Abstract
The strengthening mechanisms of hot-rolled steels micro-alloyed with Ti (ST-TQ500) and Nb-Ti (NT-TQ500) were investigated by examining the microstructures of steels using optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM). The results revealed almost no differences in the solute solution strengthening and fine-grained strengthening of the two steels, whereas the contributions of precipitation strengthening and dislocation strengthening were different for ST-TQ500 and NT-TQ500. The measured precipitation strengthening effect of ST-TQ500 was 88 MPa higher than that of NT-TQ500; this difference was primarily attributed to the stronger precipitation effect of the Ti-containing nanoscale particles. The dislocation strengthening effect of ST-TQ500 was approximately 80 MPa lower than that of NT-TQ500. This is thought to be related to differences in deformation behavior during the finishing rolling stage; the inhibition of dynamic recrystallization from Nb in NT-TQ500 (Nb-Ti) may lead to higher density of dislocations in the microstructure.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
C. E. Armando, C. J. María, P. J. Manuel, J. Iron Steel Res. Int. 18 (2011) Suppl. 1, 148–153.
J. Q. Xu, Y. C. Jia, H. L. Li, S. Sha, S. Jiang, J. Iron Steel Res. Int. 18 (2011) Suppl. 1, 572–575.
P. Sally, R. Andrew, W. Geoff, T. Rachel, J. Iron Steel Res. Int. 18 (2011) Suppl. 1, 208–212.
H. L. Yi, Z. Y. Liu, G. D. Wang, D. Wu, J. Iron Steel Res. Int. 17 (2010) No. 12, 54–58.
L. Q. Xie, X. P. Mao, X. D. Huo, Metallurgical Collections 155 (2005) 1–5.
X. E. Li, Z. Y. Zhao, R. D. Xue, X. Z. Yang, J. X. Xie, Iron and Steel 43 (2008) No. 6, 70–73.
D. M. Wang, F. L. Liu, X. H. Guo, Z. W. Liu, C. Y. Gu, Angang Technology 3 (2008) 21–24.
H. Y. Li, Y. L. Kang, J. J. Wang, P. Zhou, H. S. Tang, Journal of Wuhan University of Science and Technology 33 (2010) 47–52.
R. Z. Wang, H. T. Zhang, Acta Metall. Sin. 43 (2007) 1082–1090.
E. T. Turkdogan, Iron Steelmaker 16 (1989) 61–75.
J. Zhou, Y. L. Kang, X. P. Mao, L. J. Li, Z. Y. Lin, Iron and Steel 41 (2006) 343–350.
F. Brian, Picking, Microstructure and Properties of Steel, Science Press, Beijing, 1999.
X. Y. Yang, G. Xu, J. Yang, K. Zhang, S. Y. Wu, S. P. Zhang, Hot Working Technology 42 (2013) 50–52.
H. Yu, Michanism of Microstructure Refinement and Strengthening of Hot Strip of Low Carbon Steel by CSP Technology, University of Science and Technology Beijing, 2003.
Y. Q. Yang, H. Lei, Q. Gao, Y. L. Li, J. Du, Y. Yuan, Wide and Heavy Plate 19 (2013) 5–10.
H. L. Yi, L. X. Du, G. D. Wang, X. H. Liu, J. Northeast. Univ. Nat. Sci. 28 (2007) 1369–1373.
Author information
Authors and Affiliations
Corresponding author
Additional information
Foundation Item: Item Sponsored by National Natural Science Foundation of China (51374151); Foundation for Key Program of Shanxi Province of China (20111101053); Foundation for Major Coal Base New Materials Program of Shanxi Province of China (MC2014-02)
Rights and permissions
About this article
Cite this article
Meng, Cf., Wang, Yd., Wei, Yh. et al. Strengthening mechanisms for Ti- and Nb-Ti-micro-alloyed high-strength steels. J. Iron Steel Res. Int. 23, 350–356 (2016). https://doi.org/10.1016/S1006-706X(16)30056-5
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1016/S1006-706X(16)30056-5