Abstract
The intermetallic compounds formed at the interfaces between In-49Sn solder balls and Au/Ni/Cu pads during the reflow of In-49Sn solder, ball-grid array (BGA) packages are investigated. Various temperature profiles with peak temperatures ranging from 140°C to 220°C and melting times ranging from 45 sec to 170 sec are plotted for the reflow processes. At peak temperatures below 170°C, a continuous double layer of intermetallics can be observed, showing a composition of Au(In,Ni)2/Au(In,Ni). Through selective etching of the In-49Sn solders, the intermetallic layer is made up of irregular coarse grains. In contrast, a number of cubic-shaped AuIn2 intermetallic compounds appear at the interfaces and migrate toward the upper domes of In-49Sn solder balls after reflow at peak temperatures above 200°C for longer melting times. The upward floating of the AuIn2 cubes can be explained by a thermomigration effect caused by the temperature gradient present in the liquid solder ball. The intermetallic compounds formed under various reflow conditions in this study exhibit different types of morphology, yet the ball shear strengths of the solder joints in the In-49Sn BGA packages remain unaffected.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
D.M. Jacobson and G. Humpston, Gold Bull. 22, 9 (1989).
N.C. Lee, Solid Surf. Mount Technol. 26, 65 (1997).
I. Shohji, S. Fujiwara, S. Kiyono, and K.F. Kobayashi, Scripta Mater. 40, 815 (1999).
F.G. Yost, F.P.G. Anyard, and M.M. Karnowsky, Metall. Trans. A 7A, 1141 (1976).
Z. Mei and J.W. Morris, J. Electron. Mater. 21, 599 (1992).
S.K. Kang and A.K. Saarkhel, J. Electron. Mater. 23, 701 (1994).
J. Glazer, Int. Mater. Rev. 40, 65 (1995).
K. Shimizu, T. Nakauishi, K. Karasawa, K. Hashimoto, and K. NiWa, J. Electron. Mater. 25, 39 (1996).
Z. Mei and J. Morris, J. Electron. Mater. 21, 401 (1992).
E. Zintl, A. Harder, and W. Haucke, Z. Phys. Chem. B 35, 354 (1937).
S.K. Kang and V. Ramachandran, Scripta Metall. 14, 421 (1980).
Y.H. Lin, Y.L. Chen, and T.H. Chuang, J. Electron. Mater. 29, 1047 (2000).
Y.H. Tseng (Ph.D. thesis, National Taiwan University, 2000).
S. Bader, W. Gust, and H. Hieber, Acta Metall. Mater. 43, 329 (1995).
G.J. Van Gurp, P.J. de Waard, and F.J. du Chatenier, J. Appl. Phys. 58, 728 (1985).
T.Y. Tan, Appl. Phys. Lett. 73, 2678 (1998).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Chuang, T.H., Chang, S.Y., Tsao, L.C. et al. Intermetallic compounds formed during the reflow of In-49Sn solder ball-grid array packages. J. Electron. Mater. 32, 195–200 (2003). https://doi.org/10.1007/s11664-003-0193-0
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s11664-003-0193-0