Abstract
With the increasing demand of light-weight alloys, such as magnesium (Mg) and aluminum (Al), the need for joining these two alloys is unavoidable. In this study, AZ31B Mg and 1060 Al alloys were joined by continuous wave laser micro-welding using a 0.05 mm thick Cu/Zn interlayer. The microstructure and phases constituent of the weld seam were examined by optical microscope, SEM and EDS. The formation and distribution of the intermetallic compounds (IMCs) and the relationship between these structures and the micro-hardness of the weld were discussed in detail. The effect of Cu/Zn interlayer on the performance of Mg/Al joint was also analyzed. The results showed that Mg/Al IMCs were formed in the weld, which indicates that the Cu/Zn foil could not prevent the reaction between Mg and Al. However, the addition of Cu and Zn into the weld pool refined the microstructure by improving the number of eutectic structures. The micro-hardness of Mg/Al IMCs in the middle of the weld was very high which can be detrimental to the toughness of the Mg/Al joints.
Access provided by CONRICYT-eBooks. Download conference paper PDF
Similar content being viewed by others
Keywords
1 Introduction
Light-weight components are of high interest for aerospace and automotive industries because such components permit reducing fuel consumption and ease pressure on the fuel economy. This has led to the development of novel materials and advanced processing techniques. Magnesium and aluminum are preferred for their outstanding performance, low density (light weight) and high strength to weight ratio which are the most important characteristics in the manufacturing industries within the transportation sector. The continuous exploitation of applications for these alloys will lead to a broader use of Mg/Al composite structures in order to reduce the total weight of the structures without compromising the required strength [1,2,3]. However, it is still a challenge to produce reliable Mg/Al joints due to their different physical properties and the formation of excessive Mg-Al intermetallic compounds (IMCs) when both metals are mixed together. Hence, the way to produce high quality and high strength Mg/Al joints is still one of the main research topics worldwide. Previous researchers have focused their work on controlling the reaction between Mg and Al to a minimum level to minimize the formation of Mg-Al IMCs. The authors have used the following welding processes: TIG [4], spot welding [5], MIG [6], laser [7, 8], laser-MIG hybrid [9], friction stir welding [10, 11] and diffusion bonding [12] between others. However, the formation of Mg/Al IMCs is still.
Laser processing uses a high power density heat source and offers significant advantages when compared to arc welding low heat input is the main advantage because it not only reduces the distortion [13] but also minimizes the dilution of Mg into Al and vice-versa. Therefore, laser welding is a promising process to join Mg to Al. An alternative approach to reduce the formation of Mg/Al IMCs is by changing the chemical composition of the melt pool by using an interlayer and alloying the weld. No research about Mg/Al dissimilar welding with Cu/Zn interlayers has been carried out. Hence, in this study, 1060 Al alloy and AZ31B Mg alloy were welded by continuous wave (CW) laser welding. The microstructure and composition of the welds were investigated as well as the mechanical properties of the joints.
2 Experimental Details
Sheets of 1050 aluminum (0.5 × 30 × 105 mm) and AZ31B magnesium (1 × 30 × 105 mm) were used as base materials in this work. The typical chemical composition of the base metals is shown in Table 1. Interlayers of 0.05 mm thick copper brass (63 wt% Cu and 37 wt% Zn) were added between the Mg and Al sheets. The schematic diagram of the laser welding process set-up is shown in Fig. 1. The Mg sheet was placed on the top of Al sheet because the absorption of the laser radiation (1070 nm of wavelength) by Al is lower than that of Mg. Thus, the laser process becomes more efficient with Mg on the top because more energy is absorbed by the material. Mg and Al alloys are both active. Thus, shielding gas is generally required during the welding process. In this work pure shield argon was used with 15 l/min flow rate. Before welding, the surfaces of the base materials were ground with a grinder and degreased with acetone to remove the oxides and oil from the material surface. A CW fibre laser with 3 kW of maximum power was used. The characteristics of laser is listed in Table 2. The laser beam was characterized using a Primes GmbH focus monitor system and the D4σ method. The optimal parameters were power 525 W, travel speed 96 mm/s. The characteristics of laser used in this study is listed in Table 2.
After welding, the cross sections of the Mg/Al joints were prepared for microstructural analysis. The samples were ground and polished by abrasive papers and diamond polishing paste, following standard metallographic procedure. The micrographs of the full section of the welds were taken by a camera installed in the optical microscope. The microstructure of the welds was observed under a scanning electron microscope (SEM) (FEI Quanta 250F environment scanning electronic telescope) equipped with an energy dispersive x-ray spectrometer (EDS). The composition and distribution of the IMCs present in the joints were determined by EDS. Micro-hardness tests were carried out by a Vickers hardness tester (HVS-1000Z) with 0.98 N.
3 Results and Discussion
3.1 Macrostructure of Mg/Al Joint
The initial observation of the results indicates that Mg and Al alloys can be successfully welded by CW laser welding with brass foil. The appearance of the Mg/Al joint with brass interlayer can be seen in Fig. 2. The micrograph shows a smooth weld seam with no visible defects. Due to the small laser beam diameter (192 μm) the width of weld seam is extraordinary small, nearly 1 mm wide, which is much smaller than the width of the weld seams produced by the arc welding processes, normally (10 mm wide).
The cross section of the weld is shown in Fig. 3. The weld seam is 943.3 μm wide and 1450.6 μm deep, which means that the weld is not fully penetrating. It is also clear that the microstructure within the melt pool is not uniform because different zones with different colours can be observed under the optical microscope. The dark, light black and white zones are set as zone A, B, C, respectively. The EDS elemental mapping is presented in Fig. 4(b), (c). It is clearly seen that every element is unevenly distributed within the weld pool. Mg diffused into Al substrate and was mixed with Al. The elements from the interlayer, Cu and Zn, are evenly dispersed in the weld. The uneven distribution of each element explains the distinct zones with different colours visible in the micrograph. The chemical composition of each zone was investigated by SEM and EDS analysis. The results are discussed as follows.
3.2 Microstructure of Mg/Al Joint
Figure 5(a) shows the SEM micrographs of zone A in Fig. 3. Figure 5(b) presents the microstructure of the interface and bottom of the weld. The micrographs with higher magnification of zones I, II, III in Fig. 5(b) are shown in Fig. 5(c), (d), (e), respectively. The chemical composition of the points 1 to 6 in Fig. 6 is listed in Table 3. The grey dendritic crystal shown in Fig. 5(a) (point 1) is composed by 76.8 at % Mg, 20 at % Al, 1.6 at % Zn and 1.6 at % Cu. This phase has been identified as Mg-based solid solution and Mg-Al eutectic structure, according to the Mg-Al binary phase diagram (see Fig. 6). According to Fig. 5(c), the microstructure of zone I (zone B in Fig. 3) is mainly composed by a continuous IMC with dendritic structure, identified as Al12Mg17. However, eutectic structures were found to segregate the continuous dendrite to a dispersed and small size dendrite matrix. It can be indicative that the Cu and Zn has a high tendency to form the eutectic dendritic structures. Figure 5(d) shows the microstructure of the bottom of weld which turned to be eutectic dendritic corresponding to zone C in Fig. 3. Point 3 is composed by 19.4 at % Mg, 75.7 at % Al, 1.5 at % Zn, and 3.4 at % Cu, which is considered as Al-based solution and Al3Mg2 IMCs. The content of Cu in point 3 is higher than that in point 1. That could be explained by the solubility of Cu in Al to be higher than that in Mg. More Cu has been dissolved in Al solution. The composition in point 4 is 36.4 at % Mg, 59.4 at % Al, 1.5 at % Zn and 2.7 at % Cu corresponding to Mg based solution and Al12Mg17 eutectic structure. The magnified morphological features of zone III is presented in Fig. 5(e), which shows two parallel structures with different morphologies. In point 5, the microstructure has lamellar eutectic structures regarded as Mg-Al eutectic (Al3Mg2, Al12Mg17 and Mg based solution). In addition, the microstructure in Point 6 is a cellular crystal with composition of 54.7 at % Mg, 41.6 at % Al, 2.1 at % Zn and 1.6 at % Cu, which can be considered as Mg based solution and Al17Mg12.
It can be concluded that the addition of 0.5 mm brass interlayer could not prevent the diffusion of Mg and Al due to the full fusion of both alloys, Mg and Al. The addition of Cu and Zn element promoted the formation of branch crystals. In Fig. 3, the darker phase corresponded to higher content of Mg. Hence, the darkness feature in Fig. 4 (zone A) is Mg based solution and eutectic structure. The light dark feature in zone B in Fig. 3 is a mixture of Mg and Al which corresponds to Mg-Al IMCs. The white structures in zone C of Fig. 3 were Al based solution and eutectic structures.
3.3 Micro-hardness Analysis
The micro-hardness distribution of the weld seam has an important effect on the performance of the joint. Based on the micro-hardness of the weld it is possible to infer the strength and identify the weakest points on the joints. Figure 7(c) shows the direction and relative position of the indentations to the weld pool. The micro-hardness distribution along the vertical path, represented by line 1, is shown in Fig. 7(a), while the micro-hardness distribution along the horizontal path, represented by line 2 is drawn in Fig. 7(b). In Fig. 7(a), the micro-hardness in the middle of the weld seam is higher, above 300 HV, than that in the top and bottom of the weld seam. According to the previous analysis of the microstructure, the phase composition in the top of the weld seam is Mg-based solution and eutectic structure. Therefore, the micro-hardness in this zone is lower than others but higher than that of Mg substrate. The feature in the middle of the weld is a mixture of Mg and Al as a form of Mg and Al IMCs which explains the higher micro-hardness. However, the value of the micro-hardness in the middle of the weld is not constant. The drop-down values confirms that the phase composition is not continuous. In the Al side, the average micro-hardness of the weld is lower due to the formation of Al based solution and eutectic structures.
In Fig. 7(b), the micro-hardness of weld seam near fusion line is about 150 HV, which is lower than the value in middle of weld seam but higher than that of the Al alloy. One possible reason is that in that zone the branch crystal is an Al based solution which has a relatively low value of micro-hardness. This can have a positive impact on the toughness of Mg/Al joint. In the middle of the weld, the micro-hardness reaches just above 300 HV due to the formation of Mg/Al IMCs.
4 Conclusion
AZ31B Mg and 1060 Al thin sheets were successfully joined by CW laser micro-welding using Cu/Zn composite interlayer. The addition of 0.05 mm thick Cu/Zn interlayer could not avoid the formation of Mg/Al IMCs but refined the microstructure of weld seam (improve the formation of dendritic structure), which can improve the toughness of Mg/Al joints.
The microstructure of weld seam was uneven and formed by different phases. In the top of weld, zone A was composed of Mg-based solution, zone B was composed of Mg/Al IMCs and zone C composed of Al-based solution.
The distribution of IMCs in the weld seam affects the micro-hardness. The micro-hardness in zone A, top of the weld pool, was lower than that of the Mg and Al mixture region composed of Mg/Al IMCs. The micro-hardness on the sides of the weld seam was lower than that in the middle of weld due to the formation of solid solution, which indicates that the increasing number of solid solution can improve the toughness of Mg/Al joint.
References
Schubert, E., Klassen, M., Zerner, I., Walz, C., Sepold, G.: Light-weight structures produced by laser beam joining for future applications in automobile and aerospace industry. J. Mater. Proc. Tech. 115, 2–8 (2001)
Miller, W.S., Zhuang, L., Bottema, J., Wittebrood, A.J., De Smet, P., Haszler, A., Vieregge, A.: Recent development in aluminum alloys for the automotive industry. Mater. Sci. Eng., A 280, 37–49 (2000)
Mordike, B.L., Ebert, T.: Magnesium: properties-applications-potential. Mater. Sci. Eng., A 302, 37–45 (2001)
Zhang, H.T., Dai, X.Y., Feng, J.C.: Joining of aluminum and magnesium via pre-roll-assisted A-TIG welding with Zn interlayer. Mater. Lett. 122, 49–51 (2014)
Macwan, A.: D.L. Chen.: Ultrasonic spot welding of rare-earth containing ZEK100 magnesium alloy to 5754 aluminum alloy. Mater. Sci. Eng., A 666, 139–148 (2016)
Wang, J., Feng, J.C., Wang, Y.X.: Microstructure of Al–Mg dissimilar weld made by cold metal transfer MIG welding. Mater. Sci. Tech. 24, 827–831 (2008)
Liu, L., Wang, H.: Microstructure and Properties Analysis of Laser Welding and Laser Weld Bonding Mg to Al Joints. Meta. Mater. Trans. A 42, 1044–1050 (2011)
Scherm, F., Bezold, J., Glatzel, U.: Laser welding of Mg alloy MgAl3Zn1 (AZ31) to Al alloy AlMg3 (AA5754) using ZnAl filler material. Sci. Tech. Weld. Join. 17, 364–367 (2012)
Liu, L.M., Liu, X.J., Liu, S.H.: Microstructure of laser-TIG hybrid welds of dissimilar Mg alloy and Al alloy with Ce as interlayer. Scrip. Mater. 55, 383–386 (2006)
Liang, Z., Qin, G., Wang, L., Meng, X., Li, F.: Microstructural characterization and mechanical properties of dissimilar friction welding of 1060 aluminum to AZ31B magnesium alloy. Mater. Sci. Eng., A 645, 170–180 (2015)
Champagne III, V.K., West, M.K., Rokni, M.R., Curtis, T., Champagne Jr., V., McNally, B.: Joining of Cast ZE41A Mg to wrought 6061 al by the cold spray process and friction stir welding. J. Therm. Spray. Tech. 25, 143–159 (2016)
Shang, J., Wang, K.H., Zhou, Q., Zhang, D.K., Huang, J., Ge, J.Q.: Effect of joining temperature on microstructure and properties of diffusion bonded Mg/Al joints. Trans. Non. Metal. Soc. China 22, 1961–1966 (2012)
Meco, S., Ganguly, S., Williams, S., Mcpherson, N.: Effect of laser processing parameters on the formation of intermetallic compounds in Fe-Al dissimilar welding. J. Mater. Per. Eng. 23, 3361–3370 (2014)
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2017 Springer Nature Singapore Pte Ltd.
About this paper
Cite this paper
Gao, Q., Meco, S., Wang, K., Guo, S. (2017). Light-Weight Mg/Al Dissimilar Structures Welded by CW Laser for Weight Saving Applications. In: Fei, M., Ma, S., Li, X., Sun, X., Jia, L., Su, Z. (eds) Advanced Computational Methods in Life System Modeling and Simulation. ICSEE LSMS 2017 2017. Communications in Computer and Information Science, vol 761. Springer, Singapore. https://doi.org/10.1007/978-981-10-6370-1_35
Download citation
DOI: https://doi.org/10.1007/978-981-10-6370-1_35
Published:
Publisher Name: Springer, Singapore
Print ISBN: 978-981-10-6369-5
Online ISBN: 978-981-10-6370-1
eBook Packages: Computer ScienceComputer Science (R0)