Abstract
Novel chondroitin sulfate (CS) — poly(ethylene oxide) (PEO) hydrogel was synthesized and evaluated by a mechanism of self cross-linking of CS derivative with PEO with hexa-thiols (PEO-SH). A derivative of CS was synthesized by the sequential grafting of adipic acid dihydrazide (ADH) and acrylic acid: chemical grafting of ADH to the carboxylic acid in CS (CS-ADH) followed by grafting of the acrylic acid to the free amine groups in the CSADH (CS-ADH-Ac). The synthesis of CS-ADH-Ac molecules was confirmed by observing new acrylate peaks in CS-ADH-Ac by FTIR, ESCA, and NMR. The CS-PEO hydrogel was self cross-linked through a Michael type addition reaction between the acrylate end groups of CS-ADH-Ac and the thiol end groups of the PEO-SH. the gelation behavior of 10% CS-PEO was evaluated by rheological analyses from the changes in the solution properties, such as phase angles and visco-elasticities. Rheological analysis indicated that the gelation process was complete within 2 min after mixing two polymer solutions of CS-ADH-Ac and PEO-SH. The fabricated CS-PEO hydrogel was analyzed by measuring both its swelling under different water pHs and its mechanical strength against compression. The morphological shapes of both its surface and cross sections were also evaluated after the sequential processes of gel swelling to equilibrium followed by dehydration. Both the gelation time and swelling of the fabricated hydrogel were dependent on the pH of the polymer solutions and swelling medium, showing quicker gel formation and better swelling behaviors under basic conditions than under acidic conditions. The equilibrated gel showed different morphologies depending on its location, i.e. its cross sections demonstrated more homogeneous morphologies than the surfaces. While the dehydrated hydrogel demonstrated 8–10 μm pore sizes on its cross sections, the compression strength of the hydrogel ranged from 1.4 to 2.8 Pa depending on its gel concentration. Toluidine blue molecules as a model drug were released from the hydrogel over a period of more than 5 days. These hydrogel properties, such as formation of in situ gel, release behaviors of toluidine blue, and porous structures and mechanical properties of the fabricated gel, highlighted the potential of a hydrogel as a carrier for local drug delivery and a scaffold for tissue engineering.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
M. Lovu, G. Dumais, and P. du Souich, Osteoarthritis Cartilage, 16, S14 (2008).
O. Bruyere and J. Y. Reginster, Drug & Aging, 24, 573 (2007).
R. J. Linhardt and R. E. Hileman, Gen. Pharmac., 26, 443 (1995).
A. Rebaudi, P. Silvestrini, and P. Trisi, Int. J. Periodontics Restorative Dent, 23, 371 (2003).
A. Rubinstein, D. Nakar, and A. Sintov, Int. J. Pharm., 84, 141 (1992).
A. P. Asimakopoulou, A. D. Theocharis, G. N. Tzanakakis, and N. K. Karamanos, In vivo, 22, 385 (2008).
S. C. Wang, B. H. Chen, L. F. Wang, and J. S. Chen, Int. F Pharm., 329, 103 (2007).
H. Cao and S.-Y. Xu, J. Mater. Sci. Mater. Med., 19, 567 (2008).
C. T. Lee, C. P. Huang, and Y. D. Lee, Biomacromolecules, 7, 2200 (2006).
B. Huang, C. Q. Li, Y. Zhou, G. Luo, and C. Z. Zhang, J. Biomed. Mater. Res. B, 74, 159 (2009).
J. F. Piai, A. F. Rubina, and E. C. Muniz, Acta Biomater., 5, 2601 (2009).
S. Varghese, N. S. Hwang, and A. C. Canver, Matrix Biol., 27, 12 (2008).
L. Vodná, S. Bubeníková, and D. Bakos, Macromol. Biosci., 7, 629 (2007).
M. Brittberg, A. Lindahl, A. Nilsson, C. Ohlsson, O. Isaksson, and L. Peterson, N. Engl. J. Med., 331, 889 (1994).
D. A. Grande, M. I. Pitman, L. Peterson, D. Menche, and M. Klein, J. Orthop. Res., 7, 208 (1989).
I. S. Kim, Y. M. Song, T. H. Cho, Y. D. Park, K. B. Lee, I. Noh, F. Weber, and S. J. Hwang, Dev. Growth Differ., 50, 553 (2008).
I. Noh, Y. J. Choi, M. S. Kim, and G. Tae, J. Biomed. Mater. Res., 83A, 674 (2007).
G. W. Kim, Y. J. Choi, Y. Park, K. B. Lee, I. S. Kim, S. J. G. Hwang, and I. Noh, Curr. Appl. Phys., 7S1, e28 (2007).
J. Kim, Y. Park, G. Tae, K. B. Lee, S. J. Hwang, I. S. Kim, I. Noh, and K. Sun, J. Mater. Sci.-Mater. Med., 19, 3311 (2008).
L. F. Wang, S. S. Shen, and S. C. Lu, Carbohydr. Polym., 52, 389 (2003).
D. A. Wang, S. Varghese, B. Sharma, I. Strehin, S. Fermanian, J. Gorham, D. H. Fairbrother, B. Cascio, and J. H. Elisseeff, Nat. Mater., 6, 385 (2007).
M. F. Tsai, H. Y. Tsai, Y. S. Peng, L. F. Wang, J. S. Chen, and S. C. Lu, J. Biomed. Mater. Res. Part A, 84A, 727 (2007).
I. Villanueva, S. K. Gladem, J. Kessler, and S. J. Bryant, Matrix. Biol., 29, 51 (2010).
M. Balci, Basic 1 H-13 C-NMR spectroscopy, 1st ed, Amstersam, Elsevier B. V, 2005, pp 379–406.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Jo, S., Kim, D., Woo, J. et al. Development and physicochemical evaluation of chondroitin sulfate-poly(ethylene oxide) hydrogel. Macromol. Res. 19, 147–155 (2011). https://doi.org/10.1007/s13233-011-0205-5
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13233-011-0205-5