Abstract
Nanocellulose antioxidant (Aox-NCC) was used as reinforcement and crosslinking agent in nitrile butadiene rubber (NBR) composites. The crosslinking density and volume of rubber bonded in the matrix were increased up to 3 phr and no significant improvement between 4 phr and 5 phr was recorded. The interactions of gallic acid and NCC was found to occur between the -OH and -COOH groups, as revealed by Fourier Transform Infra-Red (FTIR) and Nuclear Magnetic Resonance (NMR) analysis. Crystallinity index of Aox-NCC was increased more than 11 %, recorded by X-ray diffraction (XRD) analysis. Meanwhile, the thermal stability of Aox-NCC was increased 30°C, analyzed by thermogravimetry (TG). With the addition of 3 phr Aox-NCC, tensile strength and modulus at 500 % for NBR composites were increased significantly up to 20 %. There was no significant improvement on modulus at 100 %, modulus at 300 %, elongation at break and tear strength. The degradability of NBR composites within 6 months period was improved significantly at 5 phr of Aox- NCC. Increase in carbonyl group after soil burial test with the existence of cracks, voids and degradable parts of NBR composites were revealed. This demonstrated that, Aox-NCC plays a secure function to reinforce NBR composites.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
P. Lu and Y.-L. Hsieh, Carbohydr. Polym., 82, 329 (2010).
X. Wang, P. Qu, and L. Zhang, Fiber. Polym., 15, 302 (2014).
A. L. S. S. Pereira, D. M. do Nascirnento, M. D. M. M. Souza, J. P. S. S. Moraisd, N. F. Vasconcelos, J. P. A. A. Feitosa, A. I. S. S. Brigida, and M. D. Rosa, Carbohydr. Polym., 112, 165 (2014).
J. Araki, Soft Mater., 9, 4125 (2013).
K.-Y. Lee, Y. Aitomäki, L. A. Berglund, K. Oksman, and A. Bismarck, Compos. Sci. Technol., 105, 15 (2014).
L. V. Abad, L. S. Relleve, C. T. Aranilla, A. K. Aliganga, C. M. San Diego, and A. M. dela Rosa, Polym. Degrad. Stabil., 76, 275 (2002).
K. M. Z. Z. Hossain, N. Sharif, N. Dafader, M. Haque, and A. Chowdhury, ISRN Polym. Sci., 2013 (2013).
A. Ikram, M. Ma Azam, M. Amir Hashim, M. Fauzi, A. Shamsul Bahri, and S. Kamaruzaman, J. Rubber Res., 8, 220 (2005).
R. N. Phalen, T. Le, and W. K. Wong, J. Occup. Environ. Hyg., 11, 716 (2014).
M. M. Aliabadi, G. Naderi, S. J. Shahtaheri, A. R. Forushani, I. Mohammadfam, and M. Jahangiri, Iran. Polym. J., 23, 289 (2014).
Z. Wei, Y. L. Lu, Y. Meng, and L. Q. Zhang, J. Appl. Polym. Sci., 124, 4564 (2012).
Y. K. Chen, C. H. Xu, and Y. P. Wang, J. Reinf. Plast. Compos., 31, 705 (2012).
C. Sirisinha and N. Prayoonchatphan, Plast. Rubber Compos., 30, 24 (2001).
M. M. Salehi, T. Khalkhali, and A. A. Davoodi, Polym. Sci. Ser. A, 58, 567 (2016).
V. K. Singh, A. Shukla, M. K. Patra, L. Saini, R. K. Jani, S. R. Vadera, and N. Kumar, Carbon, 50, 2202 (2012).
D. E. El-Nashar and E. M. Sadek, High Perform. Polym., 24, 664 (2012).
A. Mohamed, T. Ardyani, S. A. Bakar, P. Brown, M. Hollamby, M. Sagisaka, and J. Eastoe, Adv. Colloid Interface Sci., 230, 54 (2016).
L. D. Perez, M. A. Zuluaga, T. Kyu, J. E. Mark, and B. L. Lopez, Polym. Eng. Sci., 49, 866 (2009).
P. A. Carson, “Hazardous Chemicals Handbook”, Butterworth-Heinemann, 2002.
X. Ge, M. C. Li, X. X. Li, and U. R. Cho, Appl. Clay Sci., 118, 265 (2015).
M. Liu, Q. Peng, B. Luo, and C. Zhou, Eur. Polym. J., 68, 190 (2015).
X. Cao, C. Xu, Y. Wang, Y. Liu, Y. Liu, and Y. Chen, Polym. Test., 32, 819 (2013).
I. Shahabi-Ghahafarrokhi, F. Khodaiyan, M. Mousavi, and H. Yousefi, Fiber. Polym., 16, 529 (2015).
W. T. Wulandari, A. Rochliadi, and I. M. Arcana, IOP Conf. Ser. Mater. Sci., 107, 012045 (2016).
X. Luo and X. Wang, BioResources, 12, 5826 (2017).
M. R. K. K.Sofla, R. J. Brown, T. Tsuzuki, and T. J. Rainey, Adv. Nat. Sci.-Nanosci Nanotechnol., 7, 035004 (2016).
S. Y. Oh, D. I. Yoo, Y. Shin, and G. Seo, Carbohydr. Res., 340, 417 (2005).
A. de Cristo Soares Alves, R. M. Mainardes, and N. M. Khalil, Mater. Sci. Eng. C-Mater. Biol. Appl., 60, 126 (2016).
S.-D. Yoon, Y.-M. Kim, B. I. Kim, and J.-Y. Je, J. Photochem. Photobiol. B-Biol., 176, 145 (2017).
A. El Oudiani, Y. Chaabouni, S. Msahli, and F. Sakli, Carbohydr. Polym., 86, 1221 (2011).
N. Wang, E. Ding, and R. Cheng, Polymer, 48, 3486 (2007).
T. Fattahi Meyabadi, F. Dadashian, G. Mir Mohamad Sadeghi, and H. Ebrahimi Zanjani Asl, Powder Technol., 261, 232 (2014).
D. Singh, M. Singh Maniyari Rawat, A. Semalty, and M. Semalty, Lett. Drug Des. Discov., 8, 284 (2011).
L. C. Yeng, M. U. Wahit, and N. Othman, J. Teknol., 75, 107 (2015).
J. I. Morán, V. A. Alvarez, V. P. Cyras, and A. Vázquez, Cellulose, 15, 149 (2008).
M. Przybyłek, M. Bakar, M. Mendrycka, U. Kosikowska, A. Malm, M. Worzakowska, T. Szymborski, and K. Kędra-Królik, Mater. Sci. Eng. C-Mater. Biol. Appl., 76, 269 (2017).
W. J. Chen, J. Gu, and S. H. Xu, Express Polym. Lett., 8, 659 (2014).
V. Baheti, R. Mishra, J. Militky, and B. K. Behera, Fiber. Polym., 15, 1500 (2014).
C. Sareena, M. Sreejith, M. Ramesan, and E. Purushothaman, J. Reinf. Plast. Compos., 33, 412 (2014).
D. A. Baeta, J. A. Zattera, M. G. Oliveira, and P. J. Oliveira, Braz. J. Chem. Eng., 26, 23 (2009).
S. Rajesh Kumar, P. M. Asseref, J. Dhanasekaran, and S. K. Mohan, RSC Adv., 4, 12526 (2014).
M. M. Hassan, R. O. Aly, A. El-Ghandour, and H. A. Abdelnaby, J. Elastomer Plast., 45, 77 (2013).
L. M. Wu, D. S. Tong, L. Z. Zhao, W. H. Yu, C. H. Zhou, and H. Wang, Appl. Clay Sci., 95, 74 (2014).
M. H. Izmar, M. M. Afiq, and A. R. Azura, Compos. Pt. BEng., 43, 2746 (2012).
T. W. Cho and S. W. Kim, J. Appl. Polym. Sci., 121, 1622 (2011).
M. Musioł, H. Janeczek, S. Jurczyk, I. Kwiecień, M. Sobota, A. Marcinkowski, and J. Rydz, Fiber. Polym., 16, 1362 (2015).
Y. Zhou, M. Fan, L. Chen, and J. Zhuang, Compos. Pt. BEng., 76, 180 (2015).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Taib, M.N.A.M., Yehye, W.A. & Julkapli, N.M. Influence of Crosslinking Density on Antioxidant Nanocellulose in Bio-degradation and Mechanical Properties of Nitrile Rubber Composites. Fibers Polym 20, 165–176 (2019). https://doi.org/10.1007/s12221-019-8575-y
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12221-019-8575-y