Abstract
In this study, a combined method is proposed for the machining of SiC/Al matrix composites to achieve high efficiency and better surface quality based on blasting erosion arc machining (BEAM) and computer numerical control (CNC) milling. The combined method consists of two stages. BEAM is adopted in the first stage to achieve a high machining efficiency. During this stage, the negative BEAM is used for improving material removal rate (MRR) while positive BEAM is adopted to reduce roughness of machined surface. In the second stage, CNC milling is utilized to achieve a fine surface. Firstly, in order to perform the combined processing, a special machine tool system is designed. Secondly, machining efficiency of the combined processing is discussed. It is disclosed that in the negative BEAM step, when peak current is 600 A, MRR of 20 vol.% SiC/Al and 50 vol.% SiC/Al composites can be as high as 10,200 and 7500 mm3/min separately. Thirdly, comparison experiments are designed and surface integrity (e.g., surface topography, surface roughness, heat affect zone, surface hardness, compositions) of each machining stage is analyzed. It is demonstrated that in the CNC milling stage, side effects of BEAM on the workpiece (e.g., rough surface, thick heat affect zone) can be eliminated effectively. The roughness of the machined surface can be lower than Ra 0.5 μm; heat affect zone (HAZ) and debris almost cannot be observed. Finally, a SiC/Al workpiece is machined to demonstrate the advantages of the combined machining of SiC/Al matrix composites.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Koczak MJ, Khatri SC, Allison JE, Bader MG (1993) Chapter 16–metal-matrix composites for ground vehicle, aerospace, and industrial applications. Funda Metal-Matrix Compos 297–326
Bhushan RK, Kumar S, Das S (2010) Effect of machining parameters on surface roughness and tool wear for 7075 Al alloy SiC composite. Int J Adv Manuf Technol 50(5):459–469
Zhang ZH, Wang FC, Luo J, Lee SK, Wang L (2010) Microstructures and mechanical properties of spark plasma sintered Al–SiC composites containing high volume fraction of SiC. Mater Sci Eng A 527(27–28):7235–7240
Fard RK, Afza RA, Teimouri R (2013) Experimental investigation, intelligent modeling and multi-characteristics optimization of dry wedm process of Al–SiC metal matrix composite. J Manuf Process 15(4):483–494
Karthikeyan R, Ganesan G, Nagarazan RS, Pai BC (2001) A critical study on machining of Al/SiC composites. Materi Manuf Processes 16(16(1)):47–60
Bhushan RK (2013) Optimization of cutting parameters for minimizing power consumption and maximizing tool life during machining of Al alloy SiC particle composites. J Clean Prod 39(1):242–254
Haq AN, Marimuthu P, Jeyapaul R (2008) Multi response optimization of machining parameters of drilling Al/SiC metal matrix composite using Grey relational analysis in the Taguchi method. Int J Adv Manuf Technol 37(3):250–255
Thiagarajan C, Sivaramakrishnan R, Somasundaram S (2011) Experimental evaluation of grinding forces and surface finish in cylindrical grinding of Al/SiC metal matrix composites. Proc Instit Mech Engi Part B J Eng Manuf 225(9):1606–1614
Muguthu JN, Dong G, Ikua B (2015) Optimization of machining parameters influencing machinability of Al2124SiCP. 45 J Compos Mater 49(2):217–229
Mohan B, Rajadurai A, Satyanarayana KG (2004) Electric discharge machining of Al–SiC metal matrix composites using rotary tube electrode. J Mater Process Technol 153–154(1):978– 985
Senthilkumar C, Ganesan G, Karthikeyan R (2009) Study of electrochemical machining characteristics of Al/SiCP composites. Int J Adv Manuf Technol 43(3):256–263
Seo YW, Kim D, Ramulu M (2006) Electrical discharge machining of functionally graded 15–35 vol % SiCP/Al composites. Mater Manuf Process 21(5):479–487
Zhao W, Gu L, Xu H, Li L, Xiang X (2013) A novel high efficiency electrical erosion process—blasting erosion arc machining 621–625
Gu L, Chen J, Xu H, Zhao W (2016) Blasting erosion arc machining of 20 vol.% SiC/Al metal matrix composites. Int J Adv Manuf Technol 87(9-12):1–10
Xu H, Gu L, Chen J, Hu J, Zhao W (2015) Machining characteristics of nickel-based alloy with positive polarity blasting erosion arc machining. Int J Adv Manuf Technol 79(5):937–947
Chen J, Gu L, Xu H, Zhao W (2016) Study on blasting erosion arc machining of Ti–6Al–4V alloy. Int J Adv Manuf Technol 85(9):2819–2829
Bhushan RK, Kumar S, Das S (2013) Fabrication and characterization of 7075 Al alloy reinforced with SiC particulates. Int J Adv Manuf Technol 65(5-8):611–624
Chen J, Gu L, Zhu Y, Zhao W (2017) High efficiency blasting erosion arc machining of 50 vol. Institut Mech Eng Part B J Eng Manuf 1–9
Abbate C, Busatto G, Cova P, Delmonte N, Giuliani F, Iannuzzo F, Sanseverino A, Velardi F (2014) Thermal damage in SiC Schottky diodes induced by Se heavy ions. Microelectron Reliab 54(9-10):2200–2206
Bhatnagar M, Baliga BJ (1993) Comparison of 6H-SiC, 3C-SiC, and Si for power devices. IEEE Trans Electron Dev 40(3):645–655
Lee JM, Kang SB, Kamio A, Sato T, Tezuka H (1999) Microstructural changes in Al-Cu-Mn alloy reinforced with SiC particles on holding at high temperatures. Mater Trans Jim 40(6):537–545
Yang Y, Cho YI, Fridman A, Yang Y, Cho YI, Fridman A (2012) Plasma discharge in liquid: water treatment and applications. Aiche J 59(11):4451–4451
Wei R, Song S, Yang K, Cui Y, Peng Y, Chen X, Hu X, Xu X (2013) Thermal conductivity of 4H-SiC single crystals. J Appl Phys 113(5):283
Acknowledgements
The authors acknowledge the tests developed at the Instrumental Analysis Center of SJTU.
Funding
This work is supported by the Natural Science Foundation of China [51235007, 51575351], the Innovative Group Grant of NSFC [51421092], the State Key Laboratory of Mechanical and Vibration Focus Fund, Shanghai Jiao Tong University [MSV201305], and the grant of USCAST [2015-19]. The author are grateful to the supports mentioned above.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Chen, J., Gu, L., Liu, X. et al. Combined machining of SiC/Al composites based on blasting erosion arc machining and CNC milling. Int J Adv Manuf Technol 96, 111–121 (2018). https://doi.org/10.1007/s00170-017-1296-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00170-017-1296-8