Abstract
The precipitation behavior of a commercial high-strength low-alloy (HSLA) steel microalloyed with 0.086 wt pct Nb and 0.047 wt pct Ti has been investigated using transmission electron microscopy (TEM) and mechanical testing. The emphasis of this study is to compare an industrially hot-rolled steel and samples from a laboratory hot torsion machine simulation. From TEM observations, the Ti and Nb containing precipitates could be grouped according to their size and shape. The precipitates in order of size were found to be cubic TiN particles with sizes in the range of 1 µm, grain boundary precipitates with diameters of approximately 10 nm, and very fine spherical or needle-shaped precipitates with sizes on the order of 1 nm. The needlelike precipitates were found on dislocations in ferrite and constituted the dominant population in terms of density. Thus, they appear to be responsible for the precipitation strengthening observed in this steel. Aging tests were carried out at 650°C to evaluate the precipitate strengthening kinetics in detail. The strengthening mechanisms can be described with a nonlinear superposition of dislocation and precipitation hardening. The mechanical properties of torsion-simulated material and as-coiled industrial material are similar; however, there are some microstructural differences that can be attributed to the somewhat different processing routes in the laboratory as compared to hot strip rolling.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
I. Tamura, H. Sekine, T. Tanaka, and C. Ouchi: Thermomechanical Processing of High Strength Low Alloy Steels, Butterworth and Co., London, 1988.
M. Militzer, E.B. Hawbolt, and T.R. Meadowcroft: Metall. Mater. Trans. A, 2000, vol. 31A, pp. 1247–59.
E.V. Pereloma and J.D. Boyd: Mater. Sci. Technol., 1996, vol. 12, pp. 808–17.
M. Militzer, D.Q. Jin, and I.V. Samarasekera: in Advances in Industrial Materials, D.S. Wilkinson, W.J. Poole, and A. Alpas, eds., The Metallurgical Society of CIM, Montreal, 1998, pp. 63–77.
C.M. Sellars and J.A. Whiteman: Met. Sci., 1979, vol. 13, pp. 187–94.
P.D. Hodgson and R.K. Gibbs: Iron Steel Inst. Jpn. Int., 1992, vol. 32, pp. 1329–38.
I.V. Samarasekera, D.Q. Jin, and J.K. Brimacombe: 38th Mechanical Working and Steel Processing Conf. Proc., ISS, Warrendale, PA, 1997, vol. XXXIV, pp. 313–27.
B. Dutta and C.M. Sellars: Mater. Sci. Technol., 1987, vol. 3, pp. 197–206.
W.P. Sun, M. Militzer, D.Q. Bai, and J.J. Jonas: Acta Metall. Mater., 1993, vol. 41, pp. 3595–3604.
S.F. Medina: Mater. Sci. Technol., 1998, vol. 14, pp. 217–21.
S.F. Medina and J.E. Mancilla: Acta Metall. Mater., 1994, vol. 42, pp. 3945–51.
J. Andorfer, D. Auzinger, B. Buchmayr, W. Giselbrecht, G. Hribernig, G. Hubmer, A. Luger, and A. Samoilov: in Thermec ’97, T. Chandra and T. Sakai, eds., TMS, Warrendale, PA, 1997, pp. 2069–75.
A. Prasad, S. Jha, and N.S. Mishra: Steel Res., 1995, vol. 66, pp. 416–23.
M. Militzer, W.J. Poole, and W.P. Sun: Steel Res., 1998, vol. 69, pp. 279–85.
H.R. Shercliff and M.F. Ashby: Acta Metall. Mater., 1990, vol. 38, pp. 1789–1802.
A.J. DeArdo, J.M. Gray, and L. Meyer: in Niobium, H. Stuart, ed., TMS-AIME, Warrendale, PA, 1984, pp. 685–759.
R.M. Brito and H.J. Kestenbach: J. Mater. Sci., 1981, vol. 16, pp. 1257–63.
H.J. Kestenbach: Mater. Sci. Technol., 1997, vol. 13, pp. 731–39.
A. Itman, K.R. Cardoso, and H.J. Kestenbach: Mater. Sci. Technol., 1997, vol. 13, pp. 49–55.
D. Hall and J. Worobec: in Phase Transformations During the Thermal/Mechanical Processing of Steel, E.B. Hawbolt and S. Yue, eds., The Metallurgical Society of CIM, Montreal, 1995, pp. 305–16.
Z. Chen, M.H. Loretto, and R.C. Cochrane: Mater. Sci. Technol., 1987, vol. 3, 836–44.
R.G. Baker and J. Nutting: in Precipitation Processes in Steels, The Iron and Steel Institute, London, 1959, pp. 1–21.
M. Umemoto, A. Hiramatsu, A. Moriya, T. Watanabe, S. Nanba, N. Nakajima, G. Anan, and Y. Higo: Iron Steel Inst. Jpn. Int., 1992, vol. 32, pp. 306–15.
J. Bošansky, D.A. Porter, H. Åström, and K.E. Easterling: Scand. J. Metall., 1977, vol. 6, pp. 125–31.
JCPDS-International Center for Diffraction Data, Version 2.12, JCPDS-ICDD, Swarthmore, PA, 1991.
M.T. Miglin, J.P. Hirth, A.R. Rosenfeld, and W.A.T. Clark: Metall. Trans. A, 1986, vol. 17A, pp. 791–98.
P. Choquet, P. Fabrègue, J. Giusti, B. Chamont, J.N. Pezant, and F. Blanchet: in Mathematical Modelling of Hot Rolling of Steels, S. Yue, ed., The Metallurgical Society of CIM, Montreal, 1990, pp. 34–43.
E. Nes: Progr. Mater. Sci., 1997, vol. 41, pp. 129–93.
H.J. Frost and M.F. Ashby: Deformation-Mechanisms Maps, Pergamon Press, Oxford, United Kingdom, 1982.
T. Gladman: Mater. Sci. Technol., 1999, vol. 15, pp. 30–36.
D. Hull and D.J. Bacon: Introduction to Dislocations, 3rd ed, Pergamon Press, Oxford, United Kingdom, 1984.
M.F. Ashby: Cambridge Materials Selector, Software Version 2.02, Granta Design Ltd., Cambridge, UK, 1994.
L.M. Brown and R.K. Ham: in Strengthening Methods in Crystals, A. Kelly and R.B. Nicholson, eds., John Wiley & Sons, New York, NY, 1971, pp. 12–135.
T. Gladman: The Physical Metallurgy of Microalloyed Steels, Institute of Materials, London, 1997.
A.J.E. Foreman and M.J. Makin: Can. J. Phys., 1967, vol. 45, pp. 511–17.
K.A. Taylor: Scripta Metall. Mater., 1995, vol. 32, pp. 7–12.
M. Vivas, P. Lours, C. Levaillant, A. Couret, M.J. Casanove, and A. Coujou: Mater. Sci. Eng. A, 1997, vols. A234–A236, pp. 664–67.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Charleux, M., Poole, W.J., Militzer, M. et al. Precipitation behavior and its effect on strengthening of an HSLA-Nb/Ti steel. Metall Mater Trans A 32, 1635–1647 (2001). https://doi.org/10.1007/s11661-001-0142-6
Received:
Issue Date:
DOI: https://doi.org/10.1007/s11661-001-0142-6