The latest three-dimensional (3D) chip-stacking technology requires the repeated stacking of additional layers without remelting the joints that have been formed at lower levels of the stack. This can be achieved by transient liquid-phase (TLP) bonding whereby intermetallic joints can be formed at a lower temperature and withstand subsequent higher-temperature processes. In order to develop a robust low-temperature Au/In TLP bonding process during which all solder is transformed into intermetallic compounds, we studied the Au/In reaction at different temperatures. It was shown that the formation kinetics of intermetallic compounds is diffusion controlled, and that the activation energy of Au/In reaction is temperature dependent, being 0.46 eV and 0.23 eV for temperatures above and below 150°C, respectively. Moreover, a thin Ti layer between Au and In was found to be an effective diffusion barrier at low temperature, while it did not inhibit joint formation at elevated temperatures during flip-chip bonding. This allowed us to control the intermetallic formation during the distinct stages of the TLP bonding process. In addition, a minimal indium thickness of 0.5 μm is required in order to enable TLP bonding. Finally, Au/In TLP joints of ∅40 μm to 60 μm were successfully fabricated at 180°C with very small solder volume (1 μm thickness).
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
J.W. Roman and T.W. Eagar, Proceedings of the International Society for Hybrid Microelectronics (ISHM) (1992), p.␣1.
Bernstein L. 1966. J. Electrochem. Soc. 113: 1282. doi:10.1149/1.2423806.
S. Wakiyama, H. Ozaki, Y. Nabe, T. Kume, T. Ezaki, and T.␣Ogawa, Proc. of ECTC (2007), p. 610.
K. Sakuma, P.S. Andry, B. Dang, J. Maria, C.K. Tsang, C.␣Patel, S.L. Wright, B. Webb, E. Sprogis, S.K. Kang, R.␣Polastre, R. Horton, and J.U. Knickerbocker, Proc. of ECTC (2007), p. 627.
A. Munding, A. Kaiser, P. Benkart, E. Kohn, A. Heittmann, and U. Ramacher, Proc. of IEEE (2006), p. 262.
So W.W., Lee C.C. 2000. IEEE T. Compon. Pack. T. 23: 377. doi:10.1109/6144.846777.
Wang T.B., Shen Z.Z., Ye R.Q., Xie X.M., Stubhan F., Freytag J. 2000. J. Electron. Mater. 29: 443. doi:10.1007/s11664-000-0158-5.
Lee C.C., Wang C.Y. 1993. IEEE Trans. Comp. Hybrids Manufact. Technol. 16: 311. doi:10.1109/33.232058.
Liu C.-C., Lin Y.-K., Houng M.-P., Wang Y.-H. 2003. IEEE T. Compon. Pack. T. 26: 635. doi:10.1109/TCAPT.2003.817655.
Mori M., Saito M., Hongu A., Niitsuma A., Ohdaira H. 1990. IEEE Trans. Comp. Hybrids Manufact. Technol. 13: 444. doi:10.1109/33.56182.
Bjontegaard J., Buene L., Finstad T., Lonsjo O., Olsen T. 1983. Thin Solid films 101: 253. doi:10.1016/0040-6090(83)90252-3.
Shieu F.S., Chen C.F., Sheen J.G., Chang Z.C. 1999. Thin Solid Films 346: 125. doi:10.1016/S0040-6090(98)01737-4.
Quitoriano N., Wong W.S., Tsakalakos L., Cho Y., Sands T. 2001. J. Electron. Mater. 30: 1471. doi:10.1007/s11664-001-0204-y.
Simic V., Marinkovic Z. 1977. Thin Solid Films 41: 57. doi:10.1016/0040-6090(77)90009-8.
M. Paulasto, F. van Loo, and J.K. Kivilahti, J. Alloy Compd. 220, 136 (1995).
Vianco P., Erickson K., Hopkins P. 1994. J. Electron. Mater. 23: 721. doi:10.1007/BF02651365.
Haimovich J. 1993. AMP Journal of Technology 3: 46.
Laurila T., Vuorinen V., Kivilahti J.K. 2005. Mat. Sci. Eng. R49: 1.
Paul A., Kodentsov S., van Loo F. 2006. Intermetallics 14: 1428. doi:10.1016/j.intermet.2006.01.051.
Liu Y.M., Chuang T.H., Electro J. 2003. Mater. 29: 405.
Shohji G.I., Fujiwara S., Kiyono S., Kobayashi K.F. 1999. Scrip. Mater. 40: 815. doi:10.1016/S1359-6462(99)00007-X.
Hasumi Y. 1985. J. Appl. Phys. 58: 3081. doi:10.1063/1.335808.
Yost F.G. 1977. Gold Bull. 10: 94.
Millares M., Pieraggi B., Lelievre E. 1993. Solid State Ionics 63–65: 575. doi:10.1016/0167-2738(93)90161-U.
Waelti M., Schneeberger N., Brand O., Baltes H. 2000. Mat. Res. Soc. Symp. Proc. 605: 183.
Zhang W., Brongersma S. H., Richard O., Brijs B., Balmans R., Froyen L., Maex K. 2004. J. Vac. Sci. Technol. B 22: 2715. doi:10.1116/1.1819899.
Jacobson D.M., Humpston G. 1989. Gold Bull. 22: 9.
R. Labie, W. Ruythooren, K. Baert, E. Beyne, and B. Swinnen, accepted for IITC 2008.
Acknowledgement
The authors would like to thank Dr. Matin for the SEM measurements.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Zhang, W., Ruythooren, W. Study of the Au/In Reaction for Transient Liquid-Phase Bonding and 3D Chip Stacking. J. Electron. Mater. 37, 1095–1101 (2008). https://doi.org/10.1007/s11664-008-0487-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-008-0487-3