Abstract
The static and impact fracture toughnesses of a polybutylene terephthalate/polycarbonate/impact modifier (PBT/PC/IM) blend were studied at different temperatures. The static fracture toughness of the blend was evaluated via the specific fracture work concept and the J-integral analysis. A comparison of these two analytical methods showed that the specific essential fracture work, W e, was equivalent to the \(J_{|{\text{C}}_{{\text{ - 81}}} } \) obtained by the ASTM E813-81 procedure, representing the crack initiation resistance of the material. The discrepancy between W e and \(J_{|{\text{C}}_{{\text{ - 89}}} } \) of ASTM E813-89 was caused by the extra energy component in \(J_{|{\text{C}}_{{\text{ - 89}}} } \) consumed by a 0.2 mm crack growth. Impact fracture toughness was also analysed using the specific essential fracture work approach. When the fracture was elastic, W e was equivalent to the critical potential energy release rate, G IC, obtained via LEFM analysis. Temperature and strain-rate effects on the fracture toughness were also studied. The increase in impact toughness with temperature was attributed to two different toughening mechanisms, namely, the relaxation processes of the rubbery particles and the parent polymers in a relatively low-temperature range and thermal blunting of the crack tip at higher temperatures. The enhancement in static fracture toughness at temperatures below — 60 °C was thought to be caused by plastic crack-tip blunting, but the monotonic reduction in yield stress was largely responsible for the toughness decreasing with higher temperatures. The temperature-dependent fracture toughness data obtained in static tests could be horizontally shifted to match roughly the data for the impact tests, indicating the existence of a time-temperature equivalence relationship.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
J. G. Williams, “Fracture Mechanics of Polymers” (Ellis Horwood, Chichester, 1984).
M. K. V. Chan and J. G. Williams, Polym. Engng Sci. 21 (1981) 1019.
P. Flueler, D. R. Roberts, J. F. Mandell and F. J. McGerry, ASTM STP 736 (American Society for Testing and Materials, Philadelphia, PA, 1981) p. 15.
J. R. Rice, J. Appl. Mech. 35 (1968) 379.
J. A. Begley and J. D. Lands, in “Fracture Toughness”, ASTM STP 514 (American Society for Testing and Materials, Philadelphia, PA, 1972) pp. 1–20.
J. D. Lands and J. A. Begley, ibid.in “, p. 24.
J. D. Sumpter and C. E. Turner, Int. J. Fract. 9 (1973) 320.
ASTM Standard E813-81, 1981 Annual Book of ASTM Standards, Part 10 (American Society for Testing and Materials, Philadelphia, PA, 1981) p. 810.
ASTM Standard E813-87, 1987 Annual Book of ASTM Standards, Part 10 (American Society for Testing and Materials, Philadelphia, PA, 1987) p. 1968.
ASTM Standard E813-89, 1989 Annual Book of ASTM Standards, Part 10 (American Society for Testing and Materials, Philadelphia, PA, 1989) p. 700.
S. Hashemi and J. G. Williams, Polymer 27 (1986) 384.
D. D. Huang and J. G. Williams, J. Mater. Sci. 22 (1987) 2503.
I. Narisawa and M. T. Takemori, Polym. Engng Sci. 29 (1989) 671.
H. Swei, B. Crist and S. H. Carr, Polymer 32 (1991) 1440.
Y.-W. Mai and B. Cotterell, Int. J. Fract. 32 (1986) 105.
Y.-W. Mai, in Proceedings of International Symposium on “How to improve the toughness of polymers and composites”, Yamagata University, Yamagata, Japan, 8 October 1990, pp. 138–45.
B. Cotterell and J. K. Reddell, Int. J. Fract. 13 (1977) 267.
Y.-W. Mai and B. Cotterell, Engng Fract. Mech. 21 (1985) 123.
B. Cotterell, E. Lee and Y.-W. Mai, Int. J. Fract. 20 (1982) 243.
Y.-W. Mai and B. Cotterell, J. Mater. Sci. 15 (1980) 2296.
C. B. Bucknall, “Toughened Plastics” (Applied Science, London, 1977).
A. S. Wood, Modern Plastics April (1985) 81.
K. Weirauch, Kunststoffe 75 (1985) 700.
G. P. Marshall, J. G. Williams and C. E. Turner, J. Mater. Sci. 8 (1973) 949.
H. R. Brown, J. Mater. Sci. 8 (1973) 941.
M. Bramuzzo, Polym. Engng Sci. 29 (1989) 1077.
T. Vu-Khanh, Polymer 29 (1988) 1979.
P. C. Paris, H. Tada, A. Zahoor and H. Ernst, in ASTM STP 668 (American Society for Testing and Materials, Philadelphia, PA, 1979) p. 5.
A. Zahoor and P. C. Paris, J. Eng. Mater. Tech. 103 (1981) 46.
Y.-W. Mai, Polym. Commun. 30 (1989) 330.
J. S. Wu and Y.-W. Mai, J. Mater. Sci. 28 (1993)
D. C. Wahrmund, D. R. Paul and J. W. Barlow, J. Appl. Polym. Sci. 22 (1978) 2155.
G. P. Marshall, L. H. Coutts and J. G. Williams, J. Mater. Sci. 9 (1974) 1409.
M. Parvin and J. G. Williams, ibid. 10 (1975) 1883.
F. M. Burdekin and D. E. W. Stone, J Strain Anal. 1 (1966) 145.
M. W. Birch and J. G. Williams, Int. J. Fract. 14 (1978) 69.
E. Plati and J. G. Williams, Polym. Engng Sci. 15 (1975) 470.
S.-X. Wu, Y.-W. Mai and B. Cotterell, Int. J. Mech. Sci. 29 (1987) 557.
S.-X. Wu, PhD thesis, The University of Sydney, Sydney, Australia (1990).
F. Speroni, E. Castoldi, P. Fabbri and T. Casiraghi, J. Mater. Sci. 24 (1989) 2165.
P. I. Vincent, Polymer 15 (1974) 111.
S. Yamini and R. J. Young, ibid. 18 (1977) 1075.
A. J. Kinloch, S. J. Shaw, D. A. Tod and D. L. Hunston, ibid. 24 (1983) 1341.
Idem, ibid. 24 (1983) 1355.
M. Kisbenyi, M. W. Birch, J. M. Hodgkinson and J. G. Williams, ibid. 20 (1979) 1289.
E. Plati and J. G. Williams, ibid. 16 (1975) 915.
I.-M. Low and Y.-W. Mai, J. Mater. Sci. 24 (1989) 1634.
J. G. Williams and J. M. Hodgkinson, Proc. R. Soc. Lond. A375 (81) 231.
A. J. Kinloch and R. J. Young, “Fracture Behaviour of Polymers” (Applied Science, London, 1983).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Wu, J., Mai, Y.W. & Cotterell, B. Fracture toughness and fracture mechanisms of PBT/PC/IM blend. JOURNAL OF MATERIALS SCIENCE 28, 3373–3384 (1993). https://doi.org/10.1007/BF00354261
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00354261