Abstract
This article presents the results of casting and spiral fluidity in a Al-7 wt% Si alloy reinforced with 10,15, and 20 vol% SiC particles in permanent molds. The fluidity of the Al-SiC slurry increases linearly with temperature up to about 760 °C. Above this temperature, the casting fluidity of the Al-SiC particle slurry does not change significantly with an increase in temperature. In several cases, the fluidity decreased at temperatures above 760 °C. The fluidity of Al-SiC melts containing 9-μm SiC particles decreased with an increase in volume percentage of SiC up to 15 vol% (the range studied), presumably due to an increase in the viscosity of the melt with increasing volume percentage of dispersoid and changes in thermophysical properties of the composite. However, the fluidity of Al-20 vol% SiC of 14-μm particle size is higher than the fluidity of Al-15 vol% SiC 9-μm particles, indicating the role of particle size and surface area in de-creasing fluidity. Composite slurries travel farther in a channel of larger cross sections compared to channels of smaller cross sections under similar conditions. Casting fluidity increases linearly with an in-crease in cross section of the channel. A model has been proposed to calculate the values of fluidity of the composite as a function of particle volume percent, superheat, flow velocity of the melt, and the cross sec-tion of the flow channel. Experimental observations have been compared with the predictions of the model, and some deviations have been attributed to settling and segregation of SiC particles observed through microstructural examination.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
P.K. Rohatgi, inMetals Handbook, Vol 15, 9th ed., ASM, 1988, p 840
D.M. Shuster, M.D. Skibo, and W.R. Hoover,Light Metal Age, 1989, p 15
Z. Zhu, “Literature Survey on Fabrication Methods of Cast Rein- forced Metal Composites,” Cast Metal Matrix Composites Proc, Vol 1, S.G. Fishman and A.K. Dhingra, Ed., ASM, 1988, p 93–98
M. Skibo, P.L. Morris, and D.J. Lloyd, “Structure and Properties of Liquid Metal Processed SiC Reinforced Aluminum,” Cast Metal Matrix Composites Proc, Vol 1, S.G. Fishman and A.K. Dhingra, Ed., ASM, 1988, p 257–259
D.J. Lloyd, The Solidification Microstructure of Particulate Re- inforced Al-SiC Composites,Comp. Sci. Technol., Vol 35, 1989, p 159
D.J. Lloyd and B. Chamberlain, “Properties of Shape Cast Al-SiC Metal Matrix Composites,” Cast Metal Matrix Composites Proc, S.G. Fishman and A.K. Dhingra, Ed., Vol 1, 1988, p 263–269
F.R. Mollard, M.C. Flemings, and E.F. Niyama, Understanding Aluminum Fluidity: The Key to Adranad Products,AFS Trans., 1988,p647
J.L. Jorstad, Communication Letter to the American Die Casting Institute, 1987, p 1–3
M.R. Sheshradri and A. Ramachandran, Casting Fluidity and Flu- idity of Aluminum and its Alloys,AFS Trans., 1965, p 273
C.J. Cooksey et al., The Casting Fluidity of Some Foundry Al- loys,The British Foundrymen, 1959, p 381–386
F.L. Arnold, J.L. Jurstad, and G.E. Stein, Fluidity Characteristics of Some Alloys in the Aluminum-Silicon System,Current Engi- neering Practice, 1963, p 10–15
M.K. Surappa and P.K. Rohatgi,Metall. Trans., 1981, p 128
D. Nath and P.K. Rohatgi,J. Mater. Sci., Vol 15 (No. 11), p 2777
M.K. Surappa and P.K. Rohatgi,Met. Technol., Vol 7, 1980, p 378
M.C. Flemings,Solidification Processing, Chapt. 7, McGraw- Hill, 1974
F.M. Yarnadi, “Melting and Casting Characteristics of Al A-356 SiC Particulate Reinforced Cast Composites,” Ph.D thesis, Uni-versity of Wisconsin—Milwaukee, Aug 1991, p 87
Author information
Authors and Affiliations
Additional information
(on leave from Dept. of Metallurgy, University of Roorkee, Roorkee (U.P.)-247667, India)
Rights and permissions
About this article
Cite this article
Yarandi, F.M., Rohatgi, P.K. & Ray, S. Fluidity and microstructure formation during flow of Al- SiC particle composites. JMEP 2, 359–364 (1993). https://doi.org/10.1007/BF02648823
Issue Date:
DOI: https://doi.org/10.1007/BF02648823