Abstract
Microstructural evolution in a new kind of aluminum (Al) alloy with the chemical composition of Al-8.82Zn-2.08Mg-0.80Cu-0.31Sc-0.3Zr was investigated. It is found that the secondary phase MgZn2 is completely dissolved into the matrix during a short homogenization treatment (470°C, 1 h), while the primary phase Al3(Sc,Zr) remains stable. This is due to Sc and Zr additions into the Al alloy, high Zn/Mg mass ratio, and low Cu content. The experimental findings fit well with the results calculated by the homogenization diffusion kinetics equation. The alloy shows an excellent mechanical performance after the short homogenization process followed by hot-extrusion and T6 treatment. Consequently, a good combination of low energy consumption and favorable mechanical properties is obtained.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
H.A. Godinho, A.L.R. Beletati, E.J. Giordano, and C. Bolfarini, Microstructure and mechanical properties of a spray formed and extruded AA7050 recycled alloy, J. Alloys Compd., 586(2014), No. S1, p. S139.
L. Rogal, J. Dutkiewicz, H. Atkinson, L. Litynska-Dobrzynska, T. Czeppe, and M. Modigell, Characterization of semi-solid processing of aluminium alloy 7075 with Sc and Zr additions, Mater. Sci. Eng. A, 580(2013), p. 362.
W.B. Li, Q.L. Pan, Y.P. Xiao, Y.B. He, and X.Y. Liu, Microstructural evolution of ultra-high strength Al-Zn-Cu-Mg-Zr alloy containing Sc during homogenization, Trans. Nonferrous Met. Soc. China, 21(2011), No. 10, p. 2127.
S.Y. Chen, K.H. Chen, GS. Peng, X.H. Chen, and Q.H. Ceng, Effect of heat treatment on hot deformation behavior and microstructure evolution of 7085 aluminum alloy, J. Alloys Compd., 537(2012), p. 338.
X.G. Fan, D.M. Jiang, Q.C. Meng, and L. Zhong, The microstructural evolution of an Al-Zn-Mg-Cu alloy during homogenization, Mater. Lett., 60(2006), No. 12, p. 1475.
L.M. Wu, W.H. Wang, Y.F. Hsu, and S. Trong, Effects of homogenization treatment on recrystallization behavior and dispersoid distribution in an Al-Zn-Mg-Sc-Zr alloy, J. Alloys Compd., 456(2008), No. 1–2, p. 163.
Y.L. Deng, Y.Y. Zhang, L. Wan, A.A. Zhu, and X.M. Zhang, Three-stage homogenization of Al-Zn-Mg-Cu alloys containing trace Zr, Metall. Mater. Trans. A, 44(2013), No. 6, p. 2470.
H. Li, D.H. Cao, Z.X., Wang, and Z.Q. Zheng, High-pressure homogenization treatment of Al-Zn-Mg-Cu aluminum alloy, J. Mater. Sci., 43(2008), No. 5, p. 1583.
A.F. Norman, P.B. Prangnell, and R.S. McEwen, The solidification behaviour of dilute aluminium–scandium alloys, Acta Mater., 46(1998), No. 16, p. 5715.
I.G. Brodova, D.V. Bashlikov, and I.V. Polents, Influence of heat time melt treatment on the structure and the properties of rapidly solidified aluminum alloys with transition metals, Mater. Sci. Forum, 269–272(1998), p. 589.
S. Golubev, O. Korzhavina, P. Popel, V. Kononenko, I. Brodova, I. Polents and T. Shubina, Effect of viscosity and electrical-resistance of the structural state of Al-Sc melts and the structure of the cast metal, Russ. Metall., (1991), No. 1, p. 44.
E.A. Marquis and D.N. Seidman, Coarsening kinetics of nanoscale Al3Sc precipitates in an Al-Mg-Sc alloy, Acta Mater., 53(2005), No. 15, p. 4259.
J.D. Robson and P.B. Prangnell, Modelling Al3Sc dispersoid precipitation in multicomponent aluminium alloys, Mater. Sci. Eng. A, 352(2003), No. 1–2, p. 240.
N. Blake and M. Hopkins, Constitution and age hardening of Al-Sc alloys, J. Mater. Sci., 20(1985), No. 8, p. 2861.
M.J. Jones and F.J. Humphreys, Interaction of recrystallization and precipitation: the effect of Al3Sc on the recrystallization behaviour of deformed aluminium, Acta Mater., 51(2003), No. 8, p. 2149.
D.N. Seidman, E.A. Marquis, and D.C. Dunand, Precipitation strengthening at ambient and elevated temperatures of heat-treatable Al (Sc) alloys, Acta Mater., 50(2002), No. 16, p. 4021.
Y. Deng, Z.M. Yin, K. Zhao, J.Q. Duan, and Z.B. He, Effects of Sc and Zr microalloying additions on the microstructure and mechanical properties of new Al-Zn-Mg alloys, J. Alloys Compd., 530(2012), p. 71.
K.B. Hyde, A.F. Norman, and P.B. Prangnell, The effect of cooling rate on the morphology of primary Al3Sc intermetallic particles in Al-Sc alloys, Acta Mater., 49(2001), No. 8, p. 1327.
J. Røyset and N. Ryum, Scandium in aluminium alloys, Int. Mater. Rev., 50(2005), No. 1, p. 19.
Y. Deng, Z.M. Yin, and F.G. Cong, Intermetallic phase evolution of 7050 aluminum alloy during homogenization, Intermetallics, 26(2012), p. 114.
X.M. Li and J.J. Yu, Modeling the effects of Cu variations on the precipitated phases and properties of Al-Zn-Mg-Cu alloys, J. Mater. Eng. Perform., 22(2013), No. 10, p. 2970.
S.K. Maloney, K. Hono, I.J. Polmear, and S.P. Ringer, The chemistry of precipitates in an aged Al-2.1Zn-1.7Mg at.% alloy, Scripta Mater., 41(1999),No.10, p. 1031.
M. R. Clinch, S. J. Harris, W. Hepples, N. J. H. Holroyd, M. J. Lawday, and B. Noble, Influence of zinc to magnesium ratio and total solute content on the strength and toughness of 7xxx series alloys, Mater. Sci. Forum, 519(2006), p. 339.
H.J. Wang, J. Xu, Y.L. Kang, M.G. Tang, and Z.F. Zhang, Study on inhomogeneous characteristics and optimize homogenization treatment parameter for large size DC ingots of Al-Zn-Mg-Cu alloys, J. Alloys Compd., 585(2014), p. 19.
O.N. Senkov, R.B. Bhat, S.V. Senkova, and J.D. Schloz, Microstructure and properties of cast ingots of Al-Zn-Mg-Cu alloys modified with Sc and Zr, Metall. Mater. Trans. A, 36(2005), No. 8, p. 2115.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Liu, T., He, Cn., Li, G. et al. Microstructural evolution in Al-Zn-Mg-Cu-Sc-Zr alloys during short-time homogenization. Int J Miner Metall Mater 22, 516–523 (2015). https://doi.org/10.1007/s12613-015-1101-3
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12613-015-1101-3