The effects of glass-fibre reinforcement and annealing on the deformation and fracture behaviour of nylon 6,6 were investigated. The roles of glass fibres were examined by varying the glass fibre content and the fibre length, and by in situ fracture studies in front of crack tips. The effects of microstructural changes were investigated by imposing various annealing conditions on the specimens. The results indicated that the fracture toughness showed a sharp decrease due to stress concentrations at fibre ends when the fibre volume fraction was small. Above a critical fibre volume fraction, it was found that the fracture toughness can be substantially increased by enhanced localized matrix plasticity at fibre ends. The competing roles of glass fibre ends were consistent with microstructure sensitive fracture mechanics models of failure based on the attainment of a critical stress or strain over a critical microstructural distance in the crack-tip region. Upon annealing above a critical annealing time the unreinforced nylon 6,6 showed a drastic decrease in the strength and ductility, corresponding to a loss of the constant-load deformation region prior to necking. However, the fracture toughness of unreinforced nylon 6,6 was only moderately reduced by annealing. On the other hand, the fracture toughness of the composites showed a significant increase upon annealing. The combined effects of glass fibres and annealing on microstructures and overall property optimization of the composites are also discussed.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
M. F. Ashby, Acta Metall. 37 (1989) 1273.
T. Vu-Khanh, Polym. Compos. 8 (1987) 363.
P. K. Mallick, “Fiber-reinforced Composites: Materials, Manufacturing and Design” (Marcel Dekker, New York, 1988) p. 1.
D. W. Clegg and A. A. Collyer (eds), “Mechanical Properties of Reinforced Thermoplastics” (Applied Science, New York, 1986).
W. V. Totow and B. J. Lanham, “Reinforced Thermoplastics” (Applied Science, London, 1975) p. 1.
M. J. Folkes, “Short Fiber Reinforced Thermoplastics” (Research Studies Press, Chichester, 1982) p. 31.
P. T. Curtis, M. G. Bader and J. E. Bailey, J. Mater. Sci. 13 (1978) 377.
N. Sato, T. Kurauchi, S. Sato and O. Kamigaito, ibid. 26 (1991) 3891.
K. Takahashi and N. S. Choi, ibid. 26 (1991) 4648.
S. V. Nair, M. L. Shiao and P. D. Garrett, ibid. 27 (1992) 1085.
B. Lauke, B. Schultrich and W. Pompe, Polym. Plast. Technol. Eng. 29 (1990) 607.
J. M. Schultz, Polym. Eng. Sci. 24 (1984) 770.
A. J. Kinloch and R. J. Young, “Fracture Behavior of Polymers” (Applied Science, London, 1983) Ch. 9.
A. Peterlin, J. Appl. Phys. 35 (1964) 75.
E. W. Fisher, Pure Appl. Chem. 31 (1972) 113.
H. W. Starkweather Jr, G. E. Moore, J. E. Hansen, T. M. Roder and R. E. Brooks, J. Polym. Sci. XXI (1956) 189.
G. C. Alfonso, E. Pedemonte and C. Ponzetti, Polymer 20 (1979) 104.
D. P. Russell and P. W. R. Beaumont, J. Mater. Sci. 15 (1980) 216.
J. P. Bell and J. H. Dumbleton, J. Polym. Sci. A-2 7 (1969) 1033.
R. Elenga, R. Seguela and F. Rietsch, Polymer 32 (1991) 1975.
R. S. Schotland, Polym. Eng. Sci. 6 (1966) 244.
B. Wunderlich, “Macromolecular Physics”, Vol. 3 (Academic Press, New York, 1980) Ch. 9.
M. J. McCready and J. M. Schultz, J. Polym. Sci. Polym. Phys. 17 (1979) 725.
S. Nagou and S. Oba, J. Macromol. Sci. Phys. B18 (1980) 281.
G. P. Desio and L. Rebenfeld, J. Appl. Polym. Sci. 39 (1990) 825.
T. Bessell and J. B. Shortfall, J. Mater. Sci. 10 (1975) 2035.
M. L. Shiao, S. V. Nair, P. D. Garrett and R. E. Pollard, ibid. (1994).
“Protocal on Plain-Strain Fracture Toughness and Strain Energy Release Rate of Plastic Materials”, ASTM Subcommittee D20.10.21 (American Society for Testing and Materials, Philadelphia, PA, 1989).
P. Chang and J. A. Donovan, J. Mater. Sci. 24 (1989) 816.
B. D. Aggarwala and E. Saibel, Phys. Chem. Glasses 2 (1961) 137.
T. J. Bessell, D. Hull and J. B. Shortfall, J. Mater. Sci. 10 (1975) 1127.
J. C. Haplin and J. L. Kardos, Polym. Eng. Sci. 16 (1976) 344.
M. I. Kohan (ed.), “Nylon Plastics” (Wiley, New York, 1973) p. 333.
P. Chang, PhD thesis, University of Massachusetts, Amherst (1992).
Y. Liu and J. A. Donovan, private communication (1992).
E. Dobrovolny-Marand, PhD thesis, University of Massachusetts, Amherst (1987).
B. Budiansky, J. W. Hutchinson and J. C. Lambropoulos, Int. J. Solids Struct. 19 (1983) 337.
R. K. Pandey and S. Banerjee, Int. Fract. Mech. 10 (1978) 817.
R. O. Ritchie, W. L. Server and R. A. Wullaert, Metall. Trans. 10A (1979) 1557.
J. R. Rice and M. A. Johnson, “Inelastic Behavior of Solids”, edited by M. F. Kanninen, W. F. Adler, A. R. Rosenfield and R. I. Jaffee, (McGraw Hill, New York, 1970) p. 641.
S. V. Nair and M. L. Shiao, to be published.
F. J. Padden and H. D. Keith, J. Appl. Phys. 30 (1959) 1479.
N. Sato, T. Kurauchi, S. Sato and O. Kamigaito, J. Compos. Mater. 22 (1988) 850.
J. C. Watkins, P. C., Gaa and R. G. Swisher, in “Proceedings of the ANTEC '88”, Atlanta, April 1988 (Society of Plastic Engineers, Brookfield, CT, 1988) p. 528.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Shiao, M.L., Nair, S.V., Garrett, P.D. et al. Effect of glass-fibre reinforcement and annealing on microstructure and mechanical behaviour of nylon 6,6. JOURNAL OF MATERIALS SCIENCE 29, 1739–1752 (1994). https://doi.org/10.1007/BF00351291
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF00351291