Abstract
Nano-fillers reinforced with polymer-based composites have found to enhance the tribological properties in polymer composites. Alumina (Al2O3) and molybdenum-di-sulphide (MoS2) were selected as nano-fillers in the present research work. Al2O3 and MoS2 fillers were mixed with the epoxy resin in the concentration of 0.1, 0.2, 0.4 and 0.7% by volume of the epoxy resin. The reinforced epoxy resin was used as a matrix material along with the aircraft grade carbon fabric as the primary reinforcement. Test panels were fabricated using vacuum-assisted resin transfer moulding technique (VARTM), and samples were extracted using water jet cut as per the dimensions given in the ASTM standards of three-body wear (ASTM G-65) and two-body wear (ASTM G-99). Scanning electron microscopic (SEM) studies revealed the even distribution of the MoS2 when disbursed with ultrasonicator than by manual mixing. The three-body and two-body wear tests were carried out at a load of 24 and 48 N. The composite reinforced with 0.4% of MoS2 particulate has shown the decrease in wear rate by 20.45% as compared to that of the Al2O3 particulate-based composites in three-body wear test when the applied load was 48 N, whereas in two-body wear test, the composite reinforced with 0.4% of MoS2 particulate has shown the decrease in wear rate by 16.13% as compared to that of the Al2O3 particulate-based composites. SEM studies of worn-out surfaces revealed that the mode of failure in worn-out samples was due to delaminate at the fibre matrix interface. SEM images also revealed that better bonding between fibre and matrix can be well achieved for the 0.4% concentration of nano-reinforcements as compared to that of the composites with 0.2% concentration of nano-reinforcements.
Access provided by Autonomous University of Puebla. Download conference paper PDF
Similar content being viewed by others
Keywords
1 Introduction
Carbon fibre-reinforced polymer composites command the major share in the structural polymer composite industry. It is widely used for various applications such as aerospace, aeronautical, automobile, locomotive, and recreational applications. Amongst the various advantages, the polymer composites offer one noticeable advantage which is its flexibility in allowing the user to tailor the properties as per the end application needs. The few amongst them are higher strength-to-weight ratio, higher stiffness and higher fatigue resistance. Profound tests were carried out to determine the array of properties related to structural as well as tribological properties of the carbon fibre-reinforced polymer composites [1]. However, the research work to evaluate the significance of nano-sized reinforcements on the tribological properties of the carbon fibre-reinforced polymer composites has not been dealt in an intense manner [2]. Hence, this research work aimed at studying the significance of reinforcing the carbon fibre-reinforced composites with alumina (Al2O3) and molybdenum-di-sulphide (MoS2) separately and compared their effect on the tribological properties based on test results that obtained by three-body wear tests and two-body wear tests.
2 Literature Review
GuangShi et al. had assessed the impact of nano-sized alumina fillers on the sliding wear behaviour on the epoxy-based polymer composites. The researchers were successful in reducing the specific wear rate by 97% when the volume of the nano-alumina used was 0.24 vol.% than compared to the bare epoxy resin [3]. B Suresha et al. evaluated the tribological properties of carbon–epoxy and glass–epoxy-reinforced polymer composites using pin-on-disc apparatus. It was found that carbon–epoxy samples showed lower friction and lower slide wear loss [3, 4]. A Shafiei-Zarghani et al. had developed the Al2O3 nano-composite surface layer on an Al alloy using friction stir welding (FSP). FSP made significant enhancement in the mean microhardness of the nano-composite layered composite by three times as compared to the bare aluminium substrate [5].
V.P. Gordienko et al. studied the significance of adding additives less than one micrometer (<1 µm) with polyolefin such as polyethylene and polypropylene by hot pressing under a pressure of 35 MPa for 20 min by adding inorganic additive molybdenum-di-sulphide in the range of 0.1 to 10% by volume. It was found that there was increase in the hardness due to the addition of molybdenum in a tracer quantity of 0.3 to 0.5% which enhanced the wear resistance of the composite by 8 to 10% [6]. Zhu Peng et al. conducted the study of the tribology performance of molybdenum-di-sulphide reinforced thermoplastic polyamide under dry and wet lubrication conditions. It was found that mechanical performances were superior the thermoplastic filled with molybdenum-di-sulphide [7]. P. H. Sivaraman et al. studied the influence of molybdenum-di-sulphide composition on the wear characteristics of the composites fabricated. SEM images were used to study the worn surfaces. It was found that the there was a significant improvement in the composite properties which were doped with molybdenum-di-sulphide than compared with that of the bare composite [8].
From the above discussion, it was concluded that there is enough documented research work carried out in fabrication polymer-based nano-composites using nano-sized alumina and nano-sized molybdenum-di-sulphide. Most of the work involved fabricating the samples from hand layup and compression moulding. But no evident was found about fabrication of composite using VARTM method and testing the composites with three-/two-body abrasive wear test and traditional pin-on-disc apparatus. Hence, the present research work concentrated on developing the VARTM fabricated nano-composites reinforced with nano-sized filler in different proportions and conducting three-body abrasive wear and two-body abrasive wear for performance study.
3 Materials and Method of Fabrication
Structural grade carbon fabric used as a primary fibre and epoxy resin HTR 212 were mixed with hardener HTR-386-99 for preparing the composites. These materials were procured from Aircraft Spruce, USA. It is noted from the supplier that the size of alumina (Al2O3) particles is about 18 nm and the size molybdenum-di-sulphide (MoS2) particle is in range of 80 nm–100 nm with 99.9% purity. These particles were used as nano-fillers in the volume of 0.1, 0.2, 0.4 and 0.7% to develop nano-filler-reinforced polymer composites. Vacuum-assisted resin transfer moulding (VARTM) method was used for fabricating the composite panels. The ultrasound powered ultrasonicator is used for uniform distribution of the nano-fillers in the pure epoxy resin. The whole set-up is shown in Fig. 1. Panels were fabricated resembling the size of the VARTM mould, and samples were extracted by water jet cutting as per the ASTM standards. The photographs of the extracted samples are as shown in Fig. 2. The scanning electron microscope (SEM) studies were conducted to understand the significance of using the ultrasonicator to mix the nano-reinforcements into the epoxy resin as compared to that of the manual mixing. The SEM micrographs reveal that MoS2 nano-filler in the epoxy resin is evenly distributed when it is mixed with ultrasonicator. The SEM micrographs also disclose that the porosity level is almost nil due to ultrasonication.
4 Experimental Testing
4.1 Three-Body Abrasive Wear Test
Three-body abrasive wear tests were conducted in accordance with ASTM G-65. The equipment used for conducting the three-body wear test is shown in Fig. 3. The initial weight of the specimen was recorded. The velocity and test time were set. Abrasive particles from the hopper were introduced between the test specimen and rotating cholorobutyl rubber tyre abrasive wheel (hardness; Durometer-A 58-62). At the end of the set duration, specimen was removed and cleaned thoroughly. The final weight of the tested specimen was recorded for measuring the wear loss. The above procedure was repeated for varying abrading radius for different concentrations of the nano-fillers. These experiments were carried out at two different loads, i.e., 24 N and 48 N [8].
4.2 Two-Body Wear Test
Two-body abrasive wear tests were conducted in accordance with ASTM G-99. The rotating disc of the apparatus was cleaned using the acetone to remove any dirt, grease or any material debris attached from the previous test. Initial weight of the sample was measured and recorded, and the specimen was fixed to the sleeve based upon the preselected abrading radius. The specimen was loaded by the predefined magnitude of weight and brought in contact with the rotating disc. As the machine was switched on, the specimen in contact with the rotating disc abraded gradually. The test was performed for a fixed duration of time as per standard, and finally, the weight of the specimen measured after the test was conducted, thus measuring the wear loss. The above procedure was repeated for varying abrading radius for different concentrations of the nano-fillers used at two different weights of 24 N and 48 N [9] (Fig. 4).
5 Results and Discussions
5.1 Scanning Electron Microscope (SEM) Studies
Figure 5 shows the SEM images of MoS2 dispersement into the epoxy resin matrix done manually as well as by using the ultrasonicator. The figure reveals composites developed by the dispersing the reinforcements by manually mixing (Fig. 5a) is more porous that the dispersement done using the ultrasonicator (Fig. 5b).
5.2 Three-Body Wear Test
The plots shown in Figs. 6 and 7 show the variation of wear rate against the abrading distance for the various reinforcements (Al2O3 and MoS2) used at an operating load of 24 N and 48 N, respectively. The three-body wear test was conducted at above-mentioned loads at various (0.0, 0.1, 0.2, 0.4 and 0.7%) concentrations of Al2O3 and MoS2. In the plots shown in Figs. 6 and 7, it can be observed that the wear rate was directly proportional to the abrading distance; hence, the gradual increase in the wear rate can be observed for all the concentrations of reinforcement studied irrespective of whether it was Al2O3 reinforced composites or MoS2 reinforced composite. But however the detailed observation of the plots demonstrated that the wear rate in MoS2 reinforced composites is substantially lower as compared to that with composited reinforced with Al2O3. For instance, at 0.4% concentration Al2O3 sample wear rate was 0.135 units whereas that of the MoS2 was 0.1 units; i.e., the wear resistance of the MoS2 was approximately 25% more than that of the Al2O3 reinforced composites. This behaviour of the material could be attributed for the fact that Al2O3 being a hard reinforcement gets wore out and material gets removed from the specimens in the form of flakes; hence, the volume of material removed is higher, whereas in the case of MoS2, the very nature of the MoS2 is to act as a lubricating agent which in turn reduces the friction during the abrasion and also MoS2 is a soft reinforcement; hence, the material gets removed in the form of small powders, thereby reducing the rate of the material removal and hence the lesser wear rate. The behaviour of the samples tested at a load of 48 N has shown the similar trend.
5.3 Two-Body Wear Test
With reference to the above discussion in Sect. 5.2, the results obtained in the two-body wear test are shown in the plots given in Figs. 8 and 9. The results showed the similar trends as that in case of three-body wear test. However, the wear rate obtained was far more less as compared to that of the three-body wear results. The abnormalities in the last plot shown in Figs. 8 and 9 can be attributed for the reason of loose gripping of sample in the pin-on-disc machine.
5.4 Surface Morphology
Figures 10 and 11 show the SEM images of the worn-out surfaces of the composites with Al2O3 and MoS2 as nano-reinforcements with 0.2% and 0.4% of the concentrations. The severity of the wear in composites with 0.2% alumina is more than compared to that of composites reinforced with 0.2% MoS2. In the SEM micrographs shown in Fig. 10a, b it is evident that the failure is due to delamination at the fibre matrix interface. However, in the composites reinforced with 0.4% of Al2O3 and MoS2 as nano-reinforcements, the bonding is better as compared to the composites with 0.2% of the nano-reinforcements of Al2O3 and MoS2 as shown in Fig. 11a, b.
6 Conclusions
-
i.
Composite panels with Al2O3 and MoS2 nano-fillers were fabricated using vacuum-assisted resin transfer moulding (VARTM) in the varying concentrations discussed above, and performance study has been carried out in three-body and two-body abrasive wear test.
-
ii.
The nano-reinforcement of MoS2 was well distributed by the use of ultrasonicator as shown in the figure.
-
iii.
The results obtained clearly depicted that composites reinforced with MoS2 showed better wear resistance at all the concentrations studied as compared to that of the composites reinforced with Al2O3 nano-filler.
-
iv.
The Al2O3 being a hard reinforcement gets wore out in the form of flakes; hence, the wear rate is more as compared to MoS2, which by very nature acts as a lubricating agent which in turn reduces the friction during the abrasion as shown in Figs. 6.4 and 6.5.
-
v.
MoS2 is a soft reinforcement; hence, the material gets removed in the form of small powders, thereby reducing the rate of the material removal and hence the lesser wear rate.
-
vi.
The SEM images shown in Fig. 6.4 depict the severity of the worn-out surfaces of the composites 0.2% of nano-reinforcement of Al2O3 and MoS2 signifies that the mode of failure is due to fibre and matrix debonding.
-
vii.
The SEM micrographs shown in Fig. 6.5 reveal that the composites fabricated with 0.4% of nano-reinforcement of Al2O3 and MoS2 showed better bonding than that of the composites with 0.2% of nano-reinforcements.
References
Mallick PK (2007) Fiber reinforced polymer composites, materials, manufacturing and design. CRC Press, New York
Gopala Krishnaa K, Divakar C, Venkatesha K, Mohana CB, Mahesh Lohith KS (2010) Bulk temperature estimation during wear of a polymer composite pin. Wear 268:346–351
Soutis C (2005) Fiber reinforced composites in aircraft construction. Program Aero Sci 41(2):143–151
Shi G, Zhang MQ, Rong MZ, Wetzel B, Friedrich K (2004) Sliding wear behavior of epoxy containing nano-Al2O3 particles with different pretreatments. Wear 256:1072–1081
Suresha B, Chandramohan G, Samapthkumaran P, Seetharamu S, Vynatheya S (2006) Friction and wear characteristics of carbon-epoxy and glass-epoxy woven roving fiber composites. J Reinf Plast Compos 25(7):771–782
Gordienko VP, Sal’nikov VG, Podlesnyi RV, Kasperskii AV (2009) Hardness and wear resistance of certain polyolefins with additions of molybdenum-di-sulphide. Plasticheskie Massy (Plastic Weight) 10:13–15
Peng Z, Xiao W, Xiao-dong W, Pei H, Jun S (2013) Tribology performances of molybdenum disulfide reinforced thermoplastic polyimide under dry and water lubrication conditions. Ind Lubr Tribol 58(4):195–201
Sivaraman PH, Vimal R, Badrinarayanan S, Vignesh Kumar R (2017) Study of wear properties of jute/banana fibers reinforced molybdenum-di-sulphide modified epoxy composites. Mater Today Proc, Part A 4(2):2910–2919
ASTM G65-04 (2004) Standard test method for measuring abrasion using the dry sand/rubber wheel apparatus, Annual Book of ASTM Standards, vol 03.02
ASTM G99-17 (2017) Standard test method for wear testing with a pin-on-disk apparatus, ASTM International, West Conshohocken, PA
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2020 Springer Nature Singapore Pte Ltd.
About this paper
Cite this paper
Siddalingappa, S.K., Pal, B., Haseebuddin, M.R., Gopalakrishna, K. (2020). Tribological Behaviour of Carbon Fibre Polymer Composites Reinforced with Nano-fillers. In: Voruganti, H., Kumar, K., Krishna, P., Jin, X. (eds) Advances in Applied Mechanical Engineering. Lecture Notes in Mechanical Engineering. Springer, Singapore. https://doi.org/10.1007/978-981-15-1201-8_84
Download citation
DOI: https://doi.org/10.1007/978-981-15-1201-8_84
Published:
Publisher Name: Springer, Singapore
Print ISBN: 978-981-15-1200-1
Online ISBN: 978-981-15-1201-8
eBook Packages: EngineeringEngineering (R0)