Abstract
Iron molybdate (Fe2MoO4) powders with an average particle size of 100 µm were reduced by hydrogen using a fluidized-bed batch reactor in the temperature range of 923 to 1173 K. The extent of the reaction was followed as a function of time by gas chromatography. The fluidizing-gas velocity was set at about 1.5 times the minimum fluidization velocity. The ratio of the height of the static bed to its diameter is about 1. Under the prevailing experimental conditions, it was found that the chemical reaction was the rate-controlling factor. The activation energy for this process was 158±17 kJ/mol. The crystal size of the Fe2Mo powder produced at lower temperatures was in the nanometer range, indicating the possibility of mass production of alloys and intermetallics in the nanorange, using a fluidized bed.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
R. Morales, I. Arvanitidis, Du Sichen, and S. Seetharaman: Metall. Mater. Trans. B, 2002, vol. 33B, pp. 589–94.
R. Morales, V. Agarwala, and S. Seetharaman: J. Mater. Res., 2002, vol. 17 (8), pp. 1954–59.
M.A. Doheim, M.Z. Abdel-Wahab, and S.A. Rassoul: Metall. Trans. B, 1976, vol. 7B, pp. 477–83.
S. Hovmand, W. Freedman, and J.F. Davinson: Trans. Inst. Chem. Eng., 1979, vol. 49, pp. 149–62.
J.C. Slattery and R.B. Bird: AIChE J., 1958, vol. 4, pp. 137–42.
J. Zsekely, J.W. Evans, and Y.H. Sohn: Gas-Solid Reactions, Academic Press, New York, NY, 1976, p. 18.
O. Levenspiel: Chemical Reaction Engineering, John Wiley & Sons, New York, NY, 1962, ch. 12.
D. Filippou, N. Katiforis, N. Papassiopi, and K. Adam: J. Chem. Technol. Biotechnol., 1999, vol. 74, pp. 322–28.
R.D. Rawlings and C.W.A. Newey: J. Iron Steel Inst., 1968, vol. 206, p. 723.
C.P. Heijwegen and G.D. Rieck: J. Less-Common Met., 1974, vol. 37, pp. 115–21.
S.R. Baen and P. Duwez: J. Met., 1951, vol. 3, pp. 331–35.
J.W. Putman, R.D. Potter, and N.J. Grant: Trans. ASM, 1951, vol. 43, pp. 824–47.
H. Kleykamp and V. Schauer: J. Less-Common Met., 1981, vol. 81, pp. 229–38.
R.P. Zaletaeva, N.F. Lashko, M.D. Nesterova, and S.A. Yuganova: Dokl. Akad. Nauk. SSSR, 1951, vol. 81, pp. 415–16.
C.J. Bechtoldt and H.C. Vacher: J. Res. NBS, 1957, vol. 58, pp. 7–19.
J. Higgings and P. Wilkes: Phil. Mag., 1972, vol. 25, pp. 599–623.
T. Miyazaki, S. Takagishi, H. Mori, and T. Kozakai: Acta Metall., 1980, vol. 28, pp. 1143–53.
K. Sinha, R.A. Buckley, and W. Hume-Rothery: J. Iron Steel Inst., 1967, vol. 205, pp. 191–95.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Morales, R., Sichen, D. & Seetharaman, S. Reduction kinetics of Fe2MoO4 fine powder by hydrogen in a fluidized bed. Metall Mater Trans B 34, 661–667 (2003). https://doi.org/10.1007/s11663-003-0037-6
Received:
Issue Date:
DOI: https://doi.org/10.1007/s11663-003-0037-6