Abstract
Eight investment castings of Inconel 713C superalloy were fabricated, varying in the melt-pouring temperature, from 1400 to 1520 °C, and CoAl2O4 inoculant content, 0 or 5 wt.%, in the primary coat. Their influence on grain size on tensile and creep properties was investigated. The best combination of yield stress (815 MPa) and elongation (A4 = 7.65%) at ambient temperature was obtained in surface-modified castings poured from 1520 °C. The longest time to rupture was for the unmodified castings (76.8 h) poured from 1520 °C, while for the modified variant, the time to rupture was lower around, 7.4 h, which was still a satisfactory value. During tensile testing, microcracks were formed in large eutectic γ′, carbides and borides, due to the accumulation of stress at interfaces with the matrix. During creep, N-type rafting of γ′ precipitates and phase transformation MC + γ → γ′ + M23C6 took place.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
Precipitation-strengthened nickel-based superalloys are widely used in the manufacturing of turbine blades and vanes, which operate in hot sections, both in turbochargers of combustion engines and turbofan jet engines (Ref 1, 2). One of the most important representatives of this group is Inconel 713C. This alloy is also extensively used in the automotive, power and oil and gas industries due to a unique combination of strength at operating temperature and excellent hot corrosion resistance. The very good castability, low-cycle fatigue resistance (LCF) and microstructural stability determine the wide use of the Inconel 713C for low-pressure turbine (LPT) guide vanes in GP7200 engines (Ref 3,4,5,6). Usually, superalloys are heat-treated (solution + aging); however, Inconel 713C achieves sufficiently high properties in the as-cast condition, and so increase in mechanical properties is by optimization of investment casting parameters and composition of the shell mold (Ref 7). Major features of investment castings are macrostructural coarseness and non-uniformity of grain size, which may reduce the fatigue life and reliability of turbine vanes in the intermediate temperature range. The microstructure improvement of cast superalloys may be obtained by more uniform equiaxed grain size (Ref 8,9,10). Desired grain size can be achieved by selection of melt-pouring temperature, preheat of ceramic shell mold, and/or introduction of an inoculant into the primary coat (Ref 11, 12). Grain refinement through the addition of inoculants is an important way to increase the strength of cast polycrystalline superalloys. At a relatively low temperature, the strength of the grain boundary is higher than that of the grain interior and so increasing the area of grain boundaries can increase the strength of superalloys. However, with the increase in operating temperature, the strength of grain boundary decreases more quickly than the grain interior strength. Increasing the grain boundary area can, therefore, lead to a significant reduction in strength. Grain refinement by the addition of inoculants has several benefits, namely a substantially easy operation, no change in production equipment and a very good refining effect (Ref 13, 14). It has been reported (Ref 13, 15,16,17,18) that inoculants have a favorable influence on grain refinement and thus low-temperature mechanical properties. The main aim of this research was to determine the influence of the melt-pouring temperature and the CoAl2O4 inoculant in the prime coat of the shell mold on the structure and mechanical properties of IN713C superalloy castings.
Material and Experimental Procedure
Ni-based superalloy Inconel 713C was used as the casting and the gating system. Result of chemical composition analysis obtained by optical emission spectroscopy is shown in Table 1.
The eight shell molds were fabricated in the Investment Casting Division of Consolidated Precision Products Corp. Each of the disposable wax assemblies consisted of a “carrot”-type shape specimens with dimensions: bottom diameter 23 mm, upper diameter 12 mm and height 90 mm. Four vents were prepared in order to stabilize and strengthen the wax models and also for better wax melting. The wax patterns were injection molded, and then, the ceramic monolithic mold was built up around these patterns by a series of dip coatings (8 layers). Alumina grit was used as the primary stucco. One of the prepared shell molds is shown in Fig. 1. Two prime coats were produced for the casting:
-
(a)
Shell molds no. 1, 3, 5, 7: zircon filler and colloidal silica binder,
-
(b)
Shell molds no. 2, 4, 6, 8: zircon filler and colloidal silica binder plus 5 wt.% of CoAl2O4 inoculant.
The wax patterns were removed from the shell molds in boilerclave and then covered with alumina silicate Fiberfrax® insulation. All molds were then fired to increase the strength and remove the wax residue. Directly before melt-pouring, the molds were placed in a heating chamber preheated to 1000 °C for 100 min. The temperature was controlled by Pt/Pt-Rh thermocouples. The raw ingots were melted in a zirconia crucible placed in a vacuum induction furnace. The Inconel 713C superalloy was inductively melted in a vacuum of 2.9 × 10−3 Pa. The liquid superalloy was poured into molds at four different temperatures: 1400, 1450, 1480 and 1520 °C. A total of 40 specimens were machined for microstructural and mechanical properties investigations. Those for macroscopic and microscopic examinations were mounted in resin, metallographically prepared (grinding and polishing) and finally chemically etched in 50 mL lactic acid, 30 mL nitric acid, 2 mL hydrofluoric acid (macro) and electrochemically (micro) in 10% CrO3. Tensile tests were carried out at ambient temperature according to ASTM E8M-13a standard (Ref 19) using INSTRON 3382 tester, and yield strength and elongation A4 were determined. The geometry of the sample is presented in Fig. 2.
Creep tests were performed on a Walter + Bai AG LFMZ-30 machine in accordance with the requirements of ASTM E139-11 standard (Ref 20). The samples were preheated to 982 °C, annealed for 60 min, and then loaded with an axial force, which produced in their cross sections an initial tensile stress of 151.8 MPa. Two specimens were prepared for creep and two for the tensile testing (for each variant presented in Table 2), and finally, average values were calculated. The solidus temperature of Inconel 713C is 1263 °C (Ref 11), so creep testing was at a high homologous temperature, 0.82.
Results and Discussion
Microstructure of Castings
The microstructures of castings did not reveal casting defects like cracks, porosity and misruns (Fig. 3). The increase in melt-pouring temperature induced a decrease in cooling rate which led to grain growth. The microstructure showed that cobalt aluminate (CoAl2O4) was an effective modifier for Inconel 713C in the whole range of melt-pouring temperatures, especially at 1450 and 1520 °C. Differential thermal analysis of IN713C indicated that the creation of the first γ primary dendrites started at 1342 °C (liquidus) (Ref 11). The solidification finished at 1263 °C, and so liquidus–solidus range is relatively wide, 79 °C. Table 1 indicates that IN713C consists of highly reactive alloying elements like chromium, aluminum, as well as titanium, characterized by high oxygen affinity. During the contact of the primary coat with the liquid alloy, cobalt aluminate was reduced and metallic cobalt was created in accordance with the reactions (Ref 13):
Cobalt from the inoculant was superseded by Al, Cr and Ti, and then, Co fine particles were formed on the internal surfaces of shell molds. Above 450 °C, cobalt and γ (Ni) phase have the same crystallographic structure (face-centered cubic). The lattice constants are aCo = 3.5480 Ǻ and aNi = 3.5805 Ǻ, respectively, which gives a low lattice misfit (Ref 21, 22). In accordance with the equation \( f = \frac{{a_{\text{Ni}} - a_{\text{Co}} }}{{a_{\text{Co}} }} \times 100 \% \), misfit is only 0.9% and Co can act as a good nucleation substrate. The heterogeneous nucleation rate of the cast surface was increased. The modification gave an exothermic reaction during pouring, which prevented the formation of a chill zone structure. It is also important to mention that some other variables have also an influence on the microstructure of superalloys, and consequently on mechanical properties. An increase in the melt-pouring temperature influences strongly the reactivity of the molten alloy with the crucible and filter. Alloys poured from higher temperatures have also a higher concentration of vacancies, which is important for mechanical properties at high homologous temperatures (Ref 1, 2).
Tensile Tests Results and Changes of Microstructure
The results of the tensile tests are shown in Fig. 4. The averaged values calculated are joined by the green line for the modified samples and by the red line for the unmodified. According to the AMS 5391 standard (Ref 23), Inconel 713C castings should be characterized by the following properties: yield strength 689.5 MPa (100 psi) and elongation A4 min. 3%. Yield stress in all samples significantly exceeded the required minimum (Fig. 4a). With the exception of the melt-pouring temperature of 1400 °C, higher average values were obtained for the modified samples. The difference between the highest (830 MPa) and the lowest mean value was around 76 MPa. For unmodified samples, yield stress decreased as the casting temperature increased. The elongation A4 is presented in Fig. 4(b). Relatively low values were measured in unmodified samples poured from 1400 °C. The highest A4 values for both modified and unmodified samples were obtained for 1520 °C pouring temperature. The results of single measurements for melt-pouring temperatures of 1450 and 1480 °C were close to 4% minimum.
Macrostructures of cross-sectioned specimens after the tensile test are shown in Fig. 5. The complex character of cracking indicated structural heterogeneity of the castings. Conventionally, higher yield strength was associated with finer grain size. High strength also results from a high volume fraction of the γ′ precipitates, narrow matrix channels and the solid solution strengthening effect in both matrix and γ′ phases. The total content of γ′ formers exceeded 6.6 wt.%, which is a relatively high value in comparison with other equiaxed superalloys widely used in aircraft engines (Ref 24). Plastic deformation of the superalloys occurs through dislocations slip in the matrix channels. A high volume fraction of the γ′ phase and the substantial local grain-boundary curvature in castings effectively block their movement.
The microstructural changes, the location of EDS points and results of the analysis are presented in Fig. 6 and Table 3. Numerous cracks have been observed inside many large precipitates. The results of analysis no. 1 and 2 revealed the increased concentration of Ni and Al which confirmed the presence of eutectic γ′. Precipitates strongly enriched in Nb, Ti and Mo were MC-type carbides (points 3 and 4), while the precipitates with a total concentration of around 75 at.% of Mo and Cr were M3B2 borides (points 5 and 6). The uncracked precipitates along interdendritic spaces were Ni7Zr2 intermetallic compounds formed from the residual liquid phase through the eutectic transformation. The deformation of γ′ phase takes place by slip on systems {111}<110>. The dislocation in γ′ phase has a length of Burger vector a√2, which is twice as long as in γ. Dislocation slip in the γ′ by one length of the Burgers vector disturbs the lattice order. This leads to the formation of a high energy defect, so dislocation movement in the γ′ is more difficult (Ref 25). The microstructural observations and tensile tests results indicated that the deformation of IN713C was dominated by the type of primary precipitates and dislocation movement in the matrix. Due to the high stiffness of eutectic γ′ phase, carbides and borides, accumulation of created dislocations occurred in the γ matrix and interfaces. Microcracks of large precipitates confirmed the stress concentration along interfaces with the matrix. In the Ni-based superalloys, interfaces γ/MC-type carbides and γ/eutectic γ′ are areas of increased stress concentration (Ref 26, 27).
Creep Tests Results and Changes of Microstructure
The AMS5391 (Ref 23) standard indicates that with the assumed test parameters the time to rupture should be at least 30 h. The creep properties of castings tested at 982 °C and 151.8 MPa as a function of melt-pouring temperature are presented in Fig. 7(a) and (b). The creep life was improved with increasing pouring temperature, and in addition, the mean time to rupture for each melt-pouring temperature was higher for the unmodified samples (Fig. 7a). The mean time to rupture for unmodified and modified castings poured from 1400 °C was 48.1 and 46.0 h, respectively. Increasing the pouring temperature by 120 °C contributed to the increase in these values by more than 50%, namely to 76.8 h and 69.4 h. The minimum value defined by the standard has been exceeded twice. The effect of cobalt aluminate was most pronounced at 1480 °C, with a difference in mean time to rupture over 11 h. Depending on the temperature and the load, three creep ranges were observed. At high temperature and low stress (982 °C/151.8 MPa), curves showed a short primary stage and steady state characterized by a plateau and pronounced strain at the tertiary stage.
The steady-state creep rate decreased with an increase in the melt-pouring temperature, both for the unmodified and the modified castings (Fig. 7b). The highest creep rate for the modified variant was 0.035%/h (1450 °C), while the lowest 0.0245%/h (1520 °C). In the unmodified castings, the difference between the highest 0.0306%/h (1400 °C) and the lowest creep rate (1520 °C) was 0.0093%/h. The creep rate of modified samples was higher for each melt-pouring temperature, although the value calculated for the 1520 °C variant was the second lowest in the entire study. The comparison of creep curves which represents variants with the highest (modified at 1450 °C) and the lowest (unmodified at 1520 °C) steady-state creep rate is presented in Fig. 7(c). Generally, the creep mechanisms can be divided into dependent and independent of the grain size (Ref 1, 8, 28). In both cases, the creep rate is related to the diffusion rate. Creep diffusion via formation and disappearance of vacancies at the boundaries depends strongly on grain size, but dislocation creep which occurs inside the grains is independent of their size. Under constant stress and temperature, as the grain size increases, the contribution of dislocation creep drops rapidly, while creep rate through a diffusion mechanism decreases. The microstructure of crept Inconel 713C is shown in Fig. 8. Intergranular cracks with numerous secondary cracks and voids were observed. The main microstructural change in the dendrite cores was directional growth (rafting) of γ′ precipitates (Fig. 9). The rafting process of γ′ phase in Ni-based superalloys is induced by several factors, namely the value and direction of the external stress, the value of misfit coefficient and the elastic constant of γ′ and γ phases (Ref 29).
The morphology change in γ′ phase was N-type rafting, in which the lamellae of γ′ phase were perpendicular to the applied tensile stress direction. Lattice misfit is defined as \( \delta = 2\left( {a_{{\gamma^{\prime } }} - a_{\gamma } } \right)/\left( {a_{{\gamma^{\prime}}} + a_{\gamma } } \right) \), where aγ′ and aγ are lattice constants (Ref 31). When lattice misfit is negative, it can be concluded that the rafting is a sequential process (Ref 32, 33). At the beginning, plastic deformation of the matrix takes place, which leads to a loss of coherency at the γ/γ′ interface and decrease in the misfit stress. Tensile stresses act in the γ′ precipitates parallel to the matrix channels. Compressive stresses in the surfaces of matrix channels balance these forces, and moreover, they are much higher than the tensile stress components perpendicular to the channels. The combination of internal stresses yields a specific value for the hydrostatic stress, which is well known to directly affect the chemical potential of atoms (Ref 30). If the superalloy is not loaded (σ = 0), the tendency to reduce the overall γ/γ′ interface energy leads to non-directional coarsening of cubic precipitates (Fig. 10a). In this case, the chemical potentials of the γ′ phase at points 1 and 2 are equal. When the external stress is applied, the stress components at positions 1 and 2 are not the same (Fig. 10b). The local stresses inside material are modified in the direction of the applied external stress. The internal stresses change to perpendicular to the external stress axis because of the difference in values of Poisson’s ratio of the matrix and the precipitates. The effective stress in the perpendicular channels of the matrix is greater than in the parallel channels, which favors diffusion processes and dislocation movement in the perpendicular channels. The result is rafting of γ′ perpendicularly to the external tensile direction.
Morphology of constituents and location of EDS lines are shown in Fig. 11 and 12. Microstructural observations in interdendritic spaces revealed much more complex changes, and so selected regions were subjected to EDS analysis. In Fig. 12(a), the enrichment in Nb and Ti was observed, which suggests that it was a primary Nb-rich carbide surrounded by the coarse-grained γ′. M3B2 boride enriched in Mo and Cr (Fig. 12b) did not transform during creep. Intermetallic compound Ni7Zr2 (Fig. 12c) was also stable during exposure to 982 °C. Inside interdendritic γ′ phase, near the MC-type carbides, precipitates strongly enriched in Cr were observed (Fig. 12d). These precipitates were not present in the as-cast state. In Ni-based superalloys, MC-type carbides can decompose during exposure to high temperature by one of the transformations: MC + γ → M23C6 + γ′, MC + γ → M6C + γ′ and/or MC + γ → M23C6 + η. Despite intensive observation, M6C carbide and intermetallic η phase were not observed in IN713C, which was earlier reported by (Ref 6).
Conclusions
Melt-pouring temperature and the composition of the primary coat in the shell mold influenced grain size of IN713C castings and consequently their mechanical properties both at ambient temperature and 982 °C. This work combines two variants of the primary coat, without and with the addition of 5% CoAl2O4 inoculant, and also four pouring temperatures from 1400 to 1520 °C. The main conclusions of the research are:
-
(a)
The compound CoAl2O4 is suitable for surface modification of IN713C castings. The highest grain refinement was obtained in castings poured between 1450 and 1520 °C,
-
(b)
The mean yield strength in unmodified samples decreased with the increase in melt-pouring temperature, while elongation A4 had the opposite relation. The highest mean yield strength (815 MPa) was obtained in modified samples poured from 1520 °C,
-
(c)
The time to rupture increased with the increase in melt-pouring temperature both for unmodified and modified castings. The difference between the lowest and the highest time to rupture (72.8 h) for unmodified castings was 28.7 h. Modified castings were characterized by a similar difference between the lowest and highest time to rupture (69.4 h) at 1520 °C, equal to 26.4 h,
-
(d)
The changes in microstructure during tensile testing included microcracking of large strengthening phases,
-
(e)
During creep, N-type rafting of γ′ and transformation of MC carbides to M23C6 carbides in interdendritic spaces (MC + γ → M23C6 + γ′) were observed,
-
(f)
The best combination of mechanical properties, for application in intermediate service temperature (LPT section) in jet engines, was for modified IN713C with 1520 °C pouring temperature. The temperature is below the creep range, where stresses originating from centrifugal loads are high. In this case, the best combination of tensile strength and creep resistance is required.
References
R. Reed, The Superalloys: Fundamentals and Applications, Cambridge University Press, Cambridge, 2006
H. Long et al., Microstructural and Compositional Design of Ni-Based Single Crystalline Superalloys—A Review, J. Alloys Compd., 2018, 743, p 203–220. https://doi.org/10.1016/j.jallcom.2018.01.224
Ł. Rakoczy and R. Cygan, Analysis of Temperature Distribution in Shell Mould During Thin-Wall Superalloy Casting and its Effect on the Resultant Microstructure, Arch. Civ. Mech. Eng., 2018, 18, p 1441–1450. https://doi.org/10.1016/j.acme.2018.05.008
F. Zupanic et al., Structure of Continuously Cast Ni-Based Superalloy Inconel 713, J. Alloys Compd., 2001, 329, p 290–297. https://doi.org/10.1016/S0925-8388(01)01676-0
M. Azadi et al., Effects of Solutioning and Ageing Treatments on Properties of Inconel-713C Nickel-Based Superalloy Under Creep Loading, Mater. Sci. Eng. A, 2018, 711, p 195–204
H. Matysiak et al., The Microstructure Degradation of the IN 713C Nickel-Based Superalloy After the Stress Rupture Tests, J. Mater. Eng. Perform., 2014, 23(9), p 3305–3313. https://doi.org/10.1007/s11665-014-1123-4
A. Szczotok and H. Matysiak, Influence of Constituents of Shell Mold on the Morphology and Chemical Composition of Carbides Occurring in IN 713C Superalloy Castings, J. Mater. Eng. Perform., 2014, 23(8), p 2748–2759. https://doi.org/10.1007/s11665-014-1035-3
L. Thébaud et al., Is There an Optimal Grain Size for Creep Resistance in Ni-Based Disk Superalloys?, Mater. Sci. Eng. A, 2018, 716, p 274–283. https://doi.org/10.1016/j.msea.2017.12.104
J. Salvant Canto et al., A Study of Low Cycle Fatigue Life and Its Correlation with Microstructural Parameters in IN713C Nickel Based Superalloy, Mater. Sci. Eng. A, 2018, 718, p 19–32. https://doi.org/10.1016/j.msea.2018.01.083
K. Young-Wang et al., A Numerical Model to Predict Mechanical Properties of Ni-Base Disk Superalloys, Int. J. Plast., 2018, 110, p 123–144. https://doi.org/10.1016/j.ijplas.2018.06.011
H. Matysiak et al., The Influence of the Melt-Pouring Temperature and Inoculant Content on the Macro and Microstructure of the IN713C Ni-Based Superalloy, J. Miner., 2016, 68(1), p 185–197. https://doi.org/10.1007/s11837-015-1672-5
C.H. Konrad et al., Determination of Heat Transfer Coefficient and Ceramic Mold Material Parameters for alloy IN738LC Investment Castings, J. Mater. Proc. Technol., 2011, 211, p 181–186. https://doi.org/10.1016/j.jmatprotec.2010.08.031
W. Jin et al., Grain Refinement of Superalloy IN100 Under the Action of Rotary Magnetic Fields and Inoculants, Mat. Let., 2008, 62, p 1585–1588. https://doi.org/10.1016/j.matlet.2007.09.028
F. Wang et al., Preparation of Inoculants Used in Superalloy and Analysis of the Atomic Matching Models, J. Mater. Sci. Technol., 2013, 29(4), p 387–392. https://doi.org/10.1016/j.jmst.2013.02.007
L. Liu et al., Grain Refinement of Superalloy K4169 by Addition of Refiners: Cast Structure and Refinement Mechanisms, Mater. Sci. Eng. A, 2005, 394, p 1–8. https://doi.org/10.1016/j.msea.2004.10.005
B. Du et al., Effects of Grain Refinement on the Microstructure and Tensile Behavior of K417G Superalloy, Mater. Sci. Eng. A, 2015, 623, p 59–67. https://doi.org/10.1016/j.msea.2014.11.041
C.N. Wei et al., A Study of IN-713LC Superalloy Grain Refinement Effects on Microstructure and Tensile Properties, Mater. Chem. Phys., 2003, 80, p 89–93
B. Du et al., Effects of grain size on the high-cycle fatigue behavior of IN792 superalloy, Mater. Des., 2015, 65, p 57–64. https://doi.org/10.1016/j.matdes.2014.08.059
ASTM E8M-13a Standard—Standard Test Methods for Tension Testing of Metallic Materials
ASTM E139-11—Standard Test Methods for Conducting Creep, Creep-Rupture, and Stress-Rupture Tests of Metallic Materials
R.W.G. Wyckoff, Crystal Structures: Cubic Closest Packed, Interscience, New York, 1963
S. Ackerbauer et al., The Constitution of the Ternary System Fe-Ni-Si, Intermet, 2009, 17(6), p 414–420. https://doi.org/10.1016/j.intermet.2008.11.016
AMS 5391 standard—Nickel Alloy, Corrosion and Heat Resistant, Investment Castings, 73Ni 13Cr 4.5Mo 2.3Cb 0.75Ti 6.0Al 0.010B 0.10Zr Vacuum Cast, As-Cast
R. Reed and C.M.F. Rae, Physical Metallurgy of the Nickel-Based Superalloys, Physical Metallurgy (Fifth Edition), 2014, p 2215–2290. https://doi.org/10.1016/B978-0-444-53770-6.00022-8
A. Epishin and T. Link, Mechanisms of High Temperature Creep of Nickel-Base Superalloys Under Low Applied Stress, Phil. Mag., 2004, 84(19), p 1979–2000. https://doi.org/10.1080/14786430410001663240
X.Z. Qin et al., Decomposition of Primary MC Carbide and its Effects on the Fracture Behaviors of a Cast Ni-Base Superalloy, Mater. Sci. Eng. A, 2008, 485(1–2), p 74–79. https://doi.org/10.1016/j.msea.2007.07.055
J. Yang et al., Effects of Different C Contents on the Microstructure, Tensile Properties and Stress-Rupture Properties of IN792 Alloy, Mater. Sci. Eng. A, 2011, 528(3), p 1534–1539. https://doi.org/10.1016/j.msea.2010.11.003
F. Nabarro, The Physics of Creep, Taylor and Francis, London, 1995
P. Nörtershäuser et al., The Effect of Cast Microstructure and Crystallography on Rafting, Dislocation Plasticity and Creep Anisotropy of Single Crystal Ni-Base Superalloys, Mater. Sci. Eng. A, 2015, 626, p 305–312. https://doi.org/10.1016/j.msea.2014.12.030
M. Kamaraj et al., On the Influence of Stress State on Rafting in the Single Crystal Superalloy CMSX-6 Under Conditions of High Temperature and Low Stress Creep, A. Metall., 1998, 38(4), p 589–594
A. Royer et al., In Situ Determination of γ′ Phase Volume Fraction and of Relations Between Lattice Parameters and Precipitate Morphology in Ni-Based Single Crystal Superalloy, Acta Mater., 1998, 46(15), p 5357–5368. https://doi.org/10.1016/S1359-6454(98)00206-7
W. Huang et al., Experimental Investigation and Modelling of Microstructure Degradation in a DS Ni-Based Superalloy Using a Quantitative Cross Correlation Analysis Method, J. Alloys Compd., 2018, 762, p 488–499. https://doi.org/10.1016/j.jallcom.2018.05.131
V. Caccuri et al., γ′-Rafting Mechanisms Under Complex Mechanical Stress State in Ni-Based Single Crystalline Superalloy, Mater. Des., 2017, 131, p 487–497. https://doi.org/10.1016/j.matdes.2017.06.018
Acknowledgments
The authors gratefully acknowledge the funding by National Centre for Research and Development Poland under Grant LIDER/227/L-6/14/NCBR/2015 “New technology for investment casting manufacturing critical engine components with a new generation ceramic materials.”
Author information
Authors and Affiliations
Corresponding author
Additional information
This article is an invited submission to JMEP selected from presentations at the 73rd World Foundry Congress and has been expanded from the original presentation. 73WFC was held in Krakow, Poland, September 23-27, 2018, and was organized by the World Foundry Organization and Polish Foundrymen’s Association.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Rakoczy, Ł., Grudzień, M. & Cygan, R. Influence of Melt-Pouring Temperature and Composition of Primary Coating of Shell Mold on Tensile Strength and Creep Resistance of Ni-Based Superalloy. J. of Materi Eng and Perform 28, 3826–3834 (2019). https://doi.org/10.1007/s11665-018-3853-1
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11665-018-3853-1