Generally, inflammatory response to the metal stents contributes to the formation of in-stent restenosis. Howerver, recent development of biodegradable stents made of magnesium alloys has a potential to overcome this drawback. Nevertheless, the degradation profile of such stents and the influence on the endothelial cells remained unclear.
In this study, the flat magnesium alloyed sheets cut by wire electrical discharge machine were immersed in distill water or culture medium. In addition, human aortic endothelial cells (HAEC) were seeded (800 cells/mm2) onto various magnesium alloyed sheets, including Mg-Al-Zn alloys (AZ31, AZ91) and Mg-Al-Mn alloy (AM60). Cells seeded onto tissue culture treated polystyrene dish coated with gelatin were used as controls. Forty-eight hours later, the cells were examined by immunofluorescence microscopy.
The results were shown that content of Mg2+ within 15 weeks gradually increased to more than 40 mg/dL in the culture medium, but remained less than 10 mg/dL in the water. For all magnesium groups the cellularity at 48 hours was less than 60% of that of the controls (p<0.01). Comparison among the magnesium alloyed groups showed that both AZ31 and AM60 have lower values of cellularity, compared to the AZ91 (AZ31: 164 cells/mm2; AM60: 318 cells/mm2; AZ91: 442 cells/mm2; AZ91 vs either AZ31 or AM60, both p<0.05). Immunfluorescence microscopy showed that cells grown on such magnesium metals expressed less amounts of Von Willebrand factor (VWF), connexin43 (Cx43) gap junctions, and endothelial nitric oxide synthase (eNOS).
The conclusion suggested that degradation of magnesium alloys are enhanced in culture medium, in which HAEC’s had a retarded growth and protein expression profile grown on the metal. Otherwise, it also suggested that strategies to improve the biocompatibility of stents made of magnesium alloy are necessary.
Access provided by Autonomous University of Puebla. Download to read the full chapter text
Chapter PDF
Similar content being viewed by others
Keywords
- Magnesium Alloy
- Wire Electrical Discharge Machine
- Human Aortic Endothelial Cell
- Magnesium Alloyed Sheet
- Metallic Sheet
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.
References
Heublein B., Rohde R., Kaese V., Niemeyer M., Hartung W. and Haverich A. (2003): “Biocorrosion of magnesium alloys: a new principle in cardiovascular implant technology?”, Heart. 89 p.p. 651–656
Carlo D M., Huw G., Omer G., Nicolas P., Jan V., Marc B., Koen D., Bernhard H., Roland R., Victor K., Charles I. and Raimund E. (2004): “Drug-eluting bioabsorbable magnesium stent”, J Interven Cardiol. 17 p.p. 391–395
Witte F., Kaese V., Haferkamp H., Switzer E., Meyer-Lindenberg A., Wirth C J. and Windhagen H. (2005): “In vivo corrosion of four magnesium alloys and the associated bone response”, Biomaterials 26 p.p. 3557–3563
Maier J A, Bernardini D, Rayssiguier Y and Mazur A. (2004): “High concentrations of magnesium modulate vascular endothelial cell behaviour in vitro”, Biochim Biophys Acta 6–12
Maier J A, Malpuech-Brugere C, Zimowska W, Rayssiguier Y and Mazur A. (2004): “Low magnesium promotes endothelial cell dysfunction: implications for atherosclerosis, inflammation and thrombosis”, Biochim Biophys Acta p.p. 13–21
Witte F, Kaese V, Haferkamp H, Switzer E, Meyer-Lindenberg A, Wirth C J and Windhagen H. (2005): “In vivo corrosion of four magnesium alloys and the associated bone response”, Biomaterials 26 p.p. 3557–3563
Michael B, Esthie R, Iris B, Arie R, Gad K and Jacob G. (2004): “Zinc reduces intimal hyperplasia in the rat carotid injury model”, Atherosclerosis 175 p.p. 229–234
Yeh H I., Lu S K., Tian T Y., Hong R C., Lee W H. and Tsai C H. (2006): “Comparison of endothelial cells grown on different stent materials” J Biomed Mater Res 76A p.p. 835–841
Lu S K., Yeh H I., Huang C W., Tian T Y., Chen C Y. and Lee W H. (2005): “Phenotypic change of HUVEC grown on stent material coated with Titanium (Ti) and Tantalum (Ta) compounds”, ICBME Int. Conf. 4A3-10 Singapore
Yeh H I., Lu S K., Tian T Y., Chiang C L., Lee W H. and Tsai C H. (2004): “Down-regulation of connexin43 Gap Junctions, eNOS, and VWF in endothelial cells grown on stent materials”, Int J Cardiol. S29 Taiwan
Tian T Y., Lu S K., Yeh H I., Chiang C L., Lee W H. and Tsai C H. (2003): “Phenotypic change of endothelial cells grown on stent materials of various properties”, Acta Cardiol Sin. 19:S200 Taiwan
Mark P S., Alexis M P., Jerawala H. and George D. (2006): “Magnesium and its alloys as orthopaedic biomaterials: A revies”, Biomaterials 27 p.p. 1728–1734
Frank W., Jens F., Jens N., Horst A C., Volker K., Alexander P., Felix B. and Henning W. (2006): “In vitro and in vivo corrosion measurements of magnesium alloys”, Biomaterials 27 p.p. 1013–1018
Author information
Authors and Affiliations
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2007 Springer-Verlag Berlin Heidelberg
About this paper
Cite this paper
Lu, S.K., Yeh, H.I., Tian, T.Y., Lee, W.H. (2007). Degradation of Magnesium Alloys in Biological Solutions and Reduced Phenotypic Expression of Endothelial Cell Grown on These Alloys. In: Ibrahim, F., Osman, N.A.A., Usman, J., Kadri, N.A. (eds) 3rd Kuala Lumpur International Conference on Biomedical Engineering 2006. IFMBE Proceedings, vol 15. Springer, Berlin, Heidelberg. https://doi.org/10.1007/978-3-540-68017-8_25
Download citation
DOI: https://doi.org/10.1007/978-3-540-68017-8_25
Publisher Name: Springer, Berlin, Heidelberg
Print ISBN: 978-3-540-68016-1
Online ISBN: 978-3-540-68017-8
eBook Packages: EngineeringEngineering (R0)