Abstract
The metallization stack Ti/Pd/Ag on n-type Si has been readily used in solar cells due to its low metal/semiconductor specific contact resistance, very high sheet conductance, bondability, long-term durability, and cost-effectiveness. In this study, the use of Ti/Pd/Ag metallization on n-type GaAs is examined, targeting electronic devices that need to handle high current densities and with grid-like contacts with limited surface coverage (i.e., solar cells, lasers, or light emitting diodes). Ti/Pd/Ag (50 nm/50 nm/1000 nm) metal layers were deposited on n-type GaAs by electron beam evaporation and the contact quality was assessed for different doping levels (from 1.3 × 1018 cm−3 to 1.6 × 1019 cm−3) and annealing temperatures (from 300°C to 750°C). The metal/semiconductor specific contact resistance, metal resistivity, and the morphology of the contacts were studied. The results show that samples doped in the range of 1018 cm−3 had Schottky-like I–V characteristics and only samples doped 1.6 × 1019 cm−3 exhibited ohmic behavior even before annealing. For the ohmic contacts, increasing annealing temperature causes a decrease in the specific contact resistance (ρ c,Ti/Pd/Ag ~ 5 × 10−4 Ω cm2). In regard to the metal resistivity, Ti/Pd/Ag metallization presents a very good metal conductivity for samples treated below 500°C (ρ M,Ti/Pd/Ag ~ 2.3 × 10−6 Ω cm); however, for samples treated at 750°C, metal resistivity is strongly degraded due to morphological degradation and contamination in the silver overlayer. As compared to the classic AuGe/Ni/Au metal system, the Ti/Pd/Ag system shows higher metal/semiconductor specific contact resistance and one order of magnitude lower metal resistivity.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
L.J. Brillson, Contacts to Semiconductors: Fundamentals and Technology (Park Ridge, New Jersey: Noyes, 1993), pp. 1–3.
D.K. Schroder and D.L. Meier, IEEE Trans. Electron. Dev. 31, 637 (1984).
V.L. Rideout, Solid State Electron. 18, 541 (1975).
A. Piotrowska, A. Guivarc’h, and G. Pelous, Solid State Electron. 26, 179 (1983).
A. Piotrowska, Acta Phys. Pol. A 84, 491 (1993).
A.G. Baca, F. Ren, J.C. Zolper, R.D. Briggs, and S.J. Pearton, Thin Solid Films 308–309, 599 (1997).
D.L. Meier and D.K. Schroder, IEEE Trans. Electron. Dev. 31, 647 (1984).
A.R. Burgers, Prog. Photovolt. 7, 457 (1999).
M.M. Shabana, M.B. Saleh, and M.M. Soliman, Solar Cells 26, 177 (1989).
N. Braslau, J.B. Gunn, and J.L. Staples, Solid State Electron. 10, 381 (1967).
T.S. Kuan, P.E. Batson, T.N. Jackson, H. Rupprecht, and E.L. Wilkie, J. Appl. Phys. 54, 6952 (1983).
Y.C. Shih, M. Murakami, E.L. Wilkie, and A.C. Callegari, J. Appl. Phys. 62, 582 (1987).
A.G. Baca and C.I.H. Ashby, Fabrication of GaAs Devices (London: Institution of Electrical Engineers, 2005), p. 196.
Y. Wang, D. Liu, G. Feng, Z. Ye, Z. Gao, and X. Wang, J. Semicond. 36, 036002 (2015).
J. Zhou, G. Xia, B. Li, and W. Liu, Appl. Phys. A 76, 939 (2003).
H. Cotal, C. Fetzer, J. Boisvert, G. Kinsey, R. King, P. Hebert, H. Yoon, and N. Karam, Energy. Environ. Sci. 2, 174 (2009).
W.K. Chong, E.F. Chor, C.H. Heng, and S.J. Chua, Inst. Phys. Conf. Ser. 156, 171 (1998).
K.C. Sahoo, C.W. Chang, Y.Y. Wong, T.L. Hsieh, E.Y. Chang, and C.T. Lee, J. Electron. Mater. 37, 901 (2008).
D.G. Ivey, S. Eicher, S. Wingar, and T. Lester, J. Mater. Sci. 8, 63 (1997).
C.-H. Hsu, H.-J. Chang, H.-W. Yu, H.-Q. Nguyen, J.-S. Ma, E.Y. Chang, and I.E.E.E. Int, Conf. Semicond. Electron. (2014). doi:10.1109/SMELEC.2014.6920866.
C. Gutsche, A. Lysov, I. Regolin, A. Brodt, L. Liborius, J. Frohleiks, W. Prost, and F.-J. Tegude, J. Appl. Phys. 110, 014305 (2011).
T.V. Blank and Y.A. Gol’dberg, Semiconductors 41, 1263 (2007).
H. Fischer and R. Gereth, IEEE Trans. Electron. Dev. 18, 459 (1971).
X. Loozen, J.B. Larsen, F. Dross, M. Aleman, T. Bearda, B.J. O’Sullivan, I. Gordon, and J. Poortmans, Energy Procedia 21, 75 (2011).
A.K. Sinha, T.E. Smith, M.H. Read, and J.M. Poate, Solid State Electron. 19, 489 (1976).
B.K. Sehgal, B. Bhattacharya, S. Vinayak, and R. Gulati, Thin Solid Films 330, 146 (1998).
T. Göksu, N. Yıldırım, H. Korkut, A.F. özdemir, A. Turut, and A. Kökçe, Microelectron. Eng. 87, 1781 (2010).
I.-H. Tan, G.L. Snider, L.D. Chang, and E.L. Hu, J. Appl. Phys. 68, 4071 (1990).
E.F. Chor, D. Zhang, H. Gong, W.K. Chong, and S.Y. Ong, J. Appl. Phys. 87, 2437 (2000).
K.A. Jones, M.W. Cole, W.Y. Han, D.W. Eckart, K.P. Hilton, M.A. Crouch, and B.H. Hughes, J. Appl. Phys. 82, 1723 (1997).
A. Katz, C.R. Abernathy, and S.J. Pearton, Appl. Phys. Lett. 56, 1028 (1990).
G.K. Reeves and H.B. Harrison, IEEE Electr. Device Lett. 3, 111 (1982).
L.J. van der Pauw, Philips Res. Rep. 13, 1 (1958).
J.-L. Lee, Y.-T. Kim, J.-W. Oh, and B.-T. Lee, Jpn. J. Appl. Phys. 40, 1188 (2001).
O. Wada, S. Yanagisawa, and H. Takanashi, Appl. Phys. Lett. 29, 263 (1976).
M. Kniffin and C.R. Helms, J. Vac. Sci. Technol. A 5, 1511 (1987).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Huo, P., Rey-Stolle, I. Ti/Pd/Ag Contacts to n-Type GaAs for High Current Density Devices. J. Electron. Mater. 45, 2769–2775 (2016). https://doi.org/10.1007/s11664-016-4432-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-016-4432-6