Abstract
The effect of cold work on the oxidation rate of 21/4 Cr-1 Mo steel in pure oxygen at 1 atm pressure at temperatures ranging from 400 to 950‡C has been studied for short exposure periods (max. 4 hr). The specimens had been cold worked up to 90% by cold rolling. The results indicate negligible effect of cold work on the oxidation kinetics up to 700‡C, beyond which there is general reduction in oxidation. The effect was pronounced at 900‡C. The increased resistance to oxidation has been attributed to the faster diffusion of chromium in the cold-worked material compared to the annealed one, leading to the formation of a chromium-rich spinel which helps in slowing down the oxidation of the alloy. The findings have been corroborated by the examination of all samples oxidized at 900‡C by optical, EPMA, SEM, and EDAX analyses.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
D. Caplan and M. Cohen,Corr. Sci. 6, 321 (1966).
D. Caplan, G. I. Sproule, and R. J. Hussey,Corr. Sci. 10, 9 (1970).
W. R. Price,Corr. Sci. 7, 473 (1967).
D. Caplan,Corr. Sci. 6, 509 (1966).
W. E. Ruther and S. Greenberg,J. Electrochem. Soc. 111, 116 (1964).
M. Warzeeet al., J. Electrochem. Soc. 112, 670 (1965).
M. K. Hossain,Corr. Sci. 19, 1031 (1979).
B. Kent and J. Davidson,Micro '74 Supplement, Proc. RMS,9(4), 74 (1974).
K. C. Tripathi and J. E. Antill,Corr. Sci. 10, 273 (1970).
M. H. Hurdus and L. Tomlinson,Br. Corr. J. 13, 158 (1978).
G. C. Wood,Corr. Sci. 2, 173 (1961).
G. O. Lloyd, S. R. J. Saunders, B. Kent, and A. Fursey,Corr. Sci. 17, 269 (1977).
G. B. Gibbs and R. Hales, Proc. Conf. ‘Point defect behavior and diffusional processes,’ The Metal Society, University of Bristol (Sept. 1976), p. 201.
M. G. C. Cox, B. McEnaney, and V. D. Scott,Philos. Mag. 26, 839 (1972).
D. P. Whittle and G. C. Wood,J. Electrochem. Soc. 114, 986 (1967).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Khanna, A.S., Gnanamoorthy, J.B. Effect of cold work on the oxidation resistance of\(2\tfrac{1}{4}\) Cr-1 Mo steel. Oxid Met 23, 17–33 (1985). https://doi.org/10.1007/BF01095805
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF01095805