Abstract
An understanding of the effects of dislocations in HgCdTe diodes is complicated by several issues such as the diode architecture, diode formation process, and the thermal history and location of the dislocations. To help decouple the effects of these factors, high stress films were used to lithographically introduce dislocations with different densities and locations during the fabrication process of ion implanted, n-on-p diodes. Both array and diode test structures were studied. After fabrication, the diodes were characterized with variable temperature I–V measurements and noise measurements. The diodes were then stripped and defect etched to quantify the density and distribution of the dislocations. The effects of these process-induced dislocations were analyzed and compared to the effects of as grown dislocations, subgrain boundaries and dislocations in other device architectures reported in the literature.1,2 In general, high densities of either as grown or process-induced dislocations in n-on-p, ion implanted diodes severely degrade device performance by producing field dependent dark current At 77K, dislocation densities greater than the mid 106 cm−2 can produce dark current densities in excess of the diode diffusion current. Dislocations located near the outer periphery of the diode produce approximately ten times the dark current of interior dislocations. Grain boundaries, sub-grain boundaries, and twins also produce sufficient field dependent dark current to limit diode performance at 77K. The dark current produced by dislocations is nearly temperature in dependent, suggesting rather severe limitations on dislocation densities for low temperature diode operation.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
R.S. List,J. Vac. Sci. Technol. B 10, 1651 (1992).
S.M. Johnson, D.R. Rhiger, J.P. Rosbeck, J.M. Peterson, S.M. Taylor and M.E. Boyd,J. Vac. Sci. Technol. B 10, 1499 (1992).
H.J. Queisser,Defects in Semiconductors, Proc. Mater. Res. Soc. Symp., eds. S. Mahajan and J.W. Corbett (Elsevier, New York, 1983), vol. 14, p. 323.
P.R. Wilshaw and T.S. Fell,Inst. Phys. Conf. Ser. 104, 85 (1989).
Defect Electronies in Semiconductors, ed. H.F. Matare, (Wiley-Interscience, New York 1971), p. 442.
Henry Kressel,Semiconductors and Semimetals, Academic Press, New York, 1981, vol. 16, p. 1.
R.G. Rhodes,Imperfections and Active Centres in Semiconductors, (Pergamon, New York, 1964).
S.R. Morrison,Grain Boundaries in Semiconductors, eds. Pike, Seager and Leamy (Elsevier, New York, 1982), p. 193.
J.H. Tregilgas, T.L. Polgreen and M.C. Chen,J. Cryst. Growth 86, 460 (1988).
P.W. Norton and A.P. Erwin,J. Vac. Sci. Technol. A 7, 503. (1989).
H.F. Schaake and A.J. Lewis,Mater. Res. Soc. Symp. Proc. 14, 301 (1983).
A.J. Syllais and L. Columbo,Proc. IEDM Conf. 1982, (IEEE, New York, 1982), p. 137.
L. Columbo and A.J. Syllais,Proc. IEDM Conf. 1983, (IEEE, New York, 1983), p. 718.
D. Chandra, J.H. Tregilgas and M.W. Goodwin,J. Vac. Sci. Technol. B 9, 1852 (1991).
H. Takigawa, T. Akamatsu, T. Kanno and R. Tsunoda,Proc. IEDM Conf, 1981 (IEEE, New York, 1981), p. 172.
H. Booyens and J.H. Basson,Phys. Status Solidi A 85, 243 (1984).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
List, R.S. Electrical effects of dislocations and other crystallographic defects in Hg0.78Cd0.22Te n-on-p photodiodes. J. Electron. Mater. 22, 1017–1025 (1993). https://doi.org/10.1007/BF02817519
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF02817519