Abstract
Silicate slags are widely used in many pyrometallurgical processes. The physiochemical properties of the slags, particularly viscosity, are closely related to their internal structures at operating conditions. To fundamentally investigate the correlation between slag structures and viscosities, the glassy samples in SiO2-CaO, SiO2-CaO-MgO and SiO2-CaO-Al2O3 systems were prepared by directly quenching to water. The quenched slags that maintain structures at high temperature were analyzed quantitatively by Raman spectrometer. The appropriate conditions of Raman spectroscopy measurements have been evaluated to obtain a better spectra for quantitative analysis. The proportions of four types of Si with different coordination can be clearly revealed from the analyses of the Raman peaks. The viscosities of the slags are correlated with the changes of the characteristic peak positions and areas.
Access provided by Autonomous University of Puebla. Download to read the full chapter text
Chapter PDF
Similar content being viewed by others
References
Paul Mcmillan, “Structural studies of silicate glasses and melts applications and limitations of Raman spectroscopy”, American Mineralogist, 69 (1984), 622–644.
Toshiharu Furukawa, et al, “Raman spectroscopic investigation of the structure of silicate glasses. III. Rman intensities and structural units in sodium silicate glasses”, The Journal of Chemical Physics, 75(1981), 3226–3237.
F.L. Galeener, “Planar rings in glasses”, Solid state Communications, 44 (1982), 1037–1040.
C.D. Yin, “Structural analysis of CaSiO3 glass by X-Ray diffraction and Raman spectroscopy”, Journal of Non-Crystalline Solid, 80 (1986), 167–174.
Corinne Remy, Bruno Reynard and Michel Madon, “Raman spectroscopic investigations of dicalcium silicate: polymorphs and high-temperature phase transformation”, 80(1997), 413–423.
Hirotaka Fujimori, et al, “ Vibrational spectra of Ca3SiO5: Ultraviolet laser Raman spectroscopy at high temperature”, Communications of the American Ceramic Society, 88 (2005), 1995–1998.
Mao Chen and Baojun Zhao, “Phase equilibrium studies of “Cu2O-SiO2-Al2O3 system in equilibrium with metallic copper”, Journal of the American Ceramic Society, 96 (2013), 3613–3636.
Kemmer G and Keller S, “Nonlinear least-squares data fitting in Excel spreadsheets”, Nature Protocols, 5(2010), 267–281.
G. Urbain and Y. Bottinga, “Viscosity of liquid silica, silicates and alumino-silicates”, Geochimica et cosmochimica acta, 46 (1982), 1061–1073.
T. Licko and V. Danek, “Viscosity and structure of melts in the system CaO-MgO-SiO2”, Physics and Chemistry of Glasses, 77 (1986), 22–26.
Tunezo. Saito and Yasuji Kawai, “On the viscosities of molten slags. I viscosities of CaO-SiO2-Al2O3 slags”, The research institute of mineral dressing and metallurgy, 1951, 492–501.
Author information
Authors and Affiliations
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2016 TMS (The Minerals, Metals & Materials Society)
About this paper
Cite this paper
Han, C., Chen, M., Rasch, R., Yu, Y., Zhao, B. (2016). Structure Studies of Silicate Glasses by Raman Spectroscopy. In: Reddy, R.G., Chaubal, P., Pistorius, P.C., Pal, U. (eds) Advances in Molten Slags, Fluxes, and Salts: Proceedings of the 10th International Conference on Molten Slags, Fluxes and Salts 2016. Springer, Cham. https://doi.org/10.1007/978-3-319-48769-4_18
Download citation
DOI: https://doi.org/10.1007/978-3-319-48769-4_18
Publisher Name: Springer, Cham
Print ISBN: 978-3-319-48625-3
Online ISBN: 978-3-319-48769-4
eBook Packages: Chemistry and Materials ScienceChemistry and Material Science (R0)