Abstract
Our studies have established that unidirectional graphite fibre composites show excellent fatigue resistance with only a 20 to 30% decrease in strength with cycling. Fatigue failures invariably occurred on the surfaces undergoing compression and were identified by scanning electron microscope studies as resulting from matrix failure adjacent to local fibre buckling failure zones. In contrast, glass fibre composites showed a much larger (70%) loss in strength under cyclic loading. At intermediate lives, failure occurred by the growth of matrix microcracks followed by delamination, while at long lives, the applied stress levels were below the microcrack initiation stress and behaviour was characterized by crack nucleation processes.
These results have suggested a criterion for predicting high cycle fatigue strength which is based on the hypothesis that for failure to occur, the maximum applied effective cyclic strain in the composite must exceed a critical value which depends upon the fatigue response of the matrix material. The main assumption is that localized fatigue failures in the matrix are the predominant contributions to the ultimate fatigue failure of the composite.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
C. K. H. Dharan, in “Fatigue of Composites”, STP 569, (American Society for Testing and Materials, Philadelphia, 1975).
M. J. Owen andS. Morris, Proceedings of the 25th Annual Technical Conference, Society of Plastics Industries, New York (1970) Paper 8E.
C. K. H. Dharan, in “Failure Modes in Composites II”, (The Metallurgical Society of AIME, New York, 1974).
W. R. Jones andJ. W. Johnson,Carbon 9 (1971) 645.
B. W. Rosen, in “Fiber Composite Materials” (American Society for Metals, Metals Park, Ohio, 1965) p. 37.
S. Hanasaki andY. J. Hasegawa,J. Comp. Mats. 8 (1974) 306.
E. V. Murphy andB. F. Jones,Carbon 9 (1971) 91.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Dharan, C.K.H. Fatigue failure in graphite fibre and glass fibre-polymer composites. J Mater Sci 10, 1665–1670 (1975). https://doi.org/10.1007/BF00554927
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00554927