Abstract
A natural sample of aegirine, ideally NaFeSi2O6, has been studied by transmission Mössbauer spectroscopy in the range 4.2–480 K. At selected temperatures, a longitudinal external field of 60 kOe was applied to the absorber. The sample was observed to order magnetically at 11±1 K. The paramagnetic Mössbauer spectra (MS) show the presence of ∼10% Fe2+ in the M1 sites of the clinopyroxene structure. These MS have been decomposed into four quadrupole doublets: two minor ones for Fe2+ on M1 sites, a dominant one due to Fe3+ on M1 sites, and a second ferric component, with a contribution of ∼3% and attributable to the tetrahedral sites. Two possibilities concerning the origin of the two distinct Fe2+ (M1) doublets are discussed. They are respectively based on inter-valence charge transfer and on the existence of distinct Fe2+ orbital configurations at the two M1 sites. Neither of the two models could be firmly excluded. The asymmetry parameter η of the electric field gradient at the Fe3+ (M1) sites is close to 1.0 and the quadrupole splitting within 0.34±0.01 mm/s at all temperatures. The MS at 4.2 K shows an asymmetric hyperfine-field distribution for Fe3+, with a maximum-probability field of 468 kOe. The maximum-probability field for Fe2+ is found to be 220 kOe. The shape of the applied-field MS at 4.2 K implies a static antiferromagnetic ordering and was successfully interpreted by a bidimensional distribution of the magnitude and orientation of the hyperfine field. Finally, the temperature variations of the respective centre shifts and quadrupole splittings could be explained on the basis of existing theoretical models.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Author information
Authors and Affiliations
Additional information
Received: 26 September 1996 / Revised, accepted: 15 November 1997
Rights and permissions
About this article
Cite this article
De Grave, E., Van Alboom, A. & Eeckhout, S. Electronic and magnetic properties of a natural aegirine as observed from its Mössbauer spectra. Phys Chem Min 25, 378–388 (1998). https://doi.org/10.1007/s002690050127
Issue Date:
DOI: https://doi.org/10.1007/s002690050127