Abstract
The nose temperature for σ-phase precipitation in super-duplex stainless steel (SDSS) UNS S32750 was evaluated by hardness method. Color-optical microscopy, scanning electron microscopy, energy spectrum analysis, impact and corrosion testing were carried out to investigate characteristics of microstructure and properties of the SDSS aged at the nose temperature. The experimental results indicate that the nose temperature of precipitation is 920 °C and aging at this temperature tiny σ phases can precipitate at phase interfaces or ferrite grain boundaries within 2 min. Prolonging aging duration the amount of σ-phase increases and a dual structure with σ and γ is obtained when aging for 120 min. The precipitation of σ-phase leads to severe deterioration in impact toughness (longitudinal/transverse direction) and corrosion resistance of SDSS.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Pardal J M, Tavares S S M, Fonseca M Cindra, et al. Influence of the Grain Size on Deleterious Phase Precipitation in Superduplex Stainless Steel UNS S32750[J]. Mater. Charact., 2009, 60: 165–172
Dobranszky J, Szabo P J, Berecz T, et al. Energy-dispersive Spectroscopy and Electron Backscatter Diffraction Analysis of Isothermally Aged SAF 2507 Type Superduplex Stainless Steel[J]. Spectrochimica Acta Part B, 2004, 59: 1781–1788
Ghosh S K, Mondal S. High Temperature Aging Behaviour of a Duplex Stainless Steel[J]. Mater. Charact., 2008, 59: 1776–1783
Calliari I, Zanesco M, Ramous E. Influence of Isothermal Aging on Secondary Phases Precipitation and Toughness of a Duplex Stainless Steel SAF 2205[J]. J Mater. Sci., 2006, 41: 7643–7649
Elmer J W, Palmer T A, Specht E D. Direct Observations of Sigma Phase Formation in Duplex Stainless Steels Using In -situ Synchrotron X-ray Diffraction[J]. Metallurgical and Materials Transactions A, 2007, 38A: 464–475
Chen T H, Weng K L, Yang J R. The Effect of High-temperature Exposure on the Microstructural Stability and Toughness Property in a 2205 Duplex Stainless Steel[J]. Mater. Sci. Eng. A, 2002, 338: 259–270
Pohl M, Storz O, Glogowski T. Effect of Intermetallic Precipitations on the Properties of Duplex Stainless Steel[J]. Mater. Charact., 2007, 58: 65–71
Zhang W, Zou D N, Fan G W, et al. Influence of Aging Time on Sigma Phase Precipitation in SAF 2507 Super-duplex Stainless Steel[J]. Materials Science Forum, 2009, 620–622: 355–358
Chen T H, Yang J R. Effects of Solution Treatment and Continuous Cooling on σ Phase Precipitation in a 2205 Duplex Stainless Steel[J]. Mater. Sci. Eng. A, 2001, 311: 28–41
Badji R, Bouabdallah M, Bacroix B, et al. Effect of Solution Treatment Temperature on the Precipitation Kinetic of σ-phase in 2205 Duplex Stainless Steel Welds[J]. Mater. Sci. Eng. A, 2008, 496: 447–454
Huang C S, Shih C C. Effects of Nitrogen and High Temperature Aging on σ Phase Precipitation of Duplex Stainless Steel[J]. Mater. Sci. Eng. A, 2005, 402: 66–75
Wu J. Duplex Stainless Steel[M]. Beijing: Metallurgical Industry Press, 1999 (in Chinese)
Deng B, Wang Z, Jiang Y, et al. Evaluation of Localized Corrosion in Duplex Stainless Steel Aged at 850 °C with Critical Pitting Temperature Measurement[J]. Electrochimica Acta, 2009, 54: 2790–2794
Author information
Authors and Affiliations
Corresponding author
Additional information
Founded by the Special Project of Shaanxi Education Department (07JK309) and Xi’an University of Architecture and Technology (JC0714)
Rights and permissions
About this article
Cite this article
Zou, D., Han, Y., Zhang, W. et al. Sigma phase precipitation and properties of super-duplex stainless steel UNS S32750 aged at the nose temperature. J. Wuhan Univ. Technol.-Mat. Sci. Edit. 26, 182–185 (2011). https://doi.org/10.1007/s11595-011-0193-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11595-011-0193-5