Abstract
A new alternative approach to fracture problems for materials and structural elements with cracks is set out. It is based on the mechanism of local instability near defects. The approach is used to study the fracture of materials compressed along interacting cracks and the fracture of thin structural members with cracks under tension with allowance for local buckling.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
REFERENCES
G. M. Bartenev and T. N. Khazanovich, “The law of highly elastic strains in cross-linked polymers,” Vysokomolek. Soed., 2, No.1, 21–28 (1960).
V. L. Bogdanov, A. N. Guz, and V. M. Nazarenko, “Fracture of semiinfinite material with a circular surface crack in compression along the crack plane,” Int. Appl. Mech., 28, No.11, 687–704 (1992).
V. L. Bogdanov, A. N. Guz, and V. M. Nazarenko, “Fracture of a half-space with a near-surface circular crack: Spatial nonaxisymmetric problem,” Dokl. AN SSSR, 319, No.4, 835–839 (1991).
V. L. Bogdanov and V. M. Nazarenko, “Study of the compressive failure of a semi-infinite elastic meterial with a harmonic potential,” Int. Appl. Mech., 30, No.10, 760–765 (1994).
V. L. Bogdanov and V. M. Nazarenko, “Compression of a composite along a near-surface macrocrack,” Mekh. Komp. Mater., 30, No.3, 352–358 (1994).
V. V. Bolotin, “Delamination-like defects in composite structures,” Mekh. Komp. Mater., No. 2, 239–255 (1984).
V. Yu. Gol’tsev, E. M. Morozov, and P. E. Nedoshivin, “Stability of a sheet sample with a crack under tension,” Zavod. Labor., No. 1, 96–98 (1969).
A. N. Guz, Brittle Fracture Mechanics of Prestressed Materials [in Russian], Naukova Dumka, Kiev (1983).
A. N. Guz, “Fracture mechanics of solids in compression along crack (two-dimensional problem),” Int. Appl. Mech., 18, No.3, 213–224 (1982).
A. N. Guz, “Mechanics of fracture of solids in compression along cracks (three-dimensional problem),” Int. Appl. Mech., 18, No.4, 285–294 (1982).
A. N. Guz, “On a failure criterion for solids compressed along a crack: A plane problem,” Dokl. AN SSSR, 259, No.6, 1315–1318 (1981).
A. N. Guz, “On a failure criterion for solids compressed along a crack: A spatial problem,” Dokl. AN SSSR, 261, No.1, 42–45 (1981).
I. A. Guz and A. N. Guz, “Stability of two different half-planes in compression along interfacial cracks: Analytical solutions,” Int. Appl. Mech., 37, No.7, 906–912 (2001).
A. N. Guz and M. Sh. Dyshel’, “Deformation of plates with an edge crack in tension,” Int. Appl. Mech., 31, No.11, 944–948 (1995).
A. N. Guz and M. Sh. Dyshel’, “Fracture and stability of notched thin-walled bodies in tension (survey),” Int. Appl. Mech., 26, No.11, 1023–1042 (1990).
A. N. Guz, V. I. Knyukh, and V. M. Nazarenko, “Three-dimensional axisymmetric problem of fracture in material with two discoidal cracks under compression along the latter,” Int. Appl. Mech., 20, No.11, 1003–1012 (1984).
A. N. Guz, V. I. Knyukh, and V. M. Nazarenko, “Delamination of composite materials under compression along internal and near-surface macrocracks,” Prikl. Mekh., 22, No.11, 40–46 (1986).
A. N. Guz, V. I. Knyukh, and V. M. Nazarenko, “Fracture of ductile materials in compression along two parallel disk-shaped cracks,” Int. Appl. Mech., 24, No.2, 112–118 (1988).
A. N. Guz, V. I. Knyukh, and V. M. Nazarenko, “Delamination of a composite compressed along two parallel macrocracks,” Fiz.-Khim. Mekh. Mater., 23, No.1, 72–78 (1987).
A. N. Guz, G. G. Kuliev, and N. Zeinalov, “Bulging of a plate with a curvilinear hole under tension,” Izv. AN SSSR, Mekh. Tverd. Tela, No. 2, 163–168 (1979).
A. N. Guz, G. G. Kuliev, and I. A. Tsurpal, “Theory of the rupture of thin bodies with cracks,” Int. Appl. Mech., 11, No.5, 485–487 (1975).
A. N. Guz and V. M. Nazarenko, “The theory of near-surface delamination in composites compressed along macrocracks,” Mekh. Komp. Mater., No. 5, 826–833 (1985).
A. N. Guz and V. M. Nazarenko, “Fracture of a material in compression along a periodic system of parallel circular cracks,” Int. Appl. Mech., 23, No.4, 371–377 (1987).
A. N. Guz and V. M. Nazarenko, “Fracture mechanics of materials under compression along cracks (survey). Hyperelastic materials,” Prikl. Mekh., 25, No.9, 3–32 (1989).
A. N. Guz and V. M. Nazarenko, “Fracture mechanics of materials under compression along cracks (survey). Structural materials,” Int. Appl. Mech., 25, No.10, 959–972 (1989).
A. N. Guz and V. M. Nazarenko, “Fracture of a half-space with a surface disk-shaped crack: Axisymmetric problem,” Dokl. AN SSSR, 274, No.1, 38–41 (1984).
A. N. Guz and V. M. Nazarenko, “Plastic near-surface fracture of materials compressed along macrocracks: Spatial problem,” Dokl. AN SSSR, 284, No.4, 812–815 (1985).
A. N. Guz and V. M. Nazarenko, “Fracture of materials compressed along periodic cracks under plane strain,” Prikl. Mat. Mekh., 51, No.2, 323–329 (1987).
A. N. Guz, V. M. Nazarenko, and S. M. Nazarenko, “Fracture of composites under compression along periodically placed parallel circular stratifications,” Int. Appl. Mech., 25, No.3, 215–221 (1989).
A. N. Guz, V. M. Nazarenko, and I. P. Starodubtsev, “A planar problem of failure of structural materials in compression along two parallel cracks,” Int. Appl. Mech., 27, No.4, 352–360 (1991).
A. N. Guz, V. M. Nazarenko, and I. Yu. Khoma, “Failure of an infinitely compressible composite containing a finite cylindrical crack in axial compression,” Int. Appl. Mech., 31, No.9, 695–703 (1995).
A. N. Guz, V. M. Nazarenko, and I. Yu. Khoma, “Fracture of a composite compressed along a cylindrical crack,” Dop. NAN Ukrainy, No. 10, 48–52 (1995).
M. M. Davidenkov, “Surface energy of mica,” Prikl. Mekh., 6, No.2, 138–142 (1960).
Yu. N. Dal’, “Local bending of a plate with a crack under tension,” Izv. AN SSSR, Mekh. Tverd. Tela, No. 4, 135–141 (1978).
M. Sh. Dyshel’, “Stability of thin plates with cracks under biaxial tension,” Int. Appl. Mech., 18, No.10, 924–928 (1982).
M. Sh. Dyshel’, “Buckling and fracture of plates with cracks under biaxial tension,” Prikl. Mekh., 19, No.6, 107–110 (1983).
M. Sh. Dyshel’, “Stability and fracture of a plate with two cracks under tension,” Prikl. Mekh., 19, No.8, 113–118 (1983).
M. Sh. Dyshel’, “Study into the deformation of a cylindrical shell near a slit under tension,” Prikl. Mekh., 20, No.3, 108–110 (1984).
M. Sh. Dyshel’, “Tension of a cylindrical shell with a slit,” Int. Appl. Mech., 20, No.10, 941–945 (1984).
M. Sh. Dyshel’, “Stability of thin plates with pointed holes under tension,” Prikl. Mekh., 21, No.2, 119–123 (1985).
M. Sh. Dyshel’, “Tension of a conic shell with a slit,” Prikl. Mekh., 22, No.6, 121–124 (1986).
M. Sh. Dyshel’, “Buckling and fracture of plates with curved cracks under tension,” Prikl. Mekh., 23, No.8, 110–114 (1987).
M. Sh. Dyshel’, “Local buckling of plates with cracks under cyclic loading,” Prikl. Mekh., 24, No.6, 118–121 (1988).
M. Sh. Dyshel’, “Influence of local buckling of plates with cracks on their crack resistance,” Prikl. Mekh., 25, No.3, 126–129 (1989).
M. Sh. Dyshel’, “Stability of a cracked cylindrical shell in tension,” Int. App. Mech., 25, No.6, 542–548 (1989).
M. Sh. Dyshel’, “Stress-intensity coefficient taking account of local buckling of plates with cracks,” Int. Appl. Mech., 26, No.1, 87–90 (1990).
M. Sh. Dyshel’, “Fracture of cylindrical panels with cracks under tension,” Prikl. Mekh., 26, No.7, 63–67 (1990).
M. Sh. Dyshel’, “Local stability loss and failure of cracked plates during the plastic deformation of materials,” Int. Appl. Mech., 30, No.1, 44–47 (1994).
M. Sh. Dyshel’, “Fracture of plates with an edge crack and local buckling under tension,” Prikl. Mekh., 32, No.2, 59–63 (1996).
M. Sh. Dyshel’, “Influence of plastic properties on the stability and fracture of plates with an edge crack,” Prikl. Mekh., 34, No.7, 73–77 (1998).
M. Sh. Dyshel’, “Fracture of two-layer plates with cracks and local buckling under tension,” Mekh. Komp. Mater., 38, No.5, 663–672 (2002).
M. Sh. Dyshel’, “Fracture and stability of plates with an edge crack under tension,” Dop. NAN Ukrainy, No. 5, 39–41 (1995).
M. Sh. Dyshel’, “Allowing for local buckling of plates with cracks in experimental determination of the intensity factor,” Dokl. AN USSR, Ser. A, No. 11, 40–44 (1988).
M. Sh. Dyshel’ and A. I. Zirka, “Stress state of a plate with a crack and local buckling under tension,” Prikl. Mekh., 22, No.9, 120–124 (1986).
M. Sh. Dyshel’, A. I. Zirka, and M. A. Mekhtiev, “Stress analysis of a plate with a hole and cracks reaching its boundary under tension with consideration of bulging,” Prikl. Mekh., 23, No.7, 110–113 (1987).
M. Sh. Dyshel’ and M. A. Mekhtiev, “Failure of tensioned plates weakened by a circular hole with radial cracks emanating from its contour,” Int. Appl. Mech., 25, No.5, 490–494 (1989).
M. Sh. Dyshel’ and O. B. Milovanova, “Local buckling of cylindrical panels with cracks under tension,” Prikl. Mekh., 25, No.11, 123–126 (1989).
M. Sh. Dyshel’ and O. B. Milovanova, “A method of experimentally analyzing the instability of plates with slits,” Int. Appl. Mech., 13, No.5, 491–495 (1977).
V. I. Knyukh, “Fracture of a material with two disk-shaped cracks in the case of axisymmetric deformation in compression along the cracks,” Int. Appl. Mech., 21, No.3, 226–231 (1985).
Z. N. Litvinenkova, “Stability of a plate with an internal crack under tension,” Izv. AN SSSR, Mekh. Tverd. Tela, 5, 148–151 (1973).
O. B. Milovanova and M. Sh. Dyshel’, “Stability of thin sheets with an oblique slit in tension,” Int. Appl. Mech., 16, No.4, 333–337 (1980).
V. M. Nazarenko, “Mutual effect of a circular surface crack and a free boundary in an axisymmetric problem of the fracture of an incompressible half space in compression along the crack plane,” Int. Appl. Mech., 21, No.2, 133–138 (1985).
V. M. Nazarenko, “Plastic rupture of materials during compression along near-surface fractures,” Int. Appl. Mech., 22, No.3, 245–250 (1986).
V. M. Nazarenko, “Fracture of materials compressed along near-surface cracks: Plane problem,” Prikl. Mekh., 22, No.10, 72–81 (1986).
V. M. Nazarenko, “The theory of fracture of materials compressed along near-surface cracks: Plane strain case,” Prikl. Mekh., 22, No.12, 96–104 (1986).
V. M. Nazarenko, “Fracture of plastic masses with translational hardening under compression along near-surface macrocracks,” Prikl. Mekh., 23, No.1, 70–75 (1987).
V. M. Nazarenko, “Fracture of plastic masses with translational strain-hardening in compression along near-surface cracks,” Int. Appl. Mech., 25, No.1, 61–65 (1989).
V. M. Nazarenko, “Compression of a material along periodic parallel circular cracks: Spatial problem,” Prikl. Mat. Mekh., 52, No.1, 145–152 (1988).
V. M. Nazarenko, “Fracture of a half-space with a surface disk-shaped crack: Axisymmetric problem,” Dokl. AN SSSR, 274, No.1, 38–41 (1984).
V. M. Nazarenko and Yu. I. Khoma, “Method for solving fracture problems for an infinite material with a cylindrical crack under axial compression (the case of unequal roots),” Dokl. AN Ukrainy, No. 7, 62–67 (1994).
V. M. Nazarenko and Yu. I. Khoma, “Compression of an infinite composite along a finite cylindrical crack,” Mekh. Komp. Mater., 31, No.1, 27–34 (1995).
A. N. Guz, M. Sh. Dyshel’, and V. M. Nazarenko, Fracture and Stability of Cracked Bodies, Vol. 4 of the four-volume five-book series, A. N. Guz (general editor), Nonclassical Problems of Fracture Mechanics [in Russian], Naukova Dumka, Kiev (1992).
A. N. Guz, M. Sh. Dyshel’, G. G. Kuliev, and O. B. Milovanova, “Fracture and local instability of thin-walled bodies with notches,” Int. Appl. Mech., 17, No.8, 707–722 (1981).
A. N. Guz, M. Sh. Dyshel’, G. G. Kuliev, and O. B. Milovanova, Fracture and Stability of Thin Bodies with Cracks [in Russian], Naukova Dumka, Kiev (1981).
I. P. Starodubtsev, “Fracture of a body compressed along two parallel cracks: Plane strain case,” Prikl. Mekh., 24, No.6, 79–84 (1988).
A. N. Guz, M. Sh. Dyshel’, G. G. Kuliev, and É. N. Mamedov, “Theoretical and experimental investigation of plates with cracks under biaxial loading,” Probl. Prochn., No. 2, 3–5 (1982).
A. N. Guz, M. Sh. Dyshel’, N. K. Zeinalov, and G. G. Kuliev, “Theoretical and experimental investigation of a plate with a noncircular hole under tension,” Dokl. AN USSR, Ser. A, No. 2, 38–41 (1980).
A. N. Guz, M. Sh. Dyshel’, G. G. Kuliev, and O. B. Milovanova, “Stability of thin plates with cracks,” Dokl. AN USSR, Ser. A, No. 5, 421–426 (1977).
G. P. Cherepanov, “Bulging of membranes with a hole under tension,” Prikl. Mekh. Mat., 27, No.2, 275–286 (1963).
V. L. Bogdanov, A. N. Guz, and V. M. Nazarenko, “Nonaxisymmetric compressive failure of a circular crack parallel to a surface of half-space,” Theor. Appl. Fract. Mech., 22, 239–247 (1995).
M. Sh. Dyshel’, “Local buckling of extended plates containing cracks and crack-like defects, subject to the influence of geometrical parameters of the plates and the defects,” Int. Appl. Mech., 35, No.12, 1272–1276 (1999).
M. Sh. Dyshel’, “Stability and fracture of plates with a central and an edge crack under tension,” Int. Appl. Mech., 38, No.4, 472–476 (2002).
M. Sh. Dyshel’, “Fracture of plates with an inclined edge crack under tension,” Int. Appl. Mech., 40, No.5, 580–582 (2004).
M. Sh. Dyshel’, “Stability of plates with an oblique edge crack under tension,” Int. Appl. Mech., 39, No.9, 1081–1083 (2003).
E. Yu. Gladun, A. N. Guz, and Yu. V. Kokhanenko, “Estimating the error of the beam approximation in the plane stability problem for a rectangular plate with a central crack,” Int. Appl. Mech., 40, No.11, 1290–1296 (2004).
A. N. Guz, “Design models in linearized solid mechanics,” Int. Appl. Mech., 40, No.5, 506–516 (2004).
A. N. Guz and M. Sh. Dyshel, “Fracture of cylindrical shells with cracks in tension,” Theor. Appl. Fract. Mech., No. 4, 123–126 (1985).
A. N. Guz and M. Sh. Dyshel, “Fracture and buckling of thin panels with edge crack in tension,” Theor. Appl. Fract. Mech., No. 36, 57–60 (2001).
A. N. Guz and M. Sh. Dyshel, “Buckling and cracking characteristics of two-layered plate in tension,” Theor. Appl. Fract. Mech., No. 38, 103–107 (2002).
A. N. Guz and M. Sh. Dyshel, “Stability and residual strength of panels with straight and curved cracks,” Theor. Appl. Fract. Mech., No. 41, 95–101 (2004).
A. N. Guz, Yu. I. Khoma, and V. M. Nazarenko, “On fracture of an infinite elastic body in compression along a cylindrical defect,” in: Advance in Fracture Research, Proc. 9th Int. Conf. on Fracture, Sydney, Australia, 4 (1999), pp. 2047–2054.
A. N. Guz, V. I. Knukh, and V. M. Nazarenko, “Compressive failure of material with two parallel cracks: small and large deformation,” Theor. Appl. Fract. Mech., 11, No.3, 213–223 (1989).
A. N. Guz and V. M. Nazarenko, “Symmetric failure of the half-space with penny-shaped cracks in compression,” Theor. Appl. Fract. Mech., 3, No.3, 233–245 (1985).
A. N. Guz, V. M. Nazarenko, and I. P. Starodubtsev, “On problems of fracture of materials in compression along two internal parallel cracks,” Appl. Math. Mech., 18, No.6, 517–528 (1997).
F. John, “Plane strain problems for a perfectly elastic material of harmonic type,” Comm. Pure Appl. Math., 13, No.2, 239–296 (1960).
I. W. Obreimoff, “The splitting strength of mica,” Proc. Royal Soc. London, A, 127, 290–297 (1930).
L. R. G. Treloar, “Large elastic deformations in rubber-like materials,” in: IUTAM Colloq., Madrid (1955), pp. 208–217.
Author information
Authors and Affiliations
Additional information
__________
Translated from Prikladnaya Mekhanika, Vol. 40, No. 12, pp. 18–64, December 2004.
Rights and permissions
About this article
Cite this article
Guz, A.N., Dyshel’, M.S. & Nazarenko, V.M. Fracture and stability of materials and structural members with cracks: approaches and results. Int Appl Mech 40, 1323–1359 (2004). https://doi.org/10.1007/s10778-005-0040-5
Received:
Issue Date:
DOI: https://doi.org/10.1007/s10778-005-0040-5