Abstract
To prevent hot-cracking, austenitic stainless steel welds generally contain a small percent of delta ferrite. Although ferrite has been found to effectively prevent hot-cracking, it can lead to embrittlement of welds when exposed to elevated temperatures. The aging behavior of type-308 stainless steel weld has been examined over a range of temperatures 400–850‡C for times up to 10,000 hr. Upon aging, and depending on the temperature range, the unstable ferrite may undergo a variety of solid state transformations. These phase changes affect creep-rupture and Charpy impact properties.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
J. C. Borland and R. N. Younger, Some aspects of cracking in austenitic steels,British-Welding J. 7(1):22–60 (1960).
F. C. Hull, Effect of delta ferrite on the hot cracking of stainless steel,Welding J. 46(9):399-s–409-s (1961).
Y. Arata, F. Matsuda, and S. Katayama, Solidification crack susceptibility in weld metals of fully austenitic stainless steel (Report 1)—fundamental investigation on solidification behavior of fully austenitic and duplex microstructures and effect of ferrite on microsegregation,Trans. Jpn. Welding Res. Ins. 5(2):35–51 (1976).
S. A. David, G. M. Goodwin, and D. N. Braski, Solidification behavior of austenitic stainless steel filler metals,Weld J. 58(11): 330s-336s (1979).
N. Suutala, T. Takalo, and T. Moisio, Relationship between solidification and microstructure in austenitic and austenitic-ferritic stainless steel welds,Metall. Trans. 10A:512–514 (1979).
T. Takalo and T. Moisio, Single phase ferritic solidification mode in austenitic-ferritic stainless steel welds,Metall. Trans. 10A: 1183–1190 (1979).
W. T. DeLong, Ferrite in austenitic stainless steel weld metal,Welding J. 53(7):273-s–286-s (1974).
S. A. David, Ferrite morphology and variations in ferrite content in austenitic stainless steel welds,Weld. J. 60(4):63s-71s (1981).
J. M. Vitek and S. A. David. The solidification and aging behavior of types 308 and 308CRE stainless steel welds,Weld. J. 63:246s-253s (1984).
J. M. Vitek and S. A. David. The sigma phase transformation in austenitic stainless steel,Weld. J. 65:106s-111s (1986).
J. M. Vitek, S. A. David, and V. K. Sikka. Examination of types 308 and 308CRE stainless steels after interrupted creep testing,Weld J. 71:421s-435s (1992).
R. T. King, J. O. Stiegler, and G. M. Goodwin, Relation between mechanical properties and microstructure in CRE type 308 weldments,Weld. J. 53:307s-313s (1974).
J. O. Stiegler, R. T. King, and G. M. Goodwin, Effect of residual elements on fracture characteristics and creep ductility of type 308 stainless steel weld metal,J. Eng. Mater. Technol. 97:245–250 (1975).
S. S. Babu, S. A. David, and J. M. Vitek, Work in progress (Oak Ridge National Laboratory, 1995).
S. A. David, J. M. Vitek, J. R. Keiser, and W. C. Oliver, Nanoindentation microhardness study of low-temperature ferrite decomposition in austenitic stainless steel welds,Weld. J. 66:235s-240s (1987).
J. M. Vitek, S. A. David, D. J. Alexander, J. R. Keiser, and R. K. Nanstad, Low temperature aging behavior of type 308 stainless steel weld metal,Acta Met. Mater. 39(4):503–516 (1991).
R. M. Fisher, E. J. Dulis, and K. G. Carroll, Identification of the precipitate accompanying 885‡F embrittlement in chromium steels,Trans. AIME 197:690–695 (1953).
R. O. Williams and H. W. Paxton, The nature of aging binary iron-chromium alloys around 500‡C,J. Iron Steel Inst. 185:358–374 (1957).
D. Chandra and L. H. Schwartz, Mossbauer effect study of the 475‡f decomposition of Fe-Cr,Metall. Trans. A. 2A:511–519 (1971).
J. Nishizawa, M. Hasebe, and M. Ko, Thermodynamic analysis of solubility and miscibility gap in ferromagnetic alpha iron alloys,Acta. Metall. 27:817–828 (1979).
T. J. Nichol, A. Dotta, and G. Aggun, Embrittlement of ferritic stainless steel,Metall. Trans. A 11A:573–585 (1980).
S. S. Brenner, M. K. Miller, and W. A. Soffa, Spinodal decomposition of iron-32 at % chromium at 470‡C,Scripta Metall. 16:831–836 (1982).
J. M. Vitek, G-phase formation in aged type 308 stainless steel,Metall. Trans. A. 18A:154–156 (1987).
H. M. Chung and O. K. Chopra, Kinetics and mechanism of thermal aging embrittlement of duplex stainless steels, inEnvironmental Degradation of Materials in Nuclear Power SystemsWater Reactors, G. J. Theus and J. R. Weeks, eds. (TMS-AIME, Warrendale, PA, 1988), p. 359.
M. K. Miller and J. Bentley, Characterization of fine-scale microstructures in aged primary coolant pipe steels, inEnvironmental Degradation of Materials in Nuclear Power Systems-Water Reactors, G. J. Theus and J. R. Weeks, eds. (TMS-AIME, Warrendale, PA, 1988), p. 341.
M. Vrinat, R. Cozar, and Y. Meyzaud, Precipitated phases in the ferrite of aged cast stainless steels,Scr. Metall. 20:1101–1106 (1986).
D. J. Alexander, J. M. Vitek. and S. A. David, Long-term aging of type 308 stainless steel welds: Effects on properties and microstructure, inInternational Trends in Welding Science and Technology, S. A. David and J. M. Vitek, eds. (ASM-International, Materials Park, Ohio, 1993), p. 557.
J. M. Vitek, S. A. David, and D. J. Alexander, Oak Ridge National Laboratory, Oak Ridge, TN (1995).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
David, S.A., Vitek, J.M. & Alexander, D.J. Embrittlement of austenitic stainless steel welds. J Nondestruct Eval 15, 129–136 (1996). https://doi.org/10.1007/BF00732040
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF00732040