Abstract
In order to improve the surface performance and increase the lifetime of P110 oil casing tube steel during operation, electroless plating was conducted to form Ni-P coating onto its surface. The surface morphology/element distribution and phase constitution of the Ni-P coating were analyzed using scanning electron microscope (SEM) equipped with energy dispersive spectrometry (EDS) and X-ray diffraction (XRD). Tribological and electrochemical measurement tests were applied to investigate the wear and corrosion resistance of P110 steel and the Ni-P coating. The results showed that a uniform and compact, high phosphorous Ni-P coating was formed. The obtained Ni-P coating indicated certain friction-reduction effect and lower mass loss during friction-wear tests. The Ni-P coating also exhibited higher corrosion resistance in comparison with bared P110 steel. The obtained Ni-P coating has significantly improved the surface performance of P110 steel.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Li H L, Zhang Y P, Han L H. Development Situation of OCTG and Production Localization of Hi-grade OCTG: Part I[J]. Steel Pipe, 2007, 36(6): 1–6 (in Chinese)
Li H L, Zhang Y P, Han L H. Development Situation of OCTG and Production Localization of Hi-grade OCTG: PartII[J]. Steel Pipe, 2008, 37(1): 1–6 (in Chinese)
Xiong Y, Chen D J. Research on CO2 Corrosion Protection Technology in Oil and Gas Field[J]. Total Corrosion Control, 2007, 21(4): 2–4 (in Chinese)
Lin N M, Xie F Q, Wu X Q, et al. Review on the Development and Prospect of Surface Protection Technology for Oil Casing Tubes[J]. Corros. Prot., 2009, 30: 801–805 (in Chinese)
Balaraju J N, Sankara Narayanan T S N, Seshadri S K. Electroless Ni-P Composite Coatings[J]. J. Appl. Eletrochem., 2003, 33: 807–816
Gu C D, Lian J S, Li G Y, et al. Electroless Ni-P Plating on AZ91D Magnesium Alloy from a Sulfate Solution[J]. J. Alloy Compd., 2005, 391: 104–109
Chen C F. Research on Electrochemical Behavior and Corrosion Scale Characteristics of CO 2 Corrosion for Tubing and Casing Steel[D]. Xi’an: Northwestern Polytechnical University, 2002
Liu N, Wang J L, Wang L D, et al. Electrochemical Corrosion Behavior of Mg-5Al-0.4Mn-xNd in NaCl Solution[J]. Corros. Sci., 2009, 51:1 328–1 333
Keshri A K, Agarwal A. Wear Behavior of Plasma-sprayed Carbon Nanotube Reinforced Aluminum Oxide Coating in Marine and High-temperature Environments[J]. J. Therm. Spray, 2011, 20: 1 217–1 230
Ye W, Li Y, Wang F H. The Improvement of the Corrosion Resistance of 309 Stainless Steel in the Transpassive Region by Nano-crystallization[J]. Electrochim. Acta, 2009, 54: 1 339–1 349
Marin E, Lanzutti A, Guzman L, et al. Corrosion Protection of AISI 316 Stainless Steel by ALD Alumina/Titania Nanometric Coatings[J]. J. Coat. Technol. Res., 2011, 8: 655–659
Author information
Authors and Affiliations
Corresponding author
Additional information
Funded by the China Postdoctoral Science Foundation (No.2012M520604), the Natural Science Foundation for Young Scientists of Shanxi Province (No.2013021013-2)
Rights and permissions
About this article
Cite this article
Lin, N., Zhou, P., Zou, J. et al. Wear and corrosion resistance of electroless plating Ni-P coating on P110 steel. J. Wuhan Univ. Technol.-Mat. Sci. Edit. 30, 622–625 (2015). https://doi.org/10.1007/s11595-015-1200-z
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11595-015-1200-z