatus, completed face up, on a base plate. The hardened steel hammer was set on top of the specimen within the bracket after the bracket with the cylindrical sleeve had been fastened in place. The drop hammer was then raised vertically, its base resting above the steel hammer. The number of blows needed to generate the first apparent fracture at the specimen's top surface and the point of eventual failure were counted after the hammer was repeatedly dropped as depicted in Table 7 including ductility index. Visual inspection allowed for the detection of the first crack. The shattered specimen butting against the base plate legs made it easy to identify the stages of final collapse.
Abrasion resistance test is an important parameter to determine the resistance of concrete against the abrasion loads due to traffic. The abrasion resistance of concrete may be calculated by adopting Cantabro abrasion test as per C1747/C1747M (2013) and surface abrasion test as per ASTM C944/C944M (2012). The Los Angeles abrasion testing machine without steel ball (Fig. 11a–c) was used for Cantabro abrasion test, and the location of each set of three cylindrical specimens, each measuring 100 mm in diameter and 50 mm in height, inside the machine is depicted in Fig. 11b. Initial weight (W1) of each specimen were noted before insertion into the apparatus. Then, this machine was permitted to rotate at rotation rates of 50, 100, 150, 200, 250, and 300 per minute. The abraded specimens were cleared of any loose material and precisely weighed to determine W2 at each level of revolution. Finally, Eq. (6) is used to compute the percentage weight loss:
where W1 denotes the test specimen’s initial weight in grams and W2 denotes its final weight in grams. All the experiments were performed for the concrete mix of 28-day curing time for a cylindrical shape (100 ɸ mm × 50 mm thickness).
The surface abrasion test was run for a total of 6 min for each type of concrete mix at 50 revolutions per minute for 300 revolutions using cube specimen of dimension 100 mm × 100 mm as per ASTM C944/C944M (2012) cured for 28 days using drill press with a rotating cutter (IS 1237:2012). Each of the concrete specimens was placed in the drill press and the rotating cutter was mounted slowly until the surface of the specimen was touched (Fig. 12a–c). Then the device was set to rotate for 2 min at a speed of 200 rpm with a vertical load of 98 N. After rotation the specimen was removed from the device and its surface was cleaned and weighed. The data were taken for each 1 min interval. Equation (7) is used to determine the weight loss due to surface abrasion:
where W1 denotes the test specimen's initial weight in grams and W2 denotes its final weight in grams.
The rapid chloride ion penetration test was done as per ASTM C1202-12 (2012). After 28 days of curing, all concrete samples (100 mm × 100 mm) were removed from the curing tank and divided into slices of 50 mm thickness using an iron cutter. The slices were then vacuum-saturated for three hours as seen in Fig. 13a and reaerated. One face of the slice was exposed in anolyte solution (0.3N NaOH) and other face in catholyte NaCl (3%) solution while connected to the power supply. Both faces of the concrete samples were exposed in solutions for 18 and a half hours before supplying power supply (Fig. 13b, c). The voltage of power supply was set 60 V. The test was lasted for six hours, with 30-min intervals for measuring the current passed through the sample specimen during that time. According to the average value of three samples, the total charge passage was recorded in terms of coulombs, which indirectly measured the Cl− passed through the sample.
The gas permeability test was performed following the protocol described by Kumar et al. (2019). A cylindrical metallic curing chamber with dimensions of 460 mm in height, 530 mm in diameter, and 2 kg/cm2 retaining pressure at the outflow and intake was made for gas permeability test (Fig. 14a, b). The specimens were evaluated for compressive strength after being cured for 28 days in a CO2 curing chamber under 20 psi of pressure. The depth of carbonation on the breakable face for each sample was determined using a phenolphthalein indicator solution (Fig. 14c). Carbonation depth was measured by digital calliper (Fig. 14c).
The elevated temperature test was performed following the protocol as suggested by Islam et al. (2022). The prepared concrete cubes after 28-day curing were heated uniformly for around 60 min at 100 °C, 200 °C and 300 °C in an enclosed muffle furnace chamber and then left in a dry environment to cool to room temperature to perform this test (Fig. 15a–c). The change in concrete's compressive strength for various combinations of mix proportions at various high temperatures was measured.
Leachability test
To assess the microplastic in concrete, the toxicity characteristic leaching procedure (TCLP) technique was modified. Concrete cube specimens of 100 mm in dimension were cast using varied amounts of plastic waste aggregate, and after air-drying for 1 day, the specimens were fully submerged in water for 28 days. The specimens were removed from the water and ground into powder after the necessary curing. For the test, crushed cube sample powder that passed through a 10-mm sieve was utilized.
In 96.5 mL of distilled water, 5 g of the crushed sample was added and agitated (Fig. 16a) for 5 min before the pH was determined for the extraction sample. All extraction samples were found to have pH values higher than 5. Then, a 3.5 mL of 1 N HCl was added with the extracted sample, mixed, heated to 50 °C for 10 min to determine PH. The PH was then measured once the solution had cooled to room temperature and found to have pH values lower than 5 (Fig. 16b). As seen in Fig. 16d, each of the flasks is then shaken by the shaker for 18 h at a temperature of around 25 °C and 60 rpm for different replacement along with both 100 g of crushed sample and 64.3 mL of 1 N NaOH solution and 5.7 mL of glacial acetic acid (98% pure) (Fig. 16c). After 18 h, the leachate was passed through the sieve (4.75 mm), and the fluid passed through the sieve (4.75 mm) was put into oven for 72 h at 70 °C for drying before being examined under a digital microscope (Fig. 16e–i) to detect the presence of microplastics following the NOAA Marine Debris Program (2015) guidelines.
Results and discussion
Mechanical property
Compressive strength test
The compressive strengths of different concrete mixes for curing ages 7, 28, and 56 days are depicted in Fig. 17. With increase of PE content in concrete in place of NFA, the compressive strength decreased. It was observed that the compressive strength reduced by 3%, 8%, 12.21%, and 22.5%, respectively, for PE 10–40 as compared to the control mix. For the same proportional mixture, the strength increased from 7 to 56 days curing period. For replacement of NCA by PET, the compressive strength reductions were even more compared to control mixture for same curing ages. The compressive strengths improved for curing age 28 days as compared to the 7 day curing age for PET10-40. For WPA 10–40, the compressive strength reduction was in between PE concrete and PET concrete for 7-day curing period with compared to the control mix. The compressive strengths improved for 56-day curing period. The compressive strength was maximum for 56-day curing period for PE 10. Though compressive strengths reduced with incorporation of PE aggregates in place of natural fine aggregates but the concrete mixture can be utilized up to 30% replacement level as M30 grade concrete, while for PET concrete and WPA concrete the permissible replacement level was obtained up to 20% for curing period of 28 days. However, all the concrete mixtures (PE10-40; PET10-40 and WPA10-40) can be utilized for structural purpose for 28-day curing period.
The decrease in compressive strength as noted may be the result of weak interfacial transition zones (ITZ) between the plastic aggregates and cement paste. In addition, the hydrophobic properties of the plastic waste aggregate in concrete prevent cement near the ITZ from hydrating, leading to a poorer bond between the cement paste and aggregates. Similar results were also reported by others researchers (Jassim 2017; Saxena et al. 2018; Needhidasan et al. 2020; Tayeh et al. 2021; Shiuly et al. 2022; Sau et al. 2023).
Durability properties
Sorptivity test
Durability properties of concrete are mostly evaluated by its porosity and water absorption capacities. Higher sorptivity coefficient and water adsorption capacity of concrete can reduce service life of concrete by allowing penetration of contaminated water containing different chemicals. On the other hand, for the concrete pavement porous structure is advantageous to increase rain water penetration to soil. Plotting the best-fitted straight line between total amount of Ca(OH)2 solution absorbed per cross-sectional area (I) against the square root of time t1/2 yielded the sorptivity coefficient (S) from the slope as shown in Fig. 18a–c and Fig. 19a–c. Sorptivity analysis was conducted for 7, 28, 56, and 90 days of curing time, and only the test results corresponding to 56 and 90 days were described for all mixtures (Fig. 18d). For 56-day test, capillary suction rate lied between 21.42–71.424% for PET10-PET40 mixtures, while for PE10-PE40, the rate varied from 4.5 to 23.64%. But for WPA10 to WPA40 concrete, enhanced capillary suction rate was observed in the range of 12–46% (Fig. 19d). For 90 days curing time, capillary suction rate lied between 8–25.80% for PET10-PET40, for PE10-PE40, capillary suction rates lied between 4.34–26.08% but for WPA10-WPA40 enhanced capillary suction rates were observed in the range of 0–51.06%. Similar results were depicted by Jayeshkumar Pitroda (2013), Suram et al. (2021). The bulk of investigations on the sorptivity of plastic waste-based concrete as a discrete material replacing natural aggregate appear to support the conclusion that, regardless of the type of plastic, the water capillary suction rate increases with an increase in plastic waste aggregates content in the mix. The reasons behind the increased sorptivity value compared to control may be the increased porosity in concrete due to plastic aggregate, evaporation of extra water that is present around hydrophobic plastic waste aggregate; weak ITZ near plastic particles due to a poor connection between plastic waste aggregate and the binder matrix; introduction of plastic species, which disturbs the mixture's homogeneity; and effects of particle size and shape of plastic waste-based aggregate on the rheology and compaction properties of the composites.
Water permeability test
Results of the water permeability test for all trials of plastic waste concrete mix are shown in Table 6 and Fig. 20. Results show that water permeability coefficient was minimum for control concrete (1.76 cm) followed by PE10-PE40 and PET10-PET40 (Fig. 20). Similar findings were made by other researchers (Coppola et al. 2018; Saxena et al. 2018; Jain et al. 2020). When both natural aggregates were replaced by plastic aggregates, i.e., for WPA10-WPA40, water permeability coefficient increased but compared to PET and PE mixes it decreased. In other way, we can write in terms of water permeability coefficient for different concrete mix Control mix < WPA concrete < PE concrete < PET concrete (Table 6). The fundamental explanation for the rise in permeability coefficient may be the increased porosity brought on by the development of fragile spots as a result of the tenuous bond between plastic waste aggregate and cement matrix in concrete and in homogeneous microstructure. The permeability of concrete can be decreased by decreasing pore density and discontinuous pore system between the cement paste and plastic waste aggregate.
Exposure test in different adverse solutions
Figure 21a, c, e presents the residual mass of different concrete specimens exposed to sulphuric acid solution for 28, 56 and 90 days. The results demonstrated that incorporation of plastic waste as aggregates increased residual mass as compared to the control mix for different curing times. The residual mass was maximum for 40% replacement of natural aggregates by PE and PET aggregates as observed. For WPA10 mix, no mass was observed to be reduced even after exposure to H2SO4 solution for 28 days. However, for WPA40 mix it was observed that the residual mass was maximum for 56-day curing time in H2SO4 acid. Control mix showed greater mass loss due to the availability of free calcium hydroxide (Ca(OH)2). The results as depicted in Fig. 21b, d, f demonstrated the strength loss for different concrete mixes for three different curing periods in H2SO4 acid solution. When a sample is immersed in H2SO4 acid solution, the strength loss was initially higher for all replacements at 7, 28 days compared to the control mix, but for 56 days of curing time, the strength loss was reduced for all replacements compared to the control mix. Sulphuric acid reacting with free Ca(OH)2 produces calcium carbonate in powder form and gypsum and eventually leading to the formation of ettringite. Ettringite causes concrete to expand, which results in internal pressure, and therefore, it deteriorates. Figure 22a, c, e presents residual mass of all samples for all trials exposed to nitric acid solution for 28, 56, and 90 days. The residual mass was maximum for 40% replacement of natural aggregates by PE and PET aggregates exposed to HNO3 solution for 7 and 56 days and WPA with 10% replacement has maximum residual mass. Figure 22b, d, f presents residual strength of all samples for all trials exposed to HNO3 solution. The residual strength was maximum at 56 days when exposed in HNO3 solution for PE-based concrete as compare to control. The residual strength was maximum at 20% replacement by PET aggregates in concrete. Similar outcomes for RM(%) and RS(%) were shown in different studies (Pather et al. 2021).
The results of exposure test in 5% NaOH solution are depicted in Fig. 23. All concrete specimens exhibit fairly similar residual strength values at 28 days when compared to the control mix meaning alkaline solution has no adverse effect on plastic waste-based concrete.
After 56 days of curing in marine water, the strength of the cubes is shown in Fig. 24. It was observed that residual strengths were maximum for concrete specimens having plastic aggregates as replacement of natural aggregates for different replacement levels as compared to the control mix. The residual strength was maximum for PE10 followed by PET10 and WPA 10 for 7-day curing time. Similar results were pointed out by several previous studies such as Bryant Mather (1964), Tijani et al. (2013). For marine water exposure test, it was observed that the degree of interaction between Ca(OH)2 and sulphate is often limited by the reduction in the amount of free Ca(OH)2 caused by the pozzolanic reaction (Massazza 1993). Additionally, it was claimed that chlorides, as found in marine water, prevent concrete from swelling and expanding as a result of sulphate attack. The increased solubility of hydrated CaSO4 in chloride solution may also inhibit swelling in damaged concrete.
The residual strengths of different concrete mixes cured in municipal wastewater are depicted in Fig. 25. It is observed from Fig. 25 that residual strength decreased for all concrete mixes for 56-day curing time. However, compared to the control mix, PE10, PET10 and WPA10 showed more residual strength for 56-day curing time.
Impact resistance test
The specimen's energy consumption until failure was taken into account as a gauge of its impact resistance. Equation (8) is used to calculate the energy consumption:
where the height is equal to the total failure heights.
Weight = Mass (kg) × g (m/sec2), where “g” stands for the gravitational acceleration.
Figure 10c displays the failure patterns of each group of specimens. Energy consumed by the specimen for first and last cracks is shown in Fig. 26.
According to the test results, the PE10-PE40 concrete specimens consumed 83.33% more energy than control mix for the detection of the first crack. Around 122.22% more energy was absorbed by PET10-PET40 concrete as compared to control mix, as indicated in Fig. 26. Around 155.55% more energy was absorbed for WPA40 mix as compared to control mix. In these three trials, the third experiment has the highest energy consumption and the highest ductility index, which agrees with past literature (Saxena et al. 2018; Al-Tayeb et al. 2017, 2021). The impact resistance of concrete is improved with the use of waste plastic aggregate (WPA). All of the researchers emphasized that WPA has a significant capacity for absorbing energy and is more flexible than control mix in addition to having a lower modulus of elasticity. These elements enable the effective transmission of impact stresses to the components of concrete, increasing concrete's resistance to impact failure. Although a plastic waste-based concrete mixture typically has a lower characteristics compressive strength of concrete (fck), which may restrict its use in some structural applications, it has several advantageous properties over conventional concrete, including lower density, greater toughness, increased impact resistance, increased ductility, and better sound and heat insulation. For a variety of building applications, these engineering characteristics are helpful.
Abrasion loss test
Cantabro abrasion loss test
In Cantabro abrasion loss test, during the first 50 and 100 rotations, no significant weight loss was observed. However, as stipulated in the normal test process, as the number of revolutions increased, the cylindrical shape (100 ɸ mm × 50 mm thickness) gradually rounded off at the edges towards the end of 300 revolutions per minute. The Cantabro weight loss changes in percentages for different concrete mixes are shown in Fig. 27a–c with different revolutions. For PE10-PE40, PET10-PET40, and WPA10-WPA40, Cantabro weight losses were less as compared to the control mix. However, for the same concrete mix, this loss increased with increase in revolutions per minute. Further, the Cantabro weight loss decreased with increase in % of plastic aggregate. Similar outcomes were demonstrated by other researchers (Ferreira et al. 2012; Saikia and de Brito 2014; Jain et al. 2020). The type and quality of the aggregates used to form the concrete have a significant impact on its surface qualities. Here plastic waste-made aggregates adsorb more impact, which results in increase abrasion resistance. As a result, the parameters of the link between the plastic aggregates and the cement paste have a big impact on the abrasion resistance.
Surface abrasion loss test
The variance of surface abrasion weight loss (%) with respect to number of revolutions is shown in Fig. 28a–c for different replacement levels of natural aggregates. As can be observed from Fig. 28a–c, surface abrasion weight loss is less for 28-day curing time for plastic aggregate-based concrete as compared to the control mix. However, for PET10-PET40 and WPA10-WPA40 the surface abrasion weight losses were minimum. Other researchers likewise reported similar outcomes like (Alqahtani et al. 2018; Galvão et al. 2011). All forms of plastic waste aggregate might give greater wear resistance because of their intrinsic hardness, plasticity nature and improved abrasion behaviour, despite the weak binding properties with the cement paste. Wear resistance is aided by the fibrous surface texture of plastic and the ability to manage cracks. Plastic waste aggregate coarser particles (PET) perform better at controlling abrasion than plastic waste aggregate smaller particles (PE). When the concrete is exposed to abrasion, the coarser particles stay attached to the paste, while the smaller particles are forced out of the matrix. The findings of several studies also showed that PET aggregates are more resistant to abrasion than PE aggregates since PET aggregates have a stronger interfacial connection between concrete and plastic aggregate and comparatively higher strength.
Gas permeability test
As indicated in Fig. 29, the outcomes in terms of compressive strength of concrete mixes for both CO2 and water curing are compared. Carbonation depth of test specimens is depicted in Table 8. For all experiments, the carbonation depth increased when there was more plastic waste aggregate in the concrete mix than when only NA was used (control mix), as indicated in Table 8. Another author likewise produced a similar outcome like (Lee et al. 2019). A rapid curing method known as carbonation involves injecting CO2 gas into the curing chamber, where it solidifies as calcium carbonates (CaCO3) at room temperature and diffuses into freshly mixed concrete under low pressure.
Early-age CO2 curing strengthens concrete products and increases their strength, surface hardness, and water resistance while decreasing efflorescence (Santhosh Kumar Balaji and KVGD Thrilok Nath Reddy 2019). Concrete naturally contains carbonates as a result of the interaction between its calcium-containing components and atmospheric carbon dioxide in the presence of water, which results in the formation of calcium carbonate. In non-reinforced concretes, it is a helpful reaction since it results in less porosity and a stronger carbonated paste. In contrast to the normal concrete, the plastic aggregate-based concrete showed opposite results that means strength reduced with increase in CO2 exposure and with increase in replacement the compressive strength decreased as shown in Fig. 29. The contrast results may be due to the increase in porosity in concrete mix due to poor bonding in ITZ.
Rapid chloride penetration test (RCPT)
Chloride migration inside concrete is a bad phenomenon that reduces its tensile strength and long-term useful life. Concrete's permeability, porosity, and absorption all have an impact on how easily chloride migrates through concrete. The RCPT tests at 28 days were used to determine the Cl− ion passing terms of coulombs for all of the concrete specimens, which were measured for 6 h (every 30 min interval) and are depicted in Fig. 30a–c. The average Cl− ion passing control mix after 28-day curing is 678 Coulombs, which is categorized as "low" chloride ion penetrability. In a similar vein, the Cl− ion passing by the plastic waste cement composite mixtures was found to be between 435 and 635 Coulombs as seen in Fig. 30a–c. In comparison with control samples, concrete samples containing plastic debris showed a generally reduced electrical current, indicating lesser chloride ion penetration. Similar findings were obtained in other researches (Alqahtani et al. 2018; Silva et al. 2013).
Elevated temperature effect test
Mechanical qualities of concrete deteriorate as a result of several physical and chemical processes brought on by exposure to high temperatures. The use of plastics as aggregate in concrete raises serious concerns about the durability of concrete at high temperatures simply because the melting temperature of plastics is substantially lower than natural aggregates. The change in concrete's compressive strength for various combinations of concrete mixtures against different high temperatures is shown in Fig. 31. Overall, it is evident that exposure to high temperatures causes a reduction in compressive strength and that reduction is linear with temperature. After being exposed to temperatures of 100 °C, 200 °C, and 300 °C for the control specimen with a w/c ratio of 0.37, the compressive strength declined by 9.88%, 15.01%, and 19.26%, respectively. When exposed to temperatures of 100 °C, 200 °C, and 300 °C, respectively, compressive strength is reduced by 20.87%, 28.43%, 20.33%, and 31.34%; 24.59%, 26.04%, 27.95%, and 26.13%; and 28.24%, 30.19%, and 25.072%, respectively, for PE10-PE40. For PET 10, the compressive strength was reduced by 30.24%, 27.07%, and 23.75% after exposure to temperatures of 100 °C, 200 °C, and 300 °C, respectively. For WPA 10 to 40, after exposure to temperatures of 100 °C, 200 °C, and 300 °C, respectively, the compressive strength was reduced by 36.65%, 39.987%, 44.85%, and 46.429%; by 39.66%, 44.19%, 48.28%, and 54.20%; and by 40.63%, 45.39%, 51.88%, and 56.44%, respectively. In short, it can be concluded that considerable decrease in strength of plastic waste aggregate concrete was observed when exposure temperature exceeds melting temperature of plastic (100–180 °C). Comparable outcomes are reported by (Saxena et al. 2018; Correia et al. 2014; Sojobi and Owamah 2014). A sizable amount of water vapour is produced inside the concrete when it is exposed to a temperature exceeding 100 °C. This water vapour in the concrete matrix causes pore pressure, which makes it easier for microcracks to spread and results in a decreased compressive strength and deterioration of durability properties. Reduced thermal stability of plastic waste aggregate; induced porosity in concrete as a result of the formation of volatile products when plastic waste aggregate is heated above their melting point; development of an unbalanced thermal gradient within the concrete; and build-up of pore pressure as a result of the confinement of water vapours in distinct pockets created after plastics breakdown may be the possible reasons for reduced strength and durability of concrete. It should be noted that exposure temperatures below 100 °C have no impact on strength values regardless of the kind of plastic waste aggregate used in concrete. The creation of new hydrate brought on by an increase in temperature is responsible for this unexpectedly favourable impact at moderate temperatures.
Leachability test
Microplastic (MP) in particular is released through leaching (Van Praagh and Modin 2016), which happens when plastic wastes in the environment come into contact with water and adverse environmental conditions. As per the results of the microplastic analysis, PE-based concrete showed more microplastic in leachate than in other trials. PET-based concrete showed less microplastic concentration during leaching as compared to other mix proportions. Table 9 shows the microplastic present or absent over various mix proportions of plastic waste-based concrete as confirmed with Fig. 16i. WPA-based concrete also showed the same results as PE-based concrete as shown in Table 9. Through the leaching test, it was observed that concrete made up of PE-based aggregate resulted in the presence of microplastic in leachate but for PET-based concrete no such MP was found.
Optical microscopy test
All trial specimens after curing for 28 days were subjected to microstructure studies using high-resolution optical microscope (Dewinter), and the outcomes are depicted in Fig. 32. The objective of the microstructure investigation was to define the morphology of the plastic waste-based hardened concrete, observe the ITZ between the plastic aggregates and cement matrix, identify the presence and intensity of air voids, and investigate the surface topography. From Fig. 32c, it is clear that the PE-based aggregates were surrounded by small NFA particles and cement paste, which made it homogeneous and compact, thus leading to improved mechanical and durable properties. In contrast, the PET-based mixture (Fig. 32b) showed a less dense microstructure, more ITZ voids, and more porosity because there was less adhesive bond between the cement matrix and the PET aggregates than there were between the cement matrix and coarse aggregates. This may have an impact on the strength loss of concrete samples. The uniform and plain surface of PET can also lead to a weaker bond between the cement matrix and PET, resulting in porous microstructures and less mechanical and durable properties. Additionally, WPA-based mixture (Fig. 32a) showed a more porous microstructure with more ITZ voids and high porosity compared to control mix due to the weaker adhesion between the cement matrix and both PE- and PET-based aggregates. This may have an impact on the strength loss of concrete samples. The compressive strength and unit weight of composite concretes may both decrease as a result of the existence of these pores or voids. Alqahtani et al. 2017; Şimşek et al. 2013; Gu and Ozbakkaloglu 2016; Belmokaddem et al. 2020; Vo et al. 2022 reported that the poor adhesion between the plastic waste-based aggregates and the cement matrix is the cause of the decreased mechanical and durability characteristics of the composites that were developed.
Disadvantages or shortcomings of using PET- and PE-based aggregates in concrete and the scope for future study:
There are still several restrictions that prevent their widespread application in concrete matrix irrespective of obvious environmental and financial advantages of using PE- and PET-based aggregates in favour of natural aggregates. The following are briefly mentioned some of the main drawbacks related to the usage of plastic waste in concrete matrix:
-
1)
The separation and preparation of PET and PE before recycling is one of the main restrictions on their use. PE and PET collected from the various waste streams where they are produced, they are frequently polluted with different kinds of organic and pathogenic contaminants.
-
2)
When used in concrete matrix for construction, PET and PE, which differ from natural aggregates, may not function isotropically.
-
3)
As PE and PET have low specific weights, therefore, they minimize the self-weight of concrete structures. Consequently, they are inappropriate for applications requiring high strength.
-
4)
Low water adsorption capacity may improve workability, but because PE and PET are hydrophobic, lots of free water accumulate on the surface and weaken the transition zone, lowering the strength of the concrete with greater percentages of PET and PE aggregates.
-
5)
As a result of the aggregate particles' smooth surfaces and flaky shapes, there is a greater space between the cement paste and the plastic aggregates, which weakens the bonding strength. Moreover, it raises the permeability of concrete and lowers the final composite's overall mechanical performance. In order to raise the surface roughness of the manufactured plastic aggregate particles and increase the bonding in the interstitial zones (ITZs), mechanical or chemical treatment is advised.
-
6)
Since the replacement ratio of aggregate made from PET and PE has a negative relationship with acid and fire resistance, it should be enclosed when utilized in building construction.
So, the main elements influencing the mechanical performance are the lower elastic modulus of the plastic waste in comparison to NA and the porosity that developed in the microstructure of the composites after its addition. Due to their poor bonding properties with the cement paste and the increase in porosity of typical cementitious materials in concrete mix, these two factors also negatively affect the durability characteristics of the concrete, particularly those related to the transfer behaviour and straining capacity of concrete. By employing some corrective procedures, these impacts that cause poor durability performance can be reduced. These include using a finer fraction of plastic waste aggregate in pellet or powder form rather than a coarser fraction or an elongated and flaky form, treating the plastic's surface to increase cement paste adhesion, using pozzolanic admixtures as an additional binder to improve the matrix's microstructure, and converting plastic particles into novel light waste aggregate through thermal treatment and agglomeration with NA or mineral admixtures. All of these corrective actions provide instruction for upcoming work.
Conclusion
The purpose of the current study was to determine the impact of recycled PE and PET aggregates on the mechanical and durability characteristics of concrete by replacing naturally obtained FA and CA, respectively, for 4 different volumetric replacement levels keeping same W/C ratio for M30 grade concrete. The following conclusions can be formed in light of the results:
-
1)
Compressive strength was reduced by the presence of plastic aggregates. The maximum reduction was observed when natural coarse aggregates were replaced by PET aggregates. Though compressive strength reduced with increase of plastic aggregates, it can be permissible up to 30% of replacement in case of PE-based concrete. However, the mixed concrete can be used for lightweight structural purpose as the minimum compressive strength was obtained greater than 17 N/mm2.
-
2)
The inclusion of PET as a replacement of NCA and both PET and PE aggregates as replacement of NCA and NFA, respectively, in concrete significantly increased the sorptivity for 10–40% replacement ratios. This performance was attributed to the increase in porosity caused by the evaporation of surplus water around the hydrophobic PET particles as well as heterogeneity in shape and superficial textures of PET at ages 7, 28, 56, and 90 days of curing. When PE was added to a concrete specimen replacing NFA, the sorptivity was reduced for a 10–40% replacement ratio at 7, 28, 56, and 90 days after curing as compared to others mix proportions.
-
3)
For water permeability test, PET-based concrete showed higher permeability coefficient value over the other mix proportions including control. The rise in permeability may be due to the increased porosity brought on by the development of fragile spots as a result of the tenuous bond between WPA and cement matrix.
-
4)
Alkaline, marine, and municipal wastewater did not show any adverse effect on the plastic-based concrete mix. Plastic waste-based concrete showed greater resistance to SO4 attack from H2SO4 exposure tests.
-
5)
For impact resistance test, it was observed that PE40 consumed 83.33% more energy for the detection of the first crack as compared to control mix. For PET40, the energy consumption was 122.22% higher as compared to control concrete. Further, for WPA40 energy consumption was 155.55% higher as compared to control mix.
-
6)
For Cantabro abrasion loss test, the incorporation of PE and PET as replacement of NFA, NCA, in concrete caused less loss of weight for all mix proportions as compared to the control mix for 28 days of curing. For WPA concrete, when both the natural aggregates were replaced by plastic aggregates the loss was even minimum as compared to control and PE and PET mix.
-
7)
For surface abrasion loss test, the incorporation of plastic aggregate reduced the surface weight loss as compared to the control mix. Surface weight loss is maximum for PE aggregates when used as replacement of FA compared to all plastic aggregate-based concrete.
-
8)
For the gas permeability test, the incorporation of WPA in concrete showed decrease compressive strength trend for CO2 curing as compared to control. Average penetration depth of CO2 increased with increase in WPA. Concrete that is supposed to have a greater capacity to evacuate gas, as in the case of pervious concrete, benefits from increased permeability caused by the use of plastic particles. Average gas penetration depths of PE- and PET-based concrete were almost same but higher when both the aggregates were replaced by PE and PET (WPA concrete).
-
9)
During elevation temperature test, the compressive strength of WPA-based concrete decreased when compare to the control mix and the decrease is increasing with increase in temperature and % replacement of aggregates. The decrease in compressive strength is minimum for PE mix followed by PET mix and WPA mix. Due to its high degree of porosity, concrete develops a temperature gradient that causes cracks to first appear.
-
10)
For rapid chloride penetration test, chloride ions penetration rate of control mix was highest as compared to other mix proportions of PWA. Chloride ion penetration rates of WPA concrete were lower as compared to PE and PET concrete mix. Chloride ions penetrability of all trials can be classified as “Low” as per (ASTM C1202-12 2012).
-
11)
For leachability test of microplastic of concrete, maximum MP concentration was observed for PE-based concrete. PET mix did not show any microplastic concentration in TCLP test.
-
12)
The microstructure analysis depicted that the uniform and plain structure of plastic-based aggregates leads to a weaker bond between plastic aggregates and cementitious materials, resulting in porous structure and reduced mechanical properties.
The findings of this experimental study support the usefulness of using WPA as a partial replacement of NCA and NFA in the production of green concrete up to 40% volumetrically. The application of PWA may not improve the mechanical properties of concrete but enhance its durability properties in terms of resistance to abrasion and impact and resistance to chloride ions. The results of this study confirm and validate the applicability of PWA in production of light weight green concrete for sustainable development. Plastic waste aggregate has a higher ratio of density reduction to loss of concrete strength than other lightweight material. Therefore, the design of earthquake-resistant structures can be benefitted from the usage of plastic waste aggregate concrete. It is desirable to employ plastic-incorporated concrete to produce pervious concrete for ground water recharge through pavement area. Because it resists chloride migration, concrete made with PET and PE can be utilized to shield the reinforcement in reinforced structures from corrosion. Last but not least, concrete for road pavements, crash barriers, etc., may be made using plastic waste cement composites because of its resilience to impact loading and abrasive pressures. Plastic may therefore become a viable replacement for traditional NA in some cases adding environmental sustainability by reducing issues related to disposal or open burning of plastic waste. It will also reduce the environmental impacts brought on by the excessive natural resource depletion to satisfy the skyrocketing demand for aggregates. The long-discussed argument for sustainability through plastic waste consumption in the construction sector may be strengthened by the measurement of the environmental benefit of employing plastic waste inside concrete in terms of carbon footprint and other consequences through life cycle assessment studies. Reusing plastic waste in construction industries and a comprehensive and efficient plan of plastic waste management may minimize microplastic pollution.
References
Akçaözoğlu S, Atiş CD, Akçaözoğlu K (2010) An investigation on the use of shredded waste PET bottles as aggregate in lightweight concrete. Waste Manage 30(2):285–290. https://doi.org/10.1016/j.wasman.2009.09.033
Almeshal I, Tayeh BA, Alyousef R, Alabduljabbar H, Mustafa Mohamed A, Alaskar A (2020) Use of recycled plastic as fine aggregate in cementitious composites: a review. Constr Build Mater 253:119146. https://doi.org/10.1016/j.conbuildmat.2020.119146
Al-Tayeb MM, Ismail H, Dawoud O, Wafi SR, Daoor IA (2017) Ultimate failure resistance of concrete with partial replacements of sand by waste plastic of vehicles under impact load. Int J Sust Built Environ 6(2):610–616. https://doi.org/10.1016/j.ijsbe.2017.12.008
Al-Tayeb MM, Zeyad AM, Dawoud O, Tayeh BA (2021) Experimental and numerical investigations of the influence of partial replacement of coarse aggregates by plastic waste on the impact load. Int J Sust Eng 14(4):735–742. https://doi.org/10.1080/19397038.2020.1774820
Alqahtani FK, Ghataora G, Khan MI, Dirar S (2017) Novel lightweight concrete containing manufactured plastic aggregate. Constr Build Mater 148:386–397. https://doi.org/10.1016/j.conbuildmat.2017.05.011
Alqahtani FK, Ghataora G, Dirar S, Khan MI, Zafar I (2018) Experimental study to investigate the engineering and durability performance of concrete using synthetic aggregates. Constr Build Mater 173:350–358. https://doi.org/10.1016/j.conbuildmat.2018.04.018
ASTM C1202-12 (2012) Standard Test Method for Electrical Indication of Concrete’s Ability to Resist Chloride Ion Penetration. ASTM Int
ASTM C1585-13 (2013) Standard Test Method for Measurement of Rate of Absorption of Water by Hydraulic-Cement Concretes.
ASTM C1898-20 (2020) Standard Test Methods For Determining The Chemical Resistance Of Concrete Products To Acid Attack
ASTM C494-19 (2019) Standard Specification for Chemical Admixtures for Concrete. ASTM International West Conshohocken.
ASTM C944/C944M (2012) Standard Test Method for Abrasion Resistance of Concrete or Mortar Surfaces by the Rotating-Cutter Method. American Society of Testing and Materials International
Bryant Mather (1964) Effects of seawater on concrete. In: Symposium on effects of aggressive fluids on concrete at the 44th annual meeting of highway research board (Committee MC-B2 on Performance of Concretes: Chemical Aspects). Publ. US Army Engineers Waterways Experiment Station
Belmokaddem M, Abdelkader M, Yassine S, Bekir YP (2020) Mechanical and physical properties and morphology of concrete containing plastic waste as aggregate. Construct Build Mater 257:119559. https://doi.org/10.1016/j.conbuildmat.2020.119559
C1747/C1747M A (2013) Standard test method for determining potential resistance to degradation of pervious concrete by impact and abrasion
Choi YW, Moon DJ, Kim YJ, Lachemi M (2009) Characteristics of mortar and concrete containing fine aggregate manufactured from recycled waste polyethylene terephthalate bottles. Constr Build Mater 23(8):2829–2835. https://doi.org/10.1016/j.conbuildmat.2009.02.036
Coppola B, Courard L, Michel F, Incarnato L, Scarfato P, Di L (2018) Hygro-thermal and durability properties of a lightweight mortar made with foamed plastic waste aggregates. Constr Build Mater 170:200–206. https://doi.org/10.1016/j.conbuildmat.2018.03.083
Correia JR, Lima JS, de Brito J (2014) Post-fire mechanical performance of concrete made with selected plastic waste aggregates. Cement Concr Compos 53:187–199. https://doi.org/10.1016/j.cemconcomp.2014.07.004
da Luz GM, Oliveira MR, Silva TN, Castro ACM (2021) Performance of mortars with PET. J Mater Cycles Waste Manag 23(2):699–706. https://doi.org/10.1007/s10163-020-01160-w
DIN 1048-5:1991-06 (2015) Testing concrete—testing of hardened concrete (specimens prepared in mould). https://www.infostore.saiglobal.com/en-us/search/standard/?sortkey=date-desc&publisher=din&productfamily=standard.
Ferreira L, de Brito J, Saikia N (2012) Influence of curing conditions on the mechanical performance of concrete containing recycled plastic aggregate. Constr Build Mater 36:196–204. https://doi.org/10.1016/j.conbuildmat.2012.02.098
Frigione M (2010) Recycling of PET bottles as fine aggregate in concrete. Waste Manag 30(6):1101–1106. https://doi.org/10.1016/j.wasman.2010.01.030
Galvão JCA, Portella KF, Joukoski A, Mendes R, Ferreira ES (2011) Use of waste polymers in concrete for repair of dam hydraulic surfaces. Constr Build Mater 25(2):1049–1055. https://doi.org/10.1016/j.conbuildmat.2010.06.073
Gavela S, Ntziouni A, Rakanta E, Kouloumbi N, Kasselouri-Rigopoulou V (2013) Corrosion behaviour of steel rebars in reinforced concrete containing thermoplastic wastes as aggregates. Constr Build Mater 41:419–426. https://doi.org/10.1016/j.conbuildmat.2012.12.043
Gondal AH, Bhat RA, Gómez RL, Areche FO, Huaman JT (2022) Advances in plastic pollution prevention and their fragile effects on soil, water, and air continuums. Int J Environ Sci Technol. https://doi.org/10.1007/s13762-022-04607-9
Gu L, Ozbakkaloglu T (2016) Use of recycled plastics in concrete: a critical review. Waste Manag 51(May):19–42. https://doi.org/10.1016/j.wasman.2016.03.005
IS 10262(REVISED) (2019) Concrete Mix Proportioning-Guidelines, New Delhi, India
IS 1237:2012 (2012) Cement concrete flooring tiles—specification
IS 383 (1970) Specification for Coarse and Fine Aggregates From Natural Sources For Concrete. New Delhi, India
IS:516-1959 (1959) Methods of test for strengt of concrete
IS-456:2000 (2000) Plain and Reinforced Concrete Code of Practice. BIS, New Delhi
Islam MJ, Shahjalal M, Haque NMA (2022) Mechanical and durability properties of concrete with recycled polypropylene waste plastic as a partial replacement of coarse aggregate. Journal of Building Engineering 54(February):104597. https://doi.org/10.1016/j.jobe.2022.104597
Islam MJ, Shahjalal M (2021) Effect of polypropylene plastic on concrete properties as a partial replacement of stone and brick aggregate. Case Stud Constr Mater 15:00627. https://doi.org/10.1016/j.cscm.2021.e00627
IS-part-I (1489). Ppc cement properties
Jadhav HS, Fulke AB, Giripunje MD (2022) Recent global insight into mitigation of plastic pollutants, sustainable biodegradable alternatives, and recycling strategies. Int J Environ Sci Technol. https://doi.org/10.1007/s13762-022-04363-w
Jain A, Siddique S, Gupta T, Sharma RK, Chaudhary S (2020) Utilization of shredded waste plastic bags to improve impact and abrasion resistance of concrete. Environ Dev Sustain 22(1):337–362. https://doi.org/10.1007/s10668-018-0204-1
Jain D, Bhadauria SS, Kushwah SS (2022) An experimental study of utilization of plastic waste for manufacturing of composite construction material. Int J Environ Sci Technol. https://doi.org/10.1007/s13762-022-04447-7
Janfeshan Araghi H, Nikbin IM, Rahimi Reskati S, Rahmani E, Allahyari H (2015) An experimental investigation on the erosion resistance of concrete containing various PET particles percentages against sulfuric acid attack. Constr Build Mater 77:461–471. https://doi.org/10.1016/j.conbuildmat.2014.12.037
Jassim AK (2017) Recycling of polyethylene waste to produce plastic cement. Procedia Manufacturing 8(October 2016):635–642. https://doi.org/10.1016/j.promfg.2017.02.081
Jayeshkumar Pitroda DFSU (2013) Evaluation of Sorptivity and Water Absorption of Concrete with Partial Replacement of Cement by Thermal Industry Waste (Fly Ash). International Journal of Engineering and Innovative Technology (IJEIT) 2(7).
Kumar TS, Balaji KVGD, Reddy STN, Rao GS (2019) Mechanical properties of concrete when cured with carbon dioxide 8958(6):2544–2549. https://doi.org/10.35940/ijeat.F8497.088619
Lee ZH, Paul SC, Kong SY, Susilawati S, Yang X (2019) Modification of waste aggregate PET for improving the concrete properties. Adv Civ Eng 2019:1–10. https://doi.org/10.1155/2019/6942052
Majeed AZ, Kurian T, Davis B, Alex ST, Fernandez KS, Mathew AV (2019) Partial replacement of aggregates with granulated waste plastic in solid concrete blocks—an intensive study, 405–415. https://doi.org/10.1007/978-981-13-1202-1_34
Massazza F (1993) Pozzolanic cements. Cement Concr Compos 15(4):185–214
Mercante I, Alejandrino C, Ojeda JP, Chini J, Maroto C, Fajardo N (2018) Mortar and concrete composites with recycled plastic: a review. Sci Technol Mater 30 (December):69–79. https://doi.org/10.1016/j.stmat.2018.11.003
Naderi M, Kaboudan A (2021) Experimental study of the effect of aggregate type on concrete strength and permeability. J Build Eng 37(October 2020):101928. https://doi.org/10.1016/j.jobe.2020.101928
Needhidasan S, Ramesh B, Joshua S, Prabu R (2020) Experimental study on use of e-waste plastics as coarse aggregate in concrete with manufactured sand. Mater Today Proc 22:715–721. https://doi.org/10.1016/j.matpr.2019.10.006
Nikbin M, Iman S, Rahimi R, Allahyari H, Fallah F (2016) Feasibility study of waste poly ethylene terephthalate (PET) particles as aggregate replacement for acid erosion of sustainable structural normal and lightweight concrete. J Clean Product 126(July):108–117. https://doi.org/10.1016/j.jclepro.2016.02.143
NOAA Marine Debris Program (2015) Laboratory Methods for the Analysis of Microplastics in the Marine Environment: Recommendations for quantifying synthetic particles in waters and sediments. National Oceanic and Atmospheric Administration U.S. Department of Commerce Technical Memorandum NOS-OR&R-48
Nvironment DGE (2011) Management PLan
Ohemeng EA, Ekolu SO (2019) Strength prediction model for cement mortar made with waste LDPE plastic as fine aggregate. J Sustain Cem Based Mater 8(4):228–243. https://doi.org/10.1080/21650373.2019.1625826
Pather B, Ekolu SO, Quainoo H (2021) Effects of aggregate types on acid corrosion attack upon fly—ash geopolymer and Portland cement concretes—comparative study. Constr Build Mater 313:125468. https://doi.org/10.1016/j.conbuildmat.2021.125468
Saikia N, de Brito J (2014) Mechanical properties and abrasion behaviour of concrete containing shredded PET bottle waste as a partial substitution of natural aggregate. Constr Build Mater 52:236–244. https://doi.org/10.1016/j.conbuildmat.2013.11.049
Santhosh Kumar Balaji KVGD, Thrilok Nath Reddy GSR (2019) Mechanical Properties of Concrete when cured with Carbon dioxide. International Journal of Engineering and Advanced Technology (IJEAT) 8(6).
Sau D, Hazra T, Shiuly A (2023) Assessment of sustainable green concrete properties using recycled plastic waste as replacement for fine aggregate using machine learning technique. Compos Mech Comput Appl Int J 14(2):1–12. https://doi.org/10.1615/CompMechComputApplIntJ.2022044775
Saxena R, Siddique S, Gupta T, Sharma RK, Chaudhary S (2018b) Impact resistance and energy absorption capacity of concrete containing plastic waste. Constr Build Mater 176:415–421. https://doi.org/10.1016/j.conbuildmat.2018.05.019
Saxena R, Gupta T, Sharma RK, Chaudhary S, Jain A (2018a) Assessment of Mechanical and Durability Properties of Concrete Containing PET Waste. Scientia Iranica. https://doi.org/10.24200/sci.2018.20334
Shiuly A, Hazra T, Sau D, Maji D (2022) Performance and optimisation study of waste plastic aggregate based sustainable concrete—a machine learning approach. Cleaner Waste Syst 2:100014. https://doi.org/10.1016/j.clwas.2022.100014
Silva RV, de Brito J, Saikia N (2013) Influence of curing conditions on the durability-related performance of concrete made with selected plastic waste aggregates. Cement Concr Compos 35(1):23–31. https://doi.org/10.1016/j.cemconcomp.2012.08.017
Sim J, Park C (2011) Compressive strength and resistance to chloride ion penetration and carbonation of recycled aggregate concrete with varying amount of fly ash and fine recycled aggregate. Waste Manag 31(11):2352–2360. https://doi.org/10.1016/j.wasman.2011.06.014
Şimşek B, Tansel İç Y, Şimşek EH (2013) A full factorial design based desirability function approach for optimization of properties of C 40/50 concrete class. Math Comput Appl 18(3):330–339. https://doi.org/10.3390/mca18030330
Sojobi A, Owamah H (2014) Evaluation of the suitability of low-density polyethylene (LDPE) waste as fine aggregate in concrete. Niger J Technol 33(4):409. https://doi.org/10.4314/njt.v33i4.1
Suram R, Varma VNK, Srinivas T (2021) Durability properties of concrete made with polyethylene terepthalate and polypropylene as replacement of fine aggregate. In: E3S web of conferences 309.
Tayeh BA, Almeshal I, Magbool HM, Alabduljabbar H, Alyousef R (2021) Performance of sustainable concrete containing different types of recycled plastic. J Clean Product 328 (October). https://doi.org/10.1016/j.jclepro.2021.129517
Thiyagarajan SV (2014) Experimental behaviour of waste tyre rubber aggregate concrete under impact loading. November 2019
Tian Y, Bourtsalas ACT, Kawashima S, Ma S, Themelis NJ (2020) Performance of structural concrete using Waste-to-Energy (WTE) combined ash. Waste Manag 118:180–189. https://doi.org/10.1016/j.wasman.2020.08.016
Tijani MN, Inim JI, Adetu SO (2013) Experimental study of influence of seawater on strength of concrete structures. In: Fifth international conference on geotechnique, construction materials and environment, Osaka, Japan, 2015 Nov:16–18, ISBN: 978-4-9905958-4-5 C3051
Van Praagh M, Modin H (2016) Leaching of chloride, sulphate, heavy metals, dissolved organic carbon and phenolic organic pesticides from contaminated concrete. Waste Manag 56:352–358. https://doi.org/10.1016/j.wasman.2016.07.009
Vo D-H, Do N-D, Mamuye Y, Liao M-C, Hwang C-L, Tran Q-T (2022) Engineering l (DMDA) Method incorporating steel reducing slag aggregate. Construct Build Mater 354 (November):129180. https://doi.org/10.1016/j.conbuildmat.2022.129180
Zega CJ, Di Maio ÁA (2011) Use of recycled fine aggregate in concretes with durable requirements. Waste Manag 31(11):2336–2340. https://doi.org/10.1016/j.wasman.2011.06.011
Zhang C, Hu M, van der Meide M, Di Maio F, Yang X, Gao X, Li K, Zhao H, Li C (2023) Life cycle assessment of material footprint in recycling: a case of concrete recycling. Waste Manag 155:311–319. https://doi.org/10.1016/j.wasman.2022.10.035
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Competing interests
On behalf of all the authors of the submission, corresponding author disclosing that any financial help and personal help is not used with other people or organizations.
Additional information
Editorial responsibility: Shahid Hussain.
Rights and permissions
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Sau, D., Shiuly, A. & Hazra, T. Utilization of plastic waste as replacement of natural aggregates in sustainable concrete: effects on mechanical and durability properties. Int. J. Environ. Sci. Technol. 21, 2085–2120 (2024). https://doi.org/10.1007/s13762-023-04946-1
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13762-023-04946-1