Abstract
The curing behaviour of bismethacryloxy derivative of diglycidyl ether of bisphenol A (vinyl ester resin) containing styrene as the reactive diluent (40% w/w) was studied using gel point determination method and DSC. Seven samples of styrene/α-methylstyrene in the ratio 40∶0, 35∶5, 30∶10, 25∶15, 20∶20, 15∶25 and 0∶40 were studied. Delayed curing was observed in samples containing increasing proportions of α-methylstyrene. The energy of activation decreased from 869 kJ mol−1 to 333 kJ mol−1 as the concentration of α-methylstyrene increased in the formulations. However, no difference in thermal stability was observed by replacement of styrene by α-methylstyrene. It was concluded that in vinyl ester resin samples 10–15% α-methylstyrene and 30-25% styrene can be used as reactive diluent.
Zusammenfassung
Mittels DSC und Bestimmung der Gelierungstemperatur wurde das Aushärteverhalften des Bismethakryloxyderivaten des Diglycidyläthers von Bisphenol A (Vinylesterharz) mit 40 Gewichtsprozenten Styrol als reaktives Streckmittel untersucht. Es würden sieben Proben mit einem Styrol/α-Methylstyrol Verhältnis von 40∶0, 35∶5, 30∶10, 25∶15, 20∶20, 15∶25 und 0∶40 untersucht. Mit steigendem Anteil an α-Methylstyrol konnte eine Verzögerung der Aushärtung sowie ein Absinken der Aktivierungsenergie von 869 kJ · mol−1 auf 333 kJ · mol−1 beobachtet werden. Der Ersatz von Styrol durch α-Methylstyrol veränderte jedoch die thermische Stabilität in keiner Weise. Vinylesterharzproben mit 10–15% α-Methylstyrol und 30–25% Styrol können als reaktive Streckmittel in Vinylesterharzen verwendet werden.
Резюме
Методом ДСК и определ ением точки гелеобразования изу чен характер отвержд ения бис-метакрилокси про изводного диглициди лового эфира бис-фенола А, содержащ его 40 вес.% стирола в качестве ре акционного разбавит еля. Изучены семь образцов стирол /α-метилстирол, взятых в соотношении 40∶0, 35∶5, 30∶10, 25∶15, 20∶20, 15∶25 и 0∶40. В образцах с увеличиваюримся сод ержаниемα-метилстир ола наблюдалось замедле ние отверждения. С увеличением концент рацииα-метилстирола энергия активации уменьшала сь от 869 до 333 кдж · моль−1. Однако, не наблюдалось различи й в термоустойчивости п ри замене стиролаαм етилстиролом.αметилстиролом. Сделано заключение, ч то образцы винилэфир ной смолы, содержащие 10–15% α-метилстирола и 30–25% ст ирола могут быть испо льзованы в качестве реактивны х разбавителей для винилэфирной смо лы.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
M. B. Launikitis, in Handbook of Composites G. Luben Ed., Van Nostrand, Reinhold Co., New York, 1982, p. 38.
R. Kay, in Fibre Composite Hybrid Materials, N. L. Hancox Ed., Applied Science Publishers Ltd., London, 1981, p. 42.
I. Yilgor, E. Yilgor, A. K. Banthia, G. L. Wilkes and J. E. McGrath, Polym. Composites, 4 (1983) 4.
I. K. Varma, B. S. Rao, M. S. Choudhary, V. Choudhary and D. S. Varma, Angew. Makromol. Chem., 130 (1985) 191.
T. C. Goel, A. Tripathi, B. S. Rao, M. S. Choudhary, V. Choudhary and I. K. Varma, J. Appl. Polym. Sci., 30 (1985) 1491.
H. V. Boening, in Unsaturated Polyester: Structure and Properties, Elsevier Pub. Co., 1964, pp. 42 and 154.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Bhatnagar, R., Varma, I.K. Effect of α-methylstyrene of the curing behaviour of vinyl ester resins. Journal of Thermal Analysis 35, 1241–1249 (1989). https://doi.org/10.1007/BF01913044
Issue Date:
DOI: https://doi.org/10.1007/BF01913044