Abstract
Crystallographic structure, phase transition and electrical properties of lead-free (Na0.535K0.485)1−x Li x (Nb0.942Ta0.058)O3 (x=0.042–0.098) (NKL x NT) piezoelectric ceramics were investigated. The experimental results show that both Li content and sintering temperature strongly affect the orthorhombic–tetragonal polymorphic phase boundary (PPB), which results in remarkable differences of the piezoelectric property and its temperature stability in the NKL x NT ceramics. Chemical analysis indicates that sodium volatilizes more seriously than potassium and lithium with increasing sintering temperature. Due to the comprehensively optimized effects of Li content and sintering temperature, an enhanced piezoelectric constant d 33 (276 pC/N) was obtained at room temperature in the ceramics with x=0.074 sintered at 1000°C. In the same composition, a further high d 33 up to 354 pC/N was obtained at 43°C, which is close to its T o−t temperature. Furthermore, better temperature stability can be obtained when x=0.082 sintered at 1000°C, whose piezoelectric constant d 33 (236 pC/N) keeps almost constant from room temperature to 100°C. Such a temperature-independent piezoelectric property is available in the NKL x NT ceramics with high Li content because its T o−t was moved below room temperature.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
B. Jaffe, R.S. Roth, S. Marzullo, J. Appl. Phys. 25, 809 (1954)
Y. Saito, H. Takao, T. Tani, T. Nonoyama, K. Takatori, T. Homma, T. Nagaya, M. Nakamura, Nature 432, 84 (2004)
K. Wang, J.-F. Li, Appl. Phys. Lett. 91, 262902 (2007)
N.M. Hagh, B. Jadidian, E. Ashbahian, A. Safari, IEEE Trans. Ultrason. Ferroelectr. Freq. Control 55, 214 (2008)
D. Lin, Q. Zheng, C. Xu, K.W. Kwok, Appl. Phys. A 93, 549 (2008)
J. Bernard, A. Benčan, T. Rojac, J. Holc, B. Malič, M. Kosec, J. Am. Ceram. Soc. 91, 2409 (2008)
D. Lin, K.W. Kwok, H.L.W. Chan, Appl. Phys. A 91, 167 (2008)
Y. Dai, X. Zhang, G. Zhou, Appl. Phys. Lett. 90, 262903 (2007)
R. Zuo, J. Fu, D. Lv, J. Am. Ceram. Soc. 92, 283 (2009)
B. Jaffe, W.R. Cook, H. Jaffe, in Piezoelectric Ceramics (Academic Press, New York, 1971), pp. 115–181
P. Zhao, B.-P. Zhang, J.-F. Li, Scr. Mater. 58, 429 (2008)
Y. Guo, K. Kakimoto, H. Ohsato, Mater. Lett. 59, 241 (2005)
Y. Zhen, J.-F. Li, J. Am. Ceram. Soc. 89, 3669 (2006)
K. Wang, J.-F. Li, N. Liu, Appl. Phys. Lett. 93, 092904 (2008)
M.S. Kim, S.J. Jeong, J.S. Song, J. Am. Ceram. Soc. 90, 3338 (2007)
B.M. Jin, I.W. Kim, J.S. Kim, D.S. Lee, C.W. Ahn, J.H. Kwon, J.S. Lee, J.S. Song, S.J. Jeong, J. Electroceram. 15, 119 (2005)
Z.Y. Shen, Y. Zhen, K. Wang, J.-F. Li, J. Am. Ceram. Soc. (2009). doi:10.1111/j.1551-2916.2009.03128.x
P. Zhao, B.-P. Zhang, J.-F. Li, Appl. Phys. Lett. 90, 242909 (2007)
J. Wu, T. Peng, Y. Wang, D. Xiao, J. Zhu, Y. Jin, J. Zhu, P. Yu, L. Wu, Y. Jiang, J. Am. Ceram. Soc. 91, 319 (2008)
S. Zhang, R. Xia, H. Hao, H. Liu, T.R. Shrout, Appl. Phys. Lett. 92, 152904 (2008)
J.F. Scott, J. Phys., Condens. Matter 20, 021001 (2008)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Shen, ZY., Wang, K. & Li, JF. Combined effects of Li content and sintering temperature on polymorphic phase boundary and electrical properties of Li/Ta co-doped (Na, K)NbO3 lead-free piezoceramics. Appl. Phys. A 97, 911–917 (2009). https://doi.org/10.1007/s00339-009-5358-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00339-009-5358-0