Abstract
An “environmental cell” located in a high voltage transmission electron microscope has been used to study the reduction of single crystal iron oxides by hydrogen and hydrogen-argon mixtures. The cell enables a direct observation of the solid during reaction, thus permitting the nucleation and growth of solid reaction products to be observed. Hematite was reduced at temperatures in the range 387 to 610°C with gas pressures up to 5.3 kP. Reduction with pure hydrogen was considerably faster than when argon was present. Lath magnetite which rapidly transforms to porous magnetite and thence (more slowly) to porous iron was observed. The reduction of magnetite and of wustite single crystals was observed in the temperature range 300 to 514°C using both hydrogen and hydrogen-argon mixtures at gas pressures up to 6.6 kP. Incubation periods were found for magnetite reduction; during these periods faceted pits formed in the oxide. Iron formed in the early stages was epitaxial with the host magnetite; at later stages the epitaxy was lost and fissures frequently formed in the metal. The morphology of the iron differed between the gas mixtures. Disproportionation accompanied the reduction of wustite, producing intermediate polycrystalline magnetite despite reducing conditions. The disproportionation appeared to be promoted by the reduction reaction. For both oxides, reduction in the hydrogen-argon mixture was slower than in pure hydrogen.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
L. von Bogdandy and H. J. Engell:The Reduction of Iron Ores, Springer-Verlag, Berlin, 1971.
J. W. Evans and C. H. Koo: inRate Processes of Extractive Metallurgy, H. Y. Sohn and M. E. Wadsworth, eds., Plenum Press, New York, NY, 1979, pp. 286–302.
J. Szekely, J. W. Evans, and H. Y. Sohn:Gas-Solid Reactions, Academic Press, New York, NY, 1976, pp. 339–47.
E. T. Turkdogan and J. V. Vinters:Metall. Trans., 1971, vol. 2, pp. 3175–88.
S. K. El-Rahaiby and Y. K. Rao:Metall. Trans. B, 1979, vol. 10B, pp. 257–69.
Y. K. Rao and M. Moinpour:Metall. Trans. B, 1983, vol. 14B, pp. 711–23.
M. M. Al-Kahtany and Y. K. Rao:Ironmaking and Steelmaking, 1980, vol. 7, pp. 49–58.
S. K. El-Rahaiby and Y. K. Rao:Trans. ISIJ, 1980, vol. 20, pp. 287–91.
E. T. Turkdogan and J. V. Vinters:Metall. Trans., 1972, vol. 3, pp. 1561–74.
J. W. Evans and K. Haase:High Temp. Sci., 1976, vol. 8, pp. 167–77.
E. T. Turkdogan, R. G. Olsson, and J. V. Vinters:Metall. Trans., 1971, vol. 2, pp. 3189–96.
C. H. Koo and J. W. Evans:Trans. ISIJ, 1980, vol. 19, pp. 95–101.
J. O. Edstrom:J. Iron & Steel Inst., 1953, vol. 175, pp. 289–304.
J. O. Edstrom and G. Bitsianes:AIME Trans., 1955, vol. 203, pp. 760–65.
H. Brill-Edwards, B. L. Daniell, and R. L. Samuel:J. Iron & Steel Inst., 1965, vol. 203, pp. 361–68.
W. Pluschkell and H. Yoshikoshi:Arch. Eisenhüttenw., 1970, vol. 41, pp. 715–21.
Y. K. Rao:Metall. Trans. B, 1979, vol. 10B, pp. 243–55.
A. V. Bradshaw and A. G. Matyas:Metall. Trans. B, 1976, vol. 7B, pp. 81–87.
D. H. St. John and P. C. Hayes:Metall. Trans. B, 1982, vol. 13B, pp. 117–24.
M. Moukassi, P. Steinmetz, B. Dupre, and C. Gleitzer:Metall. Trans. B, 1983, vol. 14B, pp. 125–32.
P. C. Hayes and P. Grieveson:Metall. Trans. B, 1981, vol. 12B, pp. 579–87.
A. Unal and A. V. Bradshaw:Metall. Trans. B, 1981, vol. 14B, pp. 743–52.
P. R. Swann and N. J. Tighe:Metall. Trans. B, 1977, vol. 8B, pp. 479–87.
J. R. Porter and P. R. Swann:Ironmaking & Steelmaking, 1977, vol. 5, pp. 300–07.
P. Baguley, D. H. St. John, and P. C. Hayes:Metall. Trans. B, 1983, vol. 14B, pp. 513–14.
J. A. Little, M. I. Perez, and J. W. Evans: Lawrence Berkeley Lab Report no. LBL-11473, 1980.
U. Finnstrom:Scand. J. Metall., 1976, vol. 5, pp. 134–36.
R. A. Rapp:Metall. Trans. B, 1984, vol. 15A, pp. 765–82.
R. T. K. Baker and P. S. Harris:J. Phys. E., 1972, vol. 5, pp. 793–97.
D. J. Coates, J. W. Evans, A. L. Cabrera, G. A. Somorjai, and H. Heineman:J. Catalysis, 1983, vol. 80, pp. 215–20.
D. J. Coates, J. W. Evans, and H. Heinemann:J. Appl. Catalysis, 1983, vol. 7, pp. 233–41.
T. Gabor and J. M. Blocher:J. Vac. Sci. Technol., 1969, vol. 6, pp. 815–27.
M. E. Hall: M. S. Thesis, LBL-18902, Lawrence Berkeley Laboratory, U.C., Berkeley, CA, 1985.
H. Hashimoto, S. Urai, H. Yotsumoto, and J. Sawamori: inProc. 7th Int. Congr. Electron Microscopy, Grenoble, 1970, vol. 2, pp. 399–400.
H. R. Harrison, R. Aragon, and C. J. Sandberg:Mat. Res. Bull., 1980, vol. 15, pp. 571–80.
D. H. St. John, S. P. Matthew, and P. C. Hayes:Metall. Trans. B, 1984, vol. 15B, pp. 709–17.
D. H. St. John, S. P. Matthew, and P. C. Hayes:Metall. Trans. B, 1984, vol. 15B, pp. 701–08.
Bulletin of Alloy Phase Diagrams, 1980, vol. 1, No. 1, p. 29.
E. N. Fuller, P. D. Schettler, and J. C. Giddings:Indust. and Eng. Chem., 1966, vol. 58, pp. 18–27.
W. Pluschkell and B. V. S. Sarma:Arch. Eisenhüttenwes. 1974, vol. 45, pp. 23–31.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Rau, MF., Rieck, D. & Evans, J.W. Investigation of iron oxide reduction by TEM. Metall Trans B 18, 257–278 (1987). https://doi.org/10.1007/BF02658451
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02658451