Hydration shrinkage generated by cement hydration is the cause of autogenous shrinkage of high strength concrete. It may result in the volume change and even cracking of mortar and concrete. According to the data analysis in a series of experimental studies, the influence of ultra-fine fly ash on the hydration shrinkage of composite cementitious materials was investigated. It is found that ultra-fine fly ash can reduce the hydration shrinkage of cement paste effectively, and the more the ultra-fine fly ash, the less the hydration shrinkage. Compared with cement paste without the ultra-fine fly ash, the shrinkage ratio of cement paste reduces from 23.4% to 39.7% when the ultra-fine fly ash replaces cement from 20% to 50%. Moreover, the microscopic mechanism of the ultra-fine fly ash restraining the hydration shrinkage was also studied by scanning electron microscopy, X-ray diffraction and hydrated equations. The results show that the hydration shrinkage can be restrained to a certain degree because the ultra-fine fly ash does not participate in the hydration at the early stage and the secondary hydration products are different at the later stage.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
WU Zhong-wei, LIAN Hui-zen. High Performance Concrete [M]. Beijing: China Railway Press, 1999. (in Chinese)
FENG Nai-qian. High Performance Concrete [M]. Beijing: China Architectural Industry Press, 1996. (in Chinese)
Tazawa E, Miyazawa S. Influence of cement and admixture on autogenous shrinkage of cement paste[J]. Cement and Concrete Research, 1995, 25(2): 281–287.
Payá J, Monzó J, Borrachero M V, et al. Mechanical treatment of fly ashes (Part I): physico-chemical characterization of ground fly ashes[J]. Cement and Concrete Research, 1995, 25(7): 1469–1479.
Payá J, Monzó J, Borrachero M V, et al. Mechanical treatment of fly ashes (Part II): particle morphologies in ground fly ashes (GFA) and workability of GFA-cement mortars[J]. Cement and Concrete Research, 1996, 26(2): 225–235.
SEN Dan-shen. Fly Ash Concrete [M]. Beijing: China Railway Press, 1989. (in Chinese)
QIAN Jue-shi. Fly Ash Performance and Fly Ash Concrete [M]. Beijing: Science Press, 2002, 5. (in Chinese)
YAN Wu-nan, PU Xin-chen, WANG Chuan, et al. Study on chemical shrinkage and drying shrinkage of ultra-high strength concrete[J]. Construction Technology, 1999, 28(5): 17–18. (in Chinese)
YANG Dong-shen. Cement Technical Test [M]. Beijing: China Architectural Industry Press, 1986. (in Chinese)
Tazawa E, Miyazawa S, Kasai T. Chemical shrinkage and autogenous shrinkage of hydrating cement paste[J]. Cementand Concrete Research, 1995, 25(2): 288–292.
SUN Wei, HUANG Wen-xi, MIN Pan-rong. Cement Technology [M]. Beijing: China Architectural Industry Press, 1986. (in Chinese)
Taylor H F. The Chemistry of Cements [M]. London and New York: Academic Press, 1964.
ZHOU Shi-qiong, LI Yi-jin, YIN Jian, et al. Research on properties of Ultra-fine Fly Ash[J]. Journal of the Chinese Ceramic Society, 2003, 31(5): 513–516. (in Chinese)
YIN Jian, ZHOU Shi-qiong, XIE You-jun, et al. Investigation on compounding and application of C80–C100 high-performance[J]. Cement and Concrete Research, 2002, 32(2): 173–177.
Lee F M, Tang M S. Cement and Concrete Chemistry[M]. Beijing: China Architectural Industry Press, 1980. (in Chinese)
Author information
Authors and Affiliations
Corresponding author
Additional information
Foundation item: Project(96-920-39-02) supported by the National Key Program of the 9th Five Year Plan of China
Rights and permissions
About this article
Cite this article
Gao, Yl., Zhou, Sq. Influence of ultra-fine fly ash on hydration shrinkage of cement paste. J Cent. South Univ. Technol. 12, 596–600 (2005). https://doi.org/10.1007/s11771-005-0129-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11771-005-0129-3