Abstract
The hydration mechanism of low quality fly ash in cement-based materials was investigated. The hydration heat of the composite cementitious materials was determined by isothermal calorimetry, and the hydration products, quantity, pore structure and morphology were measured by X-ray diffraction (XRD), thermalgravity-differential thermal analysis (TG-DTA), mercury intrusion porosimetry (MIP) and scanning electron microscopy (SEM), respectively. The results indicate that grinding could not only improve the physical properties of the low quality fly ash on particle effect, but also improve hydration properties of the cementitious system from various aspects compared with raw low quality fly ash (RLFA). At the early stage of hydration, the low quanlity fly ash acts as almost inert material; but then at the later stage, high chemical activity, especially for ground low quality fly ash (GLFA), could be observed. It can accelerate the formation of hydration products containing more chemical bonded water, resulting in higher degree of cement hydration, thus denser microstructure and more reasonable pore size distribution, but the hydration heat in total is reduced. It can also delay the induction period, but the accelerating period is shortened and there is little influence on the second exothermic peak.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
QIAN Jue-shi. Characteristics of fly ash and fly ash concrete [M]. Beijing: Science Press, 2002: 1–3. (in Chinese)
LIU Shu-hua, FANG kun-he. Comprehensive utilization of fly ash [J]. Journal of Fujian Building Materials, 2008(2): 8–9. (in Chinese)
Building materials branch of architectural society of China. Industry development and engineering application of building materials [R]. Beijing: China Architecture and Building Press, 2011: 27–32. (in Chinese)
LU Hou-gen. Introductory theory of powder engineering [M]. Shanghai: Tongji University Press, 1993: 4–7. (in Chinese)
QIN Wei-zu. The application of fly ash in concrete [J]. Journal of Comprehensive Utilization of Fly Ash, 2000(3): 1–7. (in Chinese)
LANGLEY W S, CARETTE G G, MALHOTRA V M. Structural concrete incorporating high volumes of ASTM class F fly ash [J]. ACI Materials Journal, 1989, 86(5): 507–514.
DUNSTAN M R H. Fly ash as the “fourth ingredient” in concrete mixtures, fly ash, silica fume, slag, and natural pozzolanics in Concrete [R]. Detroit, ACI SP -91, 1986: 171–197.
LANGAN B W, WENG K, WARD M A. Effect of silica fume and fly ash on heat of hydration of Portland cement [J]. Cement and Concrete Research, 2002, 32(6): 1045–1051.
SAKAI E, MIYAHARA S, OHSAWA S. Hydration of fly ash cement [J]. Cement and Concrete Research, 2005, 35(5): 1135–1140.
FAN Y M, YIN S H, WEN Z Y, ZHONG J Y. Activation of fly ash and its effects on cement properties [J]. Cement and Concrete Research, 1999, 29(3): 467–472.
WANG Lei, HE Zhen. Characterization of pozzolanic reaction and its effect on the C-S-H gel in fly ash-cement paste [J]. Journal of Wuhan University of Technology (Material Science), 2011, 26(3): 319–324.
LAM L, WONG Y L, POON C S. Effect of fly ash and silica fume on compressive and fracture behaviors of concrete [J]. Cement and Concrete Research, 1998, 28(2): 271–283.
KONG Ya-ning, XIE Guo-shuai, LIU Shu-hua. Utilization of low-quality fly ash in concrete [J]. Concrete, 2012(6): 74–76. (in Chinese)
MALTAIS Y, MARCHAND J. Influence of curing temperature on cement hydration and mechanicals of fly ash mortars [J]. Cement and Concrete Research, 1997, 27(4): 1009–1020.
DESCHNER F. Hydration of Portland cement with high replacement by siliceous fly ash [J]. Cement and Concrete Research, 2012, 42(6): 1389–1400.
POON C S, LAM L, WONG Y L. A study on high strength concrete prepared with large volumes of low calcium fly ash [J]. Cement and Concrete Research, 2000, 30(2): 447–455.
MALTAIS Y, MARCHAND J. Influence of curing temperature on cement hydration and mechanicals of fly ash mortars [J]. Cement and Concrete Research, 1997, 27(4): 1009–1020.
WANG Qiang, FENG Jing-jing, YAN Pei-yu. The microstructure of 4-year-old hardened cement-fly ash paste [J]. Construction and Building Materials, 2012, 29(1): 114–119.
RODGER S A, GROVES G W. The microstructure of tricalcium silicate/pulverized-fuel ash blended cement pastes [J]. Cement Research, 1988(1): 84–91.
DESCHNER F. Hydration of portland cement with high replacement by siliceous fly ash [J]. Cement and Concrete Research, 2012, 42(7): 1389–1400.
MEHTA P K, MONTERIO P J M. Concrete, microstructure, properties and materials [M]. 3rd ed. London, McGraw-Hill, 2006: 230–237.
LOTHENBACH B, SCRIVENER K, HOOTON R D. Supplementary cementitious materials [J]. Cement and Concrete Research, 2011, 41(6): 1244–1256.
Author information
Authors and Affiliations
Corresponding author
Additional information
Foundation item: Project(51208391) supported by the National Natural Science Foundation of China
Rights and permissions
About this article
Cite this article
Liu, Sh., Kong, Yn. & Wang, L. Hydration mechanism of low quality fly ash in cement-based materials. J. Cent. South Univ. 21, 4360–4367 (2014). https://doi.org/10.1007/s11771-014-2436-z
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11771-014-2436-z