Abstract
The microstructure of a Pt-modified γ-γ′ bond coat on CM-247LC Ni-base superalloy has been examined and its cyclic oxidation performance at 1100 °C in air is comparatively evaluated with that of a conventional β-(Ni, Pt)Al bond coat. The γ-γ′ bond coat was effective in imparting oxidation resistance to the CM-247LC alloy for about 100 h, whereas the β coating imparted oxidation resistance for significantly longer duration of about 1000 h. The nature of surface damage that occurred to the γ-γ′ coating during oxidation has been compared with that reported in the case of β coating.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Alam M Z, Chatterjee D, Venkataraman B, Varma V K and Das D K 2010a Mater. Sci. Eng. A527 6211
Alam M Z, Hazari N, Varma V K and Das D K 2010b Metall. Mater. Trans. A42 4064
Allam I M, Akuezue H C and Whittle D P 1980 Oxid. Met. 14 517
Angenete J and Stiller K 2002 Surf. Coat. Technol. 150 107
Bose Sudhangshu 2007 High temperature coatings (Oxford: Butterworth-Heinemann Publishers), p 71
Chen J H and Little J A 1997 Surf. Coat. Technol. 92 69
Chen M W, Glynn M L, Ott R T, Hufnagel T C and Hemker K J 2003 Acta Mater. 51 4279
Das D K, Roy M, Singh V and Joshi S V 1999 Mater. Sci. Technol. 15 1199
Das D K, Singh V and Joshi S V 2000a J. Metals e52 http://www.tms.org/pubs/journals/JOM/0001/Das/Das-0001.html
Das D K, Singh V and Joshi S V 2000b Metall. Mater. Trans. A 31A 2037
Das D K, Gleeson B, Murphy K S, Ma S and Pollock T M 2009 Mater. Sci. Technol. 25 300
Das D K, Singh V and Joshi S V 2003 Mater. Sci. Technol. 19 695
Deb P, Boone D H and Manley T F 1987 J. Vac. Sci. Technol. A5 3366
De Wit J H W and van Manen P A 1994 Mater. Sci. Forum 154 109
Farrell M S, Boone D H and Streiff R 1987 Surf. Coat. Technol. 32 69
Felten E J and Petit F S 1976 Oxid. Met. 10 189
Gleeson B, Wang W, Hayashi S and Sordelet D 2004a Mater. Sci. Forum 461–464 213
Gleeson B, Sordelet D and Wang W 2004b US Patent 20040229075 http://www.freepatentsonline.com/20040229075.html
Gleeson B, Li B, Sordelet D J and Brindley W J 2006 US Patent 20060127695 http://www.freepatentsonline.com/20060127695.html
Haynes J A, Pint B A, Zhang Y and Wright I G 2008 Surf. Coat. Technol. 203 413
Haynes J A, Pint B A, Zhang Y and Wright I G 2009 Surf. Coat. Technol. 204 816
Hazel B T, Darolia R, Boutwell B A and Wortman D J 2007 US Patent 7247393 http://www.freepatentsonline.com/7247393.html
Pennefather R C and Boone D H 1995 Surf. Coat. Technol. 76–77 47
Pichoir R 1978 Materials and coatings to resist high temperature corrosion (eds) D R Holmes and A Rahmel (London: Applied Science Publishers) p 271
Pint B A 2004 Surf. Coat. Technol. 188–189 71
Purvis A L and Warnes B M 2008 Surf. Coat. Technol. 146–147 1
Smialek J L and Hehemann R F 1973 Metall. Trans. 4 1571
Stacy J P, Zhang Y, Pint B A, Haynes J A, Hazel B T and Nagaraj B A 2007 Surf. Coat. Technol. 202 632
Strang A and Lang E 1982 High temperature alloys for gas turbines (ed.) R Brunetand (Holland: D. Reidel Publishing Company) p 469
Sun J H, Jang H C and Chang E 1994 Surf. Coat. Technol. 64 195
Svensson H, Christensen M, Knutsson P, Wahnström G and Stiller K 2009 Corros. Sci. 51 539
Tatlock G J and Hurd T J 1984 Oxid. Met. 22 201
Tawancy H M, UI-Hamid A, Abbas N M and Aboelfotoh M O 2008 J. Mater. Sci. 43 2978
Wu R T, Kawagishi K, Harada H and Reed R C 2008 Acta Mater. 56 3622
Zhang Y, Ballard D A, Stacy J P, Pint B A and Haynes J A 2006 Surf. Coat. Technol. 201 3857
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Alam, M.Z., Hazari, N. & Das, D.K. Microstructure and oxidation performance of a γ-γ′ Pt-aluminide bond coat on directionally solidified superalloy CM-247LC. Bull Mater Sci 37, 1551–1561 (2014). https://doi.org/10.1007/s12034-014-0110-6
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12034-014-0110-6