Abstract
The increasing usage of ultrafine ceramic powders in the fabrication of highly reliable ceramics results in a growing interest in appropriate processing conditions for these powders. During processing the extremely high surface areas might lead to significant absorbtion of oxygen even at low temperatures. But especially in this temperature regime, oxidation data of powders are rarely available; as far as the authors know, no investigations have been published in the case of ultrafine powders with particle sizes below 100 nm. In this study the oxidation kinetics of ultrafine (Si-) SiC powders (∼ 20 nm) in the temperature range between room temperature and 1000 °C in air were investigated. Thermobalance experiments showed that at least three different oxidation mechanisms are operating. At temperature above 650 °C the fraction of completion R is proportional to the square root of time, indicating a diffusion-controlled mechanism (activation energy ∼-1.8 eV). At lower temperatures the best data fit is obtained by a Cabrera-Mott-like equation. At room temperature and for thin silica-layer thicknesses a third oxidation mechanism was determined. The formation of the first monolayer of silicon oxide obeys the kinetics of a first-order reaction, namely an exponential one with a time constant of 1.25× 10−4 s−1. An investigation of the influence of oxygen pressure on the oxidation of ultrafine Si-SiC powders revealed a low pressure influence at 500 °C. An approximately linear relation between pressure and oxidation rate constant is observed between 30 and 1000 mbar air pressure at 800°C. The kinetic data were used to construct an “oxidation map” for ultrafine SiC powders, as a help to determine appropriate processing conditions.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
S. C. Singhal, in “Ceramics for High-Performance Applications”, Proceedings of 2nd Army Materials Technology Conference, Hyannis, Massachusetts, November 1973, edited by J. J. Burke, A. E. Gorom, R. N. Katz (Metals and Ceramics Information Center) p. 533.
S. Dutta, J. Mater. Sci. 19 (1984) 1307.
K. L. Luthra, J. Amer. Ceram. Soc. 74 (1991) 1095.
Gmelin Handbook, Silicon, Part B, Section 3, p. 327.
F. P. Fehlner, J. Electrochem. Soc.: Solid-State Sci. Technol 119 (1972) 1723.
G. J. Declerck, in Proceedings of NATO Advanced Study Institute on Microelectronic Materials and Processes, Ciocco, Italy, June 1986, edited by R. A. Levy (Klower Academic) p. 79.
J. Förster, M. Von Hoesslin, J. H. Schäfer, J. Uhlenbusch and W. Viöl, in Proceedings of 10th International Symposium on Plasma Chemistry, FRG, 1991, Vol. 1, p. 1.
P. J. Jorgensen, M. E. Wadsworth and I. B. Cutler, J. Amer. Ceram. Soc. 42 (1959) 613.
R. E. Carter, J. Chem. Phys. 34 (1961) 2010.
K. Motzfeld, Acta Chem. Scand. 18 (1964) 1596.
R. Ebi, thesis, University of Karlsruhe, Germany (1973).
R. C. Harris and R. L. Call, in “Silicon Carbide”, edited by R. C. Marshall, J. W. Forest and C. E. Ryan (University of South Carolina Press, Coloumbia, 1973) p. 329.
F. P. Fehlner, “Low-Temperature Oxidation” (Wiley, New York, 1986) p. 18.
R. Ghez, J. Chem. Phys. 58 (1973) 1838.
F. P. Fehlner, “Low-Temperature Oxidation” (Wiley, New York, 1986) p. 180.
R. Lenk, A. F. Kriwostschepow and J. G. Frolow, Chem. Chem. Technol. (in Russian) 54 (148) (1987) 48.
F. P. Fehlner, “Low-Temperature Oxidation” (Wiley, New York, 1986) p. 223.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Vaben, R., Stöver, D. Oxidation of ultrafine (Si-) SiC powders. JOURNAL OF MATERIALS SCIENCE 29, 3791–3796 (1994). https://doi.org/10.1007/BF00357350
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF00357350